• Fibers and Polymers
• /
• 제2권4호
• /
• pp.178-183
• /
• 2001

A pitch precursor for a general purpose carbon fiber was prepared by condensation of pyrolized fuel oil (petroleum residual oil) with bromine under nitrogen blowing. such a condensation raised the softening point of the pitch from 4$0^{\circ}C$ to $265^{\circ}$ with a yield of 43%. The pitch precurosr showed an enhanced aromaticity and enlarged molecular size, which led to a reduction in molecular mobility and optical isotropy. The precursor was spun into fibers of $20\mu\textrm{m}$ diameter at a take-up speed of 700m/min. The fiber was stepwise stabilized in air and carbonized in Ar gas to obtain an isotropic carbon fiber. The carbon fiber exhibited tensile strengths of 500-800 ㎫though the fiber was formed via a crude method. The electric conductivity of the carbon fiber was relatively high, 2.2$\times$$10^2$S/cm, sufficient to be used as electrode materials.

• Archives of Metallurgy and Materials
• /
• 제66권4호
• /
• pp.941-946
• /
• 2021

A356 Al composites reinforced by short carbon fiber were prepared through the 2-step process: fabrication of a composite precursor and ultrasonication of the precursor melt. The short carbon fibers were coated with 0.15~1.5 ㎛ thick SiC layer by a carbothermal reaction, and an amount of the carbon fiber reinforcement was determined to be 1.5 vol.% and 4.0 vol.%, respectively. The addition of the carbon fiber increased the hardness of A356 alloy. However, tensile strength did not increase in the as-cast composites regardless of the SiC coating and volume fraction of the carbon fiber, due to the debonding which reduced load transfer efficiency from matrix to fiber at the interface. After T6-treatment of the composites, a significant increase in strength occurred only in the composite reinforced by the SiC-coated short carbon fiber, which was considered to result from the formation of a precipitate improving the Al/SiC interfacial strength.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1387-1393
• /
• 1996

A study on mesophase pitch as a matrix precursor of carbon fiber reinforced carbon (C/C) composite has been recently presented. This study is concerned with the production of mesophase pitch as matrix precursors for C/C composite from coal tar pitch. A commercial coal tar pitch was heat-treated at 25$0^{\circ}C$ for 2 hours to remove low molecular weight fraction from the pitch then increasing the temperature of the pitch to between 350~45$0^{\circ}C$ to produce mesophase pitch. The pitch was continuously stirred during this time and nitrogen gas was continuously bubbled through the pitch. Spherical and bulk mesophases were formed in the pitch after heat-treatment,. Parent and mesophae pitches were characterized by elemental analysis coke yield solubi-lity in tetrahydrofuran and hexane and an optical microscopy to measure the mesiophase content. It was neces-sary to produce C/C composite that a mesophase pitch with about 30-40 vol% mesophase spherulites can be infiltrated into a fiber preform without a filter effect as a matrix precursor conditions. This condition was satisfied with mesophase pitch heat treated at 40$0^{\circ}C$ for 2 hours. The other heat treatment conditions showed the nuclei of mesophase or bulk mesophae which were not satisfied with the matix precursor condition.

• Carbon letters
• /
• 제15권4호
• /
• pp.247-254
• /
• 2014

In this work, thermal treatment accompanied with different acid treatments was applied to a commercial coal tar pitch (CTP) to obtain a spinnable precursor pitch for carbon fiber. In the case of thermal treatment only, a relatively high reaction temperature of between $380^{\circ}C$ and $400^{\circ}C$ was required to obtain a softening point (SP) range of $220^{\circ}C-260^{\circ}C$ and many meso-phase particles were created during the application of high reaction temperature. When nitric acid or sulfuric acid treatment was conducted before the thermal treatment, the precursor pitch with a proper SP range could be obtained at reaction temperatures of $280^{\circ}C-300^{\circ}C$, which were about $100^{\circ}C$ lower than those for the case of thermal treatment only. With the acid treatments, the yield and SP of the precursor pitch increased dramatically and the formation of meso-phase was suppressed due to the lower reaction temperatures. Since the precursor pitches with acid and thermal treatment were not spinnable due to the inhomogeneity of properties such as molecular weight distribution and viscosity, the CTP was mixed with ethanol before the consecutive nitric acid and thermal treatments. The precursor pitches with ethanol, nitric acid, and thermal treatments were easily spinnable, and their spinning and carbon fiber properties were compared to those of air blowing and thermal treated CTP.

