• 한국분말재료학회지
• /
• 제16권5호
• /
• pp.358-362
• /
• 2009

Ti$_{50}$Cu$_{20}$Ni$_{20}$Al$_{10}$ quaternary amorphous alloy was prepared by high-energy ball milling process. A complete amorphization was confirmed for the composition of Ti$_{50}$Cu$_{20}$Ni$_{20}$Al$_{10}$ after milling for 30hrs. Differential scanning calorimetry showed a large super-cooled liquid region ($\Delta$T$_x$ = T$_x$ T$_g$, T$_g$ and T$_x$: glass transition and crystallization onset temperatures, respectively) of 80 K. Prepared amorphous powders of Ti$_{50}$Cu$_{20}$Ni$_{20}$Al$_{10}$ were consolidated by spark-plasma sintering. Densification behavior and microstructure changes were investigated. Samples sintered at higher temperature of 713 K had a nearly full density. With increasing the sintering temperature, the compressive strength increased to fracture strength of 756 MPa in the case of sintering at 733 K, which showed a 'transparticle' fracture. The samples sintered at above 693 K showed the elongation maximum above 2%.

• 한국분말재료학회지
• /
• 제9권6호
• /
• pp.381-393
• /
• 2002

Recent developments in nanocrystalline and nanocomposite rare earth-transition metal magnets are reviewed and emphasis is placed on research work at IFW Dresden. Principal synthesis methods include high energy ball milling, melt spinning, mold casting and hydrogen assisted methods such as reactive milling and hydrogenation-disproportionation-desorption-recombination. These techniques are applied to NdFeB-, PrFeB- and SmCo-type systems with the aim to produce high remanence magnets with high coercivity. Concepts of maximizing the energy density in nanostructured magnets by either inducing a texture via anisotropic HDDR or hot deformation or enhancing the remanence via magnetic exchange coupling are evaluated. With respect to high temperature applications melt spun $Sm(Co_{0.74}Fe_{0.1}Cu_{0.12}Zr_{0.04})_{7.5}$ ribbons were prepared, which showed coercivities of up to 0.53 T at 50$0^{\circ}C$. Partially amorphous $Nd_{60}Fe_xCo_{30-x}Al_{10}(0{\leq}x{\leq}30)$ alloys were prepared by copper mold casting. The effect of transition metal content on the glass-forming ability and the magnetic properties was investigated. The $Nd_{60}Co_{30}Al_{10}$ alloy exhibits an amorphous structure shown by the corresponding diffraction pattern. A small substitution of Co by 2.5 at.% Fe results In the formation of Fe-rich crystallites embedded in the Nd-rich amorphous matrix. The Fe-rich crystallites show hard magnetic behaviour at room temperature with a coercivity value of about 0.4 T, relatively low saturation magnetization and a Curie temperature of 500 K.

• 한국분말재료학회지
• /
• 제22권1호
• /
• pp.15-20
• /
• 2015

The composite of porous silicon (Si) and amorphous carbon (C) is prepared by pyrolysis of a nano-porous Si + pitch mixture. The nano-porous Si is prepared by mechanical milling of magnesium powder with silicon monoxide (SiO) followed by removal of MgO with hydrochloric acid (etching process). The Brunauer-Emmett-Teller (BET) surface area of porous Si ($64.52m^2g^{-1}$) is much higher than that before etching Si/MgO ($4.28m^2g^{-1}$) which indicates pores are formed in Si after the etching process. Cycling stability is examined for the nano-porous Si + C composite and the result is compared with the composite of nonporous Si + C. The capacity retention of the former composite is 59.6% after 50 charge/discharge cycles while the latter shows only 28.0%. The pores of Si formed after the etching process is believed to accommodate large volumetric change of Si during charging and discharging process.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2006년도 춘계학술대회 논문집
• /
• pp.409-412
• /
• 2006

Bulk metallic glass (BMG) strips of $Cu_{54}Ni_6Zr_{22}Ti_{18}$ were produced by warm rolling of the amorphous powder canned with copper. Controlling of temperatures of the rolled sample and rolls was essential for the successive rolling process. Because improper controlling of the sample temperature gave rise to the crystallization of BMG loading to the catastrophic fracture of BMG strips, the temperature of rolls should be properly controlled for achieving successful powder rolling of BMG. The variations of the strain state and temperature in the roll gap was simulated by the finite element method(FEM) using various roll temperatures.

