• 상하수도학회지
• /
• 제21권4호
• /
• pp.477-483
• /
• 2007

A coagulation process for RO (reverse osmosis) membrane pretreatment system was an effective technology to remove colloidal and particulate matters. However, coagulant residuals from the pretreatment process may negatively affect RO membrane performance. The bench-scale coagulant exposure study was performed to investigate the effect of their residual on adsorbed mass which related to the membrane performance. Coagulant addition in this study ranged from 0 to 5mg/L ferric chloride, alum, and 2mg/L cationic polymer(poly-di-methyldiallyl ammonium chloride) as coagulant aids. This results showed that adsorbed mass is not significantly increased during short-time period, however, accumulated mass of coagulants on the membrane surface is significantly increased during long-time experimental period. The effect of pH on coagulants adsorption characteristics was significantly differed due to the electrostatic repulsive interactions between soluble coagulants and membrane surface charge. This data suggest that the RO membrane performance of drinking water treatment plant could be decreased by adsorption of residual coagulants when applied for the coagulant pretreatment process.

• 한국세라믹학회지
• /
• 제43권4호
• /
• pp.235-241
• /
• 2006

Mullite short fibers have been fabricated by adapting the Kneading-Drying-Calcination (KDC) process and characterized. The effect of the addition of foaming agent and calcination temperature on the formation of mullite fibers from coal fly ash, was examined. In the present work, ammonium alum $NH_4Al(SO_4)_2\;12H_2O$ synthesized trom coal fly ash and sodium phosphate $Na_2HPO_4\;2H_2O$ were used as foaming agents. After calcination at $1300^{\circ}C$ for 10 h and then etching with 20% HF solution at $50^{\circ}C$ for 5 h using a microwave heating source, the alumina-deficient $(AI_2O_3/SiO_2$ = 1.13, molar ratio) orthorhombic mullite fibers with a width of ${\sim}0.8mm$ (aspect ratio >30), were prepared from the coal fly ash with $AI_2O_3/SiO_2$ = 0.32, molar ratio by the addition of $NH_4AI(SO_4)_2\;12H_2O$, and with further addition of 2 wt% sodium phosphate. The excessive addition of sodium phosphate rather decreased the formation of mullite fibers, possibly due to the large amount of liquid phase prior to mullitization reaction.