• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 2001년도 정기총회 및 봄 학술발표회 초록집
• /
• pp.236-237
• /
• 2001

In this study, experiments were carried out to measure the variations in the corrosion potential and current density of polarization curves with amorphous $Fe_{70}Cr_5Si_{10}B_{15}$ and $Co_{70}Cr_5Si_{10}B_{15}$ alloy ribbon. The results were particularly examined to identify the influences of corrosion potential including various conditions such as hydrochloric acid, temperature, salt, pH, and oxygen. The optimum conditions were established with variations including temperature, salt, pH, oxygen, corrosion rate, and resistance of corrosion potential. The mass tranfer coefficient(${\alpha}$) value was determined with the Tafel's slope for the anodic dissolution based on the polarization effect with optimum conditions. The second anodic current density peak and maximum passive current density were designated as the critical corrosion sensitivity($I_{r}/I_{f}$).

• 열처리공학회지
• /
• 제14권3호
• /
• pp.160-166
• /
• 2001

The change of ribbon geometry, microstructure and shape recovery with Mn contents, wheel speed and various annealing temperature have been studied in Fe-X%Mn-5Cr-5Co-4Si (X%=15, 20, 24) shape memory alloy (SMA) ribbons rapidly solidfied by single roll chill-block melt-spinning process. The thickness and width of melt-spun ribbons are reduced, results in refining and uniformalizing grains with increasing wheel speed. In the ribbons melt-spun at a wheel speed of 15m/sec, both ${\varepsilon}$ and ${\alpha}^{\prime}$martensites are formed in ribbon 1 (15.5wt%Mn), while only ${\varepsilon}$ martensite is revealed in ribbon 2 (20.2wt%Mn) and ribbon 3 (23.5wt%Mn). The volume fraction of ${\varepsilon}$ martensite is decreased with increasing Mn contents, and those of ${\varepsilon}$ as well ${\alpha}^{\prime}$martensites are increased due to thermal stress relief and grain growth with increasing annealing temperature. Ms temperatures of the ribbons 1, 2 and 3 are fallen with increasing Mn contents. $M_s$ temperatures of the ribbons 1, 2 and 3 annealed at $300^{\circ}C$ for 3 min are risen abruptly, but are nearly constant even at higher annealing temperature, i.e., 400, 500 and $600^{\circ}C$ for 3 min. Shape recovery of the ribbons 1, 2 and 3 increased 30%, 52% and 69% with Mn contents, respectively. Shape recovery of ribbon 1 (15.5wt%Mn) formed ${\varepsilon}$ and ${\alpha}^{\prime}$martensites decreased because of the presence of ${\alpha}^{\prime}$martensite but those of ribbon 2 (20.2wt%Mn) and ribbon 3 (23.5wt%Mn) formed ${\varepsilon}$ martensite increased with increasing annealing temperature.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2000년도 International Symposium on Magnetics The 2000 Fall Conference
• /
• pp.506-507
• /
• 2000

• 분석과학
• /
• 제8권3호
• /
• pp.341-350
• /
• 1995

Melt-spinning법을 이용하여 $Nd_{14}Fe_{80}B_6$ 조성의 리본합금을 제조하고 각 제조조건별 시편에 대한 자기적 특성을 분석하였다. 리본합금의 미세구조와 자기적 특성은 냉각속도 및 열처리 조건에 민감하게 변화하였다. As-quenched 상태의 경우 wheel 속도 20m/sec에서 가장 좋은 자기적 특성을 나타내었으며, 비정질 상태의 리본시편에 대한 열처리 효과는 22m/sec에서 제조된 리본시편을 $600^{\circ}C$에서 30분간 진공열처리하였을 때 가장 좋은 결과를 얻을 수 있었다. 또한 $Nd_2Fe_{14}B$상의 결정화 온도는 DTA 분석결과 $595^{\circ}C$ 부근이었다.

• 한국전기전자재료학회논문지
• /
• 제36권2호
• /
• pp.186-190
• /
• 2023

We studied the various characteristics of Sn-In (wt%) Pb-free solders for photovoltaic ribbon application. The solders near the eutectic composition of Sn₄₈In₅₂ (wt%) existed in InSn₄ and In₃Sn alloy phases, and in In crystal phase, but not in Sn crystal phase. In addition, the InSn₄ phase (γ-alloy) existed separately from the In₃Sn (β-alloy) and the In phase confirmed by an SEM-EDS-mapping. The melting temperature of the eutectic solder of Sn₄₈In₅₂ (wt%) was 119.2℃, and when the Sn content decreased in reference to the eutectic composition, it slightly increased to 121.4℃, but when the Sn content increased, it remained almost constant at 119.1℃. The peel strength of the ribbon plated with the Sn₄₂In₅₈ (wt%) solder was 38.7 N/mm², and it tended to increase when the Sn content increased. The peel strength of the eutectic Sn₄₈In₅₂ (wt%) solder was 53.6 N/mm², and that of the Sn₅₁In₄₉ (wt%) solder was 61.6 N/mm² that was the highest.

• 소성∙가공
• /
• 제8권6호
• /
• pp.626-633
• /
• 1999

$Al_{85}Ni_{10}Y_5$ (at. %) amorphous alloy ribbons have been produced by rapidly solidification process and consolidated by the conventional powder metallurgy method. The grains with ∼90 nm were obtained in the Al85Ni10Y5 alloy extrudates by hot-pressing followed by hot-extusion. To investigate the effect of heat treatment on microstructural change of the extrudates, heat treatment was carried out from 200℃ to 400℃ at the step of 50℃. In addition, mechanical properties of the extrudates were analysed from torsion test at the temperature range or 400∼500℃ under a strain rates of 0.2, 0.5, and 1.0/sec. The extrudates showed a flow stress of ∼190 MPa and low elongation of ∼150% at 400℃, contributing to the enhancement of ductility and hardness for extrudates. Also, grain boundary sliding was occurred in the $Al_{85}Ni_{10}Y_5$ alloy during hot deformation.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1023-1024
• /
• 2006

Al-8Fe-2Mo-2V-1Zr alloys were prepared by the gas atomization/hot extrusion and the melt spinning/hot extrusion. For the gas atomized and extruded alloy, equiaxed grains with the average size of 400 nm and finely distributed dispersoids with their particle sizes ranging from 50nm to 200nm were observed. For the melt spun and hot extrusion processed alloy, refined microstructural feature consisting of equiaxed grains with the average size of 200nm and fine dispersoids with their particle sizes under 50nm appeared to exhibit a difference in microstructure. Strength of the latter alloy was higher than that for the former alloy up to elevated temperatures.

• 대한전기학회논문지
• /
• 제40권1호
• /
• pp.67-72
• /
• 1991

For improving the magnetic properties of the amorphous Fe-B-Si alloy, we annealed the sample in a magnetic field oriented in the plane of the ribbon longitudinal to its long axis. By field annealing, coercive force and total core loss are reduced from 0.04 Oe to 0.02 Oe, and from 0.25 watt/kg to 0.15 watt/kg respectively in comparsion with non-field annealed specimen. These reductions were caused by the formation of 180 dcmain wall parallel to the annealing field due to the induced anisotropy.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2011년도 임시총회 및 하계학술연구발표회
• /
• pp.166-166
• /
• 2011

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2012년도 임시총회 및 하계학술연구발표회
• /
• pp.135-135
• /
• 2012