• The KSFM Journal of Fluid Machinery
• /
• v.19 no.3
• /
• pp.48-52
• /
• 2016

Microstructure and tensile strength of the vacuum brazed stainless steel(STS304) and WC-8 %Co were investigated. For brazing, the BNi-2, 3(A.W.S standard) were used as filler metals. It was found that metallic compounds of W-Ni were observed at the between WC metrix and brazed layer. Among these filler metals, the BNi-2 showed excellent wettability, but tensile strength was lower than BNi-3. The fracture of the brazed specimens with BNi-2 was occurred at the between WC metrix and brazed layer. The fracture of the brazed specimens with BNi-3 was occurred at the between WC metrix and brazed layer, and between brazed layer and stainless steel.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.3
• /
• pp.169-175
• /
• 2012

Purpose: In this study, brazing characteristics of $ZrO_2$ and Ti-6Al-4V brazed joints with increasing temperature were investigated. Materials and methods: The sample size of the $ZrO_2$ was $3mm{\times}3mm{\times}3mm$ (thickness), and Ti-6Al-4V was $10mm(diameter){\times}5mm(thickness)$. The filler metal consisted of Ag-Cu-Sn-Ti was prepared in powder form. The brazing sample was heated in a vacuum furnace under $5{\times}10^{-6}$ torr atmosphere, while the brazing temperature was changed from 700 to $800^{\circ}C$ for 30 min. Results: The experimental results shows that brazed joint of $ZrO_2$ and Ti-6Al-4V occurred at $700-800^{\circ}C$. Brazed joint consisted of Ag-rich matrix and Cu-rich phase. A Cu-Ti intermetallic compounds and a Ti-Sn-Cu-Ag alloy were produced along the Ti-6Al-4V bonded interface. Thickness of the reacted layer along the Ti-6Al-4V bonded interface was increased with brazing temperature. Defect ratios of $ZrO_2$ and Ti-6Al-4V bonded interfaces decreased with brazing temperature. Conclusion: Thickness and defect ratio of brazed joints were decreased with increasing temperature. Zirconia was not wetting with filler metal, because the reaction between $ZrO_2$ and Ti did not occur enough.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.2
• /
• pp.137-143
• /
• 2011

Fuel Test Loop(FTL) is a facility which could conduct a fuel irradiation test at HANARO(High-flux Advanced Neutron Application Reactor). FTL simulates commercial NPP's operating conditions such as the pressure, temperature and neutron flux levels to conduct the irradiation and thermo-hydraulic tests. The In-Pile Test Section(IPS) installed in HANARO FTL is designed as a pressure vessel design conditions of $350^{\circ}C$, 17.5MPa. The instrumentation MI-cables for thermocouples, SPND and LVDT are passed through the sealing plug, which is in the pressure boundary region and is a part of instrumentation feedthrough of MI-cable. In this study, the brazing method and performance test results are introduced to the sealing plug with BNi-2 filler metal, which is selected with consideration of the compatibility for the coolant. The performance was verified through the insulation resistance test, hydrostatic test, and helium leak test.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.293-297
• /
• 2007

Microstructure and tensile strength of the vacuum brazed stainless steel(STS303) and Cu were investigated. For brazing, the BNi-2, 3, 4, 6 and 7 (A.W.S standard) were used as filler metals. The Oxides such as $Cr_2O_3$ and $SiO_2$ were observed at brazed layers between STS303 and Cu matrix. Also, the intermetallic compounds of Cr-B and Ni-P were observed at brazed layers. Brazed STS303-Cu specimens with BNi-2, 3, 4 filler metals showed almost elastic deformation followed by plastic yielding and strain hardening up to a peak stress. On the other hand, it is likely that the fracture of the brazed specimens with BNi-6 and 7 was occurred in elastic range without plastic yielding up to a peak stress. Among these filler metals, the BNi-2 brazed at $1050^{\circ}C$ showed excellent wettability and the highest tensile strength (101.6MPa).

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2001.10a
• /
• pp.269-274
• /
• 2001

Applications of Brazing in the studying fields such as High-Speed Machining are very increasing in various industry fields. Therefore, Applying to the fracture mechanics by numerical analysis method is very important to analyse the crack problem Dissimilar Materials in Brazed Interface. In this study, Stress intensity Factor (S.I.F) is analysed to investigate crack behavior on the crack tip of dissimilar materials in brazed interface such as a Hardmetal and a HSS by two dimensional(2-D) Boundary Element Method (BEM). Kelvin's solution was used as a fundamental solution in BEM analysis and stress extrapolation method was used to determine Stress Intensity Factor.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.251-253
• /
• 2007

