• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.14-16
• /
• 1995

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ co-ramic thin films were formed by spin coating method on Pt/$SiO_2$/Si substrate at 4000[rpm] for 30 [sec]. Coated specimens were dried on the hot-plate at 400[$^{\circ}C$] for 10[min]. The coating process was repeated 6 times and then sintered at temperature between 500 ~ 800[$^{\circ}C$] for 1 hour. The ferroelectric perovskite phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ thin film sintered at 700[$^{\circ}C$] for 1hour showed good dielectric constant (2133) and dielectric loss (2.2[%]) Properties. The switching voltage, switching time and leakage currents density were 3.0[V], 1.7[${\mu}$sec] , 160[pA/$\textrm{cm}^2$] repectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.168-170
• /
• 1994

Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were formed by spin coating method on Pt/$SiO_2$Si substrate at 4000ppm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500∼800[$^{\circ}C$] for 1 hour. The final thickness of the thin films were about 4800[A]. The ferroelectric perovskite phases precipitated under the heat-treated at 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ thin films heat-treated at 700[$^{\circ}C$] for 1 hour showed good dielectric and ferroclectric properties.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1454-1456
• /
• 1994

$Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were formed by spin coating method on $Pt/SiO_2/Si$ substrate at 3000rpm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500 - $800[^{\circ}C]$ for 1 hour. The final thickness of the thin films were about 4800[A]. The 100% ferroelectric perovskite phases precipitated under the heat treated at $700[^{\circ}C]$ for 1 hour. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films heat-treated at $700[^{\circ}C]$ for 1 hour showed good dielectric constant (812) property.

• Nuclear Engineering and Technology
• /
• v.52 no.10
• /
• pp.2299-2305
• /
• 2020

Zr alloy specimens were coated with Cr-Al alloy to enhance their resistance to oxidation. The coated samples were oxidized at 1200 ℃ in a steam environment for 300 s and showed extremely low oxidation when compared to uncoated Zr alloy specimens. The microstructure and elemental distribution of the oxides formed on the surface of Cr-Al alloys have been investigated by transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). A very thin protective layer of Cr₂O₃ formed on the outer surface of the Cr-Al alloy, and a thin Al₂O₃ layer was also observed in the Cr-Al alloy matrix, near the surface. Our results suggest that these two oxide layers near the surface confers excellent oxidation resistance to the Cr-Al alloy. Even after exposure to a high temperature of 1200 ℃, inter-diffusion between the Cr-Al alloy and the Zr alloy occurred in very few regions near the interface. Analysis of the inter-diffusion layer by high-resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray spectroscopy (EDS) measurement confirmed its identity as Cr₂Zr.

• Nuclear Engineering and Technology
• /
• v.55 no.9
• /
• pp.3260-3267
• /
• 2023

Zr-Nb alloy have been widely used as fuel rods in nuclear power plants. However, from the Fukushima nuclear accident, the weakness of the rod was revealed under harsh conditions, and research on the safety of these types of rods was conducted after the disaster. The method of depositing chromium onto the existing Zr-Nb alloy fuel rods is being considered as a means by which to compensate for the weakness of Zr-Nb alloy rods because chromium is strong against oxidation at high temperatures and has high strength. In order to secure these advantages, it is important to maintain the Cr thickness of the rods and properly inspect the rods before and during their use in power generation. Eddy current testing is a typical means of evaluating the thickness of thin metals and detecting surface defects. Depending on the size and shape of the inspected object, various eddy current sensors can be applied. In particular, because pancake sensors can be manufactured in very small sizes, they can be used for inspections even in narrow spaces, such as a nuclear fuel assembly. In this study, an eddy current technique was developed to confirm the feasibility of Cr coating thickness evaluations. After determining the design parameters of the pancake sensor by means of a FEM simulation, a FPCB pancake sensor was manufactured and the optimal frequency was selected by measuring minute changes in the Cr-coating thickness using the developed sensor.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.2
• /
• pp.210-225
• /
• 2004

