Production and properties of metal matrix composites reinforced with an in-situ high aspect ratio $AlB_2$ flake have been investigated. Boron 2.2wt.% was dissolved in pure Al and Al-Cu alloy at $1300^{\circ}C$ by adding directly boron oxide which resulted in 4 vol.% reinforcing phase. The in-situ $AlB_2$ flake concentration was increased up to 30 vol.% in order to increase the tensile strength of the composites. Hardness, compressive strength and tensile strength of the composite were measured and compared with their matrix. Results showed that 30 vol.% $AlB_2/Al$ composite show a 193% increase in the compressive strength and a 322% increase in compressive yield strength. Results also showed that ductility of composites decreases with adding $AlB_2$ reinforcements.

• Composites Research
• /
• v.31 no.4
• /
• pp.117-121
• /
• 2018

Various ceramic particulate such as TiC, $TiB_2$, $Al_2O_3$ reinforced SUS431 matrix composites were successfully fabricated by a novel liquid pressing infiltration process. Microstructures of the SUS431 composite were analyzed to determine manufacturability of composites. $Al_2O_3$-SUS431 composite had lots of defects due to poor wettability between the $Al_2O_3$ and steel matrix. On the other hand, TiC was uniformly dispersed in the SUS431 matrix than $TiB_2$ and $Al_2O_3$ due to good wettability and interfacial properties.