• Composites Research
• /
• 제35권2호
• /
• pp.115-119
• /
• 2022

탄소섬유의 성능은 탄소 섬유 강화 플라스틱(CFRP)과 같은 고품질 고분자 복합재료에 매우 중요하다. 이를 위해 탄소섬유 물성에 큰 영향을 주는 전구체 섬유의 기계적, 물리적, 구조적 특성을 개선할 수 있는 최적화된 방사공정과 이를 위한 적합한 전구체 공중합 고분자를 사용하는 것은 필수적이다. 본 연구에서는 메타크릴산(MAA)의 함량과 주입시간, 2,2'-아조비스(2-메틸프로피오니트릴) (AIBN)의 농도를 합성공정 변수로 설정하였으며, 용액 중합법(solution polymerization)에 의해 Poly(AN-co-MAA)가 합성되었다. 305,138 g/mol의 분자량과 4.2%의 MAA 비율을 가지는 Poly(AN-co-MAA)를 N,N-디메틸포름아미드(DMF)에 16.0 wt% 농도로 용해시킨 후 기격습식방사법(dry-jet-wet spinning)으로 전구체 섬유를 제조하였다. 섬유의 인장강도는 ~1.06 GPa, 인장탄성률은 ~22.01 GPa였으며, 섬유에서의 공극 및 구조적 결함은 관찰되지 않았다.

• Carbon letters
• /
• 제1권2호
• /
• pp.82-86
• /
• 2000

The present research was undertaken to evaluate the possibility of water purification filter with activated carbon fibers (ACFs) using a very low cost precursor consisting of phenolic resin coated on glass fibers. The simplified procedure involving coating, curing and activation and a very low cost glass fiber as a raw material were adopted in order to reduce manufacturing cost. The breakthrough curves of the manufactured ACFs and the commercial activated carbon (AC, Calgon F-200) were investigated in the initial concentration range from 19 to 49 ppm for benzene, toluene and ethylbenzene. From breakthrough profiles, the manufactured ACFs had significantly faster adsorption kinetics than the AC. Especially the benzene breakthrough curves, the manufactured ACF (13 g of ACF with 32% of carbon on the glass) was over the limited level (5 ppb) after flowing of 32 l at initial concentration of 15 ppm, while the commercial AC was shown about 3 ppm in initial adsorption.

• 방사선산업학회지
• /
• 제5권1호
• /
• pp.41-46
• /
• 2011

Polyacrylonitrile (PAN) fibers are the most widely used precursor of the materials for carbon fibers. The conventional process of carbon fibers from PAN precursor fiber includes two step; stabilization at low temperature and carbonization at high temperature. Compared to thermal stabilization, the stabilization process by electron beam (E-beam) irradiation is a advanced and brief method. However, a stabilization by E-beam irradiation was required a high dose (over 5,000 kGy) and spend over 1.5 hr (1.14 MeV, 1 mA). In the present work the main goal is exploring a quick stabilization process by cotrolling E-beam currents. The effect of various E-beam currents on stabilization of PAN precursor fiber was studied by gel fraction test, thermo gravimertic analysis (TGA), differential scanning calorimetry (DSC), tensile strength, and scanning electron microscopy (SEM) images.

