• Journal of Sensor Science and Technology
• /
• v.17 no.4
• /
• pp.281-288
• /
• 2008

Polyacrylonitrile(PAN)/metal oxide(MO) nanocomposite mats with a thickness of 0.12 mm were electrospun by adding 0 to 10 wt% of MO nanoparticles ($Fe_2O_3$, ZnO, $SnO_2$, $Sb_2O_3-SnO_2$) into PAN. Pt electrode was patterned on $Al_2O_3$ substrate by DC sputtering and then the PAN(/MO) mats on the Pt patterned $Al_2O_3$ were electrically wired to investigate the $CO_2$ gas sensing properties. As the MO content rose, the fiber diameter decreased due to the presence of lumps caused by the presence of MOs in the fiber. The PAN/2% ZnO mat revealed a faster response time of 93 s and a relatively short recovery of 54 s with a ${\Delta}R$ of 0.031 M${\Omega}$ at a $CO_2$ concentration of 200 ppm. The difference in sensitivity was not observed significantly for the PAN/MO fiber mats in the $CO_2$ concentration range of 100 to 500 ppm. It can be concluded that an appropriate amount of MO nanoparticles in the PAN backbone leads to improvement of the $CO_2$ gas sensing properties.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.10a
• /
• pp.68-71
• /
• 2006

Multi-component $ZnO-In_2O_3-SnO_2$ thin films have been prepared by RF magnetron co-sputtering using targets composed of $In_3Sn_4O_{12}$(99.99%) [1] and ZnO(99.99%) at room temperature. $In_3Sn_4O_{12}$ contains less In than commercial ITO, so that it lowers cost. Working pressure was held at 3 mtorr flowing Ar gas 20 sccm and sputtering time was 30 min. RF power ratio [RF1 / (RFI + RF2)] of two guns in sputtering system was varied from 0 to 1. Each RF power was varied $0{\sim}100W$ respectively. The thickness of the films was $350{\sim}650nm$. The composit ion concentrations of the each film were measured with EPMA, AES and XPS. The low resistivity of $1-2\;{\times}\;10^3$ and an average transmittance above 80% in the visible range were attained for the films over a range of ${\delta}\;(0.3\;{\leq}\;{\delta}\;{\leq}\;0.5)$. The films also showed a high chemical stability with time and a good uniformity.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.1985-1988
• /
• 2014

$Cu_2ZnSnSe_4$ (CZTSe) thin films were synthesized on transparent conducting oxide glass substrates via a simple, non-toxic, and low-cost process using a precursor solution paste. A three-step heating process (oxidation, sulfurization, and selenization) was employed to synthesize a CZTSe thin film as an absorber layer for use in thin-film solar cells. In particular, we focused on the effects of sulfurization conditions on CZTSe film formation. We found that sulfurization at $400^{\circ}C$ involves the formation of secondary phases such as $CuSe_2$ and $Cu_2SnSe_3$, but they gradually disappeared when the temperature was increased. The formed CZTSe thin films showed homogenous and good crystallinity with grain sizes of approximately 600 nm. A solar cell device was tentatively fabricated and showed a power conversion efficiency of 2.2% on an active area of 0.44 $cm^2$ with an open circuit voltage of 365 mV, a short current density of 20.6 $mA/cm^2$, and a fill factor of 28.7%.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.11a
• /
• pp.275-277
• /
• 2007

유리를 기판으로 하는 superstrate pin 비정질 태양전지에서 전면투명전도막(TCO)과 p-layer의 계면이 태양전지의 효율을 내는데 가장 큰 기여를 한다. 전면투명전도막(TCO)으로 현재 일반적으로 사용되는 ZnO:Al는 $SnO_2:F$ 보다 전기,광학적으로 우수하고, 안개율(Haze)높으며, 수소 플라즈마에서의 안정성이 높은 특정을 갖고 있다. 그래서 박막 태양전지 특성향상에 매우 유리하나, 태양전지로 제조했을 때, $SnO_2:F$보다 충진율(Fill factor:F.F)과 V_{\infty}$ 가 감소한다는 단점을 가지고 있다. 본 실험실에서는 $SnO_2:F$의 F.F가 72%이 나온 반면 ZnO:Al의 F.F은 68%에 그쳤다. 이들 원인을 분석하기 위해 TCO/p-layer의 전기적 특성을 알아 본 결과, $SnO_2:F$보다 ZnO:Al의 직렬저항이 높게 측정되었다. 이러한 결과를 바탕으로 p-layer 에 R={$H_2/SiH_4$}=25로 변화, p ${\mu$}c$-Si:H/p a-SiC:H 로 p-layer 이중 증착, p-layer의 boron doping 농도를 증가시키는 실험을 하였다. 직렬저항이 가장 낮았던 p ${\mu$}c$-Si:H/p a-SiC:H 로 p-layer 이중 증착에서 Voc는 0.95V F.F는 70% 이상이 나왔다. 이들 각 p층의 $E_a$(Activation Energy)를 구해본 결과, ${\mu$}c$-Si:H의 Ea 가 가장 낮은 것을 관찰 할 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.420-420
• /
• 2014

