• Progress in Superconductivity and Cryogenics
• /
• v.21 no.4
• /
• pp.34-38
• /
• 2019

Multilayered high-temperature superconductor coated conductor (CC) tapes are used in an extensive range of applications and are exposed to many stresses such as hoop stress, radial/transverse tensile stress under large Lorentz forces, and thermal stress while cooling if thermal expansion properties differ. Loads induced transversely at the tape surface inevitably create delamination phenomena in the multilayered CC tapes. Thus, delamination behaviors of CC tapes along the c-axis under transverse loading conditions, which can vary based on manufacturing process and constituent layers, must be characterized for applications. The anvil test method was used to mechanically investigate the delamination characteristics of various commercially available Ag-stabilized CC tapes at room temperature and 77 K, finding superior strength at the latter. The wide variations found depended on tape structure and fabrication technique. Fractographic morphologies of delaminated tapes supported the findings under transverse loading conditions.

• Progress in Superconductivity and Cryogenics
• /
• v.24 no.3
• /
• pp.57-61
• /
• 2022

One of the major applications of REBCO coated conductor (CC) tapes is in superconducting magnets or coils that are designed for high magnet fields. For such applications, the CC tapes were exposed to a high level of stresses which includes uniaxial tensile or transverse compressive stresses resulting from a large magnetic field. Thus, CC tapes should endure such mechanical load or deformation that can influence their electromechanical performance during manufacturing, cool-down, and operation. It has been reported that the main cause of critical current (I_c) degradation in CC tapes utilized in coil windings for superconducting magnets was the delamination due to transversely applied stresses. In most high-magnetic-field applications, the operating limits of the CC tapes will likely be imposed by the electromechanical properties together with its I_c dependence on temperature and magnetic field. In this study, we examined the influence of the transverse compressive stress on the I_c degradation behaviors in various commercially available CC tapes which is important for magnet design Four differently processed REBCO CC tapes were adopted to examine their I_c degradation behaviors under transverse compression using an anvil test method and a newly developed instantaneous I_c measurement system. As a result, all REBCO CC tapes adopted showed robustness against transverse compressive stresses for REBCO coils, notably at transverse compressive stresses until 250 MPa. When the applied stress further increased, different Ic degradation behaviors were observed depending on the sample. Among them, the one that was fabricated by the IBAD/MOCVD process showed the highest compressive stress tolerance.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.12
• /
• pp.2209-2219
• /
• 1997

A split hopkinson bar could be used for obtaining the high strain rate material properties of sheet metals for an autobody. In high speed tensile tests of sheet matals, a new design of a tension split Hopkinson bar apparatus is needed. The design of grips and an anvil length are numerically analyzed with ABAQUS/Explicit for the new apparatus of split Hopkinson bars. From the experiments with the new apparatus, the material properties of SPCEN in the high strain rate state have been acquired and compared with quasi-static experimental results. The material properties of SPCEN as well as other sheet metals in an autobody are indispensible for the analysis of crashworthness. Nevertheless the experiment of sheet metal in the high strain rate state has not been done or reported.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.3
• /
• pp.454-464
• /
• 1987

The objective of this research is to analyze and evaluate the dynamic flow curve of metals under impact loading at both high strain rate (.epsilon.=1/h dh/dt > 10$\^$3/m/s/m) and large strain (.epsilon.=In h/h$\_$0/ > 1.0). A test method for dynamic compression of metal disc is described. The velocity of the striker face and the force on the anvil are measured during the impact period. From these primitive data the axial stress, strain, and strain rate of the disc are obtained. The Strain rate is determined by the striker velocity divided by the specimen height. This gives a slightly increasing strain rate over most of the deformation period. Strain rates of 100 to 10,000 per second are achieved. Attainable final strains are 150%. A discussion of several problem areas is presented. The friction on the specimen surfaces, the determination of the frictional coefficient, the influence of the specimen geometry (h$\_$0//d$\_$0/ ratio) on the friction effect, the lock-up condition for a given configuration, the friction correction factor, and the evaluation of several lubricants are given. The flow function(stress verus strain) is dependent on the material condition(e.g., prior cold work), specimen geometry, strain rate, and temperature.