• Journal of the Korean Wood Science and Technology
• /
• v.30 no.2
• /
• pp.121-127
• /
• 2002

This research was carried out to develop the Hanji(Korean paper) sludge·wood particle composite utilizing the waste sludges occurring from the making process of Hanji(Korean paper). At the research, four mixing ratios of white or black sludge to wood particle(10:90, 20:80, 30:70 and 40:60), three types of the resin adhesives(PMDI, urea and phenol resin) and three levels of the densities(0.60, 0.75 and 0.90) were designed to investigate the mechanical properties of Hanji(Korean paper) sludge·wood particle composite. In the white and black sludge·wood particle composites, bending properties(MOR, MOE) showed the decreasing tendency according to the increase of sludge additive, but it was clearly increased with the increase of specific gravity. Also tensile strength had the same tendency as in these bending properties. The internal bond strength of white sludge·wood particle composite had no tendency, but that of black sludge·wood particle composite was decreased as an increase of Hanji sludge additive.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.4
• /
• pp.57-64
• /
• 1999

This research was carried out to investigate the effects of density, resin and particle types on the physical and mechanical properties of the composites made from various wood particles mixed with coating paper. The experiment was designed to apply with three particles (flake, chip, and fiber) and three resin types (urea, phenol and PMDI resin). The mixed ratio of coating paper to wood particle was fixed on 50 to 50% in each board making. And also it was designed to apply for four density levels (0.6, 0.7, 0.8 and 0.9 g/$cm^3$) and four mixed formulations of coating paper to wood particle (10:90, 20:80, 30:70, and 40:60 %) to analyze clearly the effects of PMDI resin. Coating paper-wood particle composites have acceptable bending strength (MOR, MOE) though the mixed ratio of coating paper was increased, but have low internal bond strength and poor dimensional stability (WA, TS, LE). Composites with high density had higher mechanical properties but showed lower physical properties than composites with low density. In conclusion, at least up to 20% mixed ratios, coating paper-wood particle composites have acceptable physical and mechanical properties, and PMDI resin has possibility for coating paper-wood particle composite manufacture.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.1
• /
• pp.37-49
• /
• 1999

The effect of fire-retardant treatment and redrying on the mechanical properties of radiata pine sapwood were evaluated. Small, clear specimens were treated with three different fire-retardant(FR) chemicals, borax-boric acid(BRX), minalith(MIN), and pyresote(PYR), with target retentions of 30 and 60kg/$m^3$, and then redried at maximum dry-bulb temperature of $25^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$ or $110^{\circ}C$. Each specimen, including untreated and water-treated controls, was tested in static bending and in compression parallel to grain. The extent of strength reduction was dependent on the type of FR chemicals, retention, and redrying temperature, and a highly significant interaction existed between FR treatment and redrying temperature. Modulus of rupture(MOR) and work to maximum load(WML) were significantly decreased by FR treatment and redrying. None of three FR chemicals adversely affect modulus of elasticity (MOE) and maximum crushing strength(MCS). MOE of BRX treatment and MCS of both BRX and PYR treatment increased significantly compared to untreated controls. No significant differences existed between retention levels except for MOE and MCS of some combinations of FR chemicals and redrying temperatures. Although MOE and MCS was not significantly affected by any of the redrying temperatures, these properties were generally decreased with the increase in redrying temperature. The significant reduction in MOR and WML was observed in BRX treatment when dried at temperatures of $60^{\circ}C$ and above, and in MIN and PYR treatment when dried at temperatures of $80^{\circ}C$ and above. Consequently, BRX-treated radiata pine should not be redried at temperatures >$60^{\circ}C$, and MIN- and PYR-treated radiata pine should not be redried at temperatures > $80^{\circ}C$ where bending strength and energy-related properties are important design considerations.

• Journal of the Korean Wood Science and Technology
• /
• v.18 no.4
• /
• pp.86-101
• /
• 1990

The primary objective of this research was to investigate the strength properties of Comply, a composite panel. fabricated with particle board as core material and veneer or plywood as face and back. 20types of comply composites were manufactured according to the four specific gravity levels(0.5, 0.6, 0.7 or 0.8) of particleboard core and three veneer or two plywood thicknesses for face and back. They were tested and compared with matching particleboard (control) on moisture content. specific gravity, bending properties(MOE, MOR SPL). nail resistance and internal bond strength. The obtained results were summarized as follows: The increasing effect of modulus of elasticity was shown by the increase of face and back veneer or plywood thickness. The modulus of rupture and stress at proportional limit of the comply composites bonded with 3mm thick veneers or 3mm thick plywood face and back were higher than 2mm thick veneer or 2mm thick plywood as face and back. Both of modulus of rupture and stress at proportional limit on bending of Comply were higher than those of control board. Also the modulus of elasticity of Comply showed much higher than that of control board. The nail resistance of Comply, composed of plywood as face and back was higher than that of veneer. The nail resistance of control board was higher than that of Comply at Sp.Gr 0.7 and 0.8 core boards. Internal bond of Comply, composed of 1mm and 2mm thick veneer as face and back was higher than that of 3mm thick veneer. The increasing effect of modulus of elasticity was shown by the increase of shelling ratio in Comply composed of veneer and plywood as face and back. The modulus of rupture was increased by the increment of shellmg ratio in Compiy, composed of plywood as face and back. The modulus of elasticity and modulus of. rupture of comply were higher than those of particleboard(control) in effect of shelling ratio. Therefore it was concluded that the mechanical property values of Comply were clearly greater than those of particleboard(control).