• Carbon letters
• /
• 제19권
• /
• pp.57-65
• /
• 2016

Isroaniso matrix precursor synthesized from commercially available petroleum pitch was stabilized in air. The influence of oxygen mass gain during stabilization on the yield of matrix precursor was studied. Additionally, the influence of pressure on the yield of the stabilized matrix precursor in a real system was studied. The fourier transform infrared spectrometry (FTIR), thermogravimetric analysis (TGA), yield, yield rate, and yield impact were used to check the effect of stabilization and pressure on the yield of the matrix precursor and the end properties of the composite thereafter. The results showed that the yield increased with stabilization duration up to 20 h whereas it decreased for stabilization duration beyond 20 h. Further results showed that the stabilized matrix precursor for a duration of 5 h could withstand almost two-fold greater hot-pressing pressure without resulting in exudation as compared to that of a 1 h stabilized matrix precursor. The enhanced hot-pressing pressure significantly improved the yield of the matrix precursor. As a consequence, the densification and mechanical properties were increased significantly. Further, the matrix precursor stabilized for a duration of 20 h or more failed to provide proper and uniform binding of the reinforcement.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.56-62
• /
• 1997

탄화된 PAN 섬유, 페놀수지, 세라믹 결합체를 혼합하여 탄소섬유-세라믹복합체를 제조한 후 활성화시켜 PAN 섬유의 탄화온도에 따른 활성탄소섬유-세라믹복합체의 비표명적과 굽힘 강도변화를 연구하였다. 안정화 PAN 섬유를 80$0^{\circ}C$와 100$0^{\circ}C$에서 각각 탄화시켜 얻은 두 종류의 탄소섬유를 복합체 제작시편의 원료로 사용하였다. 탄소섬유-세라믹복합체를 10~90분간 CO2로 85$0^{\circ}C$에서 활성화시켜 얻은 두 종류의 활성복합체에 대한 물성 측정결과, 80$0^{\circ}C$로 PAN 섬유를 탄화시켜 만든 활성복합체의 burn-off이 37%에서 76%로 증가될 때 비표면적은 493m2/g에서 1090m2/g으로 증가하였으며, 굽힘강도는 4.5 MPa에서 1.4MPa로 감소하였다. 이 값들은 안정화 PAN 섬유의 탄화온도를 100$0^{\circ}C$로하여 활성복합체 시편이 나타내는 값보다 약 2배 정도 큰 값이었다. 비표면적, 굽힘강도 측정결과와 미세조직 관찰결과, PAN 섬유의 탄화온도가 활성복합체의 비표면적과 굽힘강도에 미치는 영향은 활성화시 탄소섬유와 페놀수지탄화체 또는 세라믹 필름간에 발생되는 결합력과 상대적인 수축율에 의해 결정되는 활성복합체의 구조특성에 기인된 것으로 해석하였다.

• Carbon letters
• /
• 제12권3호
• /
• pp.131-137
• /
• 2011

Kenaf fibers, cellulose-based natural fibers, were used as precursor for preparing kenafbased carbon fibers. The effects of carbonization temperature ($700^{\circ}C$ to $1100^{\circ}C$) and chemical pre-treatment (NaOH and $NH_4Cl$) at various concentrations on the thermal change, chemical composition and fiber morphology of kenaf-based carbon fibers were investigated. Remarkable weight loss and longitudinal shrinkage were found to occur during the thermal conversion from kenaf precursor to kenaf-based carbon fiber, depending on the carbonization temperature. It was noted that the alkali pre-treatment of kenaf with NaOH played a role in reducing the weight loss and the longitudinal shrinkage and also in increasing the carbon content of kenaf-based carbon fibers. The number and size of the cells and the fiber diameter were reduced with increasing carbonization temperature. Morphological observations implied that the micrometer-sized cells were combined or fused and then re-organized with the neighboring cells during the carbonization process. By the pre-treatment of kenaf with 10 and 15 wt% NaOH solutions and the subsequent carbonization process, the inner cells completely disappeared through the transverse direction of the kenaf fiber, resulting in the fiber densification. It was noticeable that the alkali pre-treatment of the kenaf fibers prior to carbonization contributed to the forming of kenaf-based carbon fibers.