• Journal of Dental Rehabilitation and Applied Science
• /
• v.32 no.4
• /
• pp.293-300
• /
• 2016

Purpose: The purpose of this study is finding proper bonding agents to be used when adding bis-acryl composite provisional materials. Materials and Methods: Three bonding agents with different chemical compositions were included in this study. Forty disk shaped specimens of bis-acryl composite provisional material were prepared and divided into 4 groups according to the bonding agents. Control group didn't have bonding agent. Through the Teflon mould with 4.0 mm diameter hole with 4.0 mm thickness the same bis-acryl composite provisional material was added on the disks after the surface of each specimen was treated with designated bonding agent according to the manufacturer's instructions. Shear bond test was performed and the fractured surfaces were inspected with a microscope. One-way analysis of variance was conducted and the result was further analysed with Turkey post hoc test at the significance level of 0.05. Results: The highest strength was acquired from the specimens bonded with chemical cure system and it was statistically significant (P < 0.05). This group showed 100% cohesive failures. The lowest bonding strength was recorded from the specimens used conventional light cure bonding agent, and this group's result was similar with the control group. The group used a light cure bonding agent claiming improved compatibility revealed significantly higher bond strength to the traditional light cure bonding agent group in a statistically significant way (P = 0.043). Conclusion: According to the bonding agent used the shear bond strength was significantly affected. Therefore the choice of proper bonding agent is important when hiring a bonding agent to add bis-acryl composite provisional materials.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.34 no.2
• /
• pp.89-96
• /
• 2018

Purpose: The aim of this study was to evaluate the effect of delayed time, surface treatment, and repair materials on repair of bis-acryl composite resin through comparison of shear bond strength and to evaluate the utility of bis-acryl composite resin repair using polymethyl methacrylate resin. Materials and Methods: A total of 90 bis-acryl composite resin specimens were fabricated and classified into 9 test groups, each of 10 pieces according to delayed time, surface treatment and repair material. The shear bond strength of each specimen was measured using a universal testing machine immediately after fabrication and analyzed using a statistical analysis program (IBM SPSS statistics 20). After the shear bond strength measurement, the fracture surface of the specimen was observed. Results: The highest shear bond strength ($17.54{\pm}3.14MPa$) was observed in the experimental group bonded immediately with a light-curing flowable composite resin using a bonding agent. Conclusion: When repairing bis-acryl composite resin, it is necessary to consider whether to remake according to the delayed time. For effective repair, it is desirable to consider appropriate materials and surface treatment methods according to the site or purpose of use.