• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.134-137
• /
• 2009

Commercially available elemental powders of Cu, Zn, Sn and Se were employed for crystallizing a stannite-type $Cu_2ZnSnSe_4$ compound by means of solid state reaction. $Cu_2ZnSnSe_4$ reaction chemistry was also modeled based on differential-thermal analysis and X-ray powder diffraction results. It was observed that Se tends to react preferably with Cu to form CuSe and $CuSe_2$ phases at low reaction temperature. The formation of $Cu_5Zn_8$ intermetallic phase was found to be the intermediate reaction path for the binary ZnSe formation. A solid state reaction at $320^{\circ}C$ reacted elemental powderst obinary selenides of CuSe, ZnSe and SnSe completely. The crystallization of $Cu_2ZnSnSe_4$ was was detected to begin at $300^{\circ}C$ and its weight fraction increased with an increase of reaction temperature, which most probably formed from the reaction between $Cu_2SnSe_3$ and ZnSe.

• Bulletin of the Korean Chemical Society
• /
• 제35권12호
• /
• pp.3601-3608
• /
• 2014

RGB light emitting ZnSe based nanocrystals: ZnSe (blue), ZnSe:Cu (green) and ZnSe:Mn (red) were synthesized by capping the surface of the nanocrystals with oleic acid. The obtained nanocrystal powders were characterized by using XRD, HR-TEM, ICP-AES, FT-IR, and FT-Raman spectroscopies. The optical properties were also measured by UV/Vis and photoluminescence (PL) spectroscopies. The PL spectra showed broad emission peaks at 471 nm (ZnSe), 530 nm (ZnSe:Cu) and 665 nm (ZnSe:Mn), with relative PL efficiencies in the range of 0.7% to 5.1% compared to a reference organic dye standard. The measured average particle sizes from the HR-TEM images for those three nanocrystals were 4.5 nm on average, which were also supported well by the Debye-Scherrer calculations. The elemental compositions of the ZnSe based nanocrystals were determined by ICP-AES analyses. Finally, the drawn CIE diagram showed the color coordinates of (0.15, 0.16) for ZnSe, (0.22, 0.57) for ZnSe:Cu, and (0.62, 0.35) for ZnSe:Mn respectively, which were fairly well matched to that of the RGB color standards.

• 한국재료학회지
• /
• 제23권3호
• /
• pp.183-189
• /
• 2013

$Cu_2ZnSn(S,Se)_4$ material is receiving an increased amount of attention for solar cell applications as an absorber layer because it consists of inexpensive and abundant materials (Zn and Sn) instead of the expensive and rare materials (In and Ga) in $Cu(In,Ga)Se_2$ solar cells. We were able to achieve a cell conversion efficiency to 4.7% by the selenization of a stacked metal precursor with the Cu/(Zn + Sn)/Mo/glass structure. However, the selenization of the metal precursor results in large voids at the absorber/Mo interface because metals diffuse out through the top CZTSe layer. To avoid the voids at the absorber/Mo interface, binary selenide compounds of ZnSe and $SnSe_2$ were employed as a precursor instead of Zn and Sn metals. It was found that the precursor with Cu/$SnSe_2$/ZnSe stack provided a uniform film with larger grains compared to that with $Cu_2Se/SnSe_2$/ZnSe stack. Also, voids were not observed at the $Cu_2ZnSnSe_4$/Mo interface. A severe loss of Sn was observed after a high-temperature annealing process, suggesting that selenization in this case should be performed in a closed system with a uniform temperature in a $SnSe_2$ environment. However, in the experiments, Cu top-layer stack had more of an effect on reducing Sn loss compared to $Cu_2Se$ top-layer stack.

• Applied Microscopy
• /
• 제27권3호
• /
• pp.235-241
• /
• 1997

(001) GaAs 기판 위에 성장된 (ZnSe/FeSe) 초격자의 구성층 사이에 상호확산으로 형성된 $Zn_{1-x}Fe_xSe$ 의 미세구조가 고분해능 투과전자현미경과 컴퓨터 이미지 시뮬레이션에 의해 연구되었다. 컴퓨터 이미지 시뮬레이션은 multislice 방법으로 여러 시편 두께와 초점 거리에서 실시되었다. 컴퓨터 시뮬레이션에 의해 얻은 이미지는 실험에 의해 얻은 이미지와 비교되었다. 또한, CuAu-I 형태 규칙화가 $Zn_{1-x}Fe_xSe$ 상호화산층에서 일어났다. 이 CuAu-I 형태 규칙격자는 <100>과 <110> 방향에 따라서 ZnSe와 FeSe 층이 교대로 구성되어 있다.

• 신재생에너지
• /
• 제3권4호
• /
• pp.54-62
• /
• 2007

In this paper, we report the research highlight on the preparation and characterization of Indium-free $Cu_2ZnSnSe_4$ and Indium-reduced $CulnZnSe_2$ thin films in order to seek the viability of these absorber materials to be applied in thin film solar cells. The films of $Cu_2ZnSnSe_4\;and\;CulnZnSe_2$ were prepared using mixed binary chalcogenides powders. It was observed that Cu concentration was a function of substrate temperature as well as CuSe mole ratio in the target. Under an optimized condition, $Cu_2ZnSnSe_4\;and\;CulnZnSe_2$ thin films grew with strong [112]. [220/204] and [312/116] reflections. Both $Cu_2ZnSnSe_4\;and\;CulnZnSe_2$ films were found to exhibit a high absorption coefficient of $104^4cm^{-1}\;Cu_2ZnSnSe_4$ film showed a band gap of 1.5eV which closes to the optimum band gap of an ideal solar absorber for a solar cell. On the other side, an increase of optical band gap from 1.0 to 1.25eV was found to be proportional with an increase of Zn concentration in the $CulnZnSe_2$ film. All films in this study revealed a p-type semiconductor characteristic.

