In this study, the electrochemical investigation of various electrodes for reverse electrodialysis using potassium ferrocyanide and potassium ferricyanide as a redox system was carried out. Cyclic voltammetry was the employed method for this electrochemical study. From the results of cyclic voltammograms for various electrode materials, i.e., Au, Vulcan supported Pt, activated carbon, carbon nanofiber, Vulcan, the Vulcan electrode showed the lowest overpotential, but the Pt electrode having slightly higher overpotential obtained slightly higher anodic and cathodic current densities for the $Fe(CN)_6{^{4-}}/Fe(CN)_6{^{3-}}$ redox couple. The cyclic voltammograms for the Vulcan electrode confirmed very good electrochemical reversibility and kinetic behavior. As a result, among the electrode materials, the Vulcan electrode is the most promising electrode material for reverse electrodialysis.

• 전기화학회지
• /
• 제4권3호
• /
• pp.113-117
• /
• 2001

탄소계 전극을 사용하는 EDLC(Electric Double Layer Capacitor)용의 축전용량과 충방전속도는 전해질의 종류, 충방전 조건 그리고 탄소계 물질의 물리화학적 성질에 따라 크게 달라질 수 있다. 이에 본 연구에서는 dip coating method에 의해 제조된 EDLC용 활성탄소 전극에서 유기 전해질의 종류를 달리하여 충방전 실험과 전기화학적인 실험을 시행하였다. 또한 충전전류밀도와 방전전류밀도의 변화에 따른 비축전 용량의 변화를 조사하였고, 최적 유기전해질의 조건에서 leakage current 특성, 자가방전 특성 그리고 시간전압곡선을 기존의 $1M-Et_4NBF_4/PC$와 비교하였다 활성탄, 소전극으로 비표면적이 $2000m^2/g$인 MSP-20을 사용하고 유기전해질로는 $1M-LiPF_6/PC-DEC(1:1)$를 사용한 EDLC에서 130 F/g 정도의 우수한 비축전 용량을 나타내었고 저항면에서도 가장 낮은 수치를 나타내었다 $1M-LiPF_6/PCDEC(1:1)$를 사용한 EDLC는 15분동안 0.0004A의 낮은 leakage current와 100시간 경과 후 0.8V의 우수한 자가 방전 특성 그리고 IR-drop이 적은 선형의 시간-전압곡선을 보여주었다.

• 한국수소및신에너지학회논문집
• /
• 제30권5호
• /
• pp.418-427
• /
• 2019

Activated carbon was synthesized from bamboo charcoal by KOH activation at various temperatures for electrochemical double layer capacitor applications. The micro-structural and surface properties of all the samples were characterized by X-ray diffraction, scanning electron microscopy and N2 adsorption/desorption isotherm method. The electrochemical properties of the activated bamboo charcoal were examined by cyclic voltammetry in the potential window of -1.0 to 0.2 V in 6 M KOH electrolyte at different scan rates. An electrode made from the sample activated with 7.5 M KOH and heat treated at $750^{\circ}C$ for 3 h gave a maximum capacitance of 553 F/g at 1 mV/s and 450 F/g at 10mV/s.

• Carbon letters
• /
• 제15권2호
• /
• pp.113-116
• /
• 2014

Due to their morphology, electrochemical stability, and function as a conducting carbon matrix, graphene nanosheets (GNS) have been studied for their potential roles in improving the performance of sulfur cathodes. In this study, a GNS/sulfur (GNS/S) composite was prepared using the infiltration method with organic solvent. The structure, morphology and crystallinity of the composites were examined using scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The electrochemical properties were also characterized using cyclic voltammetry (CV). The CV data revealed that the GNS/S composites exhibited enhanced specific-current density and ~10% higher capacity, in comparison with the S-containing, activated-carbon samples. The composite electrode also showed better cycling performance for multiple charge/discharge cycles. The improvement in the capacity and cycling stability of the GNS/S composite electrode is probably related to the fact that the graphene in the composite improves conductivity and that the graphene is well dispersed in the composites.

• 자원리싸이클링
• /
• 제8권3호
• /
• pp.18-25
• /
• 1999

화학제염이나 전지화학제염을 통해 발생된 방사성 폐액을 정화처리할 수 있는 새로운 방법으로, 다공성 활성탄소섬유(ACF)상에서 폐액중 코발트이온의 전기적 흡·탈착에 대한 연구를 수행하였다. 회전원판 전극을 사용하여 순환전압전류법으로 전기이중층 충전만이 발생하는 전위 영역을 조사하였다. ACF 전극을 사용한 회분식 전기흡착 실험결과, 음의 전위 가용은 저위 미가용 시의 흡착에 비해 코발트이온의 흡착을 증가시켰다. 또한 흡착된 코발트 이온은 역전된 가용전위에 의해 용액으로 용출되었으며 이와 동시에 탄소체 전극이 재생되어, 전기흡착 공정의 가역성을 확인 할 수 있었다.

