• Steel and Composite Structures
• /
• 제45권6호
• /
• pp.819-830
• /
• 2022

This paper presented an experimental study of the bond-slip behavior of reactive powder concrete (RPC)-filled square steel tube. A total of 18 short composite specimens were designed forstatic push-out test, and information on their failure patterns, load-slip behavior and bond strength was presented. The effects of width-to-thickness ratio, height-to-width ratio and the compressive strength of RPC on the bond behavior were discussed. The experimental results show that:(1) the push-out specimens remain intact and no visible local buckling appears on the steel tube, and the interfacial scratches are even more pronounced at the internal steel tube of loading end; (2) the bond load-slip curves with different width-to-thickness ratios can be divided into two types, and the main difference is whether the curves have a drop in load with increasing slip; (3) the bond strength decreases with the increase of the width-to-thickness ratio and height-width ratio, while the influence of RPC strength is not consistent; (4) the slippage has no definite correlation with bond strength and the influence of designed parameters on slippage is not evident. On the basis of the above analysis, the expressions of interface friction stress and mechanical interaction stress are determined by neglecting chemical adhesive force, and the calculation model of bond strength for RPC filled in square steel tube specimens is proposed. The theoretical results agree well with the experimental data.

• Computers and Concrete
• /
• 제8권4호
• /
• pp.465-472
• /
• 2011

This paper investigates bond behavior of structural lightweight concrete (SLWC) and ordinary concrete (OC) comparatively using bending test called Standard Belgium Hinged Beam Test (SBHBT). For this purpose the experiments were carried out as three series on 36 beam specimens (12 specimens of SLWC and OC with $20{\phi}$ development length, 12 specimens of SLWC with $25{\phi}$ development length). For each series bond behavior of steel rebars with 8, 10, 12, 14 mm diameters were tested. The results indicate that bond strength of SLWC is considerable lower than OC and $20{\phi}$ development length is insufficient for steel rebars with 12 mm and 14 mm diameters. Therefore development length of SLWC was extended to $25{\phi}$, even if 8 and 10 mm steel rebars provided acceptable bond strength. In this way, bond strength between SLWC and 8 and 10 mm steel rebars was developed. In addition, adequate bond behavior was achieved for 12 mm rebar but the beam in which 14 mm rebar used exceeded their bearing capacity by shear forces before yield stress. This result shows that SBHBT is more convenient for small sized steel rebars.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.309-312
• /
• 2006

An experimental study for bond slip behavior of concrete and a FRP plank was used as the both formwork and the tensile reinforcement for a concrete structural member is described. For the FRP plank and the concrete to act as a composite structural member a satisfactory bond at the interface between the smooth surface of the FRP and the concrete must be developed. This study focuses on investigation of the bond slip behavior of sand coated interface between FRP and cast-in-place concrete experimentally.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.965-970
• /
• 2002

The strengthening of concrete structures in situ with externally bonded carbon fiber is increasingly being used for repair and rehabilitation of existing structures. Carbon fiber is attractive for this application due to its good tensile strength, resistances to corrosion, and low weight. Generally bond strength and behavior between concrete and carbon fiber mesh(CFM) is very important, because of the enhanced bond of CFM. Therefore if bond strength is sufficient, it will be expected to enhance reinforcement effect. If insufficient, reinforcement effect can not be enhanced because of bond failure between concrete and CFM. This study is to investigate the bond strength of CFM to the concrete using direct pull-out test and tensile-shear test. The key variables of the experiment are the location of clip, number of clips and thickness of cover mortar. The general results indicate that the clip anchorage technique for increasing bond strength with CFM appear to be effective to maintain the good post-failure behavior.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.510-513
• /
• 2004

The objectives of this research are to evaluate the effect of the compressive strength of concrete, reinforcing bar size, spacing of column transverse bars related to the concrete confinement effects on anchorage bond strength and bond behavior of beam-column joints subjected to cyclic loading and to predict the bond behavior of beam-column joints according to the variables by Finite Element Analysis appling the interface element between concrete and reinforced bar surface in a three-dimensional configuration. This paper shows that to verify the results by three-dimensional nonlinear finite element analysis appling a interface element, the test results that were already conducted are compared with analytic results. The behavior of bond and anchorage of beam bar is expressed by a local bond stress-slip relationship and the failure mode of bond is predicted by principal stress contour.

