• Journal of Conservation Science
• /
• v.34 no.6
• /
• pp.459-470
• /
• 2018

Cellulose nitrates were used for folklore artifacts(ornamental beads and pipes in hatstrings, frames of eyeglasses, ornamental eyeglass cases, headband ornaments, and jeogori buttons) between the 19th and 20th centuries; however, they are susceptible to cracking, crazing, embrittlement, and crumbling due to deterioration. To consolidate and adhere deteriorated cellulose nitrate folklore artifacts, water-soluble acrylic emulsion adhesives were investigated. For consolidation, Plextol D 498, which has the lowest viscosity in low concentrations, was used. In adhesive films whose glass transition temperature(Tg) is lower than room temperature, the tensile stress and modulus decreased and the strain increased; therefore, the flexibility was high. The Plextol D 498 and Plextol D 498 and Dispersion K 52 films maintained their adhesiveness and flexibility after artificial-sunlight-accelerated ageing, and Plextol D 498 and Dispersion K 52 films hardly caused yellowing. Plextol D 498 was the most stable for accelerating ageing. A low concentration of Plextol D 498 emulsion resulted in the best permeability on the surface of cellulose nitrate, compared with other acrylic emulsions. To prevent ornamental hatstrings from cracking, crazing, embrittlement, and crumbling, a Plextol D 498 emulsion was used. After applying low concentrations(1%, 3%) of the emulsion to consolidate the fragments and high concentration to adhere the fragments, the ornamental hatstrings were protected from crumbling by deterioration, and their fragments were well-adhered. To preserve it from deterioration by oxygen and humidity, the treated ornament was sealed with an oxygen-barrier film using a low-humidity oxygen scavenger.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1970-1971
• /
• 2007

The efficiency of such work highly depend on the worker's safety, who is protected by tools such as gloves, sleeves, blankets and flexible coverings among other manufactured natural-rubber goods. Use, storage and maintenance of these tools guarantee the quality and durability of the material. However, it might be observed that good tools made of such material are disapproved of when received from manufacturers or when they are removed from the warehouse for replacement. This work shows the experimental results obtained from ageing at a temperature of $100^{\circ}C$ for 48, 70 and 312 h, although the application of AC electrical tension in samples and the measuring of current leakage are presented. The measurements in samples were carried out with samples prepared from the deformulated commercial materials and respectively reformulated into thin films. The obtained results showed the mechanisms of conduction of samples in low and high electric fields. It was also identified an electric tension transition showing that in low fields it prevails the Ohm's law conduction, and in high electric fields it prevails the conduction of space charge limited current (SCLC). These results can support the natural rubber formulation process having as their main objective the reducing of the mechanisms that occur under high conduction current in high electric fields, which leads the material to a dielectric breakdown. It is necessary to research this raw material from different internationally standard clones to characterize dielectric and electric properties for industrial applications. Moreover, this natural material has a low commercial price when compared to the synthetic ones.