• Steel and Composite Structures
• /
• 제19권3호
• /
• pp.777-787
• /
• 2015

Production and properties of metal matrix composites reinforced with an in-situ high aspect ratio $AlB_2$ flake have been investigated. Boron 2.2wt.% was dissolved in pure Al and Al-Cu alloy at $1300^{\circ}C$ by adding directly boron oxide which resulted in 4 vol.% reinforcing phase. The in-situ $AlB_2$ flake concentration was increased up to 30 vol.% in order to increase the tensile strength of the composites. Hardness, compressive strength and tensile strength of the composite were measured and compared with their matrix. Results showed that 30 vol.% $AlB_2/Al$ composite show a 193% increase in the compressive strength and a 322% increase in compressive yield strength. Results also showed that ductility of composites decreases with adding $AlB_2$ reinforcements.

• Composites Research
• /
• 제31권4호
• /
• pp.117-121
• /
• 2018

본 연구에서는 용융가압함침 공정을 이용하여 TiC, $TiB_2$, $Al_2O_3$ 세라믹 입자가 분산된 SUS431 금속복합재료를 제조하고 미세조직을 분석하여 세라믹 입자에 따른 제조성에 대해 검토하였다. 젖음성이 나쁜 $Al_2O_3$의 경우 내부에 결함이 다수 존재함을 알 수 있었으며, $TiB_2$ 및 TiC 입자 강화 복합재의 경우 상대적으로 결함이 적고 강화재가 균일 분산되었음을 확인하였다. 특히, TiC-SUS431 복합재료의 경우 TiC와 Fe계 기지합금의 우수한 젖음성 및 용융가압함침공정 적용으로 우수한 계면 특성을 가지며 결함이 적고 균일한 미세조직을 가지는 것을 확인하였다.