• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.963-967
• /
• 2001

The effects of the sintering additives such as Bi$_2$O$_3$and V$_2$O$_{5}$ on the microwave dielectric and sintering properties of ZnTiO$_3$system were investigated. Densities of >97% of the theoretical densities have been attained for ZnTiO$_3$at the sintering temperature range of 870~90$0^{\circ}C$ with Bi$_2$O$_3$and V$_2$O$_{5}$ additions of $_3$were obtained with 0.6wt% Bi$_2$O$_3$and 0.5wt% V$_2$O$_{5}$; Qxf$_{o}$ = 48,400 GHz, $\varepsilon$$_{r}$ = 22, and $\tau$$_{f}$ = -43 PPm/$^{\circ}C$. In order to improve temperature coefficient of resonance frequency, TiO$_2$was added to the above system. The optimum amount of TiO$_2$was 15mo1% when sintered at 87$0^{\circ}C$, at which we could obtain following results ; Qxf$_{o}$ = 44,700 GHz, $\varepsilon$$_{r}$ = 26, and $\tau$$_{f}$ = 0 ppm/$^{\circ}C$.EX>.>.EX>.>.>.EX>.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.561-565
• /
• 2002

The effects of sintering additives such as $Bi_2O_3$ and $V_2O_5$ on the microwave dielectric and sintering properties of (Zn, Mg)$TiO_3$ system were investigated. Highly dense samples were obtained for $(Zn_{0.8}Mg_{0.2})TiO_3$ at the sintering temperature range of $870{\sim}900^{\circ}C$ with $Bi_2O_3$ and $V_2O_5$ additions of <1wt.%, respectively. The microwave dielectric properties of $(Zn_{0.8}Mg_{0.2})TiO_3$ with 0.45 wt.% $Bi_2O_3$ and 0.55 wt.% $V_2O_5$ sintered at $900^{\circ}C$ were as follows: $Q{\times}f_o$=56,800 GHz, ${\varepsilon}_r$=22, and ${\tau}_f=-53ppm/^{\circ}C$. In order to improve temperature coefficient of resonant frequency, $TiO_2$ was added to the above system. The optimum amount of $TiO_2$ was 15 mol.% when sintered at $870^{\circ}C$, at which we could obtain following results: $Q{\times}f_o$ = 32,800 GHz, ${\varepsilon}_r$ = 26, and $\tau_f=0ppm/^{\circ}C$.

• 한국전기전자재료학회논문지
• /
• 제15권1호
• /
• pp.30-36
• /
• 2002

The effects of the sintering additives such as B $i_2$ $O_3$ and $V_2$ $O_{5}$ on the microwave dielectric and sintering properties of ZnTi $O_3$ system were investigated. Highly dense samples were obtained for ZnTi $O_3$ at the sintering temperature range of 870~90$0^{\circ}C$ with B $i_2$ $O_3$ and $V_2$ $O_{5}$ additions of <1 wt.%, respectively. The microwave dielectric properties of ZnTi $O_3$ with 0.6 wt.% B $i_2$ $O_3$ and 0.5 wt.% $V_2$ $O_{5}$ were as follows: Qx $f_{o}$ = 48,400 GHz, $\varepsilon$$_{r}$= 22, and $\tau$$_{f}$ = -43 ppm/$^{\circ}C$. In order to improve temperature coefficient of resonant frequency, Ti $O_2$ was added to the abode system. The optimum amount of Ti $O_2$was 15 mol.% when sintered at 87$0^{\circ}C$, at which Ive could obtain following results: Qx $f_{O}$ = 44,700GHz, $\varepsilon$$_{r}$ = 26, and $\tau$$_{f}$ = 0 PPm/$^{\circ}C$.>.EX>.>.>.EX>.>.>.