• 한국분말재료학회지
• /
• 제29권5호
• /
• pp.370-375
• /
• 2022

Cu-doped ZnSe quantum dots were successfully synthesized in an aqueous solution using an internal doping method. The effects of ligand type, CuSe synthesis temperature, and heating time on Cu-doped ZnSe synthesis were systematically investigated. Of MPA, GSH, TGA, and NAC used as ligands, MPA was the optimal ligand as determined by PL spectrum analysis. In addition, the emission wavelength was found to depend on the synthesis temperature of the internal doping core of CuSe. As the temperature increased, the doping of Cu²⁺ was enhanced, and the emission wavelength band was redshifted; accordingly, the emission peaks moved from blue to green (up to 550 nm). Thus, the synthesis of Cu:ZnSe using internal doping in aqueous solutions is a potential method for ecomanufacturing of color-tuned ZnSe quantum dots for display applications.

• Bulletin of the Korean Chemical Society
• /
• 제35권8호
• /
• pp.2331-2334
• /
• 2014

$Cu_2SnSe_3$ (CTSe) and $Cu_2ZnSnSe_4$ (CZTSe) nanoparticles were synthesized by sonochemical reactions under multibubble sonoluminescence (MBSL) conditions. First, $Cu_2SnSe_3$ nanoparticles were synthesized by the sonochemical method with an 85% yield, using CuCl, $SnCl_2$, and Se. Second, ZnSe was coated on the CTSe nanoparticles by the same method. Then, they were transformed into CZTSe nanoparticles of 5-7 nm diameters by heating them at $500^{\circ}C$ for 1 h. The ratios between Zn and Sn could be controlled from 1 to 3.75 by adjusting the relative concentrations of CTSe and ZnSe. With relatively lower Zn:Sn ratios (0.75-1.26), there are mostly CZTSe nanoparticles but they are believed to include very small amount of CTS and ZnSe particles. The prepared nanoparticles show different band gaps from 1.36 to 1.47 eV depending on the Zn/Sn ratios. In this sonochemical method without using any toxic or high temperature solvents, the specific stoichiometric element Zn/Sn ratios in CZTSe were controllable on demand and their experimental results were always reproducible in separate syntheses. The CZTSe nanoparticles were investigated by using X-ray diffractometer, a UV-Vis spectrophotometer, scanning electron microscope, Raman spectroscopy, and a high resolution-transmission electron microscope.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2007년도 추계학술대회 논문집
• /
• pp.270-273
• /
• 2007

In this report, Indium-free and Indium-reduced thin film materials for solar absorber were studied in order to search alternative materials for thin film solar cell. The films of $Cu_2ZnSnSe_4$ and $Cu_2ZnSnSe_2$ were deposited using mixed binary chalcogenides powders. From the film bulk analysis result, it is observed that Cu concentration is a function of substrate temperature as well as CuSe mole ratio in the target. Under optimized conditions, $Cu_2ZnSnSe_4$ and $Cu_2ZnSnSe_2$ thin films grow with strong (112), (220/204) and (312/116) reflections. Films are found to exhibit a high absorption coefficient of $10^4$ $cm^{-1}$. $Cu_2ZnSnSe_4$ film shows a 1.5 eV band gap. On the other side, an increasing of optical band gap from 1.0 eV to 1.25 eV ($CuInSnSe_2$) is found to be proportional with an increasing of Zn concentration. All films have a p-type semiconductor characteristic with a carrier concentration in the order of $10^{14}$ $cm^{-3}$, a mobility about $10^1$ $cm^{2{\cdot}-1.}S^{-1}$ and a resistivity at the range of $10^2-10^6$ ${\Omega}{\cdot}m$.

• Bulletin of the Korean Chemical Society
• /
• 제16권7호
• /
• pp.588-591
• /
• 1995

Single crystals of (ZnSe)1-x(CuMSe2)x (M=Al, Ga, or In) were grown by chemical vapor transport technique. Powdered polycrystalline samples of (ZnSe)1-x(CuMSe2)x (M=Al, Ga, or In) were also prepared by the direct combination of the elements. The chemical composition of these single crystals was determined by comparing their lattice parameters with those of the standard polycrystalline samples. The IR transmission range of single crystals of (ZnSe)1-x(CuMSe2)x (M=Al, Ga, or In) is slightly narrower than that observed for pure ZnSe. However, these materials still show good transmission in the long-wavelength IR range. The addition of small amounts of CuMSe2 (M=Al, Ga, or In) considerably increases the hardness of ZnSe.

• Current Photovoltaic Research
• /
• 제10권2호
• /
• pp.39-48
• /
• 2022

A Se-containing Cu/SnSe₂/ZnSe precursor was employed to introduce S to the precursor to form Cu₂ZnSn(S,Se)₄ (CZTSSe) film. The morphology of CZTSSe films strongly varied with two different pre-annealing environments: S and N₂. The CZTSSe film with S pre-annealing showed a dense morphology with a smooth surface, while that with N₂ pre-annealing showed a porous film with a plate-shaped grains on the surface. CuS and Cu₂Sn(S,Se)₃ phases formed during the S pre-annealing stage, while SnSe and Cu₂SnSe₃ phases formed during the N₂ pre-annealing stage. The SnSe phase formed during N₂ pre-annealing generated SnS₂ phase that had plate shape and severely aggravated the morphology of CZTSSe film. The power conversion efficiency of the CZTSSe solar cell with S pre-annealing was low (1.9%) due to existence of Zn(S.Se) layer between CZTSSe and Mo substrate. The results indicated that S pre-annealing of the precursor was a promising method to achieve a good morphology for large area application.