• Journal of the Korean Wood Science and Technology
• /
• v.22 no.1
• /
• pp.44-53
• /
• 1994

This research was carried out to investigate the effect of paper sludge addition on formaldehyde emission, and physical and mechanical properties of UF-particleboard. In order to investigate the effect of paper sludge addition to resin, particleboards were bonded with urea-formaldehyde resins containing 5, 10, 15% paper sludge powders of three types(A Type: -200 mesh, B Type: -100~+200 mesh. C Type: -50~+100 mesh), based on weight of resin solid. Also the effect of paper sludge addition to furnish was studied from particleboards fabricated with ratios of sludge to particle of 5:95, 10:90, 15:85 based on oven-dry weight. Tests were conducted on the manufactured particleboards to determine formaldehyde emission, bending properties, internal bond strength and thickness swelling. The obtained results were summarized as follows: The addition of paper sludge powder to resin yielded a higher pH of cured resin. Formaldehyde emission decreased with the increase of paper sludge powder addition to resin and paper sludge composition ratio to furnish. Particleboard bonded with urea-formaldehyde resin containing paper sludge powder and particleboard mixed with paper sludge have similar bending properties(MOR, MOE) and thickness swelling compared with control particleboard. Internal bond strength of particleboards treated with paper sludge were lower than that of control particleboard. The use of paper sludge as scavenger was achieved reduction of formaldehyde emission without depression of physical and mechanical properties of particleboard. Also the use of paper sludge was able to concluded that there is possibility of partial substitution of wood particle materials.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.31-37
• /
• 1999

This study was carried out to develop the Korean paper(Hanji) sludge-wood fiber composite boards utilizing the relinquished sludges occurring from the making process of Korean classic paper Hanji. The bark of paper mulberry(Broussonetia kazinoki Sieb.) has been used as a raw material since past hundreds and thousands years. Korean paper(Hanji) sludge was divided into two kinds, the one was the white sludge from the first stage and the other was the black sludge occurring from the final stage of Korean paper(Hanji) making. Four levels of the mixed ratio of each white or black sludge to wood fiber(10:90, 20:80, 30:70 and 40:60), three levels of the resin adhesives(PMDI, urea and phenol resin) and three levels of the density(0.60, 0.75 and 0.90) were designed to investigate the mechanical properties of Korean paper(Hanji) sludge-wood fiber composite boards. From the results and discussion, it could be concluded as follows : 1. In the white and black sludge-wood fiber composite boards, bending modulus of rupture showed the clear decreasing tendency according to the increase of sludge additive, but it was clearly increased with the increase of specific gravity. Modulus of elasticity showed the same tendency as in the modulus of rupture, and also tensile and internal bonding strength had the same tendencies as in these bending properties. 2. Among the resin adhesives, PMDI or urea resin showed great values in MOR of white sludge-wood fiber composite board, but urea resin was greater than PMDI in MOR and MOE of black sludge-wood fiber composite board. Tensile and internal bonding strength showed the same tendencies as in white sludge-wood fiber composite board. 3. It is suggested that the white sludge-wood fiber composite boards bonded with PMDI or black sludge-wood fiber composite boards bonded with urea resin were able to made similar boards to general fiberboard by the mixed ratio 20:80 of sludge to wood fiber.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.3
• /
• pp.184-191
• /
• 2009

In the southern part of the Korean Peninsula including Jeju-island, the production amount of domestic cedar has increased gradually. However, their low qualities, expected to be caused by the low density and frequent knots, have restricted their practical utilization as the high value-added products. In this study, it is aimed to look for the new uses of domestic cedar and to examine the applicability for lamination lumbers of structural glued laminated timber (glulam). Above all, machine stress ratings for individual sawn lumbers confirmed that modulus of elasticity (MOE) of cedar lumber was lower than that of other common softwood species in Korea. On the other hand, cedar lumbers have enough stiffness to manufacture the structural glulam in accordance with Korean Industrial Standard (KS). The bonding strength and durability also met the KS limitation. Nevertheless, from the result of bending tests for cedar glulam, it was shown that the modulus of elasticity (MOE) did not meet the KS limitation. Therefore, it was concluded that additional researches were needed for reinforcing the stiffness of cedar glulam.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.2
• /
• pp.55-69
• /
• 1995

