• Journal of Sensor Science and Technology
• /
• v.8 no.1
• /
• pp.24-31
• /
• 1999

Ammonia gas sensors were fabricated with ZnO-based thin films grown by RF-magnetron sputtering method. The films which were doped with $MoO_3$ catalysts of various weight percents were grown in different sputtering gases to fabricate the sensors with a high sensitivity, low working temperature and rapid response time. To improve electrical stability, the films were aged in various conditions. The sensors doped with the catalysts and grown in oxygen sputtering gas showed the improvement of sensitivity. These exhibited the increase of surface carrier concentration and electron mobility. The sensor with 0.875wt.% $MoO_3$ catalysts showed the maximum sensitivity of 70 in ammonia gas concentration of 160 ppm at a working temperature of $300^{\circ}C$. The sensor which is aged at $330^{\circ}C$ for 72hrs in oxygen ambient exhibited tourer sensitivity of 57, but more stable properties, excellent linearity.

• Journal of the Korean Ceramic Society
• /
• v.48 no.4
• /
• pp.328-333
• /
• 2011

The influence of Al-doped ZnO (AZO) thin films degraded under high temperature and damp heat on the performance deterioration of Cu(In,Ga)$Se_2$ (CIGS) solar cells was investigated. CIGS solar cells with AZO/CdS/CIGS/Mo structure were prepared on glass substrate and exposed to high temperature ($85^{\circ}C$) and damp heat ($85^{\circ}C$/85% RH) for 1000 h. As-prepared CIGS solar cells had 64.91% in fill factor (FF) and 12.04% in conversion efficiency. After exposed to high temperature, CIGS solar cell had 59.14% in FF and 9.78% in efficiency, while after exposed to damp heat, it had 54.00% in FF and 8.78% in efficiency. AZO thin films in the deteriorated CIGS solar cells showed increases in resistivity up to 3.1 times and 4.4 times compared to their initial resistivity after 1000 h of high temperature and damp heat exposure, respectively. These results can be explained by the decreases in carrier concentration and mobility due to diffusion or adsorption of oxygen and moisture in AZO thin films. It can be inferred that decreases in FF and conversion efficiency were caused by an increase in series resistance, which resulted from an increase in resistivity of AZO thin films degraded under high temperature and damp heat.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.154-154
• /
• 2003

A stoichiometric mixture of evaporating materials for CuGaSe2 single crystal thin films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal CuGaSe2, it was found tetragonal structure whose lattice constant at and co were 5.615 ${\AA}$ and 11.025 ${\AA}$, respectively. To obtain the single crystal thin films, CuGaSe2 mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (MWE) system. The source and substrate temperatures were Slot and 450$^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (UXD). The carrier density and mobility of CuGaSe2 single crystal thin films measured with Hall effect by van der Pauw method are 5.0l${\times}$10$\^$17/ cm$\^$-3/ and 245 $\textrm{cm}^2$/V$.$s at 293K, respectively. The temperature dependence of the energy band gap of the CuGaSe2 obtained from the absorption spectra was well described by the Varshni's relation, Eg(T) = 1.7998 eV - (8.7489${\times}$10$\^$-4/ eV/K)T$^2$/(T + 335 K. After the as-grown CuGaSe2 single crystal thin films was annealed in Cu-, Se-, and Ca-atmospheres, the origin of point defects of CuGaSe2 single crystal thin films has been investigated by the photoluminescence(PL) at 10 K The native defects of V$\_$CU/, V$\_$Se/, Cu$\_$int/, and Se$\_$int/ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted CuGaSe2 single crystal thin films to an optical n-type. Also, we confirmed that Ga in CuGaSe2/GaAs did not form the native defects because Ga in CuGaSe2 single crystal thin films existed in the form of stable bonds.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.315-315
• /
• 2013