최근, 과학 기술이 발달함에 따라 현장에서의 실시간 검사 및 자가 지단 등 질병 치유에 대한 사람들의 관심이 증가하고 있으며, 이에 따라 의료, 환경, 산업과 같은 많은 분야에서 바이오 센서에 대한 연구가 활발하게 이루어지고 있다. 그 중, EGFET는 전해질 속의 각종 이온 농도를 전기적으로 측정하는 바이오 센서로, 외부 환경으로부터 안전하고, 제작이 쉬우며, 재활용이 가능하여 비용을 절감 할 수 있다는 장점을 가지고 있다 [1]. EGFET는 감지부와 FET부로 분리된 구조를 가지고 있으며, 감지부의 감지막으로는 Al2O3, HfO2, $TiO_2$, SnO2 와 같은 다양한 물질들이 사용되고 있다. 그 중, SnO2는 우수한 감도와 안정성을 가지고 있는 물질로 추가적인 열처리 공정 없이도 우수한 감지 특성을 나타내기 때문에 본 연구에서 감지막으로 사용하였다. 한편, EGFETs 의 FET부로는 기존의 비정질 실리콘 TFTs 에 비해 10배 이상의 높은 이동도와 온/오프 전류비를 갖는 InGaZnO 를 채널층으로 사용한 TFTs 를 사용하였다. a-IGZO 는 넓은 밴드 갭으로 인해 가시광 영역에서 투명하며, 향후 투명 바이오센서 제작 시, 물질들 사이의 반응을 전기적 신호뿐만 아니라 광학적인 분석 방법으로도 검출이 가능하기에 고 신뢰성을 갖는 센서의 제작이 가능할 것으로 기대된다. 한편, a-IGZO TFTs 의 경우 우수한 전기적 특성을 나타냄에도 불구하고 소자 동작 시 문턱 전압이 불안정하다는 단점이 있으며 [2], 이러한 문제의 개선과 향후 투명 기판 위에서의 소자 제작을 위해서는 저온 열처리 공정이 필수적이다. 따라서, 본 연구에서는 저온 열처리 공정인 u-wave 열처리를 통하여 a-IGZO TFTs 의 전기적 특성 및 안정성을 향상시켰으며, 9.51 [$cm2/V{\cdot}s$]의 이동도와 135 [mV/dec] 의 SS값, 0.99 [V]의 문턱 전압, 1.18E+08의 온/오프 전류 비를 갖는 고성능 스위칭 TFTs 를 제작하였다. 최종적으로, 제작된 a-IGZO TFTs 를 SnO2 감지막을 갖는 EGFETs 에 적용함으로써 우수한 감지 특성과 안정성을 갖는 바이오 센서를 제작하였다.

• Korean Journal of Organic Agriculture
• /
• v.20 no.3
• /
• pp.385-397
• /
• 2012

A pot experiment was carried out to examined the effect of electrolyzed micronutrients (Fe, Mn, Zn, Sr, Se, Sn, Co, Ti, and V) solution treatments with nutrient solution and SCB slurry on the mineral content and growth of tomato in cherry tomato (Lycopersicon esculentum). The treatment of nutrient solution (NS)+micronutrients solution (MS) significantly increased the concentrations of Li, Zn, Sr, Se, Ti as compared with that of NS alone in the cherry tomato fruits, and SCB+MS solution treatment significantly increased Li, Zn, Se, Co, Sr, and Ti contents as compared with SCB treatment. The micronutrient contents of MN+SCB+MS treatment were significantly higher in Li, Zn, Se, Co and in Ti than those of SCB and NS treatment, respectively. The growth and yield of cherry tomato fruits was highest with NS treatment. The yield indices of cherry tomato treated with NS+MS treatment and SCB+NS+MS were 97% and 94% of NS treatment. In conclusion, it seems to be possible to produce micronutrient-fortified cherry tomato by the mixed treatment of electrolyzed micronutrients.

