• 한국재료학회지
• /
• 제4권1호
• /
• pp.75-80
• /
• 1994

2-관능성 DGEBA-4-관능성 TGDDM 블렌드를 DDM으로 경화시킨 경호물의 굴곡 특성과 열 안정성을 혼합비에 대하여 조사하였다. 굴곡 탄성율과 유리 전이 온도는 TGDDM이 증가 될수록 증대되었고, 20-40 중량%의 TGDDM조성에서 불연속적으로 변화하는데, 이것은 이 저성 부근에서 ductile/brittle의 구조적 상변화가 일어나고 있기 때문인 것으로 추정된다. TGDDM성분이 증가될수록 최대 열분해 온도는 고온쪽으로 shift되는 경향을 보이지만, 분해에 대한 활성화 에너지는 오히려 감소했다.

• Nuclear Engineering and Technology
• /
• 제34권6호
• /
• pp.574-585
• /
• 2002

The microstructural characteristics and its related mechanical properties of RPV cladding have been investigated using small punch (SP) tests. SA508 Cl.3 RPV steel plates were overlay cladded with the type ER309L welding consumables by submerged arc welding process. Although the RPV clad material had a small portion of 5 ferrite phase, it still showed the ductile to brittle transition behavior The transition temperature was determined by the SP test and it depended on the content of $\sigma$ phase, specimen size, and determination methods. The fracture appearance of SP specimen was changed from circumferential to radial cracking as test temperature became low, and below the transition temperature region, ER309L cladding usually fractured along the 6 ferrite by the low temperature failure of ferrite phase.

• 대한기계학회논문집A
• /
• 제21권1호
• /
• pp.93-103
• /
• 1997

Charpy V-notch impact tests were performed on the full-, half-and third-size specimens from two ferritic SA 508 Cl. 3 steels for nuclear pressure vessel. New normalization factors were proposed to predict the upper shelf energy(USE) and the ductile-brittle transition temperature(DBTT) of full-size specimens from the measured data on sub-size specimens. The factors for the USE and the DBTT are $(Bb^2/Kt); and; (Bb/R)^1/2/, $ respectively, where B the width, b the ligament size, $K_{t}$ the elastic stress concentration factor, and R the notch root radius. These correlations successfully estimated the USE and DBTT of the full-size specimens based on sub-size specimen data. In addition, the size effects were studied to develop the correlations among absorbed energy, lateral expansion(LE) and displacement. It was also found that the LE was able to be estimated from the displacement obtained by the instrumented impact test, and that the displacement would be used as a criterion for the toughness of the steels corresponding to change in their yield strength.h.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.105-110
• /
• 2000

The Micromechanics test is new test method which uses comparatively smaller specimen than that required in conventional material tests. There are several methods, such as small-specimen creep test, the continuous indentation test, and small punch(SP) test. Among them, the small punch(SP) test method has been applied to many evaluation fields, such as a ductile-brittle transition temperature, stress corrosion cracking, hydrogen embrittlement, and fracture properties of advanced materials like FGM or MMC. In this study, the small punch(SP) test is performed to evaluate the mechanical properties at high/low temperature from $-196^{\circ}C$ to $650^{\circ}C$ and the material degradation for virgin and aged materials of 9Cr1MoVNb steel which has been recently developed. The ${\Delta}P/{\Delta}{\delta}$ parameter defined a slope in plastic membrane stretching region of SP load-displacement curve decreases according to the increase of specimen temperature, and that of aged materials is higher than the virgin material in all test temperatures. And the material degradation degrees of aged materials with $630^{\circ}C$ -500hrs and $630^{\circ}C$ -1000hrs are $36^{\circ}C$ and $38^{\circ}C$ respectively. These behaviors are good consistent with the results of hardness($H_v$) and maximum displacement(${\delta}_{max}$).

• Composites Research
• /
• 제16권3호
• /
• pp.41-48
• /
• 2003

본 연구에서는 고온 산화분위기 하에서 탄소/탄소 복합재료의 내산화 특성 향상을 위해 사용된 이규화 몰리브덴(MoSi$_2$)의 함량(0. 4, 12. 그리고 20 wt%)에 따른 복합재료의 충격특성에 관하여 고찰하였다. 결과로서, MoSi$_2$가 함침된 탄소/탄소 복합재료는 이를 함유하지 않은 것에 비하여 충격특성 향상의 원인이 되는 탄소섬유와 매트릭스 수지간의 계면결합력 증가를 가져왔으며, 특히 12 wt% MoSi$_2$가 현재의 시스템에서 가장 우수한 충격특성을 나타내었다. 이는 복합재료 내의 탄소섬유, 필러, 그리고 매트릭스 수지간의 계면 접착력의 증가를 가져오는 90$0^{\circ}C$ 전후에서 MoSi$_2$의 취성­연성 전이(BDT) 작용 때문이라 사료된다.

