• Korean Journal of Materials Research
• /
• v.7 no.12
• /
• pp.1063-1069
• /
• 1997

For me1t-spun Fe-Nd-C alloys, variation of phase development and magnetic properties with the variety of alloy compositions and production conditions were investigated. To find out whether hard magnetic $Fe_{14}Nd_2C$ is crystallized direct1y from the melt by rapid quenching, the phase development of the as-spun ribbons spun at various speed was a1so studied. For the ribbons spun at 10m/s, ${\alpha}-Fe$ was the primary crystallization phase followed by the secondary $Fe_{17}Nd_2C$. At 20m/s ${\alpha}-Fe$ was suppressed so that the primary $Fe_{17}Nd_2C$ coexisted with the secondary ${\alpha}-Fe$ and the amorphous phase. Above 30m/s the ribbons were a1most amorphous, and the amorphization was complete at 40m/s. $Fe_{14}Nd_2C$ therefore was not found in as-spun state but obtained after heat treating the ribbons. The effective temperature range ($700{\sim}900^{\circ}C$) in which $Fe_{14}Nd_2C$ can be obtained was wider than that of a cast alloy. An alloy made with the wheel speed of 20 or 30m/s yielded higher coercivities after heat treatment. In iron-rich Fe-Nd-C, the composition range in which a high coercivity (more than 10kOe) is expected is narrow, i.e., 77~78 Fe and 7~8 C(at.%).

• Journal of the Korean Magnetics Society
• /
• v.19 no.3
• /
• pp.89-93
• /
• 2009

Amorphous $Ge_{1-x}Mn_x$ semiconductor thin films grown by low temperature vapor deposition were annealed, and their electrical and magnetic properties have been studied. The amorphous thin films were $1,000{\sim}5,000\;{\AA}$ thick. Amorphous $Ge_{1-x}Mn_x$ thin films were annealed at $300^{\circ}C$, $400^{\circ}C$, $500^{\circ}C$, $600^{\circ}C$ and $700^{\circ}C$ for 3 minutes in high vacuum chamber. X-ray diffraction analysis reveals that as-grown $Ge_{1-x}Mn_x$ semiconductor thin films are amorphous and are crystallized by annealing. Crystallization temperature of amorphous $Ge_{1-x}Mn_x$ semiconductor thin films varies with Mn concentration. Amorphous $Ge_{1-x}Mn_x$ thin films have p-type carriers and the carrier type is not changed during annealing, but the electrical resistivity increases with annealing temperature. Magnetization characteristics show that the as-grown amorphous $Ge_{1-x}Mn_x$ thin films are ferromagnetic and the Curie temperatures are around 130 K. Curie temperature and saturation magnetization of annealed $Ge_{1-x}Mn_x$ thin films increase with annealing temperature. Magnetization behavior and X-ray analysis implies that formation of ferromagnetic $Ge_3Mn_5$ phase causes the change of magnetic and electrical properties of annealed $Ge_{1-x}Mn_x$ thin films.

• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.191-197
• /
• 2005

In the fabrication process of Fe-based amorphous alloy powder cores by pulverization of the melt-spun ribbons and cold compaction, the effects of powder preparation method on the magnetic & electric properties, powder shapes and microstructure of cores have been investigated. The powder cores made by using rotor mill showed low effective permeability as compared to the cores prepared by ball milling. However the frequency dependence and quality factor properties were superior in the case of rotor-milling. Further the powders prepared by rotor mill had homogeneous and round shapes through strong shearing in the sieve ring, while the ball milled powders were inhomogeneous and relatively small. The lower permeability of the powder cores fabricated with rotor mill was considered to be due to the high internal stress occurred by very intensive shearing. Moreover the powder cores produced by rotor-milling showed lower core loss and good frequency dependence of effective permeability possibly due to the higher electrical insulation between magnetic particles. The dc bias property of the powder cores made by rotor-milling was better than the one by ball-milling.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.377-377
• /
• 2010

FINEMET type nanocrystalline materials synthesized by controlled crystallization of amorphous ribbons[1] exhibit excellent soft magnetic properties making them attractive for technological applications. Present work reports the electronic structure studies of Co-substituted FINEMET to get information on the effect of successive Co substitution on local environment around Fe and Co atom by using near edge x-ray absorption fine structure (NEXAFS) and x-ray magnetic circular dichroism (XMCD) measurements. NEXAFS spectroscopy and XMCD measurements have been carried out at Fe $L_{3,2}$ and Co $L_{3,2}$-edges to investigate the chemical states and electronic structure of FINEMET [$(Fe_{100-x}Co_x)_{78}Si_9Nb_3Cu_1Ba$](0$L_{3,2}$-edge reveal that Fe is in 2+ state and in tetrahedral symmetry with other elements. The magnetic properties exhibiting soft magnetic behavior[2] are discussed on the basis of the electronic structure studied through XMCD.

• Journal of the Korean Ceramic Society
• /
• v.43 no.3 s.286
• /
• pp.143-147
• /
• 2006

Co-Fe-Al-O nanogranular thin films were fabricated by RF-magnetron sputtering under an $Ar+O_2$ atmosphere. High resolution transmission electron microscopy revealed that the Co-Fe-Al-O films are composed of bcc (Co, Fe) nanograins finer than 5 nm and an Al-O amorphous phase. A very large electrical resistivity of $374{\mu}{\Omega}cm$ was obtained, together with a large uniaxial anisotropy field of 50 Oe, a hard axis coercivity of 1.25 Oe, and a saturation magnetization of 12.9 kG. The actual part of the relative permeability was measured to be 260 at low frequencies and this value was maintained up to 1.3 GHz. The ferromagnetic resonance frequency was 2.24 GHz. The resulting Co-Fe-Al-O nanogranular thin films with a high electrical resistivity and high resonance frequency are considered to be suitable for GHz magnetic device applications.

• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.79-84
• /
• 2011

Double-walled carbon nanotubes (DWCNTs) with high purity were produced by the catalytic decomposition of tetrahydrofuran (THF) using a Fe-Mo/MgO catalyst at $800^{\circ}C$. The as-synthesized DWCNTs typically have catalytic impurities and amorphous carbon, which were removed by a two-step purification process consisting of acid treatment and oxidation. In the acid treatment, metallic catalysts were removed in HCl at room temperature for 5 hr with magnetic stirring. Subsequently, the oxidation, using air at $380^{\circ}C$ for 5 hr in the a vertical-type furnace, was used to remove the amorphous carbon particles. The DWCNT suspension was prepared by dispersing the purified DWCNTs in the aqueous sodium dodecyl sulfate solution with horn-type sonication. This was then air-sprayed on ITO glass to fabricate DWCNT field emitters. The field emission properties of DWCNT films related to transmittance were studied. This study provides the possibility of the application of large-area transparent CNT field emission cathodes.

• Korean Journal of Metals and Materials
• /
• v.48 no.4
• /
• pp.335-341
• /
• 2010

High-quality single-walled carbon nanotubes (SWCNTs) were synthesized by catalytic decomposition of $C_2H_2$ using Fe-Mo/MgO catalyst at $800^{\circ}C$. The as-synthesized SWCNTs typically occurred in the form of a bundle with a diameter of 10~20 nm together with amorphous carbon and catalytic impurities, which were removed by a two-step purification process consisting of oxidation and an acid treatment. The oxidation step, using an $O_2$-Ar mixture at $380^{\circ}C$ for 5 hr in a vertical-type furnace and a $HNO_3$ treatment at $100^{\circ}C$ for one hour, was utilized to remove the amorphous carbon particles. Subsequently, metallic catalysts were removed in HCl at room temperature for 5 hr under magnetic stirring. The SWCNT suspension was prepared by dispersing the purified SWCNTs in an aqueous sodium dodecyl benzene sulfonate solution with horn-type sonication. This was then air-sprayed on glass to fabricate CNT field emitters. The samples had a turn-on field value of 4 V/${\mu}m$ and a current density of 0.67 mA/$cm^2$ at 9 V/${\mu}m$. Increasing the HCl treatment time improved the field emission properties.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.171-174
• /
• 2000

In this study, the laser patterning of sputter-deposited amorphous CoNbZr films has been tried usig Nd: YAG laser. However, the metal film was not removed because of its high reflectance of the alser on the metal surface. To solve this problem, authors tried to screen-print a block polymer on the metal film and then irradiate the laser on the polymer. This is a new method which was suggested by this study. Using this new method, the metal films were effectively removed with the laser power of 114W even though the metal films was not removed with the laser power of 332W using the conventional method. This result leads to the conclusion that the block polymer acts as a laser energy absorbing and transferring layer.

• Journal of the Korean Magnetics Society
• /
• v.7 no.6
• /
• pp.293-298
• /
• 1997

$Fe_5Si_Xb_{5-x}$ (x=0, 1, 2, 3) powders were prepared by mechanical alloying, and their phases and magnetic properties were investigated by using XRD, TEM, Mossbauer spectroscopy and VSM. Starting elements are incorporated into $\alpha$-Fe in the early stage of mechanical alloying, and the stable phases are formed as the milling proceeds. After the annealing at 80$0^{\circ}C$ for 2 hours, it is found that the FeB and $Fe_2B$ phases coexist for the $Fe_5B_5$(x=0) composition. By substituting Si for B, the formation of $Fe_2B$ phase is restricted and the $Fe_5SiB_2$, $Fe_2Si_{0.4}B_{0.6}$ and paramagnetic phase begin to appear. The FeB phase has wide range of hyperfine magnetic field because it is not fully crystallized on the annealing at 800 $^{\circ}C$. On the contrary, others have good crystalline phases and show well-defined hyperfine magnetic field. Magnetic saturation is highest for the $Fe_5B_5$ composition where the amount of the $Fe_2B$ phase in large.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.5
• /
• pp.411-414
• /
• 2009

It has been investigated for the film uniformity and deposition rate of a-C:H films on glass substrate and polymeric materials in the presence of the modulated crossed magnetic field. We used Plasma CVD, i.e, using a crossed electromagnetic field, for uniform depositing thin film. The optimum discharge condition has been discussed for the gas pressure, the magnetic flux density and the distance between substrate and electrodes, As a result, it is found that the optimum discharge conditions are $CH_4$ concentration $CH_4$=10 %, modulated magnetic flux density B=48 Gauss, pressure P=100 mTorr, discharge power supply voltage V=l kV under these experimental conditions. By using these experimental condition, it is possible to prepare the most uniform film extends over about 160 mm of the film width. In this study, we deposited a-C:H thin film on glass substrate, and have a plan that using this condition, study depositing a-C:H thin film on polymeric substrate in next studies.