• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.155-160
• /
• 2003

The effect of the temperature, current density and deposit time on hard chromium deposition in trivalent chromium bath was investigated. Cathode current efficiency increased with increasing current density. Increasing bath temperature from $20^{\circ}C$ to $50^{\circ}C$, chromium deposits were produced in higher current density and the maximum current efficiency was increased. At the plating conditions of $40^{\circ}C$, $30A/dm\m^2$, the deposition thickness increased in proportion to increasing electrolysis time The rate is$ 90\mu\textrm{m}$/hrs. for 2 hours. Microhardness of chromium deposits increased with increasing bath temperature and decreasing current density, and it was constant with electrolysis time. All of bath conditions, microstructure of chromium deposits has nodular structure with some cracking pattern and nodule size increased with increasing deposit thickness.

• Journal of the Korean institute of surface engineering
• /
• v.17 no.3
• /
• pp.78-86
• /
• 1984

Hard anodic oxide film was investigated formed on pure aluminium with various temperature (30$^{\circ}-60^{\circ}C$), current densities (1.5-3.0A/$dm^2$) and concentrations(3-15g/l) of oxalic acid in 0.5M malic acid bath. The resulting characteristic of the anodic oxide film obtained were summarized as follows in the view point of physical and mechanical properties in relation with the above process variables. 1. The film thickness increased with oxalic acid concentration and bath temperature, while the reversed phenomena were obtained at a high concentration of oxalic acid and high temperature due to the severe dissolution of the anodic oxide film. 2. The hardness and the abrasion resistance were improved by lowering the addition of oxalic acid and the bath temperature. This feature was directly dependent on the porosity formed on the anodic oxide film. 3. The maximum hardness of anodic oxide film showed Hv 579 in the temperature of 30$^{\circ}C$ with the current density, 2.5A/$dm^2$ in the 0.5M malic acid bath mixed with 5g/l oxalic acid.

• Journal of Home Health Care Nursing
• /
• v.24 no.2
• /
• pp.189-199
• /
• 2017

Purpose: This study aimed to investigate the effects of foot bath therapy on the symptom intensity, distress, and interference with usual activities due to chemotherapy-induced peripheral neuropathy (CIPN) in patients with metastatic and recurrent cancer. Methods: Foot bath therapy was administered to the experimental group for >8 sessions in 2 weeks, and the chemotherapy-induced peripheral neuropathy assessment tool (CIPNAT) was used to measure its effects on the symptom intensity, distress, and interference with usual activities due to CIPN. SPSS was used to perform data analyses including descriptive statistics, chi-square test, Fisher's exact test, t-test, paired t-test, and repeated measures ANCOVA. Results: A statistically significant difference in the variation of the symptom intensity, distress, and interference with usual activities due to CIPN was observed between the two groups; however, a statistically insignificant difference was observed between the groups and time of interaction. Conclusion: Foot bath therapy can be used as a simple and effective clinical or home care nursing intervention to improve the symptom intensity, distress and interference with usual activities due to CIPN.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.2
• /
• pp.47-50
• /
• 2010

This work discusses a two-step electroless plating method for preparing a Pt thin film on p-type InGaAs substrate, which is defined as Pt I and Pt II. A thin Pt catalytic layer formed in Pt I bath on the substrate at $65^{\circ}C$. In the following Pt II bath, thick Pt films then easily grew on the sensitized layer on InGaAs previously formed in the Pt I bath. The growth of Pt film is strongly influenced by the plating temperature and pH value. To study the plating time effect, the plating of Pt II bath is 5 to 40 min at $80^{\circ}C$ after using Pt I bath at 50~$65^{\circ}C$ for 5min of pH 8~13. Pt film for ohmic contact to p-type InGaAs was successfully prepared by using the two-step Pt electroless plating.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.2
• /
• pp.140-145
• /
• 1996

