• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.141-142
• /
• 2005

To investigate the ZnO thin films which is interested in the next generation of short wavelength LEDs and Lasers, our ZnO thin films were deposited by RF sputtering system. At sputtering process of ZnO thin films, substrate temperature, work pressure respectively is $300^{\circ}C$ and 5.2 mTorr, and the purity of target is ZnO 5N. The thickness of ZnO thin films was about $1.9{\mu}m$ at SEM analysis after sputtering process. Phosphorus (P) and arsenic (As) were diffused into ZnO thin films sputtered by RF magnetron sputtering system in ampoule tube which was below $5\times10^{-7}$ Torr. The dopant sources of phosphorus and arsenic were $Zn_3P_2$ and $ZnAs_2$. Those diffusion was perform at 500, 600, and $700^{\circ}C$ during 3hr. We find the condition of p-type ZnO whose diffusion condition is $700^{\circ}C$, 3hr. Our p-type ZnO thin film has not only very high carrier concentration of above $10^{19}/cm^3$ but also low resistivity of $5\times10^{-3}{\Omega}cm$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.132-132
• /
• 2000

Cu는 Al에 비하여 낮은 저항(1.8 $\mu$$\Omega$-cm)과 높은 EM 저항성을 가지고 있어 미래의 고속 ULSI 배선물질로 그 중요성이 더욱 증가되고 있으며, 현재까지 많은 연구가 진행되고 있다. 따라서, 본 논문에서는 이러한 방법들을 고려하여 CVD Cu의 문제점인 낮은 성장률의 개선과 Cu 박막의 특성을 향상하고자 수소 플라즈마 공정을 이용하여 plasma 전처리가 초기 Cu 핵생성에 미치는 영향에 대하여 연구하였다. 본 실험에 사용된 장비는 Cu RPCVD/MOCVD이다. 초기 Cu 핵의 생성에 있어서의 수소 플라즈마의 효과를 조사하기 위하여 다음과 같은 3가지의 방법으로 행하였다. 첫 번째는 Cu 박막 형성에서 플라즈마를 사용하지 않은 방법, 두 번째는 플라즈마 전처리공정을 행한 뒤, Cu 박막 증착시 플라즈마는 사용하지 않은 방법, 세 번재는 플라즈마 전처리공저을 행한 뒤 Cu 증착시에도 플라즈마를 사용한 방법이다. 이 세가지 방법의 핵생성 차이를 분석하기 위해서 각각 10초, 20초, 40초 증착시킨 후 grain의 크기와 개수를 비교하였다. 또한 플라즈마의 power에 따른 Cu 핵생성율도 조사하였다. 수소 전처리동안 working pressure는 10분 동안 1 torr로 유지되었으며 substrate의 온도는 20$0^{\circ}C$, r.f.power는 100watt로 설정하였다. Cu RPCVD의 증착조건은 r.f.power는 10watt, substrate의 온도는 20$0^{\circ}C$, gas pressure는 1 torr, Ar carrier gas는 50sccm, hydrogen processing gas는 100sccm, bubbler 온도는 4$0^{\circ}C$, gas line의 온돈느 6$0^{\circ}C$, shower head의 온도는 $65^{\circ}C$로 설정하였다. 증착된 Cu 박막은 SEM, XRD, AFM를 통해 제작된 박막의 특성을 비교.분석하였다. 초기 plasma 처리를 한 경우에는 그림 1에서와 같이 현저히 증가한 초기 구리 입자들이 관측되었으며, 이는 도상 표면에 활성화된 catalytic site의 증가에 기인한다고 보여진다. 이러한 특성은 Cu films의 성장률을 향상시키고, 또한 voids를 줄여 전기적 성질 및 surface morphology를 향상시키는 것으로 나타났다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.141-141
• /
• 2010

