• Journal of the Korean institute of surface engineering
• /
• v.13 no.3
• /
• pp.146-154
• /
• 1980

The effects of various electrodeposition conditions (deposition temperature and cathode current density) on preferred orientation and microhardness of electrodeposited Ni-Sn and Sn-Zn alloys were studied. At deposition temperatures from 25$^{\circ}$ to 95$^{\circ}C$ and constant cathode current density of 270 and 530 A/$m^2$ Ni-Sn and Sn-Zn were codeposited in chloride-fluoride acid and stannate-cyanide alkaline electrolyte bath respectively. Ni-Sn alloy deposited at temperatures from 25$^{\circ}$ to 35$^{\circ}C$ was composed of single phase of $Ni_3Sn_4$ with 73 wt.% Sn and the one deposited at temperatures from 45$^{\circ}$ to 95$^{\circ}C$ was made of multiphase mixture of NiSn, $Ni_3Sn_2$ and $Ni_3Sn_4$ with nearly equiatomic composition (65.5 wt.% Sn). The random orientation of thermody-namically metastable NiSn phase (hexagonal structure) predominated at deposition temperature range 25$^{\circ}$-45$^{\circ}C$, and the strong (110) preferred orientation was found at 65$^{\circ}$-85$^{\circ}C$ and then disappeared again at 95$^{\circ}C$. The microhardness of Ni-Sn deposits increased with deposition temperature up to 85$^{\circ}C$, and then decreased at constant cathode current density. The preferred orientation and the maximum microhardness were discussed in terms of lattice contractile stress which result from desorption of hydrogen atom absorbed in deposit lattice. The Sn content of Sn-Zn alloy deposits increased with deposition temperature up to 75$^{\circ}C$, and then decreased at constant cathode current density of 530 A/$m^2$. It also decreased with cathode current density up to 530 A/$m^2$, and then increased at constant deposition temperature of 25$^{\circ}C$. Sn-Zn alloy deposits were composed of two-phase mixture of ${beta}$-Sn and Zn. The preferred orientations of ${beta}$-Sn (tetragonal structure) changed with deposition temperature. The microhardness of Sn-Zn deposits decreased with deposition temperature. It also increased with cathode density up to 530 A/$m^2$, and then decreased at constant deposition temperature of 25$^{\circ}C$. The microhardness of Sn-Zn deposits was observed to be determinded more by the Sn content than by the preferred orientation.

• Journal of Powder Materials
• /
• v.25 no.3
• /
• pp.208-212
• /
• 2018

In this paper, a new $Co_{10}Fe_{10}Mn_{35}Ni_{35}Zn_{10}$ high entropy alloy (HEA) is identified as a strong candidate for the single face-centered cubic (FCC) structure screened using the upgraded TCFE2000 thermodynamic CALPHAD database. The $Co_{10}Fe_{10}Mn_{35}Ni_{35}Zn_{10}$ HEA is fabricated using the mechanical (MA) procedure and pressure-less sintering method. The $Co_{10}Fe_{10}Mn_{35}Ni_{35}Zn_{10}$ HEA, which consists of elements with a large difference in melting point and atomic size, is successfully fabricated using powder metallurgy techniques. The MA behavior, microstructure, and mechanical properties of the $Co_{10}Fe_{10}Mn_{35}Ni_{35}Zn_{10}$ HEA are systematically studied to understand the MA behavior and develop advanced techniques for fabricating HEA products. After MA, a single FCC phase is found. After sintering at $900^{\circ}C$, the microstructure has an FCC single phase with an average grain size of $18{\mu}m$. Finally, the $Co_{10}Fe_{10}Mn_{35}Ni_{35}Zn_{10}$ HEA has a compressive yield strength of 302 MPa.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.392-397
• /
• 2000

The effect of pressure on the phase transformation in Fe-30Ni-0.35C Alloy and pure metals was investigated by using PDSC(pressure differential scanning calorimeter). As the pressure increased from 1 atm to 60 atm, the $A_s$points of the ausformed martensite and the marformed martensite in Fe-30Ni-0.35C Alloy were lowered about $2~4^{\circ}C$ at reverse transformation. This is why the volume change came down at phase transition(from martensite to autenite). As the pressure increased from 1 atm to 60 atm, $A_f$ points were constant or slightly increased. This is due to the promotion of carbide precipitation with increasing pressure. The enthalpy change of the ausformed martensite in Fe-30Ni-0.35C Alloy was increased by 10~14J/g. The melting points of the pure metals, Se, Sn, Pb, Zn and Te were slightly increased with increasing pressure. The enthalpy changes of the pure metals at melting were little changed or slightly increased with increasing pressure.

• Korean Journal of Metals and Materials
• /
• v.47 no.10
• /
• pp.605-612
• /
• 2009

The suitability of twin roll strip casting for Ag-27.5%Cu-20.5%Zn-2.5%Mn-0.5%Ni brazing alloy (known as HS-49D) was examined in the present work and the mechanical properties and microstructure of the strip were also investigated. The effect of annealing heat treatment on the properties was also studied. The new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analyses of the Ag-27.5%Cu-20.5%Zn-2.5%Mn-0.5%Ni strip revealed a eutectic microstructure of an Ag-rich matrix (FCC) and a Cu-rich phase (FCC) regardless of heat treatment. The results of mechanical tests showed tensile strength of 434 MPa and 80% elongation for the twin roll casted strip. Tensile results showed decreasing strengths and increasing elongation with annealing heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.

