• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2015년도 제49회 하계 정기학술대회 초록집
• /
• pp.188.1-188.1
• /
• 2015

For present investigation Fe/MgO/Fe/Co multilayer stack is grown on Si substrate using e-beam evaporation in ultrahigh vacuum. This stack is irradiated perpendicularly by 120 MeV $Ag^{8+}$ at different fluences ranging from $1{\times}10^{11}$ to $1{\times}10^{13}ions/cm^2$ in high vacuum using 15UD Pelletron Accelerator at Inter University Accelerator Centre, New Delhi. Magnetic measurements carried out on pre and post irradiated stacks show significant changes in the shape of perpendicular hysteresis which is relevant with previous observation of re-orientation of magnetic moment along the direction of ion trajectory. However increase in plane squareness may be due to the modification of interface structure of stacks. X-ray reflectivity measurements show onset of interface roughness and interface mixing. X-ray diffraction measurements carried out using synchrotron radiation shows amorphous nature of MgO and Co layer in the stack. Peak corresponding body centered Fe [JCPDS-06-0696] is observed in X-ray diffraction pattern of pre and post irradiated stacks. Peak broadening shows granular nature of Fe layer. Estimated crystallite size is $22{\pm}1nm$ for pre-irradiated stack. Crystallite size first increases with irradiation then decreases. Structural quality of these stacks was further studied using transmission electron microscopic measurements. Thickness from these measurements are 54, 36, 23, 58 and 3 nm respectively for MgO, Fe, MgO, Fe+Co and Au layers in the stack. These measurements envisage poor crystallinity of different layers. Interfaces are not clear which indicate mixing at interface. With increase fluence mixing and diffusion was increased in the stack. X-ray absorption spectroscopic measurements carried out on these stacks show changes of Fe valence state after irradiation along with change of O(2p)-metal (3d) hybridized state. Valence state change predicts oxide formation at interface which causes enhanced in-plane magnetization.

• 한국재료학회지
• /
• 제27권8호
• /
• pp.409-415
• /
• 2017

For enhanced cavitation erosion resistance of vessel propellers, an electroless Ni-P plating method was introduced to form a coating layer with high hardness on the surface of Cu alloy (CAC703C) used as vessel propeller material. An electroless Ni-P plating reaction generated by Fe atoms in the Cu alloy occurred, forming a uniform amorphous layer with P content of ~10 wt%. The amorphous layer transformed to (Ni3P+Ni) two phase structure after heat treatment. Cavitation erosion tests following the ASTM G-32 standard were carried out to relate the microstructural changes by heat treatment and the cavitation erosion resistance in distilled water and 3.5 wt% NaCl solutions. It was possible to obtain excellent cavitation erosion resistance through careful microstructural control of the coating layer, demonstrating that this electroless Ni-P plating process is a viable coating process for the enhancement of the cavitation erosion resistance of vessel propellers.

• 한국표면공학회지
• /
• 제50권3호
• /
• pp.177-182
• /
• 2017

The properties of electroless Ni-B thin film on diamond powder with different parameters (temperature, pH, surfactant etc.) were studied. The surface morphology, structure and composition distribution of the Ni-B film were observed by field effect scanning electron microscope (FE-SEM), energy-dispersive spectrometer (EDS), X-ray diffraction (XRD) and Auger electron spectroscopy (AES). The growth rate of Ni-B film was increased with increase of bath temperature. The B content in Ni-B film was reduced with increase of bath pH. As a result the structure of Ni-B film was changed from amorphous to crystalline structure. The PVP in solution plays multi-functional roles as a dispersant and a stabilizer. The Ni-B film deposited with adding 0.1 mM-PVP was strongly introduced an amorphous structure with higher B content (25 at.%). Also the crystallite size of Ni-B film was reduced from 12.7 nm to 5.4 nm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.309-309
• /
• 2009

In-Ga-Zn-O (IGZO) has drawn much attention as a compatible material for transparent thin film transistors (TTFT) channel layer due to its high mobility and optical transparency at low processing temperatures. In this work, we investigated the effect of oxygen ambient on structural, electrical and optical properties of amorphous In-Ga-Zn-O (IGZO) thin films by using pulsed laser deposition (PLD). The films were deposited at various oxygen pressures and the structural, electrical and optical properties were investigated. X-ray diffraction (XRD) analysis showed that amorphous IGZO films were grown at all oxygen pressures. The surface morphology and optical properties with various oxygen pressures were studied by field emission scanning electron microscopy (FE-SEM) and UV-VIS spectroscopy, respectively. The grain boundary was observed more apparently and the calculated optical band gap became larger as oxygen pressure increased. To examine the electrical properties, Hall-effect measurements were carried out. The films showed high mobility.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.383-390
• /
• 1992

We investigated the effect of substrate on the properties of the Ni-Zn-Cu ferrite thin films deposited on SiO2 (1000∼3000${\AA}$) / Si (100) substrate at various conditions by rf magnetron sputtering. A disktype Ni-Zn-Cu ferrite sintered by conventional ceramic process and argon gas were used as a target and a sputtering gas, repectively. The compositions of the thin films measured by EPMA were similar to target composition (Fe: 65.8 at%, Ni: 12.7 at%, Cu: 6.7 at%, Zn: 14.8 at%) irrespective of substrate temperature. Amorphous thin films were deposited when substrate was not intentionally heated, but the films came to crystallize with increasing substrate temperature, and crystalline thin films were deposited at substrate temperature above 200$^{\circ}C$. Below 250$^{\circ}C$ saturation magnetization (Ms), remanence (Mr) and coercivity (Hc) of the ferrite thin film increased with the substrate temperature due to the increase of grain size and the improvement of crystallinity. And above 250$^{\circ}C$, Ms, Mr increased slightly, but Hc of the amorphous thin films increased due to crystallization, whereas that of the crystalline thin films decreased because of grain growth and stress release.