We report the electronic structure modification in the swift heavy ion (SHI) irradiated N-doped ZnO thin films prepared by RF sputtering from ZnO target in different ratio of Ar/$N_2$ gas mixture using highly pure $N_2$ gas. The different N-ZnO thin lms were then irradiated with 120 MeV Ag ion beam with different doses ranging from $1{\times}10^{11}$ to $5{\times}10^{12}$ ions/$cm^2$ and characterized by XRD and near edge X-ray absorption ne structure (NEXAFS) at N and O K-edges. The NEXAFS measurements provide direct evidence of O 2p and Zn 3d orbital hybridization and also the bonding of N ions with Zn and O ions. The minimum value of resistivity of $790{\Omega}cm$, a Hall mobility of $22cm^2V^-1s^-1$ and the carrier concentration of $3.6{\times}10^{14}cm^{-3}$ were yielded at 75% $N_2$. X-ray diffraction (XRD) measurements revealed that N-doped ZnO films had the preferential orientation of (002) plane for all samples, while crystallinity start decreasing at 32.5% $N_2$. The average crystallite size varies from 5.7 to 8.2 nm for 75% and then decreases to 7.8 nm for 80% $Ar:N_2$ ratio.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.1
• /
• pp.68-74
• /
• 2018

All transparent UV photodetector based on ZnO was fabricated with structure of NiO/ZnO/$SnO_2$/ITO by using RF and DC magnetron sputtering system. ZnO was deposited with 4 inch ZnO target (purity 99.99%) for a quality film. In order to build p-n junction up, p-type NiO was formed on n-type ZnO by using reactive sputtering method. The indium tin oxide (ITO) which is transparent conducting oxide (TCO) was applied as a transparent electrode for transporting electrons. To improve the UV photodetector performance, a functional $SnO_2$ layer was selected as an electron transporting and hole blocking layer, which actively controls the carrier movement, between ZnO and ITO. The photodetector (NiO/ZnO/$SnO_2$/ITO) shows transmittance over 50% as similar as the transmittance of a general device (NiO/ZnO/ITO) due to the high transmittance of $SnO_2$ for broad wavelengths. The functional $SnO_2$ layer for band alignment effectively enhances the photo-current to be $15{\mu}A{\cdot}cm^{-2}$ (from $7{\mu}A{\cdot}cm^{-2}$ of without $SnO_2$) with the quick photo-responses of rise time (0.83 ms) and fall time (15.14 ms). We demonstrated the all transparent UV photodetector based on ZnO and suggest the route for effective designs to enhance performance for transparent photoelectric applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.125-126
• /
• 2006

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films. $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}cm^{-3}$. $345cm^2/V{\cdot}s$ at 293 K, respectively. From the photoluminescence measurement on $CdGa_2Se_4$ single crystal thin film, we observed free excition ($E_x$) existing only high quality crystal and neutral bound exiciton ($D^{\circ},X$) having very strong peak intensity. Then. the full-width-at -half-maximum(FWHM) and binding energy of neutral donor bound excition were 8 meV and 13.7 meV, respectivity. By Haynes rule. an activation energy of impurity was 137 meV.

• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.591-595
• /
• 1998

In this work, the freestanding GaN single crystalline substrates without cracks were grown by hydride vapor phase epitaxy (HVPE) and its some properties were investigated. The GaN substrate, having a current maximum size of 350 $\mu\textrm{m}$-thickness and 100$\textrm{mm}^2$ area, were obtained by HVPE growth of thick film GaN on sapphire substrate and subsequent mechanical removal of the sapphire substrate. A lattice constant of $C_o$= 5.18486 $\AA$ and a FWHM of DCXRD was 650 arcsec for the single crystalline GaN substrate. The low temperature PL spectrum consist of three excitonic emission and a deep D- A pair recombination at 1.8eV. The Raman E, (high) mode frequency was 567$cm^{-1}$ which was the same as that of strain free bulk single crystals. The Hall mobility and carrier concentration was 283$cm^3$<\ulcornerTEX>/ V.sand 1.1$\times$$10^{18}cm^{-3}$, respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.62.2-62.2
• /
• 2011

