• 대한기계학회논문집
• /
• 제19권3호
• /
• pp.705-712
• /
• 1995

The wear characteristics and wear mechanisms in TiN coating deposited on high speed steel and alloy tool steel by ion plating were investigated. Pin on V-block wear tester was used for a wear test method. The specimen was composed of three kinds of high speed steel and alloy tool steel which had different hardness by changing the heat treating condition. Three kinds of coating thickness were also applied to each specimen. Microscopic observation of worn surfaces was made by SEM. The scratch test of coating surface by the ion plating showed that critical load to break the coating interface was greater than 50N. The critical load increased with both substrate hardness and coating thickness. The wear resistance of TiN coated high speed steel became 10 times greater than that of non-coated ones. SEM observation showed that leading edge of contact was compressive and trailing edge was under maximum tensile stress and then surface cracking broke out perpendicular to sliding direction.

• 열처리공학회지
• /
• 제34권6호
• /
• pp.281-286
• /
• 2021

Arc ion plating (AIP), laser cladding, and nitriding are methods that can prevent mold damage or repair and create cracks and breakages on the die surface. The dissolution and soldering behavior of coated SKD61 by using arc ion plating, laser cladding, and nitriding was investigated. The structure of the coating was investigated as a function of deposition conditions by X-ray diffraction and the crystallographic orientation was determined using the texture factor. The TiAlN film deposited with AIP showed excellent corrosion resistance in the molten aluminum alloy at 680℃. In this paper, we have detailed the corrosion and mass loss phenomena associated with these steel-cast metal interactions.

• 대한치과보철학회지
• /
• 제44권5호
• /
• pp.628-641
• /
• 2006

Statement of problem: Dental magnetic materials have been applied to removable prosthetic appliances, maxillofacial prostheses, obturator and dental implant but they still have some problems such as low corrosion resistance in oral environments. Purpose: To increase the corrosion resistance of dental magnetic materials, surfaces of Sm-Co and Nd-Fe-B based magnetic materials were plated with TiN and sealed with stainless steels. Materials and methods : Surfaces of Sm-Co and Nd-Fe-B based magnetic materials were plated with TiN and sealed with stainless steels, and then three kinds of electrochemical corrosion test were performed in 0.9% NaCl solution; potentiodynamic, potentiostatic, and electrochemical impedance test. From this study, corrosion behavior, amount of elements released, mean average surface roughness values, the changing of retention force, and magnetic force values were measured comparing with control group of non-coated magnetic materials. Results: The values of surface roughness of TiN coated Sm-Co and TiN coated Nd-Fe-B based magnetic materials were lower than those of non coated Sm-Co and Nd-Fe-B alloy. From results of potentiodynamic test, the passive current density of TiN coated Sm-Co alloy were smaller than those of TiN coated Nd-Fe-B alloy and non coated alloys in 0.9% NaCl solution. From results of potentiostatic and electrochemical impedance test, the surface stability of the TiN coated Sm-Co alloy was more drastically increased than that of the TiN coated Nd-Fe-B alloy and non-coated alloy. The retention and magnetic force after and before corrosion test did not change in the case of TiN coated magnetic alloy sealed with stainless steel. Conclusion: It is considered that the corrosion problem and improvement for surface stability of dental magnetic materials could be solved by ion plating with TiN on the surface of dental magnetic materials and by sealing with stainless steels.

• Smart Structures and Systems
• /
• 제26권4호
• /
• pp.507-520
• /
• 2020

In order to achieve effective corrosion monitoring of buried metal pipelines, a Novel nondestructive Testing (NDT) methodology using ultra-long (250 mm) Polymer Optical Fiber (POF) sensors coated with the Fe-C alloy film is proposed in this study. The theoretical principle is investigated to clarify the monitoring mechanism of this method, and the detailed fabrication process of this novel POF sensor is presented. To validate the feasibility of this novel POF sensor, exploratory research of the proposed method was performed using simulated corrosion tests. For simplicity, the geometric shape of the buried pipeline was simulated as a round hot-rolled plain steel bar. A thin nickel layer was applied as the inner plated layer, and the Fe-C alloy film was coated using an electroless plating technique to precisely control the thickness of the alloy film. In the end, systematic sensitivity analysis on corrosion severity was further performed with experimental studies on three sensors fabricated with different metal layer thicknesses of 25 ㎛, 30 ㎛ and 35 ㎛. The experimental observation demonstrated that the sensor coated with 25 ㎛ Fe-C alloy film presented the highest effectiveness with the corrosion sensitivity of 0.3364 mV/g at Δm = 9.32 × 10^-4 g in Stage I and 0.0121 mV/g in Stage III. The research findings indicate that the detection accuracy of the novel POF sensor proposed in this study is satisfying. Moreover, the simple fabrication of the high-sensitivity sensor makes it cost-effective and suitable for the on-site corrosion monitoring of buried metal pipelines.

• 공업화학
• /
• 제17권5호
• /
• pp.458-464
• /
• 2006

팔라듐 합금 복합막의 제조는 니켈 분말과 무기화합물의 혼합물로 개질된 튜브형 다공성 스테인레스 스틸 지지체 표면 위에 무전해 도금법(elctroless plating technique)에 의해 팔라듐 - 니켈 - 은을 박막으로 도금하는 형태로 이루어졌다. 일반적인 다공성 금속 지지체는 기공이 크기 때문에 그 자체로서 도금에 적합한 지지층이 되기가 어렵고, 결함이 없는 팔라듐 복합막의 제조가 쉽지 않아 본 연구에서는 금속 지지체와 팔라듐 사이에 중간층(intermediate layer)을 형성하여 이와 같은 문제점을 극복하고자 하였다. 중간층의 소재인 실리카 졸, 알루미나 졸, 이산화티타늄 졸 등의 무기화합물과 니켈 분말의 혼합물로 다공성 금속 지지체 위에 코팅하여 박막을 형성하고 제조 조건에 따른 질소 투과도를 측정하고 비교하였다. SEM 분석법에 의해 니켈과 무기화합물 혼합물의 표면층의 형성 모습도 측정하였다. 제조된 중간층 가운데 이산화티타늄 졸과 니켈의 혼합물이 가장 낮은 질소 투과도와 치밀한 표면층을 나타내었다. 최종적으로 니켈과 실리카의 혼합 중간층으로 이루어진 팔라듐-니켈-은 합금 복합막을 제조하고 수소와 질소의 투과도를 측정하였다. 1기압 이하에서 질소에 대한 수소 선택도는 무한대였으며 수소투과 속도는 1 기압, $500^{\circ}C$에서 $1.39{\times}10^{-2}mol/m^2{\cdot}s$의 값을 나타냈다.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.27-33
• /
• 2013

According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).