• Advances in materials Research
• /
• 제6권4호
• /
• pp.343-348
• /
• 2017

High-pressure gas atomization was employed to prepare the Fe-based $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ alloy powder. The effect of flow rate of atomizing gas on the median powder diameter was studied. The results show that the powder size decreased with increasing the flow rate of atomizing gas. Fe-based alloy coatings with amorphous phase fraction was then prepared by high velocity oxygen fuel spraying (HVOF) of gas atomized $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ powder. Microstructural studies show that the coatings present dense layered structure and low porosity of 0.17% in about $200{\mu}m$ thickness. The Fe-based alloy coating exhibits an average hardness of about 1230 HV. Our results show that the HVOF process results in dense and well-bonded coatings, making it attractive for protective coatings applications.

• 한국분말재료학회지
• /
• 제15권4호
• /
• pp.292-296
• /
• 2008

The electromagnetic (EM) wave absorption properties of the $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline powder mixed with 5 to 20 vol% of Ni-Zn ferrites has been investigated in a frequency range from 100MHz to 10GHz. Amorphous ribbons prepared by a planar flow casting process were pulverized and milled after annealing at 425 for 1 hour. The powder was mixed with a ferrite powder at various volume ratios to tape-cast into a 1.0mm thick sheet. Results showed that the EM wave absorption sheet with Ni-Zn ferrite powder reduced complex permittivity due to low dielectric constant of ferrite compared with nanocrystalline powder, while that with 5 vol% of ferrite showed relatively higher imaginary part of permeability. The sheet mixed with 5 vol% ferrite powder showed the best electromagnetic wave absorption properties at high frequency ranges, which resulted from the increased imaginary part of permeability due to reduced eddy current.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1998년도 춘계학술대회논문집
• /
• pp.100-103
• /
• 1998

In this study, Al-Ni-Mm alloy has been produced by a gas atomization technique and consolidated by a powder extrusion method. The powders showed mixed structures of amorphous, fcc-Al phases and intermetallics. Each phase shows different size and quantity with different size of the powders due to the higher cooling rate of the finer powders. Because of the difference of the microstructure, the powders with the different size show differences of the mechanical properites of the powders and extrudates.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2005년도 추계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.44-44
• /
• 2005

• 약학회지
• /
• 제8권2호
• /
• pp.37-44
• /
• 1964

The relationships involving acid-consuming capacity and X-ray powder diffraction patterns of aluminum hydroxide gel were studied. The aging of antacid efficacy of aluminum hydroxide gel has also been characterized by using X-ray powder diffraction. The acid-consuming capacity decreased with progress of crystallization from amorphous alumino gel, and it was found that aged product at 80.deg. C had crystal structure of bohmite (.alpha.-Al.sub 2/O$_{2}$(OH)$_{2}$). It was also noted that the rate of aging decreased with decreasing pH of aluminum hydroxide gel.

• 한국분말재료학회지
• /
• 제15권1호
• /
• pp.53-57
• /
• 2008

The amorphous $Fe_{73}Si_{16}B_7Nb_3Cu_1$(at%) alloy strip was pulverized using a jet mill and an attrition mill to get flake-shaped powder. The flake powder was mixed with dielectric $BaTiO_3$ powder and its dispersant to increase the permittivity. The powders covered with dielectric powders and its dispersant were mixed with a binder and a solvent and then tape-cast to form sheets. The absorbing properties of the sheets were measured to investigate the roles of the dielectric powder and its dispersant. The results showed that the addition of $BaTiO_3$ powders and its dispersant improved the absorbing properties of the sheets noticeably. The powder sheet mixed with 5 wt% of $BaTiO_3$ powder and 1 wt% of dispersant showed the best electromagnetic wave absorption rate because of the increase of the permittivity and the electrical resistance.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 춘계학술대회 논문집
• /
• pp.236-240
• /
• 2007

In order to control the microstructure of amorphous/crystalline composites, gas atomized $Cu_{54}Ni_{6}Zr_{22}Ti_{18}$ metallic glass powders wrapped in a crystalline brass were extruded repeatedly. The size of microstructure in the resultant composites was varied depending on the pass of extrusion as well as on the area reduction ratio. The microstructure could be estimated using an equation of $r_n=r_{n-1}/R^{1/2}$, where R is reduction ratio and $r_n$ is the resultant radius of the extruded bar after n pass. Theory of microstructural refinement as well as the relationship between the resultant microstructures and mechanical properties was discussed.

• 한국세라믹학회지
• /
• 제47권2호
• /
• pp.177-182
• /
• 2010

To synthesize $Gd_2O_3:Eu^{3+}$ phosphor, gadolinium-europium oxalate precursors were prepared from oxalic acid, NaOH or aqueous ammonia via coprecipitation method. The obtained precursors were heat-treated and then characterized by XRD, SEM and PL. The kinds and amounts of coprecipitant (NaOH or aqueous ammonia) were found to affect the powder morphology and properties of gadolinium-europium oxalate precursors. Two crystalline precursors and one amorphous precursor were synthesized. The nanometer-sized amorphous gadolinium-europium oxalate precursor was first prepared using the oxalate coprecipitation technique. The calcined powders obtained from the amorphous precursor were nearly spherical in shape, and a narrow size distribution was obtained. The NaOH coprecipitant was more effective in the preparation of nanometer-sized spherical powders. A thermal decomposition process was conducted for the three kinds of precursors. The photoluminescence property was also measured as a function of europium content, and concentration quenching occurred for samples with europium concentrations of over 10 mol%.

• 한국세라믹학회지
• /
• 제23권6호
• /
• pp.71-75
• /
• 1986

The forming reaction processes of magnesium aluminate spinel by a thermal decomposition of sulfate hydrate were studied with DTA, TG. SEM and X-ray powder diffraction methods. The hydrous salt composed of the mixture of the two compounds of $MgSO_4$ $6H_2O$ and ${AL_2}({SO_4})_17H_2O_3$ in which both sulfates were crystalline. On heating the hydrous slat the crystalline magnesium and aluminum sulfate anhydride to amorphous alumina magnesium sulfate anhydride decomposed to amorphous magnesia and these amorphous oxides reacted completely each other to form a spinel at $1000^{\circ}C$ The apparent activation energy of forming reaction of spinel was 36.5 kcal/mole($900^{\circ}C$~$1000^{\circ}C$) The crystallite size of spinel obtained at $1000^{\circ}C$ after 1 h was 380$\AA$.

• 소성∙가공
• /
• 제8권6호
• /
• pp.626-633
• /
• 1999

$Al_{85}Ni_{10}Y_5$ (at. %) amorphous alloy ribbons have been produced by rapidly solidification process and consolidated by the conventional powder metallurgy method. The grains with ∼90 nm were obtained in the Al85Ni10Y5 alloy extrudates by hot-pressing followed by hot-extusion. To investigate the effect of heat treatment on microstructural change of the extrudates, heat treatment was carried out from 200℃ to 400℃ at the step of 50℃. In addition, mechanical properties of the extrudates were analysed from torsion test at the temperature range or 400∼500℃ under a strain rates of 0.2, 0.5, and 1.0/sec. The extrudates showed a flow stress of ∼190 MPa and low elongation of ∼150% at 400℃, contributing to the enhancement of ductility and hardness for extrudates. Also, grain boundary sliding was occurred in the $Al_{85}Ni_{10}Y_5$ alloy during hot deformation.