• 한국재료학회지
• /
• 제22권12호
• /
• pp.664-668
• /
• 2012

ZnO nanorods were successfully fabricated on Zn foil by chemical bath deposition (CBD) method. The ZnO precursor concentration and immersion time affected the surface morphologies, structure, and electrical properties of the ZnO nanorods. As the precursor concentration increased, the diameter of the ZnO nanorods increased from ca. 50 nm to ca. 150 nm. The thicknesses of the ZnO nanorods were from ca. $1.98{\mu}m$ to ca. $2.08{\mu}m$. ZnO crystalline phases of (100), (002), and (101) planes of hexagonal wurtzite structure were confirmed by XRD measurement. The fabricated ZnO nanorods showed a photoluminescene property at 380 nm. Especially, the ZnO nanorods deposited for 6 h in solution with a concentration of 0.005M showed a stronger (101) peak than they did (100) or (002) peaks. In addition, these ZnO nanorods showed a good electrical property, with the lowest resistance among the four samples, because the nanorods were densely in contact and relatively without pores. Therefore, a ZnO nanorod substrate is useful as a highly sensitive biochip substrate to detect biomolecules using an electrochemical method.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.184-185
• /
• 2006

Two-step growth to incorporate the Mg atoms in the ZnO nanorods fabricate by thermal evaporation process and also utilized the ZnO film as a template. In the first step of low temperature, Zn seed metals with low melting temperature formed the droplet, and then MgZnO ternary nanorods were grown by injecting oxygen and evaporating Mg atoms in high temperature process of the second step. The vertical growth of the MgZnO nanorods with large-area distribution and uniformity was successfully performed on the ZnO template. We investigated the shape of the vertically grown 1-D MgZnO nanorods and characterized the optical and crystal properties. We confirmed the incorporation of Mg atoms by the EDS and PL spectrum.

• Transactions on Electrical and Electronic Materials
• /
• 제13권6호
• /
• pp.305-309
• /
• 2012

In this study, ZnO nanorods and $SnO_2$-CuO heterogeneous oxide were grown on membrane-type gas sensor platforms and the sensing characteristics for carbon monoxide (CO) were studied. Diaphragm-type gas sensor platforms with built-in Pt micro-heaters were made using a conventional bulk micromachining method. ZnO nanorods were grown from ZnO seed layers using the hydrothermal method, and the average diameter and length of the nanorods were adjusted by changing the concentration of the precursor. Thereafter, $SnO_2$-CuO heterogeneous oxide thin films were grown from evaporated Sn and Cu thin films. The average diameters of the ZnO nanorods obtained by changing the concentration of the precursor were between 30 and 200 nm and the ZnO nanorods showed a sensitivity value of 21% at a working temperature of $350^{\circ}C$ and a carbon monoxide concentration of 100 ppm. The $SnO_2$-CuO heterogeneous oxide thin films showed a sensitivity value of 18% at a working temperature of $200^{\circ}C$ and a carbon monoxide concentration of 100 ppm.

• 한국전기전자재료학회논문지
• /
• 제23권3호
• /
• pp.222-227
• /
• 2010

ZnO nanorods array have been grown on the seed crystal coated Si(100) substrate by hydrothermal method. The growth, structural and optical properties of ZnO nanorods array were investigated with a variation of precursor concentration from 0.01 M to 0.04 M. The array density of grown ZnO nanorods per same area was increased with increasing the concentration of precursor solution. Vertically aligned ZnO nanorods with hexagonal wurtzite structure have highly preferred c-axis orientation along (002) lattice plane. Especially, ZnO nanorods array developed from 0.04 M precursor solution showed a diameter of about 85 nm and length of 1.2 {\mu}m$ without any crystallographic defects. The photoluminescence spectra of ZnO nanorods from heavier precursor concentration exhibited stronger UV emission around 380 nm corresponding with near-band-edge emission.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.232-235
• /
• 2011

ZnO nanorods for gas sensors were prepared by a hydrothermal method. The ZnO gas sensors were fabricated on alumina substrates by a screen printing method. The gas-sensing properties of the ZnO nanorods were investigated for $CH_4$ gas. The effects of growth time on the structural and morphological properties of the ZnO nanorods were investigated by X-ray diffraction and scanning electron microscope. The XRD patterns of the nanocrystallized ZnO nanorods showed a wurtzite structure with the (002) predominant orientation. The diameter and length of the ZnO nanorods increased in proportion to the growth time. The sensitivity of the ZnO sensors to 5 ppm $CH_4$ gas was investigated for various growth times. The ZnO sensors exhibited good sensitivity and rapid response-recovery characteristics to $CH_4$ gas, and both traits were dependent on the growth time. The highest sensitivity of the ZnO sensors to $CH_4$ gas was observed with the growth time of 7 h. The response and recovery times were 13 s and 6 s, respectively.

