• Textile Coloration and Finishing
• /
• v.30 no.4
• /
• pp.227-236
• /
• 2018

As consciousness of safety becomes an important social issue, the demand for protective clothing is increasing. Conventional flame-retardant cotton working wear has low durability, and working wear with m-aramid fibers are stiff, heavy, less permeable, and expensive. In this study, recycled m-aramid and cotton have been blended to produce woven fabric of different compositions to enhance high performance and comfort to solve aforementioned problems. The fabrics were analyzed according to constituents and various structural factors. Mechanical properties were measured using KES-FB system. The measured thermal properties are TGA, $Q_{max}$, TPP and RPP. Fabric with polyurethane yarn covered by m-aramid/cotton spun yarn is observed to have good wearability. The fabric of open end spun yarn showed more stiffness than that of ring spun yarn. The sample with the high count of yarn has more smooth surface. In addition, high m-aramid content fabric is considered to have relatively high stiffness when using as clothing. In TGA the fabric with higher m-aramid content showed more stable decomposition behavior. The fabric having rough surface showed lower heat transfer properties in $Q_{max}$. The influence of the fabric thickness was important in convection and radiant heat test.

• Textile Coloration and Finishing
• /
• v.25 no.4
• /
• pp.262-270
• /
• 2013

Temporarily solubilized reactive disperse dyes containing ${\beta}$-sulfatoethylsulfonyl group were applied to 100% meta-aramid knitted fabric and their dyeing properties were investigated. Reactive disperse dyes showed relatively high K/S values on meta-aramid fabric when compared with conventional disperse dye or reactive dye, which showed very low K/S values. Color yields of reactive disperse dyes were highly dependent on dyeing pH and optimum results were obtained at pH 6. Percent exhaustion of reactive disperse dye on meta-aramid fabric was over 80% at 2% o.w.f of dye concentration. Wash fastness of pyridone-based reactive disperse dyes was very good to excellent while that of aminoazobenzene reactive disperse dyes was medium to good. Light fastness of all the reactive disperse dyes was very poor which seems to be due to the low photostability of meta-aramid fiber itself.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.10a
• /
• pp.35-36
• /
• 2008

A diblock copolymer($PEO_{45}$-MeDMA) derived from [2-(methacryloyloxy) ethyl] trimethylammonium chloride(MeDMA) was synthesized and applied to the meta-aramid fibers. Meta-aramid fabric was pretreated with $PEO_{45}$-MeDMA and successfully dyed with acid dyes. The dyeability of this fabric was investigated and found to depend on the $PEO_{45}$-MeDMA concentration, pH, and dye concentration. The color fastness properties of the copolymer pretreated dyed fabric was evaluated.

• Textile Coloration and Finishing
• /
• v.29 no.1
• /
• pp.18-24
• /
• 2017

Meta-aramid fabric has been widely used as the reinforcement of composites due to its high flame resistance and tearing strength. Functionality such as abrasion resistance of fabric is very important for specialty fabrics used in car racing suits. In this study, to improve abrasion resistance property of meta-aramid fabric, silicon deposition was conducted by utilizing RF magnetron sputtering. The sputtering process parameters effects were investigated as sputtering power and substrate temperature. The obtained results suggest that the silicon deposition on the meta-aramid fabric has obvious effect upon increasing the abrasion resistance, the thermal insulation and the electric resistance condition for silicon deposition was established. In conclusion, the results of this study have made it possible to manufacture meta-aramids with higher abrasion strength.

• Textile Coloration and Finishing
• /
• v.34 no.3
• /
• pp.173-184
• /
• 2022

In this study, the TPU film was laminated on an aramid fabric or circular knits in order to implement an air cushion material that can respond to high impact forces in case of a fall and is easy to expand. To increase the bonding strength between the fabric layer and the film layer, a primer layer was formed in two ways: one for thermally bonding and laminating PET film and two for coating and aging hot melt type PUR adhesive. The tensile strength of the aramid air cushion was 2.5 times higher than that of the circular knits, but the tensile elongation of the aramid air cushion was very low compared to that of the circular knits. The tear strength of the aramid air cushion was about twice or more superior to that of the circular knits, the primer treatment method was good at A, and the peel strength was excellent at method A. The aramid air cushion was the lightest in weight. Summarizing the above results, it was best to combine the air cushion material with aramid woven fabric and primer treatment method A to cope with the high impact force applied when falling.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.131-138
• /
• 2017

Most of high performance fabrics for the car racing protective clothing have been developed to have thermal resistance, flame retardant property, impact resistance and anti-frictional properties to protect the racer from the crucial accident. In this study, the meta-aramid fabric, which has inherent flame retardant, was coated with nanoparticles of SiC to enhance the impact resistance and anti-friction properties. Uniform coating of the nanoparticles onto the fabrics was obtained by using tape casting method. As the experimental parameters, size and content of the SiC nanoparticle were varied with the coating conditions of the fabric surface. The effects of the nanoparticle coating on the properties of meta-aramid fabric were examined with various instrumental analyses such as SEM, tensile strength and abrasion test.

