• Nuclear Engineering and Technology
• /
• 제47권6호
• /
• pp.712-718
• /
• 2015

Cast duplex stainless steels are susceptible to thermal aging during long-term service at temperatures ranging from $280^{\circ}C$ to $450^{\circ}C$. To analyze the effect of thermal aging on leak-before-break (LBB) behavior, three-dimensional finite element analysis models were built for circumferentially cracked pipes. Based on the elasticeplastic fracture mechanics theory, the detectable leakage crack length calculation and J-integral stability assessment diagram approach were carried out under different bending moments. The LBB curves and LBB assessment diagrams for unaged and thermally aged pipes were constructed. The results show that the detectable leakage crack length for thermally aged pipes increases with increasing bending moments, whereas the critical crack length decreases. The ligament instability line and critical crack length line for thermally aged pipes move downward and to the left, respectively, and unsafe LBB assessment results will be produced if thermal aging is not considered. If the applied bending moment is increased, the degree of safety decreases in the LBB assessment.

• Nuclear Engineering and Technology
• /
• 제43권6호
• /
• pp.557-566
• /
• 2011

A cold spray coating (CSC) of copper was studied for its application to a high-level radioactive waste (HLW) disposal canister. Several copper coatings of 10 mm thick were fabricated using two kinds of copper powders with different oxygen contents, and SS 304 and nodular cast iron were used as their base metal substrates. The fabricated CSC coppers showed a high tensile strength but were brittle in comparison with conventional non-coating copper, hereinafter defined to as "commercial copper". The corrosion behavior of CSC coppers was evaluated by comparison with commercial coppers, such as extruded and forged coppers. The polarization test results showed that the corrosion potential of the CSC coppers was closely related to its purity; low-purity (i.e., high oxygen content) copper exhibited a lower corrosion potential, and high-purity copper exhibited a relatively high corrosion potential. The corrosion rate converted from the measured corrosion current was not, however, dependent on its purity: CSC copper showed a little higher rate than that of commercial copper. Immersion tests in aqueous HCl solution showed that CSC coppers were more susceptible to corrosion, i.e., they had a higher corrosion rate. However, the difference was not significant between commercial copper and high-purity CSC copper. The decrease of corrosion was observed in a humid air test presumably due to the formation of a protective passive film. In conclusion, the results of this study indicate that CSC application of copper could be a useful option for fabricating a copper HLW disposal canister.

• 생태와환경
• /
• 제38권4호통권114호
• /
• pp.482-493
• /
• 2005

본 연구의 목적은 2005년 6-9월까지 38개 조사지점을 대상으로 하여 채집된 어류의 종 수 및 개체 수 풍부도에 대란 전통적 채집방법 (주로, 투망 및 족대 이용)및 전기충격기를 이용하는 방법의 조사 효율성을 평가하는 것이었다. 채집도구는 전기충격기를 이용하는 방법 (EM), 전통적인 조사법 (CM) 및 이 두 가지 방법을 조합하는 기법 (CT)의 3가지로 구분하여 통계적 유의성 차이를 비교 ${\cdot}$ 검토하였다. CM기법과 EM기법사이의 어종 구성도에 있어서 뚜렷한 차이는 미꾸라지 및 참종개와 같은 저서어종 (Benthic species) 및 돌로 된 하상을 선호하는 꺽지와 같은 종에서 나타났다. 이런종들의 출현빈도는 CM기법 보다는 EM기법에 의해 통계적 유의성이 높게 나타나 기존의 조사기법을 그대로 이용할 경우 저서성 어류 혹은 돌을 선호하는 종 (Lithophilic species)의 풍부도 산정시 과소평가되는 것으로 나타났다. 한편, 피라미와 갈겨니 같은 수층종(Water column species)은 CM기법 이용 시 개체 수 증가가 뚜렷하여 이런 종류의 개체군은 과대평가 될 수 있는 것으로 나타났다. 초강천, 유구천, 대전천 및 갑천 수계의 통계적 t-검정 결과에 따르면, 이들 모든 하천에서 종 수 및 개체 수는 CM기법보다는 CT기법에 의하여 통계적으로 높게 나타났다 (t 값 =2.806-6.896, p 값<0.05, n = 5-14). 마찬가지로 계절별 통계 분석에서도 두 가지 기법 사이에 통계적 유의성이 크게 나타났다 (p 값< 0.001,n = 10-24). 이러한 연구 결과는 전기충격기를 이용한 어류채집방법이 기존의 방법에 추가되지 않는다면 실제 수환경내의 어류 개체군 및 군집분석은 과소평가되며, 저서성종 혹은 돌이나 암반을 선호하는 종은 분석에서 배제되는 것으로 나타났다. 즉, 이러한 결과는 궁극적으로 채집오류는 물론이고 어류상, 개체군 및 군집풍부도 산정 시 큰 오류를 가져오는 것으로 나타났다. 결론적으로, 우리나라에서 어류조사 시 기존의 방법과 함께 전기충격기 방법의 새로운 도입은 실제 어류개체군 및 군집에 대한 과소평가의 분석오류를 감소시킬 것으로 사료되는 바. 북미 및 유럽에서 가장 보편적으로 사용하는 전기충격 채집법은 환경부 혹은 해양수산부의 어류 현장 지침서에 추가되어야 할 것으로 사료된다.