• Journal of Conservation Science
• /
• v.31 no.1
• /
• pp.21-27
• /
• 2015

The Phoenix-shaped Glass Ewer, which is No. 193 National Treasure, was seriously damaged by a unique form of green glass pieces when excavated among a number of burial accessories of Hwangnamdaechong known to have been formed in the 5th century. While it has long been exhibited at the National Museum of Korea since its treatment for conservation treatment at conservation science laboratory in 1984, the existing adhesive materials seriously deteriorated for the 30 years, and the condition was quite unstable. The epoxy resin used as a restorative materials turned yellowing due to the light and heat so much that it was no longer able to exhibit it in a stable and effective manner. As a result, a re-treatment for conservation was conducted lately. This study focuses on the three pieces of Gold wires used to carefully wrap up the handle of the Phoenix-shaped Glass Ewer broken into three pieces, which has not been studied so far. As for the analysis method for Gold wires, SEM-EDS and Stereo Microscope were used for nondestructive analysis. First of all, the result of the SEM-EDS analysis shows that the composition was Au 91.9 wt.%-Au 92.8 w.t% and Ag 5.9 wt.%-Ag 6.5 wt.%, which indicates that it was an alloy made of Au and Ag. The production technique of Gold wires was also observed by means of optical microscopes. In general, Gold wires were manufactured by a drawing process in which a lump of gold was beaten or pulled out of a hole or by a process of twisting a gold plate. However, Gold wires separated from the handle of the Phoenix-shaped Glass Ewer did not involve any trace of twisting on the surface. Rather, fine vertical stripes were observed with the sections filled up. Hence, it is thought that this Ewer went through a drawing process and then was mended. As a result, no certain relation with the golden mending material used for the Phoenix-shaped Glass Ewer was verified. The findings above indicate that most of the existing researches on Gold wires recognized them, not as separate remains, but merely as a component of other golden remains. Thus, there has been little systematic study on the manufacturing techniques of Gold wires. The future study on Gold wires may verify the correlation between the Gold wires used to fix the handle of the Phoenix-shaped Glass Ewer, which is examined in this study, with that of golden remains in the Silla era.

• Korean Journal of Heritage: History & Science
• /
• v.46 no.1
• /
• pp.208-227
• /
• 2013

Twenty-seven bronze bowls excavated from the Goryo burial complex at Deobu-gol were examined for their microstructure and chemical composition to characterize the bronze technology practiced by commoners at the time. Results showed that the objects examined can be classified into four groups: 1) objects forged out of Cu-near 22%Sn alloys and then quenched; 2) objects cast from Cu-below 10% Sn alloys containing lead; 3) objects cast from Cu-10%~20% Sn alloys containing lead and then quenched; 4) objects forged out of Cu-10~20% Sn alloys containing lead and then quenched. This study revealed that the fabrication technique as determined by alloy compositions plays an important role in bronze technology. The use of lead was clearly associated with the selection of quenching temperatures, the character of inclusions and the color characteristics of bronze surfaces. It was found that the objects containing lead were quenched at temperatures of $520^{\circ}{\sim}586^{\circ}C$ while those without lead were quenched at the range of $586^{\circ}{\sim}799^{\circ}C$. The presence of selenium in impurity inclusions was detected only in alloys containing lead, suggesting that the raw materials, Cu and Sn, used in making the lead-free alloys for the first group were carefully selected from those smelted using ores without lead contamination. Furthermore, the addition of lead was found to have significant effects on the color characteristics of the surface of bronze alloys when they are subjected to corrosion during interment. In leaded alloys, corrosion turns the surface light green or dark green while in unleaded alloys, corrosion turns the surface dark brown or black. It was found that in fabrication, the wall thickness of the bronze bowls varies depending on the application of quenching; most of the quenched objects have walls 1mm thick or below while those without quenching have walls 1mm thick or above. Fabrication techniques in bronze making usually reflect social environments of a community. It is likely that in the late Goryo period, experiencing lack of skilled bronze workers, the increased demand for bronze was met in two ways; by the use of chief lead instead of expensive tin and by the use of casting suitable for mass production. The above results show that the Goryo bronze workers tried to overcome such a resource-limited environment through technological innovations as apparent in the use of varying fabrication techniques for different alloys. Recently, numerous bronze objects are excavated and available for investigation. This study shows that with the use of proper analytical techniques they can serve as a valuable source of information required for the characterization of the associated technology as well as the social environment leading to the establishment of such technology.