Various kinds of amorphous silicates were used as raw materials to synthesize building materials based on calcium silicate hydrates. Relationships between the reactivities of silicates and castabilities of the building materials were investigated. In addition, effects of the reactivities of silicates on the mechanical properties of casted specimens were studied by analyzing microstructures and hydrates produced. As the reactivity of silicate increase, the press castability increases and the crystal size of hydrate and pore size also increase. For the mechanical properties, the flexural strength increases with decreasing crystal size and densifing microstructure. The compressive strength is greatly dependent on the den-sification of microstructure rather than crystal size of hydrate. Based on the results, diatomous ma-terials are desirable due to high reactivity and formation of densified microstructure. Slag and fly ash may be partially used as raw materials with amorphous silicates to manufacture building materials based on calcium silicate hydrates.

• Cement Symposium
• /
• no.27
• /
• pp.6-13
• /
• 2000

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.151-152
• /
• 2020

When concrete is exposed to fire, the thermal decomposition of hydrates of Portland cement paste results in critical damage to the concrete structure of a building. Recently, nanosilica arose as the effective nano-additive which can enhance the thermal resistance of the cementitious materials. However, the mechanism of the enhancement was not elucidated specifically. In this study, we investigated the properties of calcium silicate hydrates(C-S-H)of the nanosilica incorporated cement paste after heating to different heating temperatures (200℃, 500℃, and 800℃) by 29Si nuclear magnetic resonance. The results showed that the polymerization of C-S-H of nanosilica incorporated samples was larger than ordinary cement paste after heating to 200℃, and C-S-H formed during heating process to 500℃ due to the pozzolanic reaction during heating process.

• Computers and Concrete
• /
• v.5 no.4
• /
• pp.295-328
• /
• 2008

A previously published multiscale model for early-age cement-based materials [Pichler, et al.2007. "A multiscale micromechanics model for the autogenous-shrinkage deformation of early-age cement-based materials." Engineering Fracture Mechanics, 74, 34-58] is extended towards upscaling of viscoelastic properties. The obtained model links macroscopic behavior, i.e., creep compliance of concrete samples, to the composition of concrete at finer scales and the (supposedly) intrinsic material properties of distinct phases at these scales. Whereas finer-scale composition (and its history) is accessible through recently developed hydration models for the main clinker phases in ordinary Portland cement (OPC), viscous properties of the creep active constituent at finer scales, i.e., calcium-silicate-hydrates (CSH) are identified from macroscopic creep tests using the proposed multiscale model. The proposed multiscale model is assessed by different concrete creep tests reported in the open literature. Moreover, the model prediction is compared to a commonly used macroscopic creep model, the so-called B3 model.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.491-499
• /
• 1997

High flexible lightweight composites containing tobermorite as a main mineral is produced using various amorphous silicates, lime, cement and fibers. Here, Mechanical properties of the composites were studied by observing microstructures of hydrates and fibers. Amorphous silicates having better hydraulicity retarded the crystallization of tobermorite due to better formation of C-S-H gel in water bath curing, but, difficult conversion from C-S-H gel to tobermorite in hydrothermal reaction. In the low molar ratio of CaO/SiO2 (0.67), faster crystalization was observed dued to more impurities such as Al2O3 alkali, resulting in improving mechanical properties due to small crystal size and many contact points. It was identified that a lot of calcium silicate hydates formed at surface of pulps increase bonding strength and the crack-resistance of matrix in the composites, but decrease hardness and compressive strength. The choice of amorpous silicates having better hydraulicity, low CaO/SiO2 adding each fibers bellow about 5% in the raw mixs and lower molding pressure should be needed at improve mechanical properties of composites.

• Journal of the Korean Ceramic Society
• /
• v.11 no.4
• /
• pp.25-30
• /
• 1974

The mixture of quartz powder and slaked lime with plenty water was oscillated in an autoclave and treated hydrothermally under the pressure of 10 kg/$\textrm{cm}^2$ for 8 hours. The main mineral synthesized was confirmed 11$\AA$ tobermorite by the method of X-ray diffraction and selected area electron diffraction. Tobermorite was heat-treated at 40$0^{\circ}C$, 80$0^{\circ}C$ and 100$0^{\circ}C$ for investigation of transformation of morphology and structure. Electron micrographs showed the thin platy structure of synthetic tobermorite with a little of crumpled foil or fibrous semi-crystalline calcium silicate hydrates. No difference in structure was appeared under the temperature of 80$0^{\circ}C$ but tobermorite converted gradually into wollastonite at 800$^{\circ}$~85$0^{\circ}C$. On heating, moulded material from tobermorite hardly shrinks under 80$0^{\circ}C$.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.122.1-122
• /
• 2000

• Journal of the Korean Ceramic Society
• /
• v.18 no.3
• /
• pp.157-162
• /
• 1981

A converter slag has been heat-treated above melting point at reduced condition by cokes. As the result, most iron was separated. To make hydraulic compounds, calcium oxide was added to the reduced converter slag and the mixtures were sintered. This modified converter slag clinker mainly contained tricalcium silicate and calcium aluminates, and have a great potential to be a good hydraulic cement. The hydrates of the hydraulic compounds and gypsum with and without granulated slags, were mainly C-S-H, ettringite, calcium monosulfoaluminate hydrate, calcium aluminate hydrate, and $Ca(OH)_2$

• Journal of the Korean Ceramic Society
• /
• v.15 no.1
• /
• pp.16-20
• /
• 1978

The solubility of tobermorite was measured, and it was compaired with the resultswhich calculated by thermodynamic data. As the result, 1) The type of silisic acid species in liquid phase were the both type of $H_3SiO_4$-, $H_4SiO_4$. 2) The solubility product of tobermorite represented the maximum value at 18$0^{\circ}C$.

• Advances in concrete construction
• /
• v.5 no.3
• /
• pp.289-301
• /
• 2017

The synergistic interactions of supplementary cementitious materials (SCMs) with ordinary portland cement (OPC) in multi-blended systems could enhance the mechanical and durability properties of concrete and increase the amount of cement that can be replaced. In this study, the characteristics of the hydration products as well as paste microstructure of blended cement containing 20% coal fly ash, 10% rice hull ash and 10% sugar mill lime sludge in quaternary blended system was investigated. Portlandite content, hydration products, compressive strength, pore size distribution and microstructural architecture of hydrated blended cement pastes were examined. The quaternary blended cement paste showed lower compressive strength, reduced amount of Portlandite phases, and higher porosity compared to plain hardened cement paste. The interaction of SCMs with OPC influenced the hydration products, resulting to the formation of ettringite and monocarboaluminate phases. The blended cement paste also showed extensive calcium silicate hydrates and calcium aluminate silicate hydrates but unrefined compared to plain cement paste. In overall, the expected synergistic reaction was significantly hindered due to the low quality of supplementary cementitious materials used. Hence, pre-treatments of SCMs must be considered to enhance their reactivity as good quality SCMs can become limited in the future.