The primary objective of this research was to investigate optimum manufacturing condition of thin composite panels composed of sawdust, polyethylene film and polypropylene net. At the study the experiment was designed to make thin board in which sawdust offers effectiveness as core composing material, polyethylene as adhesive with added urea resin, and polypropylene as stiffness and flexibility in the composition panel. 100 types of thin composite panels were manufactured according to press-lam and mat-forming process of various hot pressing conditions(pressure, temperature and time). They were tested and compared with control boards on bending properties(MOR, MOE, SPL, WML), internal bond strength, thickness swelling, linear expansion and water absorption. At the same time the visual inspections of each types of panels were accomplished. The physical and mechanical properties of composite types passed by visual inspection were analyzed by Tukey's studentized range test. From the statistical analysis, the optimum manufacturing condition of thin composite panels were selected. Compared with two manufacturing processes, mat-forming process performed better than press-lam process in all tested properties. The optimum manufacturing conditions resulted from the experiment and statistical analysis were able to determine as following: the press temperature was shown the most good result at 130$^{\circ}C$ in mat forming process and 140$^{\circ}C$ press lam process, the press time 4 min in both processes, but the press pressure was 25-10kg/$cm^2$ in mat forming and 15k/$cm^2$ press lam process.

• Journal of the Korean Wood Science and Technology
• /
• v.14 no.1
• /
• pp.3-44
• /
• 1986

In order to obtain the basic physical and mechanical properties of steel wire reinforced particleboard, particleboards were formed with large particles through 2.11 mm (12 meshes) and retained on 1.27mm (20 meshes) sieves and small particles through 1.27mm (20 meshes) and retained on 0.42mm (60 meshes) sieves from the plywood mill wastes of meranti (Shorea spp.) in the form of pallmanchips, applying urea-formaldehyde resin as an adhesive on the particle surface in 10 percent on the oven dried weight of particles, and arranging steel wires of 1mm in diameter 5,10,15,20, and 25mm in longitudinal and transverse direction with crossing in the mid of the board depth in single layer boards, 10mm in longitudinal or transverse direction without crossing in two layers and 10mm in longitudinal and transverse directions with and without crossing in three steel wire layers boards. The stepwise 9-minutes-multi-pressing schedule in 5 minutes at 35 kgf/$cm^2$, 2.5 minutes at 25 kgf/$cm^2$. and 1.5 minutes at 15 kgf/$cm^2$ was applied for $300{\times}200{\times}13$mm board at the temperature of 160$^{\circ}C$ in a hot press. Specific gravity, thickness swelling, bending properties of modulus of rupture (MOR), modulus of elasticity(MOE), work to proportional limit, and work to ultimate load, internal bond (IB), and screw holding power(SHP) of the reinforced boards were analyzed on the wire openings and wire layers. The results obtained are summarized as follows; 1) In specific gravity, particleboards with large particles and small particles had higher value with more steel wire placements and more steel layers composition, 2) Particleboards with large particles in accordance with more steel wire liners composition gave very poor thickness swelling. 3) The mechanical properties of particleboards formed with large or small particles were reinforced with more steel wire layers. Therefore, bending strength was improved in modulus of rupture, modulus of elasticity, and work to ultimate load. Especiallv, particleboards with two or three steel wire layers showed the tension lamination effect when the steels in lower steel wire layer were oriented parallel to the board length. 4) The modulus of rupture, modulus of elasticity, and work to ultimate load in bending varied with opening area, distance of lengthwise wires multipled by distance of transverse wires. Particleboards formed with large particles resulted in higher value in modulus of rupture with 1.5-3 $cm^2$ opening area, 1-2cm distance between transverse wires, and 1.5-2.5cm distance between lengthwise wires. Particle boards formed with small particles showed higher value with 0.5-1.5$cm^2$ or 3.75-6.25 $cm^2$ opening area, 0.5 or 2.5cm distance between transverse wires. 5) In modulus of elasticity, particleboards formed with large particles with one steel wire layer suggested higher value with 5-3$cm^2$ opening area, 1-2.5cm distance between transverse wires and also 1-2.5 cm distance between lengthwise wires. Particleboards formed with small particles showed higher value with 0.75-1.25$cm^2$ or 3-6.25$cm^2$ opening area and 0.5 or 2.5cm distance between transverse wires. 6) Particleboards formed with large particles gaved higher value in work to ultimate load with 1-3$cm^2$ opening area. Particleboards formed with small particles showed increasing tendancy with decreasing opening area. 7) In internal bond and screw holding power, particleboards formed with large particles had increasing value in two and three steel wire layers compositions, but particleboards formed with small particles showed no difference. Particleboards formed with large particles containing one steel wire layer showed no difference in internal bond and screw holding power, and particleboards formed with small panicles containing one steel wire layer resulted in increasing value in internal bond and decreasing value in screw holding power in accordance with increase in opening area.