현재 다이아몬드 공구에서 극세선에 브레이징 공정을 이용하여 다이아몬드를 접합하는 기술은 국내외 적으로 전무한 상태이다. 이 연구는 금속 와이어에 다이아몬드를 브레이징을 실시하여 최적의 와이어 브레이징 공정법을 개발 하는데 있다. 다이아몬드와 금속필러메탈 접합 계면에서의 금속성분과 탄화물의 거동을 분석하며, 브레이징에 따른 와이어의 물성 변화를 관찰하였다. 금속필러로는 Ag-Cu-5Ti(wt.%)을 사용하였으며, 와이어는 스테인리스를 이용하였다. 브레이징 공정은 진공 접합 장치를 이용하여 $800{\sim}1000^{\circ}C$에서 유지시간 $5{\sim}30$분로 실시하였다. 브레이징된 다이아몬드는 $900{\sim}950$도, 유지시간 10분 사이에서 각각 건전한 계면과 표면을 얻을 수 있었으며, 계면에서 Ti-rich상과 화합물이 확인되었다. 또한 열처리 따른 와이어의 최적의 건전한 상태를 고찰 하였다. 다이아몬드와 Ag계 브레이징 필러의 계면에서의 미세조직 및 화학반응의 메커니즘은 SEM, EPMA, XRD를 이용하여 분석하였다.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.248-250
• /
• 2007

이 연구는 cBN과 활성 Ag계 금속필러메탈을 이용하여 접합계면에서의 금속성분과 화합물, 탄화물의 거동을 분석하는데 있다. 진공 브레이징은 $900{\sim}1000^{\circ}C$에서 $25^{\circ}C$ 간격으로, 유지 시간은 각각 5, 10, 15, 20분으로 실시하였다. Ag-Cu-Ti을 사용하여 브레이징된 cBN은 $950{\sim}1000$도, 유지시간 10분 사이에서 각각 건전한 계면과 표면을 얻을 수 있었으며, 계면에서 Ti-rich상과 화합물이 확인되었다. 이상의 결과로 부터 화합물의 생성과 건전한 접합공정은 브레이징 온도와 시간이 좌우하며, N과 B, Ti의 함유량이 cBN의 브레이징 접합 특성의 중요변수로 생각되어진다. cBN과 Ag계 브레이징 필러의 계면에서의 미세조직 및 화학반응의 메커니즘은 DTA, SEM, EPMA, XRD를 이용하여 분석하였다.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.11 no.6
• /
• pp.91-97
• /
• 2002

Applications of brazing in the studying fields such as high-speed machining are very increasing in various industry fields. Therefore, applying to the fracture mechanics by numerical analysis method is very important to analyse the crack problem dissimilar materials in brazed interface. In this study, stress intensity factor(SIF) is analysed to investigate crack behavior on the crack tip of dissimilar materials in brazed interface such as a hardmetal and a HSS by two dimensional(2-D) BEM. Kelvin's solution was used as a fundamental solution in BEM analysis and stress extrapolation method was used to determine SIF.

• Journal of Welding and Joining
• /
• v.10 no.2
• /
• pp.1-10
• /
• 1992

저탄소강은 일반적으로 용접성이 우수하지만 완전한 접합 강도와 용접부에서의 결함을 방지하기 위해서는 많은 주위가 필요하다. 용접부의 기계적 성질은 그 미세구조에 따라 좌우되는데, 이 구조는 모재의 화학조성, 용접 조건 그리고 후열처리에 의하여 결정이 된다. 이와 같이 용융용 접에 의한 저탄소강의 접합부는 저탄소함량으로 응고 균열에 대한 저항이 높다. 그러나 탄소의 함량이 증가하므로서 용접성은 저하하여, 0.3% 이상에서 용접부는 과열, 과냉, 저온 균열과 porosity에 취약하게 된다. 구조용강애 있어서는 용접성에 대한 일반적인 기준이 없으므로 이 러한 재료는 모재와 용접부의 기계적 성질, 고온 및 저온 균열성, 열간 및 냉각가공성등을 고려 하게 된다. 그러나 가장 중요한 것은 용접부의 신뢰도이다. 탄소강과 저합금강에 있어서 용접은 높은 강도를 얻을 수 있어야 하며 접합부에서 모재의 원래의 특성을 유지하여야 하고 결함이 없어야 할 것이다. 이와 같은 결함은 모재의 융접 이하에서 접합을 실시하는 고상접합으로 충 분히 억제할 수가 있다. 고상접합에서는 근본적인 미세조직의 결정화도 피할 수 있으며 고온균 일과 같은 결함의 위험도 배제할 수 있다. 고상접합은 용융용접과는 달리 모재를 용융시키지 않고 고체상태에서 접합을 하는데, 신금속 및 신소재의 개발과 첨단산업의 발달로 고상접합 기 술이 크게 각광을 받고 발전하게 되었다. 이와 같은 접합기술의 발전으로 기존의 용접으로는 접합이 불가한 소재, 용접기술의 적용이 곤란한 복잡한 형상, 복합기능 소재, 고품질 및 고정밀 성이 요구되는 소재등이 접합이 가능하게 되었다. 이러한 접합기술로는 brazing, 확산접합, 마찰 용접 등이 주로 많이 이용되고 있다. Brazing은 융점이 낮은 filler metal이 모재의 사이에서 용 융상태로 유입되어 냉각되면서 접합되는 방식이고 확산접합은 모재의 접합계면에서 원자의 상호 확산으로 접합을 하게 된다. 한편 마찰용접은 계면에서 회전에 의한 마찰열고 접합하는 방식 이다. 본 기술해설에서는 이러한 고상접합 기술을 이용한 철강재료의 접합에 대하여 고찰하도록 하겠다.