• Journal of the Korean Ceramic Society
• /
• v.37 no.5
• /
• pp.403-409
• /
• 2000

The permeation characteristics and reclamation efficiency of waste lubricating oil were studied as a function of the types of ceramic composite membranes and the membrane separation process variables. The oil permeability of the TiO2 composite membrane(pore size 0.015 $\mu\textrm{m}$) was directly proportional to the crossflow velocity(0.22∼0.9 m/s) and temperature(150$^{\circ}C$∼200$^{\circ}C$). In the batch concentration process, as the concentration factor increased, both the permeability and the ash content of the permeate decreased. The average ash contents of the total permeate through the A6 alumina membrane(average pore size 0.8$\mu\textrm{m}$), Z1/A6 and Z1/A4(pore size 0.23$\mu\textrm{m}$)/A7(pore size 6$\mu\textrm{m}$) zirconia composite membrances(average pore size 0.07$\mu\textrm{m}$) were about 0.063 wt%, 0.045wt% and 0.08wt% in the region of 1∼2 concentration factor, respectively. The ash content of the mixed permeate through the A6 alumina and zirconia composite membrane was about 0.06 wt% and it can be also reduced to 0.06 wt% in the Z1/A6 membrane and below 0.003 wt% in the TiO2/Z1/A6 membrane. It was concluded that the treated oil obtained from the multi-step membrane separation process could be used as reclaimed lubricating oil as well as reclained fuel oil.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.11
• /
• pp.935-940
• /
• 2009

In this research, the composites (100-x)LCP-xBNT (x = 0, 10, 20, 30, 40 vol.%) were fabricated with thermoplastic LCP(Liquid Crystal Polymer) and BNT($BaNd_2Ti_4O_{12}$) which is a high frequency dielectric material. Their dielectric properties, mechanical strength and microstructure were investigated by Impedance analyser, Instron and SEM. In order to fabricate LCP-BNT composites, LCP resin was put into the twin screw type mixer($310^{\circ}C$), melted by keeping for 10 min. After that, BNT filler was dispersed with melted LCP resin for 15 min. in the mixer. For measuring the dielectric properties and mechanical strength, Composite specimens were made by pressing composite granule (LCP-BNT) with 7 ton in the mold at $310^{\circ}C$. With increasing the BNT content (0~40 vol.%) of the composite, Its dielectric constant increased, dielectric loss and flexural strength decreased. The dielectric constant and flexural strength of composites with 20~30 vol.% of BNT filler are 4.1~6.0 and 35~55 MPa respectively. BNT/LCP composite is the potential substrate material for the high frequency application.

• Journal of Korean Society on Water Environment
• /
• v.28 no.2
• /
• pp.197-201
• /
• 2012

The objective of this study was to evaluate the removal efficiency of arsenite and arsenate using composite adsorbents with various mixing ratio of recycled aluminum oxides and $TiO_2$. From batch adsorption experiments, while the removal of As(III) was almost same with 4 different composite samples in the entire pH range, the removal of As(V) was substantially increased as the weight ratio of $TiO_2$ in composite samples reduced and showed anionic adsorption characteristics. Both adsorption of As (III) and As(V) on composite samples followed pseudo-second-order adsorption equation and C-3 showed faster reaction rate for the removal of arsenic. From the adsorption isotherm experiments, Langmuir isotherm explained well and the maximum adsorption capacities of arsenic were obtained with C-1.

• Composites Research
• /
• v.12 no.6
• /
• pp.43-52
• /
• 1999

This paper explains the development of a concurrent engineering system for the rlesign of composite structures. The concurrent engineering system is developed to meet the demand for the better quality products with lower production cost and time. In this study, to compose the architecture of concurrent engineering system, the commercial and noncommercial programs related to design and analysis of composite structures are surveyed and classified. The concurrent engineering system is including various design modules such as design/analysis of composite structures using CLPT and FEM, buckling and post bucking analysis, thermo-elastic analysis of carbon-carbon composite, and optimum design using expert system and genetic algorithm. For the integration and management of softwares, the concurrent engineering system is realized by Microsoft visual $C++{^\circledR}$ that provide multi-tasking and graphic user interface environment.

• Journal of Magnetics
• /
• v.20 no.3
• /
• pp.215-220
• /
• 2015

The PVDF fibrous composite filled with iron oxide nanoparticles were prepared by using the electrospinning technique. The electrospun composite have the thickness in the range of $60-80{\mu}m$ with the average fibrous diameters of 500-900 nm. The magnetizations of PVDF fibrous composite filled with iron oxide nanoparticles showed 4.5 emu/g, 3.1 emu/g and 1.6 emu/g at 1.5 T of external magnetic field for 20 wt.%, 10 wt.% and 5 wt.% iron oxide nanoparticles, respectively. The heat elevation of the magnetic composite were measured under various AC magnetic fields, frequency and the ambient temperatures. The temperature reached up to $46.3^{\circ}C$ from $36^{\circ}C$ at 128 Oe and 355 kHz for 20 wt.% iron oxide nanoparticles filled in PVDF fibrous composite sheet. The specific absorption rate of theses sheets increased from 0.041 W/g to 0.236 W/g with the increment of AC magnetic field from 90 Oe to 167 Oe at 190 kHz, respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.8
• /
• pp.909-914
• /
• 1995