The effect of thermal anneal on the characteristics of structural properties and the enhancement of luminescence and photovoltaic (PV) characteristics of silicon-rich silicon-nitride films were investigated. By using an ultra high vacuum ion beam sputtering deposition, B-doped silicon-rich silicon-nitride (SRSN) thin films, with excess silicon content of 15 at. %, on P-doped (n-type) Si substrate was fabricated, sputtering a highly B doped Si wafer with a BN chip by N plasma. In order to examine the influence of thermal anneal, films were then annealed at different temperature up to $1100^{\circ}C$ under $N_2$ environment. Raman, X-ray diffraction, and X-ray photoemission spectroscopy did not show any reliable evidence of amorphous or crystalline Si clusters allowing us concluding that nearly no Si nano-cluster could be formed through the precipitation of excess Si from SRSN matrix during thermal anneal. Instead, results of Fourier transform infrared and X-ray photoemission spectroscopy clearly indicated that defective, amorphous Si-N matrix of films was changed to be well-ordered thanks to high temperature anneal. The measurement of spectral ellipsometry in UV-visible range was carried out and we found that the optical absorption edge of film was shifted to higher energy as the anneal temperature increased as the results of thermal anneal induced formation of $Si_3N_4$-like matrix. These are consistent with the observation that higher visible photoluminescence, which is likely due to the presence of Si-N bonds, from anneals at higher temperature. Based on these films, PV cells were fabricated by the formation of front/back metal electrodes. For all cells, typical I-V characteristic of p-n diode junction was observed. We also tried to measure PV properties using a solar-simulator and confirmed successful operation of PV devices. Carrier transport mechanism depending on anneal temperature and the implication of PV cells based on SRSN films were also discussed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.240.2-240.2
• /
• 2013

The device scale of flash memory was confronted with quantum mechanical limitation. The next generation memory device will be required a break-through for the device scaling problem. Especially, graphene is one of important materials to overcome scaling and operation problem for the memory device, because ofthe high carrier mobility, the mechanicalflexibility, the one atomic layer thick and versatile chemistry. We demonstrate the hybrid memory consisted with the metal-oxide quantum dots and the mono-layered graphene which was transferred to $SiO_2$ (5 nm)/Si substrate. The 5-nm thick secondary $SiO_2$ layer was deposited on the mono-layered graphene by using ultra-high vacuum sputtering system which base pressure is about $1{\times}10^{-10}$ Torr. The $In_2O_3$ quantum dots were distributed on the secondary $SiO_2$2 layer after chemical reaction between deposited In layer and polyamic acid layer through soft baking at $125^{\circ}C$ for 30 min and curing process at $400^{\circ}C$ for 1 hr by using the furnace in $N_2$ ambient. The memory devices with the $In_2O_3$ quantum dots on graphene monolayer between $SiO_2$ thin films have demonstrated and evaluated for the application of next generation nonvolatile memory device. We will discuss the electrical properties to understating memory effect related with quantum mechanical transport between the $In_2O_3$ quantum dots and the Fermi level of graphene layer.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2012.05a
• /
• pp.121-122
• /
• 2012

Iron-excess gallium ferrite, $Ga_{0.6}Fe_{1.4}O_3$ (GFO), is known to have room-temperature ferromagnetic phases and potentially exhibit ferroelectricity as well [1]. But, leaky polarization-electric field (PE) hysteresis curves of the GFO thin film are hurdle to prove its spontaneous polarization, in other words, ferroelecticity. One of the reasons that the GFO films have leaky PE hysteresis loop is carrier hopping between $Fe^{2+}$ and $Fe^{3+}$ sites due to oxygen deficiency. We focus on reducing conducting current by substituting divalent cations at $Fe^{2+}$ sites. GFO thin films were grown epitaxially along b-axis normal to $SrRuO_3/SrTiO_3$ (111) substrates by pulsed laser deposition. Current density of the ion-substituted GFO thin films was reduced by $10^3$ or more. Ferroelectric properties of the ion-substituted GFO thin films were measured using macroscopic and microscopic schemes. In particular, local ferroelectric properties of the GFO thin films were exhibited and their remnant polarization and piezoelectric d33 coefficient were obtained.

