• Journal of the Korean Wood Science and Technology
• /
• v.30 no.2
• /
• pp.121-127
• /
• 2002

This research was carried out to develop the Hanji(Korean paper) sludge·wood particle composite utilizing the waste sludges occurring from the making process of Hanji(Korean paper). At the research, four mixing ratios of white or black sludge to wood particle(10:90, 20:80, 30:70 and 40:60), three types of the resin adhesives(PMDI, urea and phenol resin) and three levels of the densities(0.60, 0.75 and 0.90) were designed to investigate the mechanical properties of Hanji(Korean paper) sludge·wood particle composite. In the white and black sludge·wood particle composites, bending properties(MOR, MOE) showed the decreasing tendency according to the increase of sludge additive, but it was clearly increased with the increase of specific gravity. Also tensile strength had the same tendency as in these bending properties. The internal bond strength of white sludge·wood particle composite had no tendency, but that of black sludge·wood particle composite was decreased as an increase of Hanji sludge additive.

• Journal of the Korean Wood Science and Technology
• /
• v.15 no.3
• /
• pp.44-55
• /
• 1987

In order to study the effect of sawdustboard combined with plastic chips, 0.5mm($T_1$), 1mm($T_2$), 1.4mm($T_3$) thick nylon fiber. polypropylene rope fiber(RP), and 0.23mm thick moth-proof polypropylene net fiber(NP) were cut into 0.5, 1, 2cm long plastic chips. Thereafter, sawdustboard combined with plastic chips prepared as the above and plastic non-combined sawdustboard(control) were manufactured into 3 types of one-, two-, and three layer with 5 or 10% combination level. By the discussions and results at this study, the significant conclusions of mechanical and physical properties were summarized as follows: 1. The MORs were shown in the order of 3 layer> 2 layer> 1 layer among plastic non-combined boards, and $T_3$ < $T_2$ < $T_1$ < RP (NP(5%) < NP(l0%) among plastic combined boards. In 2cm long plastic chip in 1 layer board, the highest strength through all the composition was recognized. 1 layer board showing the lower strength with 0.5cm plastic chip rendered to the bending strength improvement by 2 or 3 layer board composition. On the other hand, 2 or 3 layer combined with 1, 2cm long polypropylene net fiber chips incurred MOR's conspicuous decrease requiring optimum plastic chip combined level and consideration to combined type. 2. MOE in plastic non-combined 3 layer board exhibited sandwich construction effect by higher resin content application to surface layer in the order of 3layer>1layer>2layer with the highest stiffness of the board combined with polypropylene chip, while nylon chip-combined board had little difference from plastic non-combined board. In relevant to length and layer effect, 3 layer board combined with the 0.5cm long polypropylene net fiber chip in 5% and 10% combined level presented 34-43% and 44-76% stiffness increase against plastic non-combined board(control), respectively. Moreover, in 1 layer board, 30% stiffness increase with 10% against 5% combined level in the 1 and 2cm long polypropylene net fiber chip was obtained. 3. Stress at proportional limit(Spl) showing the fiber relationship (r: 0.81-0.97) between MOR presented in the order of 1 layer<2 layer<3 layer in plastic non-combined board. Correspondingly, combined effect by layer and plastic chip length was similar to MOR's. 4. Differently from previous properties(MOR, MOE, Spl). work to maximum load(Wml) of 2 layer board approached to that of 3 layer board. Conforming the above phenomenon. 2 layer combined with 0.5cm long polypropylene net fiber chip kept the greater work than 1 layer. The polypropylene combined board superior to nylon -and plastic non - combined board seemed to have greater anti - failing capacity. 5. Internal bond strength(IB), in contrast to MOR's tendency. showed in the order of T1

• Journal of the Korean Wood Science and Technology
• /
• v.40 no.1
• /
• pp.26-37
• /
• 2012

Recently, the demand and supply on the Hanok have been increased. However, Hanok should be requested larger section of structural members because of excessive roof weight. So, structural skin-timber was manufactured to get a lightweight structural member. The structural skin-timber has exterior shape with larger section but a great volume of wood be removed. The reduced strength of structural skin-timber can be supplemented by hybridizaion of structural member. Japanese larch and Domestic pine were used to manufacture the structural skin-timber. Structural skin-timbers of rectangular shape and cylinder shape were manufactured and tested to evaluate the bending properties. The intended strength property could not be obtained because member had been suffered severe damage by precision deficiency of manufacturing machine. However, if precision of manufacturing machine would be improved and additional hybridizaion of structural skin-timber would be done, lightweight structural member will be able to be manufactured. Structural skin-timber did not showed statistical significancy between two species, so it is possible to use pine mixed with larch. Only MOR of larch showed statistical significancy between rectangular shape and cylinder shape, so it is necessary to use of those as separate things. However, the rest of skin-timber can be judged mixed using because of non statistical significancy. The objective of this study was the development of lightweight larger structural member with relatively strength. If hybrid member of skin-timber could be developed with wood-ceramics, lightweight steel and more, it can be possible to be used as a building material of Hanok, interior material, post & beam construction material and more.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.4
• /
• pp.18-26
• /
• 1995