Statement of problem: Implant screw loosening has been remained problem in restorative practices. Surface treatment of screw plays a role of preventing screw from loosening in implant screw mechanism. Purpose : The purpose of this study was to investigate surface characteristics of TiN and ZrN film ion plated screw with titanium and gold alloy screw and to evaluate wear resistance, surface roughness, and film adhesion on screw surface using various instruments. Material and methods : GoldTite screws and titanium screws provided by 3i (Implant Innovation, USA) and TorqTite screws or titanium screws by Steri-Oss (Nobel Biocare, USA) and gold screws and titanium screws by AVANA (Osstem Implant, korea) were selected. Ion plating which is much superior to other surface modification techniques was carried out for gold screws and titanium screws using Ti and Zr coating materials with nitrogen gas. Ion nitrided surface of each abutment screw was observed with field emission scanning electron microscopy (FE-SEM, micro-diamond scratch tester, vickers hardness tester, and surface roughness tester. Results : 1) The surface of gold screw and GoldTite is more smooth than ones of other kinds of non coated screw. 2) The ZrN and TiN coated surface is the more smooth than ones of other kinds of screw. 3) The hardness of TiN and ZrN coated surface showed higher than that of non coated surface. 4) The TiN coated titanium screw and ZrN coated gold screw have a good wear resistance and adhesion on the surface. 5) The surface of ZrN coated screw showed low surface roughness compared with the surface of TiN coated screw. Conclusion : It is considered that the TiN and ZrN coated screw which would prevent a screw from loosening can be applicable to implant system and confirmed that TiN and ZrN film act as lubricant on surface of screw due to decrease of friction for recycled tightening and loosening.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.5
• /
• pp.232-239
• /
• 2008

The dental orthodontic mini-screw requires good mechanical properties and high corrosion resistance for implantation in the bone. The purpose of this study was to investigate the electrochemical characteristics of TiN and ZrN coated orthodontic mini-screws, mini-screws were used for experiment. Ion plating was carried out for mini-screw using Ti and Zr coating materials with nitrogen gas. Ion plated surface of each specimen w as o bserved with f ield emission scanning e lectron microscopy ( FE-SEM), e nergy dispersive x-ray spectroscopy (EDX), and electrochemical tester. The surface of TiN and ZrN coated mini-screw were more smooth than that of other kinds of non-coated mini-screw due to dercrease of machined defects. The corrosion current density of the TiN and ZrN coated mini-screw decreased compared to non-coated sample. The corrosion potential of TiN and ZrN coated mini-screw were higher than that of non-coated mini-screw in 0.9% NaCl solution. The pitting corrosion resistance increased in the order of ZrN coated, TiN coated and non-coated wire. Pitting potential of ZrN coated mini-screw was the highest in the other specimens.

• Korean Journal of Crystallography
• /
• v.14 no.2
• /
• pp.67-72
• /
• 2003

Graphite powders were coated with ZrO₂ by the controlled hydrolysis of a DI water, ethanol and DI water+ethanol solutions. The hydrolysis process was carried out with temperature control because of the low wettability of Zr ions to the surface of the graphite. PVA was added to the solution for the enhancement of metal ion adsorption. The surface of the graphite powders coated with ZrO₂ was observed by SEM and TEM. There are two types of ZrO₂ particles with the condition of ZrOCl₂°§8H₂O aqueous solutions were used; (a) primary particles a few nm in size and (b) secondary particles with ∼0.1 ㎛ size were obtained. The graphite powders coated in 50% ethanol-50% DI water solution of Zr(SO₄)₂ㆍ4H₂O have the relatively uniform coating layer and the starting temperature of oxidation was 100℃ higher than the raw graphite.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.213-213
• /
• 2012

In this study, effect of EB-PVD coated Si/HA film thickness on surface characteristics of Ti-35Nb-10Zr alloy was investigated. The Ti-35Nb-10Zr alloy was fabricated by arc melting method. The Si/HA layers were coated with 0.8 wt.% of Si in pure HA by EB-PVD method. The coating thickness was consisted with 100 - 300 nm for each group, the surface characteristics was analyzed by FE-SEM, EDS, XRD, XRF and corrosion test. The Si/HA coating layer was well deposited on the alloy surface by EB-PVD, the thickness was correlative factor with HA peaks and corrosion resistance value.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.35-36
• /
• 2006

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the Pb($Zr_xTi_{1-x}$)$O_3$(PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were PZT(70/30) and PZT(30/70), respectively. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 15M, 6-time coated showed the 698. The remanent polarization of the 1.5M, 6-time coated PZT thick films was 38.3 ${\mu}C/cm^2$.