• Journal of Magnetics
• /
• v.15 no.4
• /
• pp.190-193
• /
• 2010

The design of joints in a transformer core significantly affects the transformer's efficiency. Air gaps cause variations in the flux distribution at the joints of the laminations, which depend on the geometry. Two similar samples consisting of electrical steel strips and amorphous ribbons were made. The spatial flux distributions were determined using an array of search coils for each sample. 2D models of these samples were created and examined by finite element analysis. The magnetic flux distribution for each lamination in the samples was computed. The results show that the flux density in amorphous ribbons above and below the air gap starts to approach saturation at lower flux density levels than for electrical steel. The flux density measured using the search coil under the air gap is increased in amorphous ribbons and decreased in the electrical steel with increasing frequency.

• Journal of Korea Foundry Society
• /
• v.40 no.4
• /
• pp.113-117
• /
• 2020

A series of Fe-P-B and Fe-Si-B amorphous alloys with high Fe contents exceeding 90 wt.% was successfully prepared by combining flux treatment and melt-spinning technique. The effects of Fe content and the flux treatment on the thermal and magnetic properties of amorphous alloys were studied. The glass-forming ability and the thermal stability of amorphous ribbons can be improved by a flux treatment, revealing the effective removal of heterogeneous nucleation sites in the ribbons through the flux treatment. It was found that Fe-Si-B ribbons exhibit higher saturation magnetization levels than Fe-P-B ribbons.

• Transactions of Materials Processing
• /
• v.7 no.4
• /
• pp.333-339
• /
• 1998

Hot torsion tests were conducted to investigate the high temperature deformation behavior of $Al_{85}Ni_{10}Y_5$ alloy extrudates fabricated with amorphous ribbons. The powder metallurgy routes, hot pressing and hot extrusion were used to fabricate the extrudates. Thermal properties of amorphous ribbons with different thickness as a function of aging temperature were studied by thin film x-ray dif-fraction (XRD) and differential scanning calorimetry(DSC). The Al phase crystallite firstly formed in the amorphous ribbons and its crystallization temperature($T_x$)Was ~210${\circ}C$ During the processings of consolidation and extrusion, nano-grained structure(~100 nm) was formed in the Al85Ni10Y5 alloy extrudates. The as-extrudated Al85Ni10Y5 alloy and the $Al_{85}Ni_{10}Y_5$ alloy annealed at 250${\circ}C$ for 1 hour showed a flow curve of DRV(dynamic recovery) during hot deformation at 400-550${\circ}C$. On the other hand, the $Al_{85}Ni_{10}Y_5$ alloy annealed at 400${\circ}C$ for 1 hour showed a flow curve of DRX(dynamic recrys-tallization) during hot deformation at 450-500${\circ}C$. Also the flow stress and flow strain of the $Al_{85}Ni_{10}Y_5$ alloy extrudate annealed at 400${\circ}C$ were higher than those at 250${\circ}C$.

• Journal of Korea Foundry Society
• /
• v.36 no.1
• /
• pp.18-23
• /
• 2016

Iron based amorphous ribbons with the nominal compositions of $(Fe_{79}C_{11}B_8Si_2)_{100-X}Cr_X$ (X = 0,2,4,6,8 at%) have been developed as reinforcements that can be applied to the concrete materials. Mechanical properties and glass forming ability of the ribbons can be enhanced by the optimum amounts of Cr additions that can also improve corrosion properties of the ribbons. Vein patterns typical of the fractured surface morphology of amorphous alloys have been observed on the surfaces of ribbons after tensile tests. It is inferred from the EDS analysis results of vein patterns that carbon segregations occur within the narrow shear band regions.

• Journal of Magnetics
• /
• v.18 no.4
• /
• pp.395-399
• /
• 2013

The metallic glass ribbons of $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Mo_4$ (x = 0, 0.3, 0.6, 0.9 at.%) and $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Nb_4$ (x = 0, 0.3, 0.6, 0.9 at.%) were obtained by melt spinning with 25-30 ${\mu}m$ thickness. The thermal stability, mechanical properties and magnetic properties of Fe-Co-B-Si based systems were investigated. The values of thermal stability were measured using differential scanning calorimetry (DSC), including glass transition temperature ($T_g$), crystallization temperature ($T_x$) and supercooled liquid region (${\Delta}T_x=T_x-T_g$). These amorphous ribbons were identified as fully amorphous, using X-ray diffraction (XRD). The mechanical properties of Febased samples were measured by nano-indentation. Magnetic properties of the amorphous ribbons were measured by a vibrating sample magnetometer (VSM). The amorphous ribbons of $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Mo_4$ (x = 0, 0.3, 0.6, 0.9 at.%) and $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Nb_4$ (x = 0, 0.3, 0.6, 0.9 at.%) exhibited soft magnetic properties with low coercive force ($H_c$) and high saturation magnetization (Ms).