산업화 이후, 석탄 석유를 중심으로 한 화석연료가 이산화탄소를 대량으로 배출하며 지구 온난화를 야기함에 따라, 기존의 화석연료를 대체할 청정하고 무한 재생 가능한 대체에너지로 가장 큰 기대를 받고 있는 것은 태양에너지이며, 이에 보조를 맞춰 태양광발전에 대한 연구개발이 국내외적으로 활발히 진행되고 있는 실정이다. 태양 전지는 빛 에너지를 직접 전기 에너지로 바꿔주는 소자로, 셀의 효율을 높이기 위해서는 최대한 많은 빛을 흡수시킬 수 있는 것이 중요하다. 빛의 반사를 줄이는 방법에는 texturing과 antireflecting coating이 있다. Antireflecting coating은 반도체와 공기의 중간 굴절율을 갖는 박막을 증착하여 측면 반사를 감소시킴으로서 빛의 손실을 감소시키는 역할을 한다. 과거에 반사방지막으로 가장 많이 사용되었던 물질은 SiO로써 굴절률은 1.8~1.9로서 최소의 반사율은 1% 미만이지만, 가시광선영역에서의 흡수에 의한 손실이 생기므로, SiNx가 대체 물질로 제안되었다. SiNx의 경우 굴절률이 약 1.5로서 Si에 쉽게 형성시킬 수 있고, texturing된 Si 표면에 적합하며 반사율을 10%에서 2%로 줄일 수 있는 장점을 가지고 있다. 따라서 본 연구에서는 high power, high frequency PECVD 방법으로 $SiH_4$와 $NH_3$ gas의 비율, $N_2$ carrier gas 등 공정 변수를 변화시켜 증착한 SiNx 박막의 결정학적 특성을 X-ray diffraction 분석과 XPS (X-ray photoelectron spectroscopy)를 통해 화학적 결합을 확인하였고, 이를 FT-IR (Fourier Transform-Infrared spectroscopy)를 통해 관찰한 결과와 연관시켜 분석하였다. 굴절율의 경우 ellipsometer를 이용하여 측정하였으며 위의 측정을 통하여 SiNx박막의 반사 방지막으로써의 가능성을 확인 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.257-265
• /
• 2002

A stoichiometric mixture of evaporating materials for AgInS$_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, AgInS$_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy(HWE) system. The source and substrate temperatures were 680 $^{\circ}C$ and 410 $^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of AgInS$_2$ single crystal thin films measured from Hall effect by van der Pauw method are 9.35${\times}$10$\^$16/ cm$\^$-3/ and 294 $\textrm{cm}^2$/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of the energy band gap on AgInS$_2$ single crystal thin films was found to be E$\_$g/(T) : 2.1365 eV - (9.89 ${\times}$ 10$\^$-3/ eV) T$^2$/(2930 + T). After the as-grown AgInS$_2$ single crystal thin films was annealed in Ag-, S-, and In-atmospheres, the origin of point defects of AgInS$_2$ single crystal thin films has been investigated by using the photoluminescence(PL) at 10 K. The native defects of V$\_$AG/, V$\_$S/, Ag$\_$int/, and S$\_$int/ obtained from PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the S-atmosphere converted AgInS$_2$ single crystal thin films to an optical p-type. Also, we confirmed that In in AgInS$_2$/GaAs did not form the native defects because In in AgInS$_2$ single crystal thin films did exist in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.143-143
• /
• 2010

In this study, we demonstrate that ZnO deposited onto $SiO_2$ substrates by magnetron sputtering produces p-type ZnO at higher $O_2$ pressure and n-type ZnO at lower $O_2$ pressure. We also report the effect of hydrogen peroxide ($H_2O_2$) on the stability of undoped ZnO thin films. The films were immersed in 30% $H_2O_2$ for 1 min at $30^{\circ}C$ and annealed in $O_2$at $450^{\circ}C$. The carrier concentration, mobility. and conductivity were measured by a Hall effect measurement system. The Hall measurement results for ZnO films untreated with $H_2O_2$ but annealed in $O_2$ indicate that oxygen fraction greater than ~0.5 produces undoped p-type ZnO films, whereas oxygen fraction less than ~0.5 produces undoped n-type ZnO films. This is attributed to the fact that the oxygen vacancies ($V_o$) decrease and the oxygen interstitials ($O_i$) or zinc vacancies ($V_{Zn}$) increase with increasing oxygen atoms incorporated into ZnO films during deposition and $O_2$ post-annealing.