• Maxillofacial Plastic and Reconstructive Surgery
• /
• 제29권5호
• /
• pp.383-393
• /
• 2007

The aim of the present study is to investigate the effect of anodized surface of osseointegration implants by using of resonance frequency analysis (RFA) and histomorphometric analysis. A total of 96 screw-shaped implants were devided into 4 groups. Seventy-two implants were prepared by electrochemical oxidation with 3 different ways; Group 1 (n=24) were prepared at galvanostatic mode in 0.25M sulfuric acid and phosphoric acid, Group 2 (n=24) were prepared at galvanostatic mode in calcium glycerophosphate and calcium acetate, and Group 3 (n=24) were prepared at galvanostatic mode in 0.25M sulfuric acid and phosphoric acid followed by Calcium metaphosphate(CMP) coating. Control group (n=24) were the RBM surfaced implants. The implants were placed in the mandibles of 12 mini pigs. Bone tissue responses were evaluated by resonance frequency analysis(RFA) and histomorphometric analysis that were undertaken at 2, 4 and 6weeks after implant placement. The following result were obtained. 1. Twenty-two of 96 implants (4 in control group, 5 in group 1, 7 in group 2, and 6 in group 3) were failed due to faliure of osseoitegration. The failure rate of osseointegration was 22.9%. 2. The mean values of RFA in control, group 2 and groups 3 showed the similar values, but there was no significant difference among groups. 3. Histomorphometric evaluation demonstrated significantly higher bone-to-implant contact ratio in group 2 at 3 and 4 weeks after implant placement than other groups (p<0.05), but there was no significant difference among groups at 6weeks after implant placement.

• Journal of Periodontal and Implant Science
• /
• 제29권1호
• /
• pp.51-63
• /
• 1999

Exposure of the root surface due to gingival recession after periodontal surgery, elicit pain response when exposed to mechanical, heat, chemical or osmotic irritation. Especially patients treated with periodontal surgery, show high frequency. There have been reports that the 1 out of 7 patients complains of dentinal hypersensitivity. There have been many studies on the clinical effects of various materials on the treatment of dentinal hypersensitivity. The purposes of this study were to evaluate the effect of sodium chloride and potassium oxalate and to observe the relationship between the dentinal hypersensitivity and surface characteristics such as dentinal tubule size and number. This study included 20 teeth which were scheduled for extraction and had no pulpal disease. These teeth were divided into Root planing group, EDTA group, NaCl group and Oxalate group. Dentinal hypersensitivity is measured by tactile, pressured air and cold water using NRS (Numerical Rating Scales). Teeth were extracted under local anesthesia and each specimen was sectioned to a size about 3 X 5 mm and was examined under the scanning electron microscope (X2,000) The results were as follows, 1. The EDTA group exhibited significantly increased dentinal hypersensitivity comparing with the other groups. 2. The NaCl and Oxalate groups showed significantly reduced dentinal hypersensitivity comparing with the EDTA group. 3. As a method for dentinal hypersensitivity measurement, it was presumed thet tactile sensitivity test was not sensitive method but air blast test and cold water test were adequate method. 4. In a SEM study, the root planing group exhibited amorphous smear layer and showed no dentinal tubule orifice, but the EDTA group showed the large number of dentinal tubules. On the other hand, the NaCl and Oxalate groups did not show exposed dentinal tubules. The NaCl group showed more rough root surface than the EDTA group, and the Oxalate group showed many participates to be presumed as calcium oxalate particle. As the results from this study, root planing couldn't expose the dentinal tubule and NaCl and potassium oxalate occluded exposed dentinal tubule effectively. Dentinal hypersensitivity has close relationship with the exposure of dentinal tubules, especially with it's size and number.