• Current Applied Physics
• /
• v.18 no.11
• /
• pp.1289-1293
• /
• 2018

The influence of crystallization treatment on the structure, magnetic properties and magnetocaloric effect of $Gd_{71}Ni_{29}$ melt-spun ribbons has been investigated in detail. Annealing of the melt-spun samples at 610 K for 30 min, a majority phase with a $Fe_3C$-type orthorhombic structure (space group, Pnma) and a minority phase with a CrB-type orthorhombic structure (space group, Cmcm) were obtained in the amorphous matrix. The amorphous melt-spun ribbons undergo a second-order ferromagnetic to paramagnetic phase transition at 122 K. For the annealed samples, two magnetic phase transitions caused by amorphous matrix and $Gd_3Ni$ phases occur at 82 and 100 K, respectively. The maximum magnetic entropy change $(-{\Delta}S_M)^{max}$ is $9.0J/(kg{\cdot}K)$ (5T) at 122 K for the melt-spun ribbons. The values of $(-{\Delta}S_M)^{max}$ in annealed ribbons are 1.0 and $5.7J/(kg{\cdot}K)$, corresponding to the two adjacent magnetic transitions.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1998.03a
• /
• pp.72-75
• /
• 1998

High temperature deformation behavior of Al85Ni10Y5 alloy extrudates fabricated with amorphous ribbons was investigated at temperature range form 300 to 550$^{\circ}C$ by torsion tests. Thermal properties of amorphous ribbons as a function of aging temperature was studied by Differential Scanning Calorimetry(DSC). The Al phase crystallite firstly formed in the amorphous ribbons and its crystallization temperature(Tx) was ∼210$^{\circ}C$. During the processings of consolidation and extrusion, nano-grained structure was formed in the Al85Ni10Y5 alloy extrudates. The as-extrudated Al85Ni10Y5 alloy and the Al85Ni10Y5 alloy annealed at 250$^{\circ}C$ for 1 hour showed the flow curve of DRV(dynamic recovery) during hot deformation at 400-550$^{\circ}C$. On the other hand, the Al85Ni10Y5 alloy annealed at 400$^{\circ}C$ for 1 hour showed the flow curve of DRX(dynamic recrystallization) during hot deformation at 450-500$^{\circ}C$.

• Journal of the Korean Magnetics Society
• /
• v.5 no.4
• /
• pp.261-268
• /
• 1995

In order to investigate the origin of the asymmetric magnetization reversal effect, we studied the variation of magnetic hysteresis loops with the alloy composition in amorphous ferromagnetic alloy ribbons of ${(Fe_{1-x}Co_{x})}_{75}Si_{10}B_{15}$ system annealed at $380^{\circ}C$ for 16 hours in a zero field condition. The asymmetric magnetization reversal effect developed more strongly in amorphous ribbons having two metallic components than in ribbons having a single metallic component. The effect developed more strongly in ribbons showing a smaller value of the saturation mag¬netostriction. The development of the asymmetric magnetization reversal effect was affected by the ratio of two metallic components as well as the magnitude of the saturation magnetostriction.

• Journal of Korea Foundry Society
• /
• v.28 no.1
• /
• pp.31-36
• /
• 2008

Ti-Ni-Cu alloys are very attractive shape memory alloys for applications as actuators because of a large transformation elongation and a small transformation hysteresis. Rapidly solidified Ti-Ni alloy ribbons have been known to have the shape memory effect and superelasticity superior to the alloy ingots fabricated by conventional casting. In this study, solidification structures and shape memory characteristics of $Ti-Ni_{30}-Cu_{20}$ alloy ribbons prepared by melt spinning were investigated by means of DSC and XRD. Operating parameters to fabricate the amorphous ribbons were the wheel velocity of 55 m/s and the melt spinning temperature of $1500^{\circ}C$. The crystallization temperature was measured to be $440^{\circ}C$. The crystallized ribbons exhibited very fine microstructure after annealing at $440^{\circ}C$ for 10 minutes and $460^{\circ}C$ for 5 minutes and was deformed up to about 6.8% and 6.23% in ductile manner, respectively. Stress-strain curve of the ribbon exhibited a flat stress-plateau at 64 MPa and this is associated with the stress-induced a B2-B19 martensitic transformation. During cycle deformation with the applied stress of 220 MPa, transformation hysteresis and elongation associated with the B2-B19 transformation were observed to be $4.3^{\circ}C$ and 3.6%.

• Journal of the Korean Magnetics Society
• /
• v.12 no.4
• /
• pp.154-159
• /
• 2002

Amorphous FeBSiNb alloy ribbons having bulk glass forming ability and high saturation magnetic flux density were produced by single-roller melt spinning apparatus in the thickness range of 22∼102㎛. With the increase of thickness, the coercive force and squareness ratio decreased, while maximum permeability and AC permeability increased. However electrical resistivity was almost constant. Furthermore refined and complex magnetic domain structure was observed in thicker ribbons owing to the change in internal magnetic anisotropy. For the alloy with the thickness of 81㎛, small coercive force of 24 mOe and high effective permeability of 12,000 at 1㎑ were obtained, those are considered to be better comparing to the conventional soft magnetic amorphous alloys (∼20 ㎛). The good soft magnetic properties of the thick FeBSiNb amorphous alloys were attributed to the decrease in surface pinning effect during wall motion, appearance of perpendicular anisotropy and resulted domain refinement.