• 한국세라믹학회지
• /
• 제27권3호
• /
• pp.361-368
• /
• 1990

The properties of the powder of ZrO2＋3m/o Y2O3 system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide near by Zr(OH)4 structure showed more excellent crystallinity and lower formation temperature of tetragonal ZrO2. In the range of this study, cubic ZrO2 was not formed and stability of tetragonal ZrO2 prepared in the conditiion of pH 7 was most excellent. Average particle sizes and specific surface areas of tetragonal ZrO2 powders, prepared as calcining amorphous zirconium hydroxides at $600^{\circ}C$ for 1h, were 0.6-0.8${\mu}{\textrm}{m}$ and 45-70$m^2$/g, respectively.

• The Korean Journal of Ceramics
• /
• 제3권4호
• /
• pp.235-238
• /
• 1997

Basic properties of new cement pastes based on the system $CaO-Al_2O_3-P_O_5-H_2O$were studied Phosphoric acid solutions and calcium dialuminate clinkers synthesized by the hydration-burning method were used for liquid and powder components of the paste, respectively Variation in the compositions of the paste was achieved by changing the liquid/powder ratio and the concentration of phosphoric acid solution. The hardening rate of the paste was so largely affected by the amount of phosphoric acid that hardening was inhibited with the low-concentrated solution but was explosively accelerated with the high-concentrated solution. The phosphoric acid solutions of concentration of 45~50% and the liquid/powder ratio of 0.5~1.5 were favoured for the high early-strength cement paste with the reasonable hardening rate and high strength. The binding phase of hardened paste was the dense amorphous gel of the system $CaO-Al_2O_3-P_O_5-H_2O$. in which the unreacted calcium dialuminate grains were embeded.

• 한국분말재료학회지
• /
• 제13권6호
• /
• pp.387-395
• /
• 2006

본고에서는 고유한 원자구조에 기인한 우수한 특성으로 인해 구조재료 및 기능재료로서 그 활용이 기대되고 있는 벌크 아몰퍼스 소재에 있어 온간압출, 온간압연, 방전 플라즈마 소결(Spark Plasma Sintering)등 과냉각액체온도구간에서의 점성유동을 이용한 고화성형 공정의 최근 기술동향에 대해 간략히 소개했다.

• 한국세라믹학회지
• /
• 제32권7호
• /
• pp.832-838
• /
• 1995

The densifying behavior of ultrafine amorphous Si3N4 (about 20 nm)-$\beta$-SiC (about 40~80 nm) powders (O2 : 1.3~15wt%, 0$700^{\circ}C$ within 15 sec and then immediately cooled and held at 135$0^{\circ}C$ for 10 min in N2 atmosphere without resorting to additives using a Xe image heating apparatus. Using an ultrafine pure Si3N4 powder with particle size less than 30nm, further more, mixed with an appropriate amount of $\beta$-SiC, was found to be advantageous to obtain uniform and homogeneous microstructure. In addition, ultrafine Si3N4 powders were also proved to be effective as sintering additive on densifying large sized Si3N4 powder compacts.

• 한국분말재료학회지
• /
• 제3권1호
• /
• pp.42-48
• /
• 1996

To investigate the phase transformation behaviors of mechanically alloyed Nb-25 at%Al powders, the mixed Nb-25 at%Al powders were mechanically alloyed in SPEX 8000 Mixer/Mill. Mechanical alloying(MA) time was varied between 0.5 hour and 72 hours. The phase formation behaviors of these mechanically alloyed powders were examined using X-ray diffraction(XRD), scanning electron microscopy(SEM), transmission electron microscopy(TEM), and differential thermal analysis(DTA). Appreciable amorphization started from 6 hours of MA. The powders mechanically alloyed for 10 hours were in almost amorphous phase. DTA results showed that the powders mechanically alloyed for 12 hours had a strong exothermic peak about$600^{\circ}C$, whereas the powders mechanically alloyed for 6 hours had two exothermic peaks. The first peak was found to be due to the stress relief effect and the second one due to the formation of$Nb_{3}Al,Nb_{2}Al and Nb_{2}C$phases by crystallization.

• 한국전기전자재료학회논문지
• /
• 제16권8호
• /
• pp.681-687
• /
• 2003

The syntheses of LaNiO$_3$Perovskite crystalline phase from mixtures of La$_2$O$_3$and NiO via it mechanochemical(used planetary mill) and a wet ball mill process were investigated. A single and stable LaNiO$_3$perovskite crystalline phase was successfully prepared by using a heat free mechanochemical process which produced a fine amorphous powder, while that phase was not formed in a wet ball mill process which needed heat treatment ranging from 500 to 150$0^{\circ}C$ and produced a coarse powder. It was shown that the LaNiO$_3$ceramics made of the mechanochemically synthesized powder possesed a good metallic characteristic.