• The korean journal of orthodontics
• /
• v.34 no.5 s.106
• /
• pp.439-447
• /
• 2004

The purpose of this study was to investigate the influence of water, saliva and blood contamination on the bonding strength of metal brackets with a self-etching primer/adhesive to enamel. Ninety-six extracted human teeth were divided into four groups. The brackets were bonded to enamel with a self- etching primer (3M/Unitek Dental Products. Monorovia California) according to one of four protocols. The teeth were bonded in a dry condition (group D) or in contamination with distilled water (group W), artificial saliva (group S). or fresh human blood (group B) Shear bond strengths were tested using an Instron Universal testing machine. After debonding. bracket and tooth surfaces were examined with a stereomicroscope. In each group, four samples were selected and examined with a Scanning electron microscope of the prepared enamel surface and resin-enamel interlace. The results obtained were summarized as follows: Shear bond Strength if group D $(15.22{\pm}2.86MPa)$ and W $(15.20{\pm}3.85 MPa)$ Were higher than in group B$(12.56{\pm}2.94MPa)$ (p<0.05). There were no statistical differences in the shear bond strengths between groups D. W and S (p>0.05). There was a tendency to have less residual adhesive remaining on the enamel surfaces of group B than group D. The SEW morphology of group D and W showed a more roughened etching pattern than group S and B. Water or saliva contamination on bending of orthodontic brackets with Transbond plus self etching primer had almost no influence on bond strength In this study, the blood contaminated group showed the lowest bond strength, but it was above the clinically acceptable bond strength (5.9-7.8 MPa, Reynold, 1975). The results of this study suggest that acceptable clinical bond strengths can be obtained in wet conditions when self-etching adhesives are used.

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.1
• /
• pp.27-32
• /
• 2013

Purpose: The aims of this study were to evaluate the effect of a resin coating on the shear bond strength of indirect composite restoration bonded to dentin with a self adhesive resin cement and to compare the shear bond strength with that of a conventional resin cement. Materials and methods: The occlusal enamels of thirty six extracted noncarious human molars were removed until the dentin flat surfaces of the teeth were exposed. Then, they were divided into 3 groups. The dentin surfaces of group 1 and 3 were left without any conditioning, while the dentin surfaces of group 2 were resin-coated with Clearfil SE bond and a flowable resin composite, Metafil Flo. After all specimens were temporized for 24 hours, indirect composite resin blocks fabricated by Tescera were bonded to dentins by Unicem for group 1 and 2, and by Panavia F for group 3. After 48 hours of water storage, shear bond strengths were measured. The data was analyzed with one-way analysis of variance and multiple comparison test (Tukey method). Results: The shear bond strengths of Unicem applied to resin coated dentin surfaces were significantly higher than those of Unicem and Panavia F used to uncoated dentin surfaces (P<.0001). Conclusion: Application of a resin coating to the dentin surface significantly improved the shear bonding strength of a self adhesive resin cement in indirect restoration.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.4
• /
• pp.514-521
• /
• 2009

The aim of this study was to evaluate the bonding ability of two self etch systems to human primary and permanent enamel and the effect of additional acid etching time. Exfoliated, caries free human primary molar(n=65) and permanent molar extracted (n=65) were used. prepared enamel specimens were randomly divided into 2 test groups and a control group. The control group(n=10) were treated with 35% phosphoric acid gel and Scotchbond Multi-purpose adhesive. Experimental groups(self-etching systems) were subdivided into 6 groups(each n=10) according to additional etching time(0s, 5s, 10s, 15s, 20s, 30s). The result were as follows : 1) The shear bond strengths of the self-etching adhesives(Clearfil SE Bond, Adper Prompt L-pop) without additional etching were lower than control group(Scotch Bond Multipurpose). 2) Between the same self-etch adhesive groups, additional etched groups showed higher shear bond strength 3) There was no significant difference between primary and permanent enamel. In conclusion, bond strength of self-etch adhesives to enamel could be increased with additional etching.

• The korean journal of orthodontics
• /
• v.39 no.5
• /
• pp.320-329
• /
• 2009

Objective: The aim of this study was to evaluate the effect of metal primers and thermocycling on shear bond strength between the orthodontic bracket and gold alloy. Methods: For this study, 80 specimens made of dental gold alloy were divided into 8 groups based on the combination of metal primers (none, Alloy primer, Metaltite, V-primer) and thermocycling (with and without thermocycling). Shear bond strength testing was performed with a universal testing machine. Bond failure sites were classified by a modified ARI (Adhesive Remnant Index) score. Results: All metal primer treated groups showed a significantly higher shear bond strength than the only sandblasting treated group without thermocycling (p < 0.05). There were no significant differences on shear bond strength in the groups with thermocycling (p > 0.05). Bond failure sites of the metal primer treated group without thermocycling occurred at gold alloy/adhesive interface, whereas there were no differences on bonding failure sites in the groups with thermocycling. Conclusions: These findings suggest that using metal primer on gold alloy enhances the initial bracket bond strength. But, this effect was not shown with thermocycling.