국내 합판 산업계는 오랫동안 남양재 활엽수를 주로 사용하여 왔으나, 환경 보존적인 측면에서 열대재의 벌채를 규제하는 등 여러 요인으로 인하여 합판용 원목의 수입이 어려워지고 있다. 이에 대응하기 위하여 합판용 원목을 침엽수재로 대체할 필요가 있으며, 침엽수 합판 제조를 위한 기초 자료를 제공하기 위하여 본 연구를 수행하였다. 공시 수종은 국내에서 조림한 낙엽송과 시베리아산 낙엽송 및 뉴질랜드산 라디에타 소나무였으며, 공시원목으로부터 얻어진 단판의 품질과 이들 단판으로 제조한 합판의 접착력과 휨강도를 조사하였다. 이면 할렬실험에서 시베리아산 낙엽송은 다른 수종에 비해 할렬 밀도가 낮게 나타났다. 단판 품질은 접착력 및 휨강도에 거의 영향을 미치지 않았으나 합판의 휨강도에서는 심재와 변재에 따른 차이가 있음을 알 수 있었다. 이는 합판제조사 심재와 변재를 구별하여 사용할 필요가 있었다. 라디에타 소나무의 변재부로 만든 합판 MOR은 다른 수종에 비해 우수하게 나타났다. 접착력 실험에 있어서는 페놀 접착제를 사용하여 만들어진 합판만이 구조용으로써 사용할 수 있음을 알았다. 목파율은 동일 수종 합판에서는 라디에타 소나무 구성이 가장 높게 나타났으며, 이수종(異樹種) 합판에서는 표판을 국산 낙엽송, 심판을 라디에타 소나무를 사용하여 만든 합판에서 가장 높게 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.4
• /
• pp.456-462
• /
• 2015

365 pieces of domestic $38{\times}140{\times}3600mm$ Red pine structural lumber were machine graded conforming to a softwood structural lumber standard (KS F 3020). The allowable bending stresses calculated for each grade were compared with the values currently tabulated in the standard. Four calculation methods for lower $5^{th}$ percentile bending stress were non-parametric estimation with 75% confidence level, 2-parameter and 3-parameter Weibull distribution fit, and bending modulus of rupture (MOR)-modulus of elasticity (MOE) regression based method. Only the data set of Grades E8, E9, and E10 were statistically eligible for the $5^{th}$ percentile calculation. The MOR-MOE regression based method only was able to estimate the lower $5^{th}$ percentile values theoretically for the full range of grades. The results showed that all allowable bending stresses calculated were lower than the design values tabulated in the standard. This implies that the current machine grading system has the pitfall of structural safety. Improvement in current machine grading system could be achieved by introducing the bending strength and stiffness combination grade system.

• Journal of Korea Foresty Energy
• /
• v.25 no.2
• /
• pp.49-54
• /
• 2006

This study was carried out to provide basic data for using domestic structural softwood lumber efficiently and ensuring structural safety of timber structures. The ratios (k-factor) between static and dynamic MOE measured by ultrasonic device for $2{\times}6$ domestic softwood structural lumber are 1.0602 for Korean red pine, 1.0013 for Korean white pine and 1.2320 for Japanese larch. In machine grade using nondestructive method, 76% of Korean red pine was classified into higher than E9 grade, 85% of Korean white pine was sorted into higher than E7 grade and 68% of Japanese larch was classified into higher than E11 grade. Correlation between MOE and MOR by static bending with k-factor from nondestructive method provide a possibility to predict bending strength and allowable stress of domestic softwood structural lumber.

• Journal of the Korean Wood Science and Technology
• /
• v.29 no.3
• /
• pp.47-58
• /
• 2001

