• Journal of the Korean Wood Science and Technology
• /
• v.45 no.6
• /
• pp.872-882
• /
• 2017

The objective of this study was to evaluate the properties of bamboo oriented strand board (B-OSB) from andong (Gigantochloa psedoarundinacea) and betung (Dendrocalamus asper) with and without steam treatment. Strands were steam-treated at $126^{\circ}C$ for 1 h under 0.14 MPa pressure. The extractive content of bamboo strands before and after steam treatment were determined according to a standard (TAPPI T 204 om-88). Three-layer B-OSB with the core layer perpendicular to the surface and back layers were formed and binded with 8% of phenol formaldehyde (PF) resin with the addition of 1% of wax. The evaluation of physical and mechanical properties of the boards were conducted in accordance with the JIS A 5908:2003 standard. The results showed that steam treatment of bamboo strands significantly reduced the extractive content. Steam treatment tended to increase the dimensional stability and mechanical properties of B-OSB from andong and betung. The results showed that the dimensional stability and bending strength of B-OSB from betung was higher than those of andong. The internal bond strength of B-OSB from andong was higher than betung owing to a greater amount of extractives dissolved during the steam treatment.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.1
• /
• pp.14-22
• /
• 2021

The objective of this study was to investigate the effect of alkali-washing with different sodium hydroxide concentrations on the chemical compositions of steam-treated Betung bamboo strand. Strands were subjected to steam treatment at 126 ℃ for 1 h under 0.14 MPa pressure and followed by washing with 1-5% sodium hydroxide solution for 30 sec. The alteration of structural and non-structural chemical components content of bamboo strands was evaluated. Steam and washing treatments with various concentrations of sodium hydroxide solution considerably reduced the extractive content of bamboo strands, and the cell wall chemical components of the strand in the small degree. FTIR analysis showed noticeable changes in peaks related to hemicellulose and lignin. The relative crystallinity increased significantly after steam and washing treatment with sodium hydroxide up to 3% concentration. SEM Images showed smooth and clean strands surface after washing with 3% sodium hydroxide.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.4
• /
• pp.519-532
• /
• 2019

The objectives of this study were to evaluate the effects of shelling ratio and resin content on the properties of bamboo oriented strand board (BOSB) from betung (Dendrocalamus asper) and to determine the correlation between the results of dynamic and static bending tests. Strands were steam-treated at $126^{\circ}C$ for 1 h under 0.14 MPa pressure and followed by washing with 1% NaOH solution. Three-layer BOSB with the core layer perpendicular to the surface was formed with shelling ratios (face:core ratio) of 30:70; 40:60; 50:50; 60:40 and binded with 7% and 8% of phenol formaldehyde (PF) resin with the addition of 1% of wax. The evaluation of physical and mechanical properties of BOSB was conducted in accordance with the JIS A 5908:2003 standard and the results were compared with CSA 0437.0 standard for commercial OSB (Grade O-1). Non-destructive testing was conducted using Metriguard Model 239A Stress Wave Timer which has a wave propagation time from 1 to $9,999{\mu}s$ and a resolution of $1{\mu}s$. BOSB with 8% resin content showed better physical and mechanical properties than those with 7% resin content. The increase of the face layer ratio improved the strength of BOSB in parallel direction to the grain. The results suggested that shelling ratio of 50:50 could be used as a simple way to reduce PF resin requirements from 8% to 7% and to meet the requirements of CSA 0437.0 standard. The results of non-destructive and destructive tests showed a strong correlation, suggesting that non-destructive test can be used to estimate the bending properties of BOSB.