• Restorative Dentistry and Endodontics
• /
• v.27 no.5
• /
• pp.493-501
• /
• 2002

This study evaluated the microleakage performance of four self-etcing primer adhesives(Clearfil SE Bond, Clearfil Liner Bond 2, UniFil Bond, and FL Bond) and one self-etching adhesive(Prompt L-Pop). Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were prepared on both buccal and lingual surfaces of 50 extracted human molar teeth. Prepared teeth were randomly divided into five groups and restored using one of five adhesives and composite resins: Prompt L-Pop/Filtek Z 250(Group 1), Clearfil SE Bond/Clearfil AP-X(Group 2), Clearfil Liner Bond 2/Clearfil AP-X(Group 3), UniFil Bond/UniFil F(Group 4), and FL Bond/Filtek Z 250(Group 5). Following one day storage in room temperature water, the restored teeth were thermocycled for 500 cycles between 5$^{\circ}C$ and 55$^{\circ}C$. Marginal microleakage was assessed by dye penetration using 2% methylene blue dye. After 24 hours, the teeth were sectioned longitudinally and evaluated for microleakage under steromicroscope The data were statistically analysed by Kruskal-Wallis Test, Mann-Whitney and Wilcoxon signed ranked tests. The results of this study were as follows ; 1. The microleakges at both enamel and dentinal mal$.$gins were the lowest in group 4. increasing among groups in the following order: group 2, follwed by group 5, follwed by group 1, and the highest in group 3. 2. At the enamel margins, the microleakage of group 3 was significantly higher than those of groups 2. 4 and 5(p<0.05), and also the microleakage of group 1 was statistically higher than those of groups 2 and 5(p<0.05). 3. At the dentinal margins, microleakage of group 3 was signincantly higher than microleakages of groups 1, 2, 4 and 5(p<0.05). 4. Compared with microleakages between the enamel and dentinal margins of each group, groups 1, 4 and 5 at enamel margin and group 2 and group 3 at dentinal margin were higher microleakage. But there was no significant difference between enamel and dentinal microleakages of each group(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.31 no.4
• /
• pp.263-268
• /
• 2006

Recently, self-etching adhesive system has been introduced to simplify the clinical bonding proce- dures. It is less acidic compared to the phosphoric acid, thus there is doubt whether this system has enough bond strength to enamel. The purpose of this study was to investigate the influence of additional etching on the adhesion of resin composite to enamel. Ninety extracted bovine permanent anterior teeth were used. The labial surfaces of the crown were ground with 600-grit abrasive paper under wet condition. The teeth were randomly divided into six groups of 15 teeth each. Clearfil SE $Bond^{\circledR},\;Adper^{TM}$ Prompt L-Pop and Tyrian $SPE^{TM}$ were used as self-etching primers. Each self-etching primers were applied in both enamel specimens with and without additional etching. For additional etching groups, enamel surface was pretreated with 32% phosphoric acid (UNI-ETCH, Bisco, Inc., Schaumburg, IL. USA). Hybrid resin composite Clearfil AP-X, (Kuraray Co., Ltd., Osaka, Japan) was packed into the mold and light-cured for 40 seconds. Twenty-four hours after storage, the specimens were tested in shear bond strength. The data for each group were subjected to independent t - test at p < 0.01 to make comparisons among the groups. In Clearfil SE $Bond^{\circledR}$, shear bond strength of additional etching group was higher than no additional etching group (p < 0.01). In $Adper^{TM}$ Prompt L-Pop and Tyrian SPE, there were no significant difference between additional etching and non-etching groups (p > 0.01). In conclusion, self-etching adhesive system with weak acid seems to have higher bond strength to enamel with additional etching, while self-etching adhesive system with strong acid seems not.

• Advances in concrete construction
• /
• v.7 no.3
• /
• pp.191-201
• /
• 2019

Bamboo concrete bond behaviour is investigated through pullout test in this work. The bamboo strip to be used as reinforcement inside concrete is first treated with chemical adhesive to make the bamboo surface impermeable. Various surface coatings are explored to understand their water repellant properties. The chemical action at the bamboo concrete interface is studied through different chemical coatings, sand blasting, and steel wire wrapping treatment. Whereas mechanical action at the bamboo concrete interface is studied by developing mechanical interlock. The result of pullout tests revealed a unique combination of surface treatment and grooved bamboo profile. This combination of surface treatment and a grooved bamboo profile together enhances the strength of bond. Performance of a newly developed grooved bamboo strip is verified against equivalent plain rectangular bamboo strip. The test results show that the proposed grooved bamboo reinforcement, when treated, shows highest bond strength compared to treated plain, untreated plain and untreated grooved bamboo reinforcement. Also, it is observed that bond strength is majorly influenced by the type of surface treatment, size and spacing of groove. The changes in bamboo-concrete bond behavior are observed during the experimentation.