• Carbon letters
• /
• 제16권1호
• /
• pp.51-56
• /
• 2015

Carbonate-type organic electrolytes were prepared using propylene carbonate (PC) and dimethyl carbonate (DMC) as a solvent, quaternary ammonium salts, and by adding different contents of 1-ethyl-3-methyl imidazolium tetrafluoroborate ($EMImBF_4$). Cyclic voltammetry and linear sweep voltammetry were performed to analyze conducting behaviors. The surface characterizations were analyzed by scanning electron microscopy method and X-ray photoelectron spectroscopy. From the experimental results, increasing the $EMImBF_4$ content increased the ionic conductivity and reduced bulk resistance and interfacial resistance. In particular, after adding 15 vol% $EMImBF_4$ in 0.2 M $SBPBF_4$ PC/DMC electrolyte, the organic electrolyte showed superior capacitance and interfacial resistance. However, when $EMImBF_4$ content exceeded 15 vol%, the capacitance was saturated and the voltage range decreased.

• Carbon letters
• /
• 제20권
• /
• pp.19-25
• /
• 2016

Activated carbon fiber (ACF) surfaces are modified using an electron beam under different aqueous solutions to improve the NO gas sensitivity of a gas sensor based on ACFs. The oxygen functional group on the ACF surface is changed, resulting in an increase of the number of non-carbonyl (-C-O-C-) groups from 32.5% for pristine ACFs to 39.53% and 41.75% for ACFs treated with hydrogen peroxide and potassium hydroxide solutions, respectively. We discover that the NO gas sensitivity of the gas sensor fabricated using the modified ACFs as an electrode material is increased, although the specific surface area of the ACFs is decreased because of the recovery of their crystal structure. This is attributed to the static electric interaction between NO gas and the non-carbonyl groups introduced onto the ACF surfaces.

• 한국재료학회지
• /
• 제27권4호
• /
• pp.192-198
• /
• 2017

Carbon nanofiber (CNF) is used as an electrode material for electrical double layer capacitors (EDLCs), and is being consistently researched to improve its electrochemical performance. However, CNF still faces important challenges due to the low mesopore volume, leading to a poor high-rate performance. In the present study, we prepared the unique architecture of the activated mesoporous CNF with a high specific surface area and high mesopore volume, which were successfully synthesized using PMMA as a pore-forming agent and the KOH activation. The activated mesoporous CNF was found to exhibit the high specific surface area of $703m^2g^{-1}$, total pore volume of $0.51cm^3g^{-1}$, average pore diameter of 2.9 nm, and high mesopore volume of 35.2 %. The activated mesoporous CNF also indicated the high specific capacitance of $143F\;g^{-1}$, high-rate performance, high energy density of $17.9-13.0W\;h\;kg^{-1}$, and excellent cycling stability. Therefore, this unique architecture with a high specific surface area and high mesopore volume provides profitable synergistic effects in terms of the increased electrical double-layer area and favorable ion diffusion at a high current density. Consequently, the activated mesoporous CNF is a promising candidate as an electrode material for high-performance EDLCs.

• 한국환경과학회지
• /
• 제11권4호
• /
• pp.355-360
• /
• 2002

This study was to analyze the right of wrong of gray-water treatment by applying BPBE electrode cell to the effluence water in the terminal disposal plant of sewage. The results were as follows : The best result was obtained with applied voltage 40V and detention time 6 minutes for the BPBE electrode cell which has the graphite-plate in main electro-de, packing coconut activated carbon. The elimination rate of COD of Al-plate was higher than that of graphite-plate in main electrode. The result of electrolysis for 3 hour in parallel circuit showed the using possibility of gray-water according to each elimination rate : COD 59%, T-N 69 %, T-P 69%. The BPBE electrode cell with the Al-plate in main electrode made the best effect for the elimination of algae in lake water and algae were not occurred in electrolytic water.

• 공업화학
• /
• 제24권2호
• /
• pp.201-207
• /
• 2013

본 연구에서는 전기이중층 커패시터의 전극 활물질로 사용되는 페놀계 활성탄소의 비 정전용량의 증가를 위하여 붕산을 이용하여 표면처리를 수행하였다. 또한, 붕산 처리가 전기화학 특성에 미치는 영향에 대하여 고찰하였다. 활성탄소의 붕산 처리는 활성탄소의 표면에 전기화학적 특성 향상에 도움이 되는 퀴논형 관능기(O=C)의 비율을 효과적으로 증가시켰으며, 비표면적과 총 기공 부피 및 미세공 부피를 증가시켰다. 최적의 조건으로 붕산 처리된 활성탄소는 미처리활성탄소에 비해 비 정전용량이 약 20% 증가하였다. 이러한 결과로부터 활성탄소의 붕산 처리는 활성탄소의 비 정전용량을 효과적으로 증가시킬 수 있다고 사료된다.