• Journal of the Semiconductor & Display Technology
• /
• v.16 no.2
• /
• pp.27-31
• /
• 2017

AZO/Ag/AZO multi-layer films deposited on glass substrate by RF magnetron sputtering and thermal evaporator have a much better electrical properties than Al-doped ZnO thin films. The multi-layer structure consisted of three layers, AZO/Ag/AZO, the electrical and optical properties of AZO/Ag/AZO were changed mainly by thickness of Ag layers. The optimum thickness of Ag layers was determined to be $90{\AA}$ for high optical transmittance and good electrical conductivity. The Ag layers thickness $90{\AA}$ is an optical transmittance greater than 80% of visible light and the obtained multilayer thin film with the low resistivity of $8.05{\times}10-3{\Omega}cm$ and the low sheet resistance $5.331{\Omega}/sq$. Applying to TCO and Solar electrode will improve efficiency.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.1
• /
• pp.95-98
• /
• 2013

The photoluminescence (PT) properties of Al-doped ZnO thin films grown by the sol-gel dip-coating method have been investigated. At 12 K, nine distinct PL peaks were observed at 2.037, 2.592, 2.832, 3.027, 3.177, 3.216, 3.260, 3.303, and 3.354 eV. The deep-level emissions (2.037, 2.592, 2.832, and 3.027 eV) were attributed to native defects. The near-band-edge (NBE) emission peaks at 3.354, 3.303, 3.260, 3.216, and 3.177 eV were attributed to the emission of the neutral-donor-bound excitons ($D^0X$), two-electron satellite (TES), free-to-neutral-acceptors (e,$A^0$), donor-acceptor pairs (DAP), and second-order longitudinal optical (2LO) phonon replicas of the TES (TES-2LO), respectively. According to Haynes' empirical rule, we calculated the energy of a free exciton (FX) to be 3.374 eV. The thermal activation energy for $D^0X$ in the nanocrystalline ZnO thin film was found to be ~25 meV, corresponding to the thermal dissociation energy required for $D^0X$ transitions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.10-10
• /
• 2009

Transparent BNO thin films were grown on Al-doped ZnO (AZO)/Ag/AZO/polyethersulfon (PES) (abbreviated as AAAP) transparent electrodes at a low temperature by the NCD technique. The BNO films grown on the crystallized AZO/Ag/AZO (AAA) electrodes exhibit an amorphous phase with a root mean square (rms) roughness of approximately 2 nm in the range of deposition temperature. The capacitors (Pt/BNO/AAAP) with BNO films grown at $100^{\circ}C$ show a dielectric constant of 24 and dissipation factor of 8% at 100 kHz, a leakage current density of about $8{\times}10^{-6}A/cm^2$ at an applied voltage of 1.0V. The optical transmittances of the BNO/AAAP exhibited above 80% at wavelength of 550nm at all of deposition temperature. The mechanical stability of the BNO/AAA as well as AAA electrode with the PES substrates through the bending was ensured for flexible electronic device applications. The transparent BNO capacitors grown on AAAP are powerful candidate for integration with the transparent solar cells.

• Proceedings of the KIEE Conference
• /
• 2007.11a
• /
• pp.108-109
• /
• 2007

Microstructure and electrical properties of Ga-doped ZnO (GZO) films grown on $Al_2O_3$ templates by Pulsed Laser Deposition (PLD) are investigated utilizing X-ray diffraction method and Hall measurement, respectively. In order to determine the optimized operating condition of the PLD, statistical design of experiment (DOE) is employed. It provides the systematic and efficient methodology for characterization and modeling of PLD processing with a relatively small number of experiments. The most optimized recipe of the process factors is obtained by response optimizer in Minitab.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.175-175
• /
• 2010

Transparent conducting oxide (TCO) films are widely used as transparent conducting thin film material for application in various fields such as solar cells, optoelectronic devices, heat mirrors and gas sensors, etc. Recently the increased utilization of many transparent electrodes has accelerated the development of inexpensive TCO materials. Indium tin oxide (ITO) film is well-known for TCO materials because of its low resistivity, but there is disadvantage that it is too expensive. ZnO film is cheaper than ITO but it shows thermally poor stability. On the contrary, antimony-doped tin oxide films (ATO) are more stable than TCO films such as Al-doped zinc oxide (AZO) and ITO. Moreover, SnO2 film shows the best thermal and chemical stability, low cost and mechanical durability except the poor conductivity. However, annealing is proved to improve the conductivity of ATO film. Therefore, in this work, antimony (6 wt%) doped tin oxide films to improve the conductivity were deposited on 7059 corning glass by RF magnetron sputtering method for the application to transparent electrodes. In general, of all TCO films, glass is the most commonly selected substrate. However, for future development in flexible devices, glass is limited by its intrinsic inflexibility. In this study, we report the growth and properties of antimony doped tin oxide (ATO) films deposited on PES flexible substrate by using RF magnetron sputtering. The optimization process was performed varying the sputtering parameters, such as RF power and working pressure, and parameter effect on the structural, electrical and optical properties of the ATO films were investigated.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1859-1861
• /
• 2005

