• Elastomers and Composites
• /
• v.42 no.2
• /
• pp.86-92
• /
• 2007

A few of polytetrafluoroethylene(PTFE) membranes and PTFE fine powders were analyzed to chooce an optimum resin. The bi-axial stretching process was developed to set up the foundation of the preparation process and control the pore size and porosity of PTFE membrane. The pretreatment of PTFE fine powder used in the preparation process for PTFE was needed. The mixing of additives, the ripening of mixture, paste extrusion process of ripening powder, calendering process and the bi-axial process were conducted for controlling pore size, porosity and thckness of membrane. The aftertreatment which strengthened the mechanical properties was necessary. The control of pore size and porosity of the membrane were determined. The ratio of PTFE fine powder and additives at the paste extrusion process, the ripening time, the ripening temperature and the parameters of temperature and pressure at the paste extrusion process were optimized.

• Elastomers and Composites
• /
• v.42 no.3
• /
• pp.137-142
• /
• 2007

In the performance test of polytetrafluoroethylene (PTFE) membrane, melting temperature and crystallinity were $344.1^{\circ}C$ and 42.5%, respectively, according to TGA and DSC analysis. These values were similar to those of commercially available GE Osmonics PTFE membrane. The average of pore size was observed $0.716{\mu}m$ and the average flow rate was 1.570 LMH. These are slightly higher values than those of GE Osmonics sample. The filtering efficiency rate was 30.5%.