• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.42 no.1
• /
• pp.54-63
• /
• 2010

Recently, as the function of largest supplier of biomass for "low carbon green growth", the necessity for systematic management of afforestation areas is emphasizing. The forestation of seedling, besides the afforestation cost itself, is required some additional follow-up management costs, like mowing and fertilizing of forestation area, and removal of bindweed. The mulching mat for afforestation seedlings is available for rooting of little seedlings as well as initial forestation expenses. Mulching technique is also used to control soil temperature and moisture by covering the surface of ground. In this study, the paper based-mulching film coated with biodegradable polymer and functional additive was specially produced using laboratory bar coater, and analyzed for its degradable behavior. Coating colors were prepared by dissolving PE (polyester) 80 % and PLA(polylactic acid) 20 % in chloroform and finally applied to handsheet prepared by preceding study conditions. Base paper and polymer-coated paper were artificially aged by 2 kinds of degradation methods, which are soil degradation by microorganism and light degradation by 257 nm UV wavelengths. Strength property, oxidation index and morphological property were evaluated by reduction rates of tensile strength, FTIR spectra ratio of carboxyl and carbonyl group and SEM micrograph. As these results, polymer coated-paper was superior to base paper in degradation behaviors, having results with lower reduction rate of strength properties.

• Korean Journal of Materials Research
• /
• v.20 no.11
• /
• pp.559-569
• /
• 2010

The liquid-phase sintering method was used to prepare a glass lens forming core composed of SiC-$Al_2O_3-Y_2O_3$. Spark plasma sintering was used to obtain dense sintered bodies. The sintering characteristics of different SiC sources and compositions of additives were studied. Results revealed that, owing to its initial larger surface area, $\alpha$-SiC offers sinterability that is superior to that of $\beta$-SiC. A maximum density of $3.32\;g/cm^3$ (theoretical density [TD] of 99.7%) was obtained in $\alpha$-SiC-10 wt% ($6Al_2O_3-4Y_2O_3$) sintered at $1850^{\circ}C$ without high-energy ball milling. The maximum hardness and compression stress of the sintered body reached 2870 Hv and 1110 MPa, respectively. The optimum ultra-precision machining parameters were a grinding speed of 1243 m/min, work spindle rotation rate of 100 rpm, feed rate of 0.5 mm/min, and depth of cut of $0.2\;{\mu}m$. The surface roughnesses of the thus prepared final products were Ra = 4.3 nm and Rt = 55.3 nm for the aspheric lens forming core and Ra = 4.4 nm and Rt = 41.9 for the spherical lens forming core. These values were found to be sufficiently low, and the cores showed good compatibility between SiC and the diamond-like carbon (DLC) coating material. Thus, these glass lens forming cores have great potential for application in the lens industry.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.3 no.3
• /
• pp.201-211
• /
• 2005

In this study, conventional head-end processes of spent TRISO fuel have been reviewed to develope more effective treatment methods. The main concerns in the TRISO treatment are to effectively separate the carbon and SiC contained in the TRISO particles. The crush-burn scheme which was considered in the early stages of the development has been replaced by the crush-leach process because of $^{14}C$ problems as a second waste being generated during the process. However, there are still many obstacles to overcome in the reported processes. Hence, innovative thermomechanical concepts and a molten salt electrochemical approach to breach the coating layers of the TRISO particle with a minimized amount of second waste are proposed in this paper and their principles are described in detail.

• Composites Research
• /
• v.29 no.6
• /
• pp.336-341
• /
• 2016

This paper conducted the study on the electromagnetic and mechanical applicability of CNT-coated glass fiber for wind blades. Large-size wind blade has the serious pending problems to meet the target, such as interfering radar signals, increasing weights, and increasing repair costs. In this paper, we are suggesting the CNT-coated glass fiber in order to overcome these problems. First, the CNTs were strongly coated on the surfaces of glass fiber by suggested coating process, and the CNT-coated glass fiber/epoxy composites were fabricated by Va-RTM process. We designed and fabricated a radar absorbing structure using the CNT-coated glass fiber, which showed over 90% radar absorbing performance between 8.3 and 12.1 GHz frequency. In addition, we confirmed the improvement of mechanical properties on the strength and modulus of tensile, compressive, and in-plane shear.

• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.172-176
• /
• 2005

Four nano-sized Fe-nano particle samples synthesized by Chemical Vapor Condensation (CVC) were analyzed using $M\ddot{o}ssbauer$ spectroscopy, XRD, BET and TEM. The samples were consisted as functions of carrier gas and decomposition temperature. The synthesized nanoparticles consisted of two- or three-layers with the circular shape. The average particle size was increased with increasing the decomposition temperature. At $500^{\circ}C$ for the decomposition temperature, $Fe_3C$ was formed more under the environment of CO carrier gas than that of $CH_4$. However, at $1,100^{\circ}C$, almost of Fe-nano particles were transformed into $Fe_3C$ with using both carrier gas.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.101-106
• /
• 2008

The $SnO_2$ thin films doped with Pd and CNT as $NO_2$ gas sensor were prepared by spin coating and then the $NO_2$ gas response of these films were evaluated under $1ppm{\sim}5ppm\;NO_2$ concentration and operating temperature of $200^{\circ}C$. It was found that the sensor resistance was increased with $NO_2$ exposure and $NO_2$ concentration. The 3wt% Pd doped sample showed a sensitivity of 26.5 which was 10 times higher than that of pure $SnO_2$. And also the sensitivity of CNT doped sample increased with CNT content and it had 72 when 0.225 wt% of CNT was added under 5ppm $NO_2$ concentration.