• Progress in Superconductivity
• /
• 제13권2호
• /
• pp.122-126
• /
• 2011

Superconducting $MgB_2$ thin films were fabricated by using a novel aerosol deposition technique wherein the pre-reacted powder is directly transformed into respective thin film. The formed thin films were characterized by X-ray diffraction technique and FE-SEM to understand its structure and morphology and the superconducting behavior has been characterized with the four probe resistivity measurement. The as-deposited thin films were formed into the frustrated amorphous structure, which were relaxed on the further heat treatment at $900^{\circ}C$ for 3 hrs. The relaxed amorphous $MgB_2$ thin films showed a comparatively high superconducting onset at about 38 K.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2009년도 제40회 하계학술대회
• /
• pp.1244_1245
• /
• 2009

Coating of amorphous nitride thin layers, such as boron nitride (BN) and carbon nitride (CN), has been performed on carbon nanotubes (CNTs) for the purpose of enhancing their electron-emission performances because those nitride films have relatively low work functions and commonly exhibit negative electron affinity behavior. The CNTs were directly grown on metal-tip (tungsten, approximately 500 nm in diameter at the summit part) substrates by inductively coupled plasma-chemical vapor deposition (ICP-CVD). Sharpening of the tungsten tips were carried out by electrochemical etching. Morphologies and microstructures of BN and CN films were analyzed by field-emission scanning electron microscopy (FE-SEM), energy dispersive x-ray (EDX) spectroscopy, and Raman spectroscopy. The electron-emission properties (such as maximum emission currents and turn-on fields) of the BN-coated and CN-coated CNT-emitters were characterized in terms of the thickness of BN and CN layers.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.423-426
• /
• 2001

Recently we have reported that the meander-patterned amorphous FeCoSiB films exhibit large change in their high frequency impedance by applying a strain, suggesting that the films are very attractive for making of a highly sensitive strain sensor elements. In this study, the effect of anisotropy on a change in the impedance of sputtered amorphous film patterns was investigated in the frequency range from 1MHz to 1GHz. As a function of applied strains, the high frequency impedance was extremely changed in the case of film patterns with transverse anisotropy due to excellent magnetomechanical coupling properties. As a summary, the maximum figure of merit f has measured about 2600 in the case of transverse anisotropy, and about 500 in the case of longitudinal anisotropy at 500 MHz. These values of F are approximately more than 1000 times higher than that of a conventional metal strain gauge (F 2) and more than 10 times higher than that of a semiconductor gauge (F 200).

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2003년도 하계학술연구발표회 및 한.일 공동심포지엄
• /
• pp.88-89
• /
• 2003

During the past decade, giant magnetotransport phenomena such as giant magetoresistance (GMR) in thin films and in manganese perovskites, and, giant magnetoimpedance (GMI) in soft magnetic amorphous ribbons, have brought much interest in the basic physical understanding and their applications as magnetic recording heads and in magnetic sensors technology. Among the parameters required for the quality of a magnetic sensor, temperature dependences of GMR and GMI profiles are playing an important role. In the present work, we have studied temperature dependences of the longitudinal permeability and giant magnetoimpedance effect in $Co_{70}$F $e_{5}$S $i_{15}$ N $b_{2.2}$C $u_{0.8}$ $B_{7}$ amorphous ribbons expecting as a promising candidate in the domain of magnetic sensors.rs.rs.rs.s.

• Journal of Magnetics
• /
• 제1권1호
• /
• pp.24-30
• /
• 1996

The relationship between effective permeability and the remanence ratio of an Fe-based amorphous alloy (Metglas 2605S3A) is investigated over a wide frequency range, in an effort to understand magnetization behavior of the alloy. In the frequency range from 1 to 200 kHz, the permeability is maximum at the remanence ratio of 0.4-0.5 and, at frequencies over 500 kHz, the correlation with negative coefficients emerges indicating that the permeability decreases with the remanent ratio, except for the ribbon coated with an insulating layer of MgO which exhibits both high values of the effective permeability and remanence ratio. It is considered from the correlation results that the boundary at which the dominant magnetization mechanism changes from domain wall motion to spin rotation is near 500 kHz. The core loss is also investigated as a function of annealing time when the samples are annealed at a fixed temperature of $435^{\circ}C$. The core loss in most cases decreases with the annealing time, the degree of the loss may consist of the hysteresis loss and anomalous eddy current loss. The two loss components are considered to be of similar magnitudes at low frequencies while, at high frequencies, the dominant contribution to the total loss is the anomalous loss.