• 한국전기전자재료학회논문지
• /
• 제18권1호
• /
• pp.50-56
• /
• 2005

The electrical properties, clamping voltage characteristics, and stability of dysprosia-doped ZnO-P $r_{6}$ $O_{11}$-based varistors were investigated with different dysprosia contents from 0 to 2.0 mol%. The incorporation of dysprosia in varistor ceramics greatly increased the varistor voltage from 50 to 481.0 V/mm. It was found that the dysprosia is good additive improving a nonlinearity, in which the nonlinear exponent is above or near 50, and the leakage current is below 1.0 $\mu$A. The dysprosia-doped varistors exhibited superior clamping voltage characetristics, in which clamping voltage ratio is above or neat 2 at surge current of 50 A. The 0.5 mol% dysprosia-doped varistors only exhibited high stability, with the rate of varistor voltage of -0.9%, under DC acceleraetd aging stress, 0.95 $V_{lmA}$/15$0^{\circ}C$/24 h.h.h.h.

• 한국분말재료학회지
• /
• 제17권4호
• /
• pp.289-294
• /
• 2010

For the aim of low-temperature co-fired ceramic microwave components, sintering behavior and microwave properties (dielectric constant ${\varepsilon}_r$, quality factor Q, and temperature coefficient of resonant frequency ${\tau}_f$) are investigated in $Bi_{18}O(Ca_{0.725}Zn_{0.275})_8Nb_{12}O_{65}$ [BCZN] ceramics with addition of $V_2O_5$. The specimens are prepared by conventional ceramic processing technique. As the main result, it is demonstrated that the additives ($V_2O_5$) show the effect of lowering of sintering temperature and improvement of microwave properties at the optimum additive content. The addition of 0.25 wt% $V_2O_5$ lowers the sintering temperature to $890^{\circ}C$ utilizing liquidphase sintering and show the microwave dielectric properties (dielectric constant ${\varepsilon}_r$ = 75, quality factor $Q{\times}f$ = 572 GHz, temperature coefficient of resonance frequency ${\tau}_f\;=\;-10\;ppm/^{\circ}C$). The estimated microwave dielectric properties with $V_2O_5$ addition (increase of ${\varepsilon}_r$, decrease of $Q{\times}f$, shift of ${\tau}_f$ to negative values) can be explained by the observed microstrucure (sintered density, abnormal grain structure) and possibly high-permittivity $Bi_{18}Zn_8Nb_{12}O_{65}$ (BZN) phase determined by X-ray diffraction.

• Transactions on Electrical and Electronic Materials
• /
• 제7권3호
• /
• pp.123-128
• /
• 2006

The microstructure and electrical properties of the varistors, which are composed of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-La_2O_3-based$ ceramics, were investigated for different $La_2O_3$ contents. The increase of $La_2O_3$ content led to more densified ceramics, whereas abruptly decreased the nonlinear properties by incorporating beyond 1.0 mol%. The highest nonlinearity was obtained from 0.5 mol% $La_2O_3$, with the nonlinear coefficient of 81.6 and the leakage current of $0.2{\mu}A$. The increase of sintering time and temperature greatly decreased the nonlinear properties. As the $La_2O_3$ content increased, the donor density increased from $0.64\times10^{18}/cm^3\;to\;16.89\times10^{18}/cm^3$ and the barrier height greatly decreased with increasing $La_2O_3$ content, reaching a maximum (1.47 eV) in 0.5 mol% $La_2O_3$.

