• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.321-327
• /
• 2008

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_6$) coating was produced by cold spraying as a new fabrication process. The microstructure and macroscopic properties of amorphous coating layer was investigated and compared with those of cold sprayed pure Cu coating. Amorphous powders were prepared by gas atomization and Al 6061 was used as the substrate plate. X-ray diffraction results showed that Cu based amorphous powder could be successfully deposited by cold spraying without any crystallization. The Cu based amorphous coating layer ($300{\sim}400{\mu}m$ thickness) contained 4.87% porosity. The hardness of Cu based amorphous coating represented $412.8H_v$, which was correspond to 68% of the hardness of injection casted bulk amorphous material. The wear resistance of Cu based amorphous coating was found to be three times higher than that of pure Cu coating. The 3-point bending test results showed that the adhesion strength of Cu based amorphous coating layer was higher than that pure Cu coating. It was also observed that hard Cu base amorphous particle could easily deform soft substrate by particle collisions and thus generated strong adhesion between coating and substrate. However, the amorphous coating layer unexpectedly represented lower corrosion resistance than pure Cu coating, which might be resulted from the higher content of porosity in the cold sprayed amorphous coating.

• Journal of Welding and Joining
• /
• 제25권3호
• /
• pp.28-36
• /
• 2007

A bulk amorphous NiTiZrSiSn powder produced using an inert gas atomization was sprayed by kinetic spraying process that is basically a solid-state deposition process onto a mild steel substrate. They were successfully overlaid onto the mild steel substrate. In order to evaluate the tribological behavior of the kinetic sprayed NiTiZrSiSn BMG (Bulk Metallic Glass) coatings, a partially crystallized coating and a fully crystallized coating were prepared by the isothermal heat treatments. Tribological behaviors were investigated in view of friction coefficient, hardness and amorphous phase fraction of coating layer. Surface morphologies and depth in the wear tracks were observed and measured by scanning electron microscope and alpha-step. From the examination of the scratch wear track microstructure, transition from the ductile like deformation (micro cutting) to the brittle deformation (micro fracturing) in the scratch groove was observed with the increase of the crystallinity.

• 대한금속재료학회지
• /
• 제47권11호
• /
• pp.728-733
• /
• 2009

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_{6}$) powders were deposited onto Al 6061 substrates by cold spray process with different powder preheating temperatures (below glass transition temperature: $350^{\circ}C$, near glass transition temperature: $430^{\circ}C$ and near crystallization temperature: $500^{\circ}C$). The microstructure and macroscopic properties (hardness, wear and corrosion) of Cu based amorphous coating layers were also investigated. X-ray diffraction results showed that cold sprayed Cu based amorphous coating layers of $300{\sim}350{\mu}m$ thickness could be well manufactured regardless of powder preheating temperature. Porosity measurements revealed that the coating layers of $430^{\circ}C$ and $500^{\circ}C$ preheating temperature conditions had lower porosity contents (0.88%, 0.93%) than that of the $350^{\circ}C$ preheating condition (4.87%). Hardness was measured as 374.8 Hv ($350^{\circ}C$), 436.3 Hv ($430^{\circ}C$) and 455.4 Hv ($500^{\circ}C$) for the Cu based amorphous coating layers, respectively. The results of the suga test for the wear resistance property also corresponded well to the hardness results. The critical anodic current density ($i_{c}$) according to powder preheating temperature conditions of $430^{\circ}C$, $500^{\circ}C$ was lower than that of the sample preheated at $350^{\circ}C$, respectively. The higher hardness, wear and corrosion resistances of the preheating conditions of near $T_{g}$ and $T_{x}$, compared to the properties of below $T_{g}$, could be well explained by the lower porosity of coating layer.

• 한국재료학회지
• /
• 제24권1호
• /
• pp.60-65
• /
• 2014

Fe-based amorphous coatings were fabricated on a soda-lime glass substrate by the vacuum kinetic spray method. The effect of the gas flow rate, which determines particle velocity, on the deposition behavior of the particle and microstructure of the resultant films was investigated. The as-fabricated microstructure of the film was studied by field emission scanning electron microscopy (FE-SEM) and high resolution transmission electron microscopy (HR-TEM). Although the activation energy for transformation from the amorphous phase to crystalline phase was lowered by severe plastic deformation and particle fracturing under a high strain rate, the crystalline phases could not be found in the coating layer. Incompletely fractured and small fragments 100~300 nm in size, which are smaller than initial feedstock material, were found on the coating surface and inside of the coating. Also, some pores and voids occurred between particle-particle interfaces. In the case of brittle Fe-based amorphous alloy, particles fail in fragmentation fracture mode through initiation and propagation of the numerous small cracks rather than shear fracture mode under compressive stress. It could be deduced that amorphous alloy underwent particle fracturing in a vacuum kinetic spray process. Also, it is considered that surface energy caused by the formation of new surfaces and friction energy contributed to the bonding of fragments.