The ZnO:Al thin films were prepared on glass by Facing Target Sputtering (FTS) system. We investigated electrical, optical, and structural properties of AZO thin film with sputtering current $0.1[A]{\sim}0.6[A]$. We obtained the lowest resistivity $2.3{\times}10^{-4}[{\Omega}-cm]$ at sputtering current 0.6[A] from the 4-point probe and the strong (002) peak at sputtering current 0.3[A] from the X-ray Diffractometer (XRD ). The optical transmittance of AZO thin films show a very high transmittance of $80{\sim}95%$ in the visible range and exhibit the absorption edge of about 350nm.

• Electrical & Electronic Materials
• /
• v.8 no.6
• /
• pp.693-698
• /
• 1995

We fabricated Zinc Oxide transparent conductive thin films with 2wt% of A1203 doping using rf magnetron sputtering. And we investigated electrical and optical characteristics of them which were made with conditions ; rf power 60-300W, thickness of film 3000 11000.angs.. Resistivity, carrier concentration and Hall mobility were investigated for electrical characteristics. Transmittance and optical band gap were investigated with Spectrophotometer in the wavelength range between 200-900 nm. As a result, ZnO thin film fabricated with rf power of 180W and thickness of 5000.angs. showed the best properties. At the best condition, the sample has resistivity of 1*10$\^$-4/.ohm.cm and transmittance of 95% in the visible range.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.23-24
• /
• 2008

Bipolar pulsed dc magnetron sputtering을 이용하여 태양전지의 투명 전도막용으로 유리기판 위에 Al doped ZnO (AZO) 박막을 증착하였다. $400{\times}400\;mm$의 대면적 기판에 증착하기 위해서 $5{\times}25$ inch 대형 사각 AZO target (Al 2 wt%)을 사용했고, $50{\sim}250\;kHz$의 bipolar pulse를 인가하였다. 실제로는 $400{\times}400\;mm$ 면적의 기판에 slide glass 16개를 사용했으며, 약 700 nm 두께에서 두께와 투과도, 비저항의 균일도를 평가하였다. Bipolar pulse의 주파수 150 kHz일 때, 가장 우수한 특성을 갖는 AZO가 증착되었으며, $2.13{\times}10^{-3}{\Omega}{\cdot}cm$의 비저항에 가시광선 영역에서 82%의 투과율을 보였다. 또한, $400{\times}400\;mm$ 대면적 기판에서의 두께와 투과도, 비저항의 불균일도는 각각 5%, 1%, 9% 였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.29 no.6
• /
• pp.272-276
• /
• 2016

Al doped ZnO (AZO) single layer and AZO/Ag bi-layered films were deposited on the glass substrates by radio frequency and direct current magnetron sputtering and then the effect of Ag buffer layer on the electrical and optical properties of the films was investigated. The thicknesses of AZO upper layer was kept as 100 nm, while Ag buffer layer was varied from 5 to 15 nm. The observed results mean that opto-electrical properties of the AZO films is influenced with Ag buffer layer and AZO film with 10 nm thick Ag buffer layer show the higher opto-electrical performance than that of the AZO single layer film prepared in this study.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.471-472
• /
• 2008

The properties of Al doped ZnO (AZO) thin flim for solar cells with various input currents were studied in this paper. Using facing target sputtering with 2wt.% AZO targets, TCO films were deposited on glass(corning 2948) substrate at room temperature. AZO thin films were deposited by 0.2A, 0.4A, 0.6A and 0.8A at the thickness of 300nm. Electrical, optical and structural of thin films investigated by a Hall effect measurement (Ecopia), an UV-VIS spectrometer(HP) and a X-ray diffractometer (Rigaku). As a results, all thin films showed transmittance about 80%, respectively and resistivity was $7.67\times10^{-4}\Omega$-cm at 0.6A.