For finding both ways of recycling the wood and plastic wastes and solving the problem of free formaldehyde gas emission through manufacturing wood particle-polypropylene fiber composite board without addition of formaldehyde-based thermosetting resin adhesive, control particleboards and nonwoven web composite boards from wood particle and polypropylene fiber formulation of 50 : 50, 60 : 40, and 70 : 30 were manufactured at density levels of 0.5, 0.6, 0.7, and 0.8 g/$cm^3$, and were tested both in the physical and mechanical properties according to ASTM D 1037-93. In the physical properties, control particleboard had significantly higher moisture content than composite board. In composite board, moisture content decreased with the increase of target density only in the board with higher content of polypropylene fiber and also appeared to increase with the increase of wood particle content at a given target density. Control particleboard showed significantly greater water absorption than composite board and its water absorption decreased with the increase of target density. In composite board, water absorption decreased with the increase of target density at a given formulation but increased with the increase of wood particle content at a given target density. After 2 and 24 hours immersion, control particleboard was significantly higher in thickness swelling than composite board and its thickness swelling increased with the increase of target density. In composite board, thickness swelling did not vary significantly with the target density at a given formulation but its thickness swelling increased as wood particle content increased at a given target density. Static bending MOR and MOE under dry and wet conditions increased with the increase of target density at a given formulation of wood particle and polypropylene fiber. Especially, the MOR and MOE under wet condition were considerably larger in composite board than in control particleboard. In general, composite board showed superior bending strength properties to control particleboard, And the composite board made from wood particle and polypropylene fiber formulation of 50 : 50 at target density of 0.8 g/$cm^3$ exhibited the greatest bending strength properties. Though problems in uniform mixing and strong binding of wood particle with polypropylene fiber are unavoidable due to their extremely different shape and polarity, wood particle-polypropylene fiber composite boards with higher performance, as a potential substitute for the commercial particleboards, could be made just by controlling processing variables.

• Journal of Forest and Environmental Science
• /
• v.36 no.3
• /
• pp.219-224
• /
• 2020

Urea formaldehyde resins are widely used in the manufacturing of wood composite and their usage is always combined with release of formaldehyde characterized to be hazardous to health during and after the manufacturing of the products. This study investigates the effectiveness of wood-based adhesive from oil of pyrolysed Triplochiton scleroxylon sawdust for the production of composite board. The wood-derived Pyrolytic Oil (PyO) was blended with Urea Formaldehyde (UF) resin to formed Pyrolytic Oil-Urea Formaldehyde (PyOUF). The obtained PyOUF called Wood-Based Adhesives at four blends and control (UF) viz; 1:1, 1:2, 1:3, 2:1, 1:3 were further employed to prepare the composite board and test for their bonding strength by physical (water absorption-WA and thickness swelling-Th.S) and mechanical properties (modulus of elasticity-MOE, modulus of rupture-MOR, and impact bending-IB). Data obtained was analysed using analysis of variance at α 0.05. The result of analysis of variance conducted on physical properties show significant difference (p≤0.05) between the WA values obtained when testing the different blending proportion of PyOUF and likewise between 2 and 24 h of immersion. PyOUF had significant effect (p≤0.05) on Th. S for 24 h but no significant different (p>0.05) for the 2 h period of soaking. The analysis of variance on mechanical properties of the composite board (MOE, MOR, and IB) show significance differences (p≤0.05) between the strength values obtained when testing the different ratios of PyO with UF. PyO content influenced the properties of the boards and it is evident that PyO can be used in the manufacture of composite board.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.2
• /
• pp.245-252
• /
• 2020

This study was performed to analyze the mechanical properties of tropical hybrid cross-laminated timber (CLT) with bamboo laminated board as the core layer in order to evaluate the possibility of its use as a CLT material. Bamboo board was used as the core layer and the tropical species Acacia mangium willd., from Indonesia, was used as the lamination in the outer layer. The modulus of elasticity (MOE), modulus of rupture (MOR), and shear strength of the hybrid CLT were measured according to APA PRG 320-2018 Standard for Performance-Rated Cross-Laminated Timber. The results show that the bending MOE of the hybrid CLT was found to be 2.76 times higher than SPF (Spruce Pine Fir) CLT. The reason why the high MOE value was shown in bamboo board and hybrid CLT applied bamboo board is because of high elasticity of bamboo fiber. However, the shear strength of the hybrid CLT was 0.8 times lower than shear strength of SPF CLT.

• Journal of the Korea Furniture Society
• /
• v.27 no.4
• /
• pp.302-308
• /
• 2016

It has been known that acetylation improves the dimensional stability of wood. Liquid phase acetylation is more popular than gas-phase acetylation for the effectiveness of weight gain of wood. In this study the specimens of domestic red and Korean pines are acetylated in liquid phase and their physical properties, such as density, bending strength, anti-hygroscopicity etc., are analyzed. Acetylation increases the average weights and volume of larch specimens by 11.4% and 3.4%, respectively, and their average oven-dry densities are increased by $0.03g/cm^3$. Acetylation does not influence on Modulus of Rupture (MOR) and Modulus of Elasticity (MOE). The average Percentage Reduction in Hygroscopicity (PRH) and average Percentage Reduction in Water soaking (PRW) of larch specimens are respectively 20.2% and 20.8%. Thus it can be concluded that acetylation improves the dimensional stability of larch specimens.