• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.304-309
• /
• 1999

Aluminum-pillared clay was prepared by the intercalation of Al-hydroxy oligomer into domestic bentonite. The solid products are characterized by XRD, nitrogen adsorption/desorption, EDX, and SEM. The solid products show relatively high specific surface areas in the range of $104{\sim}228m^2/g$, and their specific surface area, micropore surface area, and micropore volume increase with increasing the mole ratio of OH/Al. From the results of pore size distribution calculated by BJH equation, it was found that aluminum-pillared clay also contains much mesopore near $40{\AA}$. These results indicate that Al-hydroxy oligomer was intercalated into bentonite, and aluminum oxide was pillared among the layers of bentonite, and micropore and mesopore was finally developed into layers. As OH/Al mole ratio increases, the thermal stability of aluminum-pillared clay increases. This result can be explained by the fact that the density of layers is increased due to the formation of aluminum pillars.

• Journal of the Korean Magnetics Society
• /
• v.14 no.4
• /
• pp.149-161
• /
• 2004

The fusion of nano technology and information technology is essential to sustain the present growth rate and to induce new industry in this ever-growing information age. Considering Korean industry whose competitiveness lies heavily on information related technologies, this field will be inevitable for future. Nano materials can be described as novel materials whose size of elemental structure has been engineered at the nanometer scale. Materials in the nanometer size range exhibit fundamentally new behavior, as their size falls below the critical length scale associated with any given property. " Bottom-up' techniques involve manipulating individual atoms and molecules. Bottom-up process usually implies controlled or directed self assembly of atoms and molecules into nano structures. It resembles more closely the processes of biology and chemistry, where atoms and molecules come together to create structures such as crystals or living cells. Nano scale sensors are included in the electronics area since the diverse sensing mechanisms are often housed on a semiconductor substrate and usually give rise to an electronic signal. The application of nano technology to the chemical sensors should allow improvements in functionality such as gas sensing. In this presentation, we will discuss about the nano scale information materials and devices fabricated by using the organic/inorganic nano templates.

• Restorative Dentistry and Endodontics
• /
• v.25 no.2
• /
• pp.262-271
• /
• 2000

The purpose of this study was to estimate shear bond strength according to difference in Targis surface treatment and storage condition. 140 non-carious extracted human molars and Targis D210(Ivoclar, Liechtenstein) were used in the present study and were divided into 7 experimental groups respectively according to surface treatment of Targis. Group 1 ; No treatment, Group 2 ; $50{\mu}m$ aluminium oxide blasting, Group 3 ; 4% HF etching for 3 minutes, Group 4 ; 4% HF etching after blasting, Group 5 ; silane treatment after blasting, Group 6 ; silane treatment after 4% HF etching, Group 7 ; silane treatment after blasting and 4% HF etching. In Each group, one half of 20 specimens was stored in distilled water at $37^{\circ}C$ for 24 hours and the other half was stored at atmosphere for 24 hours respectively. Dentin surface was etched with 10% $H_3PO_4$ for 15 seconds and luting cement(Variolink II, Vivadent, Liechtenstein) was applied by manufacturer's recommendation. Shear bond strength for each group was then measured. To examine the failure patterns after shear bond test and to observe the change after surface treatment of Targis. Specimens were fabricated and observed under the SEM. Statistical analysis was performed by One Way ANOVA test and t-test. The results were as follows ; 1. The shear bond strength of the groups stored in water significantly lower than that of groups stored at atmosphere (P<0.05). 2. There was no significant difference in shear bond strength in groups stored in water (P>0.05). 3. The shear bond strength without surface treatment of Targis were lowest among all experimental groups in atmosphere condition(P<0.05). 4. There was no significant difference in bond strength between groups using the silane or not(P>0.05). 5. The groups treated by blasting, hydrofluoric acid and silane sequentially showed highest bond strength than that of other groups in atmosphere condition, but there was no significant difference(P>0.05). 6 The proportions of the specimens showing the mixed fracture failure were 20% in HF etching group and blasting + HF group, 40% in blasting + HF + silane group in atmosphere condition. All the specimens stored in water showed adhesive fracture failure.

• Computers and Concrete
• /
• v.34 no.4
• /
• pp.489-501
• /
• 2024

Geopolymers are part of a class of materials characterized by properties combining polymers, ceramics, and cement. These include exceptionally high thermal and chemical stability, excellent mechanical strength and durability in aggressive environments. This work deals with the synthesis, characterization, and sustainability evaluation of GP_GBFS-MK geopolymers by alkaline activation of a granulated blast furnace slag-metakaolin mixture. In the first step, elemental and oxide analyses by XRF and EDS showed that the main constituents of GP_GBFS-MK geopolymers are silicon, sodium, and aluminium oxides. The structural analyses by XRD and FTIR confirmed that the geopolymerization for GP_GBFS-MK geopolymers did occur, accompanied by the formation of disordered networks from the blends and a modification to the microstructure by the geopolymerization process. Similarly, the microstructural study made by SEM showed that the GP_GBFS-MK geopolymers are constituted by aluminosilicates in the form of dense clusters on which are adsorbed particles of unreacted GBFS in the form of spheroids and white residues of the alkaline activating solution. In addition, the study of the sustainability evaluation of GP_GBFS-MK geopolymers showed that the water absorption of geopolymeric materials is lower than that of OPC cement. As for the elevated temperature resistance, the analyses indicated an excellent elevated temperature resistance of GP_GBFS-MK. In the same way, the study of the resistance to chemical aggressions showed that the GP_GBFS-MK geopolymeric materials are unattackable, contrary to the OPC cement-based materials which are strongly altered.