• Journal of dental hygiene science
• /
• v.4 no.3
• /
• pp.103-109
• /
• 2004

The present study prepared 72 test samples - 24 made of amalgam alloy, 24 of Verabond (Ni-Cr alloy) for crown and 24 of Talladium $^{TM}alloy$ for denture - according to the manufacturers' manuals and general method in consideration of the width of the mesial-distal dental crown of the lower $1^{st}$ molar and MOD cavity in clinics, put them in a 200 ml beaker containing 80 ml of artificial saliva, and measured their galvanic corrosion at distances of 0 mm, 7 mm and 40 mm after 7 days. Isolated metals in the electrolyte such as Cu, Ag, Ni, Cr, Sn, Zn and Hg were quantitatively analyzed with Inductively Coupled Plasma - Atomic Emission Spectrometer (ICP-AES, JY-50P, VG Elemental Co. France), and from the results were drawn conclusions as follows. First, Cu, Sn, Ag, Hg and Zn were highly advantageous when amalgam contacted gold alloy compared to Ni-Cr alloy for crown and Talladium alloy for denture. In addition, although gold alloy was finest in terms of oral tissue and biocompatibility, it was most disadvantageous when it was with amalgam. Second, when amalgam contacted gold alloy, heavy metals such as Ni and Cr were not isolated at all because gold alloy did not contain such elements but Sn was isolated as much as $227.1{\pm}18.0035{\mu}g/cm^2$ although it was not included in the composition either. Hg was also isolated. These elements are assumed to have been isolated from amalgam itself. Third, when amalgam alloy was apart from gold alloy 0 mm, 7 mm and 40 mm, Cu and Ag showed significance but Hg did not. This suggests that gold alloy must not be used together with amalgam, and must not be used between dissimilar prostheses regardless of distance. Fourth, when amalgam alloy contacted Ni-Cr alloy for crown, Ag was not isolated from the amalgam, but Zn, Ni, Sn, Hg and Cu were isolated in order of quantity. Significance was observed according to distance - 0 mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Ni-Cr alloy for crown, the isolation Hg was less than that when amalgam alloy contacted Ni-Cr alloy for crown. Fifth, when amalgam alloy contacted Talladium alloy for denture, significance was observed at distances of 0mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Talladium alloy for denture, the isolation Hg was less than that when amalgam alloy contacted Talladium alloy for denture. Sixth, according to the result of ICPES test on Cu, Sn, Ag, Hg, Zn, Ni and Cr of amalgam alloy, gold ally, Verabond and Talladium alloy when these alloys contacted artificial saliva, significance was observed in Cu and Hg. Seventh, when amalgam alloy contracted two non-precious metals Ni-Cr alloy for crown and Talladium alloy for denture in artificial saliva, significance was observed in the isolated by-products of Hg, Ni and Cr according to distance.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.4.2-4.2
• /
• 2009

산화아연 (ZnO)으로 대표되는 산화물반도체는 최근 다양한 비정질 산화물반도체들이 개발되고 있고 높은 이동도와 저온공정 등의 장점으로, 실리콘 기반 박막소자 (비정질-Si, 또는 다결정-Si(LTPS) 트랜지스터)를 대체할 차세대 박막 트랜지스터 (Thin-Film Transistor)의 핵심소재로 관심을 모으고 있다. 또한, 산화물 반도체는 근본적으로 투명하므로, 투명 전극 및 투명 기판재료와 함께 투명 디스플레이도 구현시킬 수 있을 것이다. 그렇지만, 핵심 전자소재로서 향후 디스플레이 및 디바이스에 성공적으로 적용되기 위해서는 소자의 특성 뿐만아니라, 전기적 신뢰성(reliability)을 강화시킬 필요가 있다. 본 발표에서는 In-Ga-Zn-oxide (IGZO), Zn-Sn-oxide (ZTO), Zn-In-Sn-oxide (ZITO) 및 도핑원소를 첨가한 소재에 이르기까지 다양한 산화물 반도체 소재 기술과 소자의 신뢰성 향상을 위한 기술 등을 소개할 것이다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.11a
• /
• pp.9-9
• /
• 2000

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.543-543
• /
• 2013

Thin-film transistors (TFTs) based on oxide semiconductors have been regarded as promising alternatives for conventional amorphous and polycrystalline silicon TFTs. Oxide TFTs have several advantages, such as low temperature processing, transparency and high field-effect mobility. Lots of oxide semiconductors for example ZnO, SnO2, In2O3, InZnO, ZnSnO, and InGaZnO etc. have been researched. Particularly, zinc-tin oxide (ZTO) is suitable for channel layer of oxide TFTs having a high mobility that Sn in ZTO can improve the carrier transport by overlapping orbital. However, some issues related to the ZTO TFT electrical performance still remain to be resolved, such as obtaining good electrical contact between source/drain (S/D) electrodes and active channel layer. In this study, the bottom-gate type ZTO TFTs with staggered structure were prepared. Thin films of ZTO (40 nm thick) were deposited by DC magnetron sputtering and performed at room temperature in an Ar atmosphere with an oxygen partial pressure of 10%. After annealing the thin films of ZTO at $400^{\circ}C$ or an hour, Cu, Mo, ITO and Ti electrodes were used for the S/D electrodes. Cu, Mo, ITO and Ti (200 nm thick) were also deposited by DC magnetron sputtering at room temperature. The channel layer and S/D electrodes were defined using a lift-off process which resulted in a fixed width W of 100 ${\mu}m$ and channel length L varied from 10 to 50 ${\mu}m$. The TFT source/drain series resistance, the intrinsic mobility (${\mu}i$), and intrinsic threshold voltage (Vi) were extracted by transmission line method (TLM) using a series of TFTs with different channel lengths. And the performances of ZTO TFTs were measured by using HP 4145B semiconductor analyzer. The results showed that the Cu S/D electrodes had a high intrinsic field effect mobility and a low effective contact resistance compared to other electrodes such as Mo, ITO and Ti.