• 한국전기전자재료학회논문지
• /
• 제13권9호
• /
• pp.735-744
• /
• 2000

The electrical procerties and stability of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Er$_2$O$_3$ (ZPCCE) based varistors were investigated in the Er$_2$O$_3$content range of 0.0 to 4.0 mol%. ZPCCE ceramics containing 2.0 mol% Er$_2$O$_3$ exhibited the highest density of 5.74 g/㎤ corresponding to 99.3% of theoretical density. The varistors with 0.5 mol% and 2.0 mol% Er$_2$O$_3$exhibited a relatively satisfying nonlinearity, which the nonlinear exponent is 40.50 and 47.15, respectively and the leakage current is 2.66 $mutextrm{A}$, respectively. Under more severe d.c. stress, such as (0.80 V$_{1mA}$/9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$/12h)+(0.90 V$_{1mA}$12$0^{\circ}C$/12h)+(0.95 V$_{1mA}$1$25^{\circ}C$12h), they showed a very excellent stability, which the variation rate of the variator voltage is -0.89% and -0.15%, the variation rate of the nonlinear coefficient is -4.67% and -3.56%, and the variation rate of leakage current is -6.02% and -19.56%, respectively. It is surely bellived that ZnO-0.5 mol% Pr$_{6}$O$_{11}$-1.0 mol% CoO-0.5 mol% Cr$_2$O$_3$-x mol% Er$_2$O$_3$(x=0.5, 2.0) based varistors will be greatly contributed to develop the advanced Pr$_{6}$O$_{11}$-based ZnO varistors in future.uture. future.uture.

• Transactions on Electrical and Electronic Materials
• /
• 제7권4호
• /
• pp.189-195
• /
• 2006

The microstructure, electrical and dielectric properties, and stability against DC accelerated aging stress of the varistors, which are composed of quaternary system $ZnO-Pr_6O_{11}CoO-Cr_2O_3-based$ ceramics, were investigated for different $La_2O_3$ contents. The increase of $La_2O_3$ content led to more densified ceramics, whereas abruptly decreased the nonlinear properties by incorporating beyond 1.0mol%. The highest nonlinearity was obtained from 0.5mol% $La_2O_3$, with the nonlinear coefficient of 81.6 and the leakage current of $0.1{\mu}A$. The varistors doped with 0.5mol% $La_2O_3$ exhibited high stability, in which the variation rates of breakdown voltage, nonlinear coefficient, leakage current, dielectric constant, and dissipation factor were -1.1%, -3.7%, +100%, +1.4%, and +8.2%, respectively, for stressing state of $0.95V_{1mA}/150^{\circ}C/24h$.

• 한국전기전자재료학회논문지
• /
• 제16권12호
• /
• pp.1071-1076
• /
• 2003

The nonlinear properties and their stability of ZPCCD- based varistors, which are composed of ZnO P $r_{6}$ $O_{ll}$ - CoO-C $r_2$ $O_3$-D $y_2$ $O_3$-based ceramics, were investigated in the D $y_2$ $O_3$ content range of 0.0∼2.0 mol%. The incorporation of D $y_2$ $O_3$ greatly affected the nonlinear properties and the best nonlinearity was obtained from 0.5 mol% D $y_2$ $O_3$ with nonlinear exponent of 66.6 and leakage current of 1.2 $\mu$A. Further addition of D $y_2$ $O_3$ deteriorated the nonlinear properties. In stability against DC accelerated aging stress state: 0.95 $V_{1mA}$/15$0^{\circ}C$/24 h, the 0.5 mol％ D $y_2$ $O_3$-doped varistor exhibited the highest stability, in which the variation rate of varistor voltage and nonlinear exponent are -1.9% and 10.5%, respectively. The remainder varistors resulted in thermal runaway due to low density of ceramics.s.s.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.352.2-352.2
• /
• 2016

In recent times, much effort has been concentrated on trivalent rare-earth ions activated ceramics or oxide phosphors to develop display industries due to their promising applications in optoelectronic devices and field-emission displays. To prepare efficient phosphors, citrate sol-gel method is one of the best synthetic methods. Green and blue emissive CaLa2ZnO5:RE3+ nanocrystalline materials are synthesized by a citrate sol-gel method. After the samples annealing at $1100^{\circ}C$, morphological and structural properties are investigated by scanning electron microscope images and X-ray diffraction patterns, respectively. At low electron beam voltage of <5 kV, the visible photoluminescence properties are obtained. Various concentrations of the RE3+ ions exhibited their characteristic emission peaks at different excitation wavelengths, respectively. Similarly, at high electron beam anodic voltage, the cathodoluminescence properties are studied as a function of acceleration voltage and filament current. The chromaticity coordinates are calculated for the optimized CaLa2ZnO5 nanocrystalline luminescent materials.