• Journal of Soil and Groundwater Environment
• /
• v.13 no.1
• /
• pp.92-100
• /
• 2008

Experimental studies were conducted to identify the active agents for reductive dechlorination of TCE in cement/Fe(II) systems focusing on cement components such as CaO, $Fe_2O_3$, and $Al_2O_3$. A hematite that was used to simulate an $Fe_2O_3$ component in cement was found to have degradation efficiencies (k = 0.641 $day^{-1}$) equivalent to that of cement/Fe(II) systems in the presence of CaO/Fe(II), only when it contained an aluminum impurity$(Al_2O_3)$. When the effect of $Al_2O_3$ content of hematite/CaO/$Al_2O_3$/Fe(II) system was tested, the mole ratio of $Al_2O_3$ to CaO affected the rate of TCE degradation with an optimum ratio around 1 : 10 that resulted in a rate constant of 0.895 $day^{-1}$. In the SEM images of hematite/CaO/$Al_2O_3$/Fe(II) systems, acicular crystals were also found that were also observed in cement/Fe(II) systems. Thus it was suspected that these crystals were reactive reductants and that they might be goethite or ettringite that are known to have acicular structures. An EDS element map analysis revealed that these crystals were not goethite crystals. A subsequent experiment that tested reactivities of compounds formed during the ettringite synthesis showed that ettringite and minerals associated with ettringite formation are not reactive reductants. These observations conclude that a mineral containing CaO and $Al_2O_3$ with a acicular structure could be a major reactive reductant of cement/Fe(II) systems.

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.3
• /
• pp.167-174
• /
• 2013

Purpose: This study was conducted to evaluate the roughness and surface alternations of three differently blasted titanium discs treated by $Nd:YVO_4$ Laser irradiation in different conditions. Materials and methods: Thirty commercially pure titanium discs were prepared and divided into three groups. Each group was consisted of 10 samples and blasted by $ZrO_2$ (zirconium dioxide), $Al_2O_3$ (aluminum oxide), and RBM (resorbable blasted media). All the samples were degreased by ultrasonic cleaner afterward. Nine different conditions were established by changing scanning speed (100, 300, 500 mm/s) and repetition rate (5, 15, 35 kHz) of $Nd:YVO_4$ Laser (Laser Pro D-20, Laserval $Korea^{(R)}$, Seoul, South Korea). After laser irradiation, a scanning electron microscope, X-ray diffraction analysis, energy dispersive X-ray spectroscopic analysis, and surface roughness analysis were used to assess the roughness and surface alternations of the samples. Results: According to a scanning electron microscope (SEM), titanium discs treated with laser irradiation showed characteristic patterns in contrast to the control which showed irregular patterns. According to the X-ray diffraction analysis, only $Al_2O_3$ group showed its own peak. The oxidation tendency and surface roughness of titanium were similar to the control in the energy dispersive X-ray spectroscopic analysis. The surface roughness was inversely proportional to the scanning speed, whereas proportional to the repetition rate of $Nd:YVO_4$. Conclusion: The surface microstructures and roughness of the test discs were modified by the radiation of $Nd:YVO_4$ laser. Therefore, laser irradiation could be considered one of the methods to modify implant surfaces for the enhancement of osseointegration.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.399-406
• /
• 2000

The effect of inlay surface treatment on bonding was investigated when resin inlay was bonded to resin-modified glass-ionomer base with resin cement. For the preparation of glass-ionomer base, resin-modified glass-ionomer cement (Fuji II LC, GC Co., Japan) was filled in class I cavities of 7mm in diameter and 2mm in depth made in plastic molds. Eighty eight resin inlay specimens were made with Charisma$^{(R)}$ (Kulzer, Germany) and then randomly assigned to the four different surface treatment conditions: Group I, $50{\mu}m$ aluminium oxide sandblasting and silane treatment ; Group II, silane treatment alone ; Group III, sandblasting alone, and Group IV (control), no surface treatment. After a dentin bonding agent with primer (One-Step$^{TM}$, Bisco Inc., IL., U.S.A.) was applied to bonding surface of resin inlay and base, resin inlay were cemented to glass-ionomer base with a resin cement (Choice$^{TM}$, Bisco Inc., IL., U.S.A.). Shear bond strengths of each specimens were measured using Instron universal testing machine (4202 Instron, lnstron Co., U.S.A.) and fractured surfaces were examined under the stereoscope. Statistical analysis was done with one-way ANOVA and Dunkan's multiple range test. The results were as follows: 1. Sandblasting and silane treatment provided the greatest bond strength(10.56${\pm}$1.95 MPa), and showed a significantly greater bond strength than sandblasting alone or no treatment (p<0.05). 2. Silane treatment provided a significantly greater bond strength(9.77${\pm}$2.04 MPa) than sandblasting alone or no treatment (p<0.05). However, there was no significant difference in bond strength between sandblasting treatment and silane one (p>0.05). 3. Sandblasting alone provided no significant difference in bond strength from no treatment (p>0.05). 4. Stereoscopic examination of fractured surface showed that sandblasting and silane treatment or silane treatment alone had more cohesive failure mode than adhesive failure mode. 5. In relationship between shear bond strength and failure mode, cohesive failure occurred more frequently as bond strength increased.