• 대한기계학회논문집
• /
• 제17권2호
• /
• pp.300-312
• /
• 1993

The material deterioration of service-exposed boiler tube steels in fossil power plant was evaluated by using the electrochemical technique namely, modified electrochemical potentiokinetic reactivation(EPR). It was focused that the passivation of Mo$_{6}$C carbide which governs the mechanical properties of Mo alloyed steels did not occur even in the passivity region of steel in sodium molybdate solution and the reactivation peak current (Ip) observed as the result of non-passivation indicating the precipitation of Mo$_{6}$C carbides. To obtain the optimal test conditions for the field test by using the specially designed electrochemical cell, the effects of scan rate, the surface roughness and the pH of electrolyte on Ip value were also investigated. Furthermore, the change of mechanical properties occurred during the long time exposure at high temperature was evlauated quantitatively by small punch(SP) tests and micro hardness test taking account of the metallurgical changes. It is known that reactivation peak current (Ip) has a good relationship with Larson-Miller Parameter(LMP) which represents the information about material deterioration occurred at high temperature environment. In addition it was possible to estimate the ductile-brittle transition temperature (DBTT) by means of the SP test. The Sp test could be, therefore, suggested as a reliable test method for evaluating the material degradation of boiler tube steels. From the good correaltion between the SP DBTT and Ip values shown in this study, it was knows that the change of mechanical properties could be evaluated non-destructively by measurring only Ip values.ues.

• Elastomers and Composites
• /
• 제39권2호
• /
• pp.142-152
• /
• 2004

서로 다른 두 종류의 폴리스타일렌(PS)을 injection 기계를 이용하여 인장 시편을 만들고, 온도와 인장 속도에 따른 crazing 거동 특성을 연구하기 위하여 다양한 시험을 하였다. 기계적물성은 craze 형성뿐만 아니라 다양한 시험 변수에 의해 영향을 받으며, brittle-ductile transition 이하의 온도에서의 인장 응력 및 최대 신율은 분자량, 인장 속도의 증가 및 온도의 감소에 따라 증가하며 craze의 수와 평균 길이 또한 증가한다. Crazing 응력도 동일한 형태로 증가함을 보여준다. 그러나, 이러한 특성은 인장 강도에 미치는 영향과 비교했을 때 보다 의존도는 상대적으로 낮다. Craze 형성과 성장에 필요한 시간으로 설명할 수 있는 crazing 응력과 인장 응력간의 차이는 분자량, 인장 속도에 따라 비례적으로 그리고, 온도가 감소함에 따라 증가함을 보여 준다. Crazing 은 ${\beta}$-relaxation 온도 근처에서 활성화된다. 이 온도에서는 crazing 응력이 급격하게 감소함을 나타낸다. 인장 평가시 craze 밀도가 적용된 응력에 따라 기하 급수적으로 증가되는데, 개시 단계에서는 craze는 서서히 형성되며, 일단 일정한 수만큼의 craze가 형성이 되면 craze 밀도가 급속도로 증가했다.

• Nuclear Engineering and Technology
• /
• 제48권2호
• /
• pp.518-524
• /
• 2016

The thermal aging effects on mechanical properties and microstructures in China low-activation martensitic steel have been tested by aging at $550^{\circ}C$ for 2,000 hours, 4,000 hours, and 10,000 hours. The microstructure was analyzed by scanning and transmission electron microscopy. The results showed that the grain size and martensitic lath increased by about $4{\mu}m$ and $0.3{\mu}m$, respectively, after thermal exposure at $550^{\circ}C$ for 10,000 hours. MX type particles such as TaC precipitated on the matrix and Laves-phase was found on the martensitic lath boundary and grain boundary on aged specimens. The mechanical properties were investigated with tensile and Charpy impact tests. Tensile properties were not seriously affected by aging. Neither yield strength nor ultimate tensile strength changed significantly. However, the ductile-brittle transition temperature of China low-activation martensitic steel increased by $46^{\circ}C$ after aging for 10,000 hours due to precipitation and grain coarsening.

• 한국주조공학회지
• /
• 제2권2호
• /
• pp.2-9
• /
• 1982

This paper is concerned with the improvement of impact and tensile Properties of spheroidal graphite cast iron of the following duplex matricess which were heat treated in the eutectic transformation temperature range (that is, $({\alpha}+{\gamma})$ coexisting range) ; ferrite-martensite, ferrite-bainite and ferrite-pearlite. The absorbed energy and maximum load was measured by recording the load-deflection curve with instrumented Charpy impact testing machine in the temperature range from $+100^{\circ}C$ to $-196^{\circ}C$. It was found the ferrite-bainite duplex matrix showed the highest toughness among the above matrices in the room temperature and the low temperature range. Comparison of this matrix to ferrite-pearlite matrix(that is, as cast) showed a lowering of $27^{\circ}C$ in the nil-ductility transition temperature (NDT) and a lowering of $40^{\circ}C$ in the ductile-brittle transition temperature (TrE), Which seems to result from the finner dimple pattern observed using miorofractography.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.431-434
• /
• 2008

Effects of microstructure on the toughness of low carbon HSLA steels were investigated. Nickel decreased the ferrite-austenite transformation temperature, resulted in increase of the fraction of bainitic ferrite. However, it was decreased with increasing deformation amount at austenite region. Since fine austenite grains formed by dynamic recrystallization under large strain transformed to acicular ferrite or granular bainite rather than bainitic ferrite. The effective grain size, thus, was decreased by deformation and it resulted in lower ductile-brittle transition temperature (DBTT). The bainitic ferrite was thought to inhibit the fracture crack initiation and to delay the crack propagation by its high dislocation density and hard interlath $2^{nd}$ phase constituents, respectively. Thus, DBTT was also decreased by Ni addition in low carbon HSLA steels.