• Textile Coloration and Finishing
• /
• v.23 no.3
• /
• pp.155-162
• /
• 2011

para-Aramid has limited dyeability because of its highly crystalline structure and compactness. To improve the dyeability of the para-aramid to reactive dyes of bright color in deep shade, the fabrics were photografted under continuous UV irradiation with dimethylaminopropyl methacrylamide and 4-benzoyl benzoic acid as a monomer and a hydrogen -abstractable photoinitiator respectively. A UV energy of 35J/$cm^2$ and a photoinitiator concentration of ten percent or more with respect to the monomer in the formulation was required for optimal photografting. Grafting yield increased with higher monomer application level. Surface analysis indicated significant alterations in the atomic composition of the photografted fabric surface and the fabric surface was covered with the grafted polymers. While the pristine para-aramid fabrics showed no appreciable dyeability to the ${\alpha}$-bromoacrylamide reactive dyes, the grafted para-aramid fabrics enhanced the dyeability to the reactive dyes substantially. In case of C.I. Reactive Blue 50, a K/S value of 8.7 can be obtained with the grafted para-aramid fabrics with a grafting yield of 2.3 %. Also the color fastness properties of the dyed fabrics was excellent in the conditions of washing, rubbing and light irradiation.

• Textile Coloration and Finishing
• /
• v.33 no.3
• /
• pp.97-104
• /
• 2021

In this study, the dyeability of m-aramid fabric with various cationic dyes using two bath two step dyeing method were investigated. The exhaustion properties of Doracryl series recommend for aramid(Doracryl^® Red GL 100%(DR), Doracryl^® Blue GL 300%(DB), Doracryl^® Yellow XGRL 200%(DY)) and commercial cationic Synocryl series(Synocryl^® Red GRL ED(SR), Synocryl^® Blue GSL ED(SB), Synocryl^® Yellow 3RL ED(SY)) for acrylic were measured by using Dye-O-meter. In the presence of carrier, the exhaustions of Doracryl series were higher to those of Synocryl series and the opposite phenomenon was observed in the absence of carrier. And the severe migrations of cationic dyes to acetate, nylon and wool fabrics were observed without carrier.

• Textile Coloration and Finishing
• /
• v.23 no.4
• /
• pp.298-303
• /
• 2011

Aramid fibers have been widely used as the reinforcement for composites due to their high modulus and strength. Nowadays the safety measures is required to improve the personal protection. The dyeing of aramid fibers is considered to be very difficult and their dyeing mechanism is not well illucidated. Therefore, this study is to establish the dyeing & printing technology for aramid fibers. The effects of swelling agent and neutral salt in the dye bath on the obtained colors were studied. Also dyeing method of aramid fibers depending on dyeing temperature and dye concentration were established. Color fastness of the dyed aramid fabric with cationic dyes were acceptable excluding light fastness.

• Korea-Australia Rheology Journal
• /
• v.19 no.1
• /
• pp.17-25
• /
• 2007

In liquid composite molding (LCM), composites are produced by impregnation of a dry preform with liquid resin. The resin flow through the preform is usually described by Darcy's law and the permeability tensor must be obtained for filling analysis. While the resin flow in the thickness direction can be neglected for thin parts, the resin flow in the transverse direction is important for thicker parts. However, the transverse permeability of the preform has not been investigated frequently. In this study, the transverse permeability was measured experimentally for five different fiber preforms. In order to verify the experimental results, the measured transverse permeability was compared with numerical results. Five different fiber mats were used in this study: glass fiber woven fabric, aramid fiber woven fabric, glass fiber random mat, glass fiber braided preform, and glass/aramid hybrid braided preform. The anisotropic braided preforms were manufactured by using a three dimensional braiding machine. The pressure was measured at the inlet and outlet positions with pressure transducers.