• Textile Coloration and Finishing
• /
• v.31 no.2
• /
• pp.88-97
• /
• 2019

In this study, when printed on a nylon material, the color strength and fastness are lower than that of a polyester material, and the nylon material shrinks due to heat and pressure, resulting in poor design and poor compatibility. To overcome this problem, we investigated the possibility of transfer DTP by adding pre-treatment process to nylon transfer DTP process. For the basic study of pre-treatment preparation, we used pure nylon material which is not compounded and dispersion ink and transfer paper applied to existing PET transfer DTP. Pre-treatment preparations were classified into three types of acryl-base polymer and pre-treated with nylon and then applied to transfer DTP to confirm their color strength and fastness. The color strength of the pre-treated nylon material increased and poly-methyl-acrylate amulsion pre-treatment showed the best color at $210^{\circ}C$, 1.5m/min and 0.3MPa. The nylon material pre-treated with washing, friction, and light fastness was judged to be more excellent and stable.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.122-130
• /
• 2017

In the direct digital textile printing process, the pre-treatment process is an essential condition for products by forming a clear pattern by sticking and penetration of DTP dye without spreading on the fabric. Recently, pre-treatment agent is changing from high viscosity to low viscosity in order to reduce defects of fabric during pre-treatment process. In this study, pre-treatment agent of acrylic polymer with low viscosity(less than 50cps) was prepared according to the solid content of the polymer, pre-treated on the cotton fabric, and direct DTP printing was performed to compare the color and sharpness. As a result, it showed high color at a viscosity of 50cps or less. When the solid content of the polyacrylic acid having a high molecular weight(A1) was 2.5wt%, when the solid content of the polyacrylic acid having a low molecular weight(A2) was 1 - 1.5wt%, the color was the best. And when the solid content of A1 and A2 was 1.5wt%, the degree of spreading was small and A1 was superior to A2 at the sharpness.