• Nano
• /
• v.13 no.10
• /
• pp.1850124.1-1850124.12
• /
• 2018

$TiO_2$ films were deposited from oxygen/titanium tetraisopropoxide (TTIP) plasmas at low temperature by Helicon-PECVD at floating potential ($V_f$) or substrate self-bias of -50 V. The influence of titanium precursor partial pressure on the morphology, nanostructure and optical properties was investigated. Low titanium partial pressure ([TTIP] < 0.013 Pa) was applied by controlling the TTIP flow rate which is introduced by its own vapor pressure, whereas higher titanium partial pressure was formed through increasing the flow rate by using a carrier gas (CG). Then the precursor partial pressures [TTIP+CG] = 0:027 Pa and 0.093 Pa were obtained. At $V_f$, all the films exhibit a columnar structure, but the degree of inhomogeneity is decreased with the precursor partial pressure. Phase transformation from anatase ([TTIP] < 0.013 Pa) to amorphous ([TTIP+CG] = 0:093 Pa) has been evidenced since the $O^+_2$ ion to neutral flux ratio in the plasma was decreased and more carbon contained in the film. However, in the case of -50 V, the related growth rate for different precursor partial pressures is slightly (~15%) decreased. The columnar morphology at [TTIP] < 0.013 Pa has been changed into a granular structure, but still homogeneous columns are observed for [TTIP+CG] = 0:027 Pa and 0.093 Pa. Rutile phase has been generated at [TTIP] < 0:013 Pa. Ellipsometry measurements were performed on the films deposited at -50 V; results show that the precursor addition from low to high levels leads to a decrease in refractive index.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.4
• /
• pp.431-437
• /
• 2022

As one of the most hazardous and deadliest pathogens, Listeria monocytogenes (LM) posed various serious diseases to the human being, thus designing effective strategy for its detection is of great significance. In this work, by preparing Ti₃C₂T_x MXenes nanoribbon (Ti₃C₂T_xR) as carrier and selecting thionine (Th) acted simultaneously as signal probe and functional monomer, a LM pathogen-imprinted polymers (PIP) integrated probe electrochemical sensor was design to monitor LM for the first time, that was carried out through the electropolymerization of Th on the Ti₃C₂T_xR/GCE surface in the existence of LM. Upon eluting the templates from the LM imprinted cavities, the fabricated PIP/Ti₃C₂T_xR/GCE sensor can rebound LM cells effectively. By recording the peak current of Th as the response signal, it can be weakened when LM cell was re-bound to the LM imprinted cavity on PIP/Ti₃C₂T_xR/GCE, and the absolute values of peak current change increase with the increasement of LM concentrations. After optimizing three key parameters, a considerable low analytical limit (2 CFU mL^-1) and wide linearity (10-10⁸ CFU mL^-1) for LM were achieved. In addition, the experiments demonstrated that the PIP/Ti₃C₂T_xR sensor offers satisfactory selectivity, reproducibility and stability.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.2
• /
• pp.197-206
• /
• 1999

The stochiometric mixture of evaporating materials for the $AgInSe_2$single crystal thin films were prepared from horizontal furnace. Using extrapolation method of X-ray diffraction patterns for the $AgInSe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0$ and $C_0$ were 6.092 $\AA$ and 11.688 $\AA$, respectively. To obtain the single crystal thin films of AgInSe$_2$, the mixed crystal was deposited on thoroughly etched semi-insulator GaAs(100) substrate by HWE system. The source and substrate temperature were fixed to $610^{\circ}C$ and $450^{\circ}C$ respectively, and the thickness of the single thin films was obtained to 3.8 $\mu\textrm{m}$. The crystallization of single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray dirrfaction (DCXD). The Hall effect was measured by the method of van der Pauw and carrier density and mobility dependence on temperature were studied. The carrier density and mobility of $AgInSe_2$single crystal thin films deduced from Hall data are $9.58{\times}10^{22} electron/m^3,\; 3.42{\times}10^{-2}m^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $AgInSe_2$single crystal thin film, the spin orbit coupling $\Delta$So and the crystal field splitting $\Delta$Cr were obtained to 0.29 eV and 0.12 eV at 20 K respectively. From PL peaks measured at 20 K, 881.1 nm (1.4071 eV) and 882.4 nm (1.4051 eV) mean $E_x^U$ the upper polariton and $E_x^L$ the lower polariton of the free exciton $(E_x)$, also 884.1 nm (1.402 eV) express $I_2 peak of donor-bound exciton emission and 885.9 nm (1.3995 Ev) emerges $I_1$ peak of acceptor-bound exciton emission. In addition, the peak observed at 887.5 nm (1.3970 eV) was analyzed to be PL peak due to DAP.