• 한국재료학회지
• /
• 제30권8호
• /
• pp.399-405
• /
• 2020

In the present investigation we show the effect of Al doping on the length, size, shape, morphology, and sensing property of ZnO nanorods. Effect of Al doping ultimately leads to tuning of electrical and optical properties of ZnO nanorods. Undoped and Al-doped well aligned ZnO nanorods are grown on sputtered ZnO/SiO₂/Si (100) pre-grown seed layer substrates by hydrothermal method. The molar ratio of dopant (aluminium nitrate) in the solution, [Al/Zn], is varied from 0.1 % to 3 %. To extract structural and microstructural information we employ field emission scanning electron microscopy and X-ray diffraction techniques. The prepared ZnO nanorods show preferred orientation of ZnO <0001> and are well aligned vertically. The effects of Al doping on the electrical and optical properties are observed by Hall measurement and photoluminescence spectroscopy, respectively, at room temperature. We observe that the diameter and resistivity of the nanorods reach their lowest levels, the carrier concentration becomes high, and emission peak tends to approach the band edge emission of ZnO around 0.5% of Al doping. Sensing behavior of the grown ZnO nanorod samples is tested for H₂ gas. The 0.5 mol% Al-doped sample shows highest sensitivity values of ~ 60 % at 250 ℃ and ~ 50 % at 220 ℃.

• Bulletin of the Korean Chemical Society
• /
• 제32권3호
• /
• pp.880-884
• /
• 2011

ZnO nanorods were grown by hydrothermal method. Two kinds of seed layers, Au film and island seed layers were prepared to investigate the effect of seed layer on ZnO nanorods. The ZnO nanorod on Au island seed layer has more unifom diameter and higher density compared to that of ZnO nanorod on Au film seed layer. The ZnO nanorods on Au island seed layer were annealed at various temperatures ranging from 300 to $850^{\circ}C$. The pinholes at the surface of the ZnO nanorods is formed as the annealing temperature is increased. It is noted that the pyramid structure on the surface of ZnO nanorod is observed at $850^{\circ}C$. The intensity of ZnO (002) diffraction peak in X-ray diffraction pattern and intensity of near band edge emission (NBE) peak in photoluminescence (PL) are increased as the ZnO nanorods were annealed at the temperature of $300^{\circ}C$.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.190-190
• /
• 2010

Zinc oxide is the most attractive material due to the large direct band gap (3.37 eV), excellent chemical and thermal stability, and large exciton binding energy (60 meV). Recently, ZnO nanorods were used as the high efficient antireflection coating layer of solar cells based on silicon (Si). In this reports, we studied the effects of rapid thermal annealing (RTA) treatment on optical properties of ZnO nanorods. For fabrication of ZnO nanorods, there are many methods such as hydrothermal method, sol-gel method, and metal organic chemical vapor deposition method. Among of them, we used the conventional wet chemical method which is simple and low temperature growth. In order to synthesize the ZnO nanorods, the ZnO films were deposited on Si substrate by RF magnetron sputtering at room temperature and the samples were dipped to aqua solution containing the zinc nitrate and hexamethylentetramines (HMT). The synthesis process was achieved in keeping with temperature of $90-95^{\circ}C$ and under constant stirring. The morphology of ZnO nanorods on glass and Si was characterized by scanning electron microscopy. For the analysis of antireflection performance, the reflectance and transmittance were measured by spectrophotometer. And for analyzing the effects of RTA treatment on ZnO nanorods, crystalline properties were investigated by X-ray diffraction measurements and optical properties was estimated by photoluminescence spectra.

• 한국재료학회지
• /
• 제13권10호
• /
• pp.668-672
• /
• 2003

The ZnO nanorods were synthesized using vapor-solid (VS) method on sodalime glass substrate without the presence of metal catalyst. ZnO nanorods were prepared thermal evaporation of Zn powder at $500^{\circ}C$. As-fabricated ZnO nanorods had an average diameter and length of 85 nm and 1.7 $\mu\textrm{m}$. Transmission electron microscopy revealed that the ZnO nanorods were single crystalline with the growth direction perpendicular to the (101) lattice plane. The influences of reaction time on the formation of the ZnO nanorods were investigated. The photoluminescence measurements showed that the ZnO nanorods had a strong ultraviolet emission at around 380 nm and a green emission at around 500 nm.

• 한국초전도ㆍ저온공학회논문지
• /
• 제11권4호
• /
• pp.16-19
• /
• 2009

The influence of nanorods grown on substrate prior to YBCO deposition has been investigated. We studied the microstructures and characteristic of $YBa_2Cu_3O_{7-\delta}$ films fabricated on $SrTiO_3$ (100) substrates with ZnO nanorods as one of the possible pinning centers. The growth density of ZnO nanorods was modulated through Au nanoparticles synthesized on top of the STO(100) substrates with self assembled monolayer. The density of Au nanoparticles is approximately $240{\sim}260\;{\mu}m^{-2}$ with diameters of 41~49 nm. ZnO nanorods were grown on Au nanoparticles by hot-walled PLD with Au nanoparticles. Typical size of ZnO nanorod was around 179 nm in diameter and $2{\sim}6\;{\mu}m$ in length respectively. The ZnO nanorods have apparently randomly aligned and exhibit single-crystal nature along (0002) growth direction. Our preliminary results indicate that YBCO film deposited directly on STO substrate shows the c-axis orientation while YBCO films with ZnO nanorods exhibit any mixed phases without any typical crystal orientation.