• Structural Engineering and Mechanics
• /
• 제72권3호
• /
• pp.305-312
• /
• 2019

This paper investigates the effect of utilizing vacuum bagging process to enhance the bond behavior between fiber reinforced polymer (FRP) composites and concrete substrate. Sixty specimens were prepared and tested using double-shear bond test. The effect of various parameters such as vacuum, fiber type, and FRP sheet length and width on the bond strength were investigated. The experimental results revealed that utilizing vacuum leads to improve the bond behavior between FRP composites and concrete. Both the ultimate bond forces and the maximum displacements were enhanced when applying the vacuum which leads to reduction in the amount of FRP materials needed to achieve the required bond strength compared with the un-vacuumed specimens. The efficiency of the enhancement in bond behavior due to vacuum highly depends on the fiber type; using carbon fiber showed higher enhancement in the bond strength compared to the glass fiber when vacuum was applied. On the contrary, specimens with glass fiber showed higher enhancement in the maximum slippage compared to specimens with carbon fibers. Utilizing vacuum does not affect the debonding failure modes but lead to increase in the amount of attached concrete on the surface of the debonded FRP sheet.

• Steel and Composite Structures
• /
• 제38권3호
• /
• pp.241-255
• /
• 2021

In order to study the interfacial bond-slip behavior of steel reinforced recycled concrete (SRRC) under cyclic loading, thirteen specimens were designed and tested under cyclic loading and one under monotonic loading. The test results indicated that the average bond strength of SRRC decreased with the increasing replacement ratio of recycled concrete, whereas the bond strength increased with an increase in the concrete cover thickness, the volumetric stirrup ratio, and the strength of recycled concrete. The ultimate bond strength of the cyclically-loaded specimen was significantly (41%) lower than that of the companion monotonically-loaded specimen. The cyclic phenomena also showed that SRRC specimens went through the nonslip phase, initial slip phase, failure phase, bond strength degradation phase and residual phase, with all specimens exhibiting basically the same shape of the bond-slip curve. Additionally, the paper presents the equations that were developed to calculate the characteristic bond strength of SRRC, which were verified based on experimental results.

• KEPCO Journal on Electric Power and Energy
• /
• 제1권1호
• /
• pp.127-134
• /
• 2015

Recently, the external bonding of carbon fiber reinforced polymer (CFRP) sheets has come to be regarded as a very effective method for strengthening of reinforced concrete structures. The behavior of CFRP-strengthened RC structure is mainly governed by the interfacial behavior, which represents the stress transfer and relative slip between concrete and the CFRP sheet. In this study, the effects of bonded length, width and concrete strength on the interfacial behavior are verified and a bond-slip model is proposed. The proposed bond-slip model has nonlinear ascending regions and exponential descending regions, facilitated by modifying the conventional bilinear bond-slip model. Finite element analysis results of interface element implemented with bond-slip model have shown good agreement with the experimental results performed in this study. It is found that the failure load and strain distribution predicted by finite element analysis with the proposed bond-slip are in good agreement with results of experiments.

• Nuclear Engineering and Technology
• /
• 제51권4호
• /
• pp.1132-1141
• /
• 2019

Steel-concrete-steel (SCS) sandwich structures have important advantages over conventional concrete structures, however, bond-slip between the steel plate and concrete may lead to a loss of composite action, resulting in a reduction of stiffness and fatigue life of SCS sandwich structures. Due to the inaccessibility and invisibility of the interface, the interfacial performance monitoring and debonding detection using traditional measurement methods, such as relative displacement between the steel plate and core concrete, have proved challenging. In this work, two methods using piezoelectric transducers are proposed to detect the bond-slip between steel plate and core concrete during the test of the beam. The first one is acoustic emission (AE) method, which can detect the dynamic process of bond-slip. AE signals can be detected when initial micro cracks form and indicate the damage severity, types and locations. The second is electromechanical impedance (EMI) method, which can be used to evaluate the damage due to bond-slip through comparing with the reference data in static state, even if the bond-slip is invisible and suspends. In this work, the experiment is implemented to demonstrate the bond-slip monitoring using above methods. Experimental results and further analysis show the validity and unique advantage of the proposed methods.

• 한국세라믹학회지
• /
• 제55권4호
• /
• pp.344-351
• /
• 2018

The effects of bond coat species on the growth behavior of thermally grown oxide (TGO) layer in thermal barrier coatings (TBCs) was investigated through furnace cyclic test (FCT). Two types of feedstock powder with different particle sizes and distributions, AMDRY 962 and AMDRY 386-4, were used to prepare the bond coat, and were formed using air plasma spray (APS) process. The top coat was prepared by APS process using zirconia based powder containing 8 wt% yttria. The thicknesses of the top and bond coats were designed and controlled at 800 and $200{\mu}m$, respectively. Phase analysis was conducted for TBC specimens with and without heat treatment. FCTs were performed for TBC specimens at $1121^{\circ}C$ with a dwell time of 25 h, followed by natural air cooling for 1 h at room temperature. TBC specimens with and without heat treatment showed sound conditions for the AMDRY 962 bond coat and AMDRY 386-4 bond coat in FCTs, respectively. The growth behavior of TGO layer followed a parabolic mode as the time increased in FCTs, independent of bond coat species. The influences of bond coat species and heat treatment on the microstructural evolution, interfacial stability, and TGO growth behavior in TBCs are discussed.