• Korean Journal of Materials Research
• /
• v.11 no.5
• /
• pp.419-426
• /
• 2001

The stochiometric $AgGaSe_2$ polycrystalline mixture of evaporating materials for the $AgGaSe_2$ single crystal thin film was prepared from horizontal furnace. To obtain the single crystal thin films, $AgGaSe_2$ mixed crystal and semi-insulating GaAs(100) wafer were used as source material and substrate for the Hot Wall Epitaxy (HWE) system, respectively. The source and substrate temperature were fixed at$ 630^{\circ}C$ and $420^{\circ}C$, respectively. The thickness of grown single crystal thin films is 2.1$\mu\textrm{m}$. The single crystal thin films were investigated by photoluminescence and double crystal X-ray diffraction(DCXD) measurement. The carrier density and mobility of AgGaSe$_2$ single crystal thin films measured from Hall effect by van der Pauw method are $4.89\Times10^{17}$ cm$^{-3}$ , 129cm2/V.s at 293K, respectively. From the Photocurrent spectrum by illumination of perpendicular light on the c-axis of the AgGaSe$_2$ single crystal thin film, we have found that the values of spin orbit splitting $$\Delta$S_{o}$ and the crystal field splitting $\Delta$C$_{r}$, were 0.1762eV and 0.2474eV at 10K, respectively. From the photoluminescence measurement of AgGaSe$_2$ single crystal thin film, we observed free excision (EX) observable only in high quality crystal and neutral bound exciton ($D^{o}$ , X) having very strong peak intensity. And, the full width at half maximum and binding energy of neutral donor bound excition were 8mev and 14.1meV, respectively. By Haynes rule, an activation energy of impurity was 141 meV.ion energy of impurity was 141 meV.

• Journal of the Korean Vacuum Society
• /
• v.15 no.6
• /
• pp.563-575
• /
• 2006

Ti(C,N) films are synthesized by pulsed DC plasma enhanced chemical vapor deposition (PEMOCVD) using metal-organic compounds of tetrakis diethylamide titanium at $200-300^{\circ}C$. To compare plasma parameter, in this study, $H_2$ and $He/H_2$ gases are used as carrier gas. The effect of $N_2\;and\;NH_3$ gases as reactive gas is also evaluated in reduction of C content of the films. Radical formation and ionization behaviors in plasma are analyzed in-situ by optical emission spectroscopy (OES) at various pulsed bias voltages and gas species. He and $H_2$ mixture is very effective in enhancing ionization of radicals, especially for the $N_2$. Ammonia $(NH_3)$ gas also highly reduces the formation of CN radical, thereby decreasing C content of Ti(C, N) films in a great deal. The microhardness of film is obtained to be $1,250\;Hk_{0.01}\;to\;1,760\;Hk_{0.01}$ depending on gas species and bias voltage. Higher hardness can be obtained under the conditions of $H_2\;and\;N_2$ gases as well as bias voltage of 600 V. Hf(C, N) films were also obtained by pulsed DC PEMOCYB from tetrakis diethyl-amide hafnium and $N_2/He-H_2$ mixture. The depositions were carried out at temperature of below $300^{\circ}C$, total chamber pressure of 1 Torr and varying the deposition parameters. Influences of the nitrogen contents in the plasma decreased the growth rate and attributed to amorphous components, to the high carbon content of the film. In XRD analysis the domain lattice plain was (111) direction and the maximum microhardness was observed to be $2,460\;Hk_{0.025}$ for a Hf(C,N) film grown under -600 V and 0.1 flow rate of nitrogen. The optical emission spectra measured during PEMOCVD processes of Hf(C, N) film growth were also discussed. $N_2,\;N_2^+$, H, He, CH, CN radicals and metal species(Hf) were detected and CH, CN radicals that make an important role of total PEMOCVD process increased carbon content.