• Composites Research
• /
• v.24 no.5
• /
• pp.17-22
• /
• 2011

Recently transparent electrodes using carbon nanotube (CNT) have been studied actively to replace conventional ITO. In this work, CNT or ITO coated poly(ethylene terephthalate) (PET) were prepared by controlling the surfaces since the cohesion degree depends upon drying conditions. As transparent electrode application, 3 drying temperatures were set as 20, 80, and $120^{\circ}C$ to produce the change of surface properties. Interfacial durability and electrical properties of prepared transparent electrodes were evaluated by electrical resistance measurement. Surface change with changing drying temperature was observed by FE-SEM, whereas the transparency change was measured by UV-spectroscopy. The electronic properties of nanoparticle coated surface were evaluated using cyclic voltametry method upon the surface change with controlled drying temperature. Durability of CNT coated surfaces was better than ITO coated ease. As drying temperature increased, better coated surface was prepared due to improved cohesion among nanoparticles, which resulted in increased electrical properties.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.691-698
• /
• 2010

Magnesium hydroxide-melamine core-shell particles were prepared through the coating of melamine monomer on the surface of magnesium hydroxide in the presence of phosphoric acid. The melamine monomer was dissolved in hot water but recrystallized on the surface of magnesium hydroxide by quenching to room temperature in the presence of phosphoric acid. The core-shell particle was applied to low-density polyethylene/ ethylene vinyl acetate (LDPE/EVA) resin by melt-compounding at $180^{\circ}C$ as flame retardant. The effect of magnesium hydroxide and melamine content has been studied on the flame retardancy of the core-shell particles in LDPE/EVA resin according to the preparation process and purity of magnesium hydroxide. Magnesium hydroxide prepared with sodium hydroxide rather than with ammonia solution revealed higher flame retardancy in core-shell particles with LDPE/EVA resin. At 50 wt% loading of flame retardant, core-shell particles revealed higher flame retardancy compared to that of the exclusive magnesium hydroxide in LDPE/EVA composite, and it was possible to satisfy the V0 grade in the UL-94 vertical test. The synergistic flame retardant effect of magnesium hydroxide and melamine core-shell particles was explained as being due to the endothermic decomposition of magnesium hydroxide and melamine, which was followed by the evolution of water from the magnesium hydroxide and porous char formation due to reactive nitrogen compounds, and carbon dioxide generated from melamine.

• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.160-166
• /
• 2007

TRISO coatings on $ZrO_{2}$ surrogate kernels were conducted by a fluidized-bed chemical vapor deposition (FBCVD) method. Effects of the deposition temperature and the gas flow rate on the properties of SiC layer were investigated in the TRISO-coated particles. Deposition rate of the SiC layer decreased as the deposition temperature increased in the temperature range of $1460^{\circ}-1550^{\circ}C$. At the deposition temperature of $1550^{\circ}C$ the SiC layer contained an excess carbon, whereas the SiC layers had stoichiometric compositions at $1460^{\circ}C\;and\;1500^{\circ}C$. Hardness and elastic modulus measured by a nanoindentation method were the highest in the SiC layer deposited at $1500^{\circ}C$. The SiC layer deposited at the gas flow rate of 4000 sccm exhibited a high porosity and contained large pores more than $1{\mu}m$, being due to a violent spouting of particles. On the other hand, the SiC layer deposited at 2500 sccm revealed the lowest porosity.

• Fire Science and Engineering
• /
• v.21 no.1 s.65
• /
• pp.90-97
• /
• 2007

Combustion characteristics and toxicity of combustion gas of wallpaper samples were analyzed to evaluate the fire risk of wallpaper furnished in living space. In this study ash residue ratio was measured with high temperature electric furnace, and thermal analysis was carried out with TGA. Combustion time and smoke concentration were measured with cone heater and combustion gas analyzer. Smoke density of samples was measured using smoke chamber of ASTM E 662. The experimental results were showed as followings. Pyrolysis of silk wallpaper started at lower temperature compared to the other samples. It means that the silk wallpaper can be ignited at low heat flux and will have more fire risk than the others. Ignition time by radiation heat flux of silk wallpaper is shorter compared to the other samples, so evacuation time must be reduced. In the case of vinyl coated silk wall paper, carbon mono oxide concentration is the highest and the toxicity and damage effect to consciousness was stronger compared to the other samples. Smoke density of silk wall paper and fire retardant mixed coated silk wall paper were very high due to vinyl coating.