• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제29권5호
• /
• pp.279-283
• /
• 2016

In this study, we intended to achieve both antibacterial properties and electromagnetic shielding using the Al-doped ZnO (AZO) films. FTS (Facial Target Sputtering) magnetron sputtering was used for the AZO thin films instead of the conventional RF sputtering because the FTS sputtering could avoid the damage for the plasma as well as fabrication of thin films with a high quality. The 300-nm thick AZO thin films grown on glass substrate showed a resistivity of about $7{\times}10^{-4}{\Omega}-cm$ and a transmittance of about 90% at a wavelength of 550 nm. AZO thin films were investigated for the electromagnetic shielding effectiveness measured by 2-port network method at 1.5 ~ 3 GHz. The AZO (300 nm)/glass films showed an EMI shielding effectiveness of approximately 27 dB. An antibacterial effect was measured by the film attachment method (JIS Z 2801). The percent reductions of bacteria by AZO films were 99.99668% and 99.99999% against Staphylococcus aureus and Escherichia coli, respectively.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1474-1476
• /
• 2005

ZnO:Al(AZO) has been investigated for the photovoltaic cell or TCO(Transparent Conductive Oxide) of the display, because it has good electrical and optical properties. In this study, the ZnO:Al(AZO) thin film prepared on variation of substrate temperature by FTS(Facing Targets Sputtering) system. In case of TCO, because resistivity and roughness values affect the lighting of the OLED, their factors are very important. Therefore, in this paper, the electrical and optical properties of the AZO thin film were investigated with the deposition conditions and its roughness was investigated on variation of the substrate temperature. In results, AZO thin film deposited with the transmittance over 80% and the resistivity was reduced from $1.36{\times}10^{-3}$ [O-cm] to $4{\times}10^{-4}$ [O-cm] with increasing the substrate temperature from R.T to $200[^{\circ}C]$. Especially, we could obtain the resistivity $4{\times}10^{-4}$ [O-cm] of AZO thin film prepared at working pressure 1[mTorr], input current 0.4[A] and substrate temperature $200[^{\circ}C]$.

• Journal of the Korean Vacuum Society
• /
• 제22권5호
• /
• pp.257-261
• /
• 2013

We have studied structural, optical, and electrical properties of the Al-doped ZnO (AZO) thin films using RF magnetron sputtering with various working pressure. To find optimal properties of AZO for transparent conducting oxides, the working pressure in sputtering process was varied as 0.07 Torr, 0.02 Torr, and 0.007 Torr, respectively. As working pressure increased, the crystallinity of AZO thin film was improved, the surface roughness of AZO thin film decreased. The transmittance of the film was over 80% in the visible light range regardless of the changes in working pressure. In case of 0.007 Torr, best electrical properties was shown due to the reduction of oxygen absorption by decreasing surface roughness.

• Proceedings of the Korean Vacuum Society Conference
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.420-420
• /
• 2012

ZnO seed layer were deposited on quartz substrate by sol-gel method and prism-like Al-doped ZnO nanorods (AZO nanorods) were grown on ZnO seed layer by hydrothermal method with various Al concentration ranging from 0 to 2.0 at.%. Structural and optical properties of the AZO nanorods were investigated by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), photoluminescence (PL). The diameter of the AZO nanorods was smaller than undoped ZnO nanorods and its diameter of the AZO nanorods decreased with increasing Al concentration. In XRD spectrum, it was observed that stress and full width at half maximum (FWHM) of the AZO nanorods decreased and the 'c' lattice constant increased as the Al concentration increased. From undoped ZnO nanorods, it was observed that the green-red emission peak of deep-level emission (DLE) in PL spectra. However, after Al doping, not only a broad green emission peak but also a blue emission peak of DLE were observed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• 제6권4호
• /
• pp.480-492
• /
• 1996

AZO (Aluminum doped Zinc Oxide) transparent conducting thin films were fabricated by reactive DC mangnetron sputtering method using zinc target containing 2 wt% of Al. Transition range with optimum transmittance and conductivity was obtained by contrlling partial pressure of reactive oxygen gas. Sputtering condition for this transition range could be kept stable by regulating the target voltage. According to XRD analysis, there was only one peak for (002) plane in AZO films and the films deposited in transition range.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• 제56권10호
• /
• pp.1782-1785
• /
• 2007

In this paper, the effect of substrate temperature on structural, electrical and optical properties of aluminium-doped zinc oxide (AZO) films were investigated. AZO thin films were prepared on glass substrate by pulsed DC magnetron sputtering technique. The properties of AZO were measured by using XRD, AFM, UV spectrophotometer, and hall effect measurement system. The resistivity of AZO films was improved under the condition of high substrate temperature. The resistivity decreased from $9.95{\times}10^{-2}\;{\Omega}-cm\;to\;1.1{\times}10^{-3}\;{\Omega}-cm$ as a result of high substrate temperature and the average transmittances in visible range were above 80%.