• The korean journal of orthodontics
• /
• v.30 no.5 s.82
• /
• pp.625-642
• /
• 2000

The purpose of this study is to evaluate the effects of mechanical and thermal fatigue stress on the shear, tensile and shear-tensile combined bond strengths(SBS, TBS, CBS) in various orthodontic brackets bonded to human premolars with chemically cured adhesive(Ortho-one, Bisco, USA). Five types of commercially available metal brackets with various bracket base configurations of Photoetched base(Tomy, Japan), Non-Etched Foil Mesh base(Dentaurum, Germany), Micro-Etched Foil Mesh base(Ortho Organizers, USA), Chessboard base(Daesung, Korea), and Integral base(3M Unitek, USA) were used. Samples were divided into 3 groups, the first group was acted with shear-tensile combined loads($45^{\circ}$) of 200g for 4 weeks(mechanical fatigue stress), the second group was subjected to the 5,000 thermocycles of 15 second dwell time each in $5^{\circ}C\;and\;55^{\circ}C$ baths(thermal fatigue stress), and the third group was the control. Bond strengths were measured at the crosshead speed of 0.5mm/min. The cross-section of bracket base/adhesive interface and the fracture surface were examined with the stereoscope and the scanning electron microscope. The resin remnant on bracket base surface was assessed by ART(Adhesive Remnant Index). The obtained results were summarized as follows, 1. In static bond strength, Photoetched base bracket showed the maximum bond strength and Integral base bracket showed the minimum bond strength(p<0.05). In all brackets, shear bond strength(SBS) was in the greatest value and shear-tensile combined strength(CBS) was in the least value(p<0.05). 2. After mechanical fatigue test, Photoetched base bracket showed the maximum bond strength and Integral base bracket showed the minimum bond strength(p<0.05). In Photoetched base bracket and Micro-Etched Foil Mesh base bracket, shear bond strength(SBS), tensile bond strength(TBS) and shear-tensile combined strength(CBS) were decreased after mechanical fatigue test(p

• Restorative Dentistry and Endodontics
• /
• v.16 no.2
• /
• pp.126-142
• /
• 1991

The purpose of this study was to evaluate the effect of various dentin surface treatments on shear bond strength, microhardness and fracture mode before and after thermocycling. Recently extracted 75 human molars were used. The teeth were sagittal sectioned faciolingually to obtain 150 specimens. They were randomly divided into six groups. Mesial and distal dentinal surfaces of specimens were exposed by grinding and treated respectively with GC-DENTIN CONDITIONER. 10-3 solution of 4-Meta, Cleansar and Primer of GLUMA, Scotchprep of Scotchbond 2, DENTIN CONDITIONER and PRIMER A, B of ALL BOND according to the manufacturers directions. Specimens of one group were not treated. Adhesive agent of Scotchbond 2, were applied and cured on the treated dentin surfaces. After P-50 were cured on them, specimens were stored in 31c water for 24 hours before shear bond strength measurement Shear bond strength was measured in 10 specimens of each group. 10 specimens of each group were thermocycled in $20^{\circ}C$, $60^{\circ}C$,$20^{\circ}C$, $4^{\circ}C$, $20^{\circ}C$ water in order, for 30 seconds respectively, 100 times a day for 7 days. After thermocycling shear bond strength was measured. Microhardness was checked on treated dentin surface and fractured dentin surface in 10 specimens respectievly. Francture modes were observed with SEM The following results were obtained. 1. Before thermocycling. shear bond strengths in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens(P<0.01). 2. After thermocycling. shear bond strengths in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of AIL BOND were significantly higher than those in specimens not: treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta(P<0.01). Shear bond strengths in the specimens treated with GC-DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens except those treated with Scotchprep of Srotchbond 2(P<0.01). 3. Shear bond strengths after thermocycling were reduced in the specimens not treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta and were increased in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2, without significance, compared with those before thermocycling. In the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, shear bond strengths after thermocycling were significantly increased, compared with those before thermocycling(P<0.01). 4. Microhardnesses in the fractured surfaces after shear bond strength measurement were significantly increased in the specimens treated with 10-3 solution of 4-Meta and significantly decreased in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, compared with those in the treated dentin surfaces(P<0.01). 5. In the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of ALL BOND, cohesive fracture modes were observed more than adhesive fracture modes.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.5
• /
• pp.539-547
• /
• 2012

To manufacture laminated wood with improved mechanical properties by providing uniform adhesiveness, the adhesive was applied and the plate adhesive was laminated on the wood surface. Then, after laminating the wood on the top part of the adhesivebond, it was heated and dried while the adhesive was stiffened using microwaves, and the test piece was manufactured by compressing it with the press machine for thirty minutes. The temperature and the water content were examined according to the heating time of the wood heated with the microwave, and testing was conducted on the shear strength and flexural strength of the wood. In addition, the microstructure of the adhesive bond between the wood was recorded to confirm the penetrabilityinto the wood structure for the adhesive. After the test was conducted, it was found that the test piece manufactured with wood that has its water content leveled with the microwave heating showed improved shear strength and bending strength compared to the standard test piece. With regard to adhesives, liquefied polyvinyl acetate resin and plate's PVB resin were found to have superior adhesive strength. Also, after filming the cellular microstructure, it was found that when the laminated wood is heated with microwaves, the infiltration of the adhesive into the inside of the wood becomes easy, which makes it effective for improving adhesiveness.