• 한국분말재료학회지
• /
• 제28권6호
• /
• pp.483-490
• /
• 2021

A new Fe-Cr-Mo-B-C amorphous alloy is designed, which offers high mechanical strength, corrosion resistance as well as high glass-forming ability and its gas-atomized amorphous powder is deposited on an ASTM A213-T91 steel substrate using the high-velocity oxygen fuel (HVOF) process. The hybrid coating layer, consisting of nanocrystalline and amorphous phases, exhibits strong bonding features with the substrate, without revealing significant pore formation. By the coating process, it is possible to obtain a dense structure in which pores are hardly observed not only inside the coating layer but also at the interface between the coating layer and the substrate. The coating layer exhibits good adhesive strength as well as good wear resistance, making it suitable for coating layers for biomass applications.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권2호
• /
• pp.159-164
• /
• 1996

The development of an insulated coating which can be used for amorphous alloys is extremely important from the practical point of view. This importance may be enhanced by the influence of the coating on the magnetic properties. The purpose of this study is to show how new developed insulating coating materials and method influence the magnetic properties of amorphous Fe/sub 87/Zr/sub 7/B/sub 5/Ag/sub 1/(at%) ribbon.

• Tribology and Lubricants
• /
• 제30권2호
• /
• pp.108-115
• /
• 2014

The friction behaviors of bulk amorphous thermal spray coating (BAC) and second phase-reinforced composite coatings using a high velocity oxy-fuel spraying process were investigated using a ball-on-disk test rig that slides against a ceramic ball in an atmospheric environment. The surface temperatures were measured using an infrared thermometer installed 50 mm from the contact surface. The crystallinities of the coating layers were determined using X-ray diffraction. The morphologies of the coating layers and worn surfaces were observed using a scanning electron microscope and energy-dispersive spectroscopy. The results show that the friction behavior of the monolithic amorphous coating was sensitive to the testing conditions. Under lower than normal loads, a low and stable friction coefficient of about 0.1 was observed, whereas under a higher relative load, a high and unstable friction coefficient of greater than 0.3 was obtained with an instant temperature increase. For the composite coatings, a sudden increase in friction coefficient did not occur, i.e., the transition region did not exist and during the friction test, a gradual increase occurred only after a significant delay. The BAC morphology observations indicate that viscous plastic flow was generated with low loads, but severe surface damage (i.e., tearing) occurred at high loads. For composite coatings, a relatively smooth surface was observed on the worn surface for all applied loads.

• 한국세라믹학회지
• /
• 제37권3호
• /
• pp.219-226
• /
• 2000

Amorphous Ge20As20Se60 chalcogenide thin films were prepared by spin coating technique from mixed solutions of As40Se60 and Ge40Se60 dissolved in ethylenediamine. Films were prepared at a roating speed of 3500 rpm and spinning time was 10 second and heat-treateed at 27$0^{\circ}C$ for 1 hour. The resulting film thickness and RMS roughness were approximately 340 nm and 15$\AA$. Photostructure changes were investigated with 514.5nm Ar+ laser irradiation and heat-treatment. After Ar+ laser irradiation, transmittance and transmission efficiency decreased respectively up to 24.9% at 2.43 eV and 67.5% at 3.27 eV, and absorption edge shifted toward long wavelength. Optical bandgap changed from 2.03 to 1.83 eV, and absoprtion coefficient and absorption efficiency increased up to 0.33$\times$105cm-1 at 3.37eV and 88.3% at 1.31 eV, respectively. These photodarkening state were recovered reversibly by heat-treatment at 27$0^{\circ}C$ for 1 hour. Photodarkening and thermal bleaching effects by laser irradiation and heat-treatment revealed reversible amorphous-to-amorphous transition varying only coordination number.

• 한국표면공학회지
• /
• 제30권4호
• /
• pp.248-254
• /
• 1997

The sulfidation behavior of a sputter-deposited amorphous coating of 69.0%Nb-16.9Ni-11.9%Al-2.2%Si (at.%) has been investigated as a funtion of temperature.(973-1173K) in pure sulfur pressure of 0.01atm. The sulfidation kinetics of the casting obyed the parabolic rate low over the whole temperature ranges studied. The stlfidation rate increased with the temperature, as expected. The sulfide scale, the composition of which was $Al_2S_3,\;NbS_2,\;Ni_{3-x}S_2\;and\;FeCrS_4$, formed on the amorphous coating was primarily bilayered. Both the outer fastgrowing non-protective 4Al_2S_3$scale and the inner slowly-growing protective $NbS_2$,/TEX> scale and the inner slowly-growing protective $NbS_2$ scale had some Fe and Cr dissolution, which evidently came from the base substrate alloy of stainless steel type 304. Belows the coating, Kirkendall void formation was noticed. Nevertheless, a dramatic improvement of sulfidation resistance was achieved by sputter-depositing Nb-2 Ni-Al-Si layer on the stainless steel 304.

• 한국분말재료학회지
• /
• 제28권3호
• /
• pp.233-238
• /
• 2021

Iron-based amorphous powder attracts increasing attention because of its excellent soft magnetic properties and low iron loss at high frequencies. The development of an insulating layer on the surface of the amorphous soft magnetic powder is important for minimizing the eddy current loss and enhancing the energy efficiency of high-frequency devices by further increasing the electrical resistivity of the cores. In this study, a hybrid insulating coating layer is investigated to compensate for the limitations of monolithic organic or inorganic coating layers. Fe₂O₃ nanoparticles are added to the flexible silicon-based epoxy layer to prevent magnetic dilution; in addition TiO₂ nanoparticles are added to enhance the mechanical durability of the coating layer. In the hybrid coating layer with optimal composition, the decrease in magnetic permeability and saturation magnetization is suppressed.