• Journal of the Korean Wood Science and Technology
• /
• v.7 no.2
• /
• pp.3-30
• /
• 1979

Larch ($\underline{Larix}$ $\underline{leptolepis}$ GORDON), one of the major afforestation species in Korea in view of its growing stock and rate of growth, is not favored as a raw material for pulp due to its low yield of pulp and difficulties with bleaching arising from the high content of extractives in wood, and the high heartwood ratio and the active phenolics, respectively. The purpose of this study is to investigate the characteristics of firstly pulping with various additives of cellulose protector for the yield of pulp, and secondly bleaching with oxygen for chlotination-alkali extraction of five stage-sequence to reduce chlorine compounds in bleaching effluents. The kraft cooking liquor for five age groups of larchwood was 18 percent active alkali with 25 percent sulfidity and 5 : 1 liquor-to-wood ratio, and each soda liquor for sap-and heart-wood of the 15-year-old larchwood was 18 percent alkali having one of the following cellulose protectors as the additive; magnesium sulfate ($MgSO_4$, 2.5%), zinc sulfate ($ZnSO_4$, 2.5%), aluminium sulfate ($Al_2(SO_4)_3$, 2.5%), potasium iodide (KI, 2.5%), hydroquinone (HQ, 2.5%), anthraquinone (AQ, 0.1%) and ethylene diamine (EDA, 2.5%). Then each anthraquinone-soda liquor for the determination of suitable cooking condition was the active alkali level of 15, 17 and 19 percent with 1.0, 0.5 and 0.1 percent anthraquinone, respectively. The cooking procedure for the pulps was scheduled to heat to 170$^{\circ}C$ in 90 minutes and to cook 90 minutes at the maximum temperature. The anthraquinone-soda pulps from both heartwood and sapwood of 15-year-old larchwood prepared with 0.5 percent anthraquinone and 18 percent active alkali were bleached in a four-stage sequency of OCED. (O: oxygen bleaching, D: chlorine dioxide bleaching and E: alkali extraction). In the first stage oxygen in atmospheric pressure was applied to a 30 percent consistency of pulp with 0.1 percent magnesium oxide (MgO) and 3, 6, and 9 percent sodium hydroxide on oven dry base, and the bleached results were compared pulps bleached under the conventional CEDED (C: chlorination). The results in the study were summarized as follows: 1. The screened yield of larch kraft pulp did not differ from particular ages to age group, but heartwood ratio, basic density, fiber length and water-extractives contents of wood and the tear factor of the pulp increased with increasing the tree age. The total yield of the pulp decreased. 2. The yield of soda pulp with various chemicals for cellulose protection of the 15-year-old larchwood increased slightly more than that of pure soda pulp and was slightly lower than that of kraft pulp. The influence of cellulose protectors was similar to the yield of pulps from both sapwood and heartwood. The effective protectors among seven additives were KI, $MgSO_4$ and AQ, for which the yields of screened pulp was as high as that of kraft pulp. Considering the additive level of protector, the AQ was the most effective in improving the yield and the quality of pulp. 3. When the amount of AQ increased in soda cooking, the yield and the quality of the pulp increased but rejects in total yield increased with decreasing the amount of active alkali from 19 to 15 percent. The best proportion of the AQ seemed to be 0.5 percent at 17 percent active alkali in anthraquinone-soda pulping. 4. On the bleaching of the AQ-soda pulp at 30 percent consistency with oxygen of atomospheric pressure in the first stage of the ODED sequence, the more caustic soda added, the brighter bleached pulp was obtained, but more lignin-selective bleaching reagent in proportion to the oxygen was necessary to maintain the increased yield with the addition of anthraquinone. 5. In conclusion, the suitable pulping condition for larchwood to improve the yield and quality of the chemical pulp to the level for kraft pulp from conventional process seemed to be. A) the selection of young larchwood to prevent decreasing in yield and quality due to the accumulation extractives in old wood, B) the application of 0.5 percent anthraquinone to the conventional soda cooking of 18 percent active alkali, and followed, C) the bleaching of oxygen in atmospheric pressure on high consistency (30%) with 0.1 percent magnesium oxide in the first stage of the ODED sequence to reduce the content of chlorine compounds in effluent.