• Journal of Electrical Engineering and Technology
• /
• 제8권1호
• /
• pp.163-167
• /
• 2013

Aluminum doped zinc oxide (AZO) thin films have been prepared on the glass substrates (Corning 1737) by sol-gel dip-coating method employing zinc acetate and aluminum chloride hexahydrate for the transparent conducting oxide (TCO) applications. 1 at% Al was doped to the ZnO thin films. The effects of post-heating temperature on the crystallization, optical and electrical properties of the AZO films have been investigated. Experimental results showed that post-heating temperature affected the microstructure, electrical resistance, and optical transmittance of the AZO films. From the X-ray diffraction analysis, all films have hexagonal wurtzite crystal structure. Optical transmittance spectra of the AZO films exhibited transmittance higher than about 80% within the visible wavelength region and the optical direct band gap ($E_g$) of these films was increased with increasing post-heating temperature. A minimum resistivity of $2.5{\times}10^{-3}{\Omega}cm$ was observed at $650^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• 제32권7호
• /
• pp.799-808
• /
• 1995

Transparent conductive films of aluminium doped zinc oxide (AZO) have been prepared by using the DC magnetron sputtering with the ZnO : Al (Al2O3 2 wt%) oxide target oriented to c-axis. Electrical and optical properties depended upon the O2/Ar gas ratio. The optical transmittance and sheet resistance of the AZO coated glass was 60~65% and 75Ω/$\square$, respectively at the O2/Ar gas ratio of 0. With the increase of the oxygen partial pressure to 2.0$\times$10-2, they were increased to the values of 81% and 1kΩ/$\square$, respectively. The films with the resistivities of 1.2~1.4$\times$10-3 Ω.cm, mobilities of 11~13 $\textrm{cm}^2$/V.sec and carrier concentrations of 3.5$\times$1020~4.0$\times$1020/㎤ were produced at the optimum O2/Ar gas ratio, which was 0.5$\times$10-2~1.0$\times$10-2. According to XRD analysis, the films have only one peak corresponding to the (002) plane, which indicates that there is a strong preferred orientation of the films. The grain size of ZnO films were calculated to 200~320 $\AA$, which was increased with the O2/Ar gas ratio and Ar gas flowrate.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• 제8권4호
• /
• pp.592-598
• /
• 1998

AZO(Aluminum doped Zinc Oxide) thin films were fabricated by reactive DC magnetron sputtering method using zinc metal target (Al 2%) and zinc oxide target ($Al_2O_3\;2%$) respectively. The intermediate condition with optimum transmittance and conductivity was obtained by controlling the sputtering parameters. Oxygen gas ratio for this condition was $0.5{\times}10^{-2}~1.0{\times}10^{-2}$ in oxide target and. In case of metal target, this optimum oxygen gas ratio at the applied power of 0.6 kW and 1.0 kW was 0.215~0.227 and 0.305~0.315, respectively. The resistivity of AZO film deposited was obtained $1.2~1.4{\times}10^{-3} {\Omega}{\cdot}$cm as deposited state regardless of target species.

• Journal of the Korean institute of surface engineering
• /
• 제40권3호
• /
• pp.107-112
• /
• 2007

Aluminum doped zinc oxide (AZO) films were deposited on non-alkali glass substrate by DC magnetron sputtering with 3 types of AZO targets (doped with 1.0 wt%, 2.0 wt%, 3.0 wt% $Al_2O_3$). Electrical, optical properties and microstructure of AZO films have been investigated by Hall effect measurements, UV/VIS/NIR spectrophotometer, and XRD, respectively. Crystallinity of AZO films increased with increasing substrate temperature ($T_s$) and doping ratio of Al. Resistivity and optical transmittance in visible light were $8.8{\times}10^{-4}{\Omega}cm$ and above 85%, respectively, for the AZO film deposited using AZO target (doped with 3.0 wt% $Al_2O_3$) at $T_s$ of $300^{\circ}C$. On the other hand, transmittance of AZO films in near-infrared region decreased with increasing $T_s$ and doping ratio of Al, which could be attributed to the increase of carrier density.