Silver deposits formed on copper substrates by replacement reactions show poor adhesion, and a silver film plated on such a deposit does not adhere. Silver ion makes a highly stable complex with cyanide ion, so that in a silver cyanide solution, the activity of silver ion is very small. This is one of the reasons for the universal use of cyanide baths in the industrial silver plating. However, the consideration of the difference between the values of the stability constants for bath the silver-iodide complex and the copper-iodide complex suggest that the rate of replacement deposition of silver on the copper substrate in si]ver-potassium iodide solution, could be comparatively low. To confirm this, the rate of replacement deposition of silver in both a silver-potassium iodide solution ($AgNO_3$0.10 mol/L, KI 2.00 mol/L ) and a strike silver plating bath (AgCN 0.028 mol/L, KCN 1.15 mol/L ) was estimated from the current density corresponding to the point of intersection of the anodic and the cathodic polarization curves. These estimated values were almost the same, and it is suggested that the silver-potassium iodide solution is not only a cyanide free silver plating bath capable of employing a copper substrate but a silver plating bath which requires no strike plating.

• Journal of Korea Multimedia Society
• /
• v.22 no.2
• /
• pp.242-249
• /
• 2019

Old people and patients with cardiovascular disease could die of a heart attack in the bath with heated water for a long time. Various researches have been studied to prevent these accidents from happening such as measuring the ECG signal when taking bath. However, these devices are hard to use and the higher price is not easily accepted by the public. In this paper, a low-cost and use-friendly, real time high precision water temperature monitoring device to prevent heart attack in the bath was developed. The device with waterproof design that lets the device can float on the surface of the water, and an accurate way to make water temperature measurement method was proposed by this paper that is immerging the sensor into water with 4cm depth to measure the temperature of underwater. The manufactured device was conducted to two experiments; one was to verify the basic functions of the device, and another one was for compare the proposed device with commercial products for monitoring the water temperature in the bathtub. As the experimental results shown, the proposed device has stable performance for the water temperature measurement and communicating with laptop in wireless.

• Korean Journal of Metals and Materials
• /
• v.48 no.3
• /
• pp.225-234
• /
• 2010

Salt bath nitriding, which has been developed recently by domestic company, is an emerging ecofriendly surface treatment. The salt bath nitriding is accompanied by the electrolysis process in the pretreatment step, and this whole processis called Pseudo-Electrolysised Salt bath Nitriding (PESN). The PESN creates only $NH_3$ and non-toxic salts without harmful $CN^{-}$ or toxic gas such as that found in previous salt bath nitriding. In general, ion nitriding and gas nitriding create high hardness and a strong brittle white layer on the surface. However, the PESN shows a thin white and gray layer. The PESN was applied to the defense material, 3%Cr-Mo-V steel, to study the surface characteristics at $480^{\circ}C$, $530^{\circ}C$, and $580^{\circ}C$ for 4 hrs, 20 hrs, 40 hrs, and 60 hrs of nitriding time condition. As a result, the best nitriding layer was found at $530^{\circ}C$ for 40 hrs. If we improve corrosion resistance and nitriding layer depth, the PESN will be able to be applied to the defense industry parts.

• Journal of the Korean institute of surface engineering
• /
• v.11 no.3
• /
• pp.3-9
• /
• 1978

Organic compounds, such as aldehydes, amines, amides, sulfur compounds of polymers, have been added to cyanide Zinc electroplating bath to achieve in improvement of the brightness and of the current efficiency. It was found that the addition of only one compound o these organic compounds in the bath were unsuitable to be used for brightener, but mixure of aldehyde and reaction products obtained from epoxides and amines and/or amides were suitable for brightener in cyanide zinc electroprating baths.

• Textile Coloration and Finishing
• /
• v.4 no.1
• /
• pp.10-15
• /
• 1992

Differential dyeing technologies for wool are discussed in one bath dyeing of cationic compound treated wool and untreated wool. By increasing the concentration of cationic compound to wool the k/s value of wool and the color difference (ΔE) between treated and untreated one become higher in one bath dyeing. The proper concentration of cationic compound to wool was 2% in one bath dyeing since the dyeing fastness became lower according to the increase of the concentration.

• The Journal of Korean Medical History
• /
• v.14 no.1
• /
• pp.61-78
• /
• 2001

Time and places of hot spring-bath were diverse such as at succeeding to the throne, after abdication, during Crown Prince and etc. Generally, average staying time was about 20 days. Beside the healing purpose, hot spring-bath was taken to inspect the people's conditions, to reduce compulsory labor or tax, to carry out "Kwagoh", the old state examination or to console the people.