From alumina powder and TEOS, $\alpha$-Al2O3/SiO2 composite powder for reaction-sintered mullite was synthesized by heterogeneous coagulation and surface coating, and investigated the mullitization reaction and sintering behavor of these powders. In $\alpha$-Al2O3/SiO2 composite powder prepared by heterogeneous coagulation, each alumina particles were surrounded by silica particles of 50~60 nm in size. And the alumina particles in composite powder prepared by surface coating were coated by uniform silica layer with thickness of 50 nm. In both methods, mullitization reaction was completed at 1$650^{\circ}C$ for 3h, and specimen sintered above 145$0^{\circ}C$ was about 95% fo the theoretical relative density. Mullite grains formed from the reaction with composite powders showed spherical shape with a size of 1~2${\mu}{\textrm}{m}$.

• Composites Research
• /
• v.24 no.3
• /
• pp.25-30
• /
• 2011

The studies on the non-destructive testing methods of the composite materials are very important for improving their reliability and safety. AE(Acoustic Emission) can evaluate the defects by detecting the emitting strain energy when elastic waves are generated by the generation and growth of a crack, plastic deformation, fiber breakage, matrix cleavage or delamination. In this paper, the AE signals of the filament wound composite cylinder and sandwich cylinder during the pressure test were measured and analyzed. The signal characteristics of PVDF sensors were measured, and an AE signal analyzer which had the band-pass filter and L-C resonance filter were designed and fabricated. Also, the crack detection capability of the fabricated AE signal analyzer wes evaluated during the pressure tests of the filament wound composite cylinder and the sandwich cylinder.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.989-994
• /
• 1995

Rigid porous carbon fiber composites with the uniform pore size distribution were prepared by vacuum forming from water slurries containing carbonized PAN fibers, a phenolic resin and ceramic binders. The composites were designed to use for highly efficient carbon fiber filters for particulate filtration and gas adsorption. As the as-received carbon fibers of 1mm in length were milled to an approximate average length of 300${\mu}{\textrm}{m}$, modulus of rupture (MOR) of the composite filter was increased from 1MPa to the value larger than 5 MPa. Modulus of rupture (MOR) for the composite filter fabricated using the milled carbon fiber was increased from 5 MPa to 10 MPa as the carbonization temperature of the PAN fiber was raised from 90$0^{\circ}C$ to 140$0^{\circ}C$. The air permeability and an average pore size of the composite filter were increased from 40 to 270cc/min.$\textrm{cm}^2$ and from 35 to 80${\mu}{\textrm}{m}$, respectively, as the apparent porosity increased from 80 to 95%. It was shown that the MOR of the carbon fiber composite filter was dependent primarily on the average length of carbon fiber, carbonization temperature and the type of bonding materials.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.10
• /
• pp.2969-2973
• /
• 2014

A new process to fabricate a composite LSCF-Ag cathode material for SOFCs by electron beam (e-beam) irradiation process has been suggested for operation under intermediate temperature range of $600-700^{\circ}C$. A composite LSCF-Ag cathode with uniformly coated Ag nanoparticles on the surface of the LSCF material was prepared by a facile e-beam irradiation method at room temperature. The morphology of the composite LSCF-Ag material was analyzed using a TEM, FE-SEM, and EDS. The prepared composite LSCF-Ag material can play a significant role in increasing the electro-catalytic activities and reducing the operating temperature of SOFCs. The performance of a tubular single cell prepared using the composite LSCF-Ag cathode, YSZ electrolyte and a Ni/YSZ anode was evaluated at reduced operating temperature of $600-700^{\circ}C$. The micro-structure and chemical composition of the single cell were investigated using a FE-SEM and EDS.

• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.444-447
• /
• 2005

In this study, $Hydroxyapatite+TiO_2(HAp+TiO_2)$ composite sol coatings on Cp-Ti substrates were deposited by using a sol-gel derived precursor. Prior to hydroxyapatite coating, the samples were micropolished and divided into three sets. The first set was coated with hydroxyapatite (HAp) directly on Cp-Ti. The second set was first coated with intermediate titania layer and then coated with HAp. The third set samples were coated with $HAp+TiO_2$ (50:50) composite sol. Each samples were predried at $200^{\circ}C$, and heat treated at $600^{\circ}C$. The formation of hydroxyapatite has been confirmed by XRD analyses and the substrate material was found to be oxidized with negligible amount of CaO in the coating. The NaOH treated samples showed the presence of rutile crystal. The SEM studies revealed surface morphologies of each samples. $HAp+TiO_2$ composite sol coating layer was found to be smooth. The bonding strength of each samples were calculated using pull out tests. The bonding strength of the $HAp+TiO_2$ composite sol coating on substrate was 29.35MPa.