• Journal of the Korean institute of surface engineering
• /
• v.56 no.3
• /
• pp.169-179
• /
• 2023

This work studies dielectric breakdown behavior of AAO (anodic aluminum oxide) films formed on pure aluminum at a constant current density in 5 ~ 20 vol.% sulfuric acid (SA) and 2 ~ 8 wt.% oxalic acid (OA) solutions. It was observed that dielectric breakdown voltage of AAO film with the same thickness increased with increasing concentration of both SA and OA solutions up to 15 vol.% and 6 wt.%, respectively, above which it decreased slightly. The dielectric breakdown resistance of the OA films appeared to be superior to that of SA films. After dielectric breakdown test, cracks and a hole were observed. The crack length increased with increasing SA film thickness but it did not increase with increasing OA film thickness. To explain the reason why shorter cracks formed on the OA films than the SA films after dielectric breakdown test, the generation of tensile stresses at the oxide/metal interface was discussed in relation to porosity of AAO films obtained from cross-sectional morphologies.

• Korean Journal of Materials Research
• /
• v.31 no.10
• /
• pp.546-551
• /
• 2021

To improve ferroelectric properties of PZT, many studies have attempted to fabricate dense PZT films. The AD process has an advantage for forming dense ceramic films at room temperature without any additional heat treatment in low vacuum. Thick films coated by AD have a higher dielectric breakdown strength due to their higher density than those coated using conventional methods. To improve the breakdown strength, glass (SiO₂-Al₂O₃-Y₂O₃, SAY) is mixed with PZT powder at various volume ratios (PZT-xSAY, x = 0, 5, 10 vol%) and coating films are produced on silicon wafers by AD method. Depending on the ratio of PZT to glass, dielectric breakdown strength and energy storage efficiency characteristics change. Mechanical impact in the AD process makes the SAY glass more viscous and fills the film densely. Compared to pure PZT film, PZT-SAY film shows an 87.5 % increase in breakdown strength and a 35.3 % increase in energy storage efficiency.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.34 no.12
• /
• pp.457-463
• /
• 1985

This paper studies on the tracking phenamena by the IEC recommended method with various polymeric insulating materials which are used in industrial fields. Under the same experimental condition, according to the materials it is observed that there are the type of tracking breakdown and the type of tracking erosion. In the tracking breakdown type materials, the tracking breakdown is occurred at a small number of drops increasing of test voltage and solution density. In the tracking erosion type materials, the erosion depth is saturated or proportioned as increasing of test voltage and solution density.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1596-1598
• /
• 1999

In order to determine what influences the interfacial breakdown between two internal dielectric surfaces. We studied the interfacial breakdown phenomena at several interfacial conditions. With the increase of interfacial pressure, at first breakdown strength in interfaces was increased, and then saturated. Breakdown strength in interface pasted with silicone oil was higher than that with silicone grease. As a function of heat treatment time in a vacuum oven interfacial breakdown strength was increased much in XLPE/EPDM laminates pasted with silicone grease but increased a little in that with silicone oil. As an increase of curing agent in silicone oil and grease, breakdown strength in interfaces was increased and then saturated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.104-104
• /
• 2010

With the advent of nano-particle fillers in insulating materials, the insulating materials of superior quality have come to fore. In the recent past, nanocomposite LDPE/XLPE (Low Density Polyethylene/Cross Linked Polyethylene) power cable dielectrics have been synthesized. A preliminary evaluation of these new class of materials seem to show that, addition of small amounts of sub-micron inorganic fillers improved the dielectric properties of the composite, in particular, the volume resistivity, and the DC breakdown strength. The thermal behaviour, for example, the stability of composites against decomposition and ensuing electrical failure, do not seem to have been addressed. In a conventional XLPE insulated cable, the average thermal breakdown strength and maximum temperature at the onset of breakdown were seen to be markedly lower than the corresponding intrinsic breakdown strength and decomposition temperature. In this page, analysis of DC Breakdown of nano-composite insulating material for HVDC Cable is introduced.

• Electrical & Electronic Materials
• /
• v.10 no.8
• /
• pp.770-777
• /
• 1997

Some polymer materials including epoxy resin are being instead of porcelain for outdoor insulating materials such as insulators bushings cable terminators and surge arrester housing. And the largest problem to be overcomed is the tracking and erosion of the outdoor polymer material brought about by dry band arcing during prolonged exposure to contaminations. In this paper the effect of surface tension wettability flow rate of contaminants with varying surfactant content and frequency of applied voltage on the tracking breakdown of epoxy insulating materials were investigated. As the flow rate of contaminant is increased the surface resistivity is decreased and the leakage current is increased the time to tracking breakdown is decreased. It is found that time to tracking breakdown depends on the surface tension of contaminant that is difference of wettability. And as the frequency of applied voltage is increased time to tracking breakdown decreased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05a
• /
• pp.52-56
• /
• 2001

The Breakdown electric field of ZnO semiconductor devices in voltage-current characteristics was increased by increasing of additive materials. The specimen that has not additive materials was not formed spinel structure. The critical voltage that has not spinel structure was 235[V]. When the additive materials has 0.5 and 2[mol%], the Breakdown electric field was 840 and 758[V] in each additive materials. The Breakdown electric field of varistors as a factor of voltage and current was increased by addition of oxide antimony. The varistors that has oxide antimony was linearly increased in low electric field.

• Electrical & Electronic Materials
• /
• v.7 no.6
• /
• pp.527-533
• /
• 1994

In this study, it was studied on dielectric breakdown strength and thennostability properties due to the structure variation of matrix resin and treatment of coupling agent of epoxy insulating materials. The interpenetrating network structure was formed by simultaneous heating curing the epoxy resin with single network structure and the methacrylic acid resin. Also inner structure was observed and the glass transition temperature was measured on these three type specimens. Dielectric breakdown properties were investigated by applying DC, AC and impulse voltage. As a result, the glass transition temperature and the dielectric breakdown strength of specimen with interpenetrating network structure was more higher than another two type specimens.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.11
• /
• pp.1463-1470
• /
• 2018

In this study, 20 types of samples were prepared by mixing different kinds of inorganic materials to develop insulation materials for epoxy - based GIS substation equipment used under high voltage environmentally friendly insulation gas. One of the electrical characteristics, AC insulation breakdown experiment was performed. As mixing ratio of mixed heterogeneous inorganic materials, the dielectric breakdown strength was increased with increasing filler ratio of micro silica, micro silica : micro Alumina, 1:9, 3:7, 5:5, 7:3, 9:1, and decreased as the filling amount of micro alumina increased. The AC insulation breakdown characteristics were the best when the composition ratio was 9:1. The higher the content of silica, the better the interfacial properties, and the larger the alumina content ratio, the worse the interfacial properties.

• Electrical & Electronic Materials
• /
• v.10 no.3
• /
• pp.247-254
• /
• 1997

Internal voids in insulators give rise to partial discharge, which causes a local breakdown and even entire insulation breakdown. Recently, the necessity of establishing the way to diagnose the aging of insulation materials and to predict of insulation breakdown become important. The purpose of our work are to investigate the treeing phenomena with an artificial needle shaped void by the charge of discharge and acoustic emission pulse in each phase angle area at the same time. We analyzed the .PHI.-QA-t pattern and .PHI.-AEA-t pattern using statistic operators such as pulse magnitude, pulse number, skewness, kurtosis. Therefore, the relation between the charge of discharge and acoustic emission pulse will be helpful to predict the breakdown just before the breakdown occur.