• Journal of the Korean institute of surface engineering
• /
• v.9 no.3
• /
• pp.1-4
• /
• 1976

In order to get high wear-resistant gold alloy plating on electronic parts, on attempt has been made, in which Cu, Ni, and Zn EDTA salts were added in gold palting solution. The results obtained on the wear resistance are as follows: 1. The addition of 0.5g/ι or over Cu in plating solution, showed 1.5 times more wear resistance than in case of no addition. 2. The addition of 1.5g/ι or over Ni, showed 3.5 times more wear-resistance . 3. The addition of 1.5g/ι and 4.0g/ι Zn , showed 3.5 times and 6.8 times more wear resistance , respectively. 4. The addition of 1.5g/ι Ni and 1.0g/ι Zn simultaneously , showed about 10 times more wear resistance than in case of no addition.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.4
• /
• pp.191-198
• /
• 1998

The effect of the additives on the Zn-Ni alloy electrocrystallization from a chloride bath was investigated by means of electrochemical methodes, scanning electron microscopy and measurement of surface appearancd, X-ray diffraction patterns. The additives thestd ware the Saccharin, surfactant of naptalene-derivative and mixed additive, The resistance of electrodeposit increased by adding the additives, whera the effect of additives on resistance was different with current density roughness, apperarance and morphology of deposit were also influenced by the type of additive. The deposir with fine, compact grains as well as good surface roughness and appearance was obtained from the mixed-additive added bath.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.5
• /
• pp.225-232
• /
• 2013

The influence of aging treatment, addition elements and rolling reduction ratio on the microstructure, mechanical, electrical and bendability properties of Cu-Ni-Si-P-x (x = Fe, Sn, Zn) alloys for connector material application was investigated. SEM/EDS analysis exhibited that Ni2-Si precipitates with a size of 20~100 nm were distributed in grains. Fe, Sn, Zn elemnets in Cu-Ni-Si-P alloy imporved the mechanical strength but it was not favor in increasing of electrical conductivity. As higher final rolling reduction ratio, the strength and electrical conductivity is increased after aging treatment, but it indicated excellent bendability. Especially, Cu-2Ni-0.4Si-0.5Sn-0.1Fe-0.03P alloy show the tensile strength value of 700MPa and the electrical conductivity was observed to reach a maximum of 40%IACS. It is optimal for lead frame and connector.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.403-403
• /
• 2010

The Pt-Ni alloy is an electro-catalyst of interest in the low temperature direct methanol fuel cells(DMFCs). It has been already reported that the Pt-Ni alloy catalysts may even have enhanced activity compared to pure platinum catalyst, depending on how the surfaces are prepared. The order-disorder transition in bimetallic alloy such as $\beta$-CuZn, Cu3Au, and CuAu have been investigated greatly by x-ray diffraction. After annealing the bimetallic alloy, the crystal structure changes as observed in the order-disorder transition of Cu3Au which changes from the face centered cubic to a simple cubic structure. Pt-Ni bimetallic alloy has been already reported to have the face centered cubic structure. However, in nano-scale Pt-Ni bimetallic alloy crystals the crystal structures changes to a simple cubic structure. In this experiment, we have studied the order-disorder transition in Pt-Ni bimetallic nanocrystals. Pt/Ni thin films were deposited on sapphire(0001) substrates by e-beam evaporator and then Pt-Ni alloy were formed by RTA at 500, 600, and $700^{\circ}C$ in a vacuum environment and Pt-Ni nano particles were formed by RTA at $1059^{\circ}C$ in a vacuum environment. We measured the structure of Pt-Ni bimetallic alloy films using synchrotron x-ray diffraction and SEM.

• Korean Journal of Materials Research
• /
• v.25 no.1
• /
• pp.43-47
• /
• 2015

$Zn(BH_4)_2$ was prepared by milling $ZnCl_2$ and $NaBH_4$ in a planetary ball mill in an Ar atmosphere, and XRD analysis, SEM observation, FT-IR analysis, DTA, and TGA were performed for synthesized $Zn(BH_4)_2$ samples. 90 wt% $MgH_2$+1.67 wt% $Zn(BH_4)_2(+NaCl)$+5 wt% Ni+1.67 wt% Ti+1.67 wt% Fe (named $90MgH_2+1.67Zn(BH_4)_2(+NaCl)$+5Ni+1.67Ti+1.67Fe) samples were also prepared by milling in a planetary ball mill in an $H_2$ atmosphere. The gas absorption and release properties of the $Zn(BH_4)_2(+NaCl)$ and $90MgH_2+1.67Zn(BH_4)_2(+NaCl)_2(+NaCl)$+5Ni+1.67Ti+1.67Fe samples were investigated. An FT-IR analysis showed that $Zn(BH_4)_2$ formed in the $Zn(BH_4)_2(+NaCl)$ samples prepared by milling $ZnCl_2$ and $NaBH_4$. At the first cycle at $320^{\circ}C$, $90MgH_2+1.67Zn(BH_4)_2(+NaCl)$+5Ni+1.67Ti+1.67Fe absorbed 2.95 wt% H for 2.5 min and 4.93 wt% H for 60 min under 12 bar $H_2$, and released 1.46 wt% H for 10 min and 4.57 wt% H for 60 min under 1.0 bar $H_2$.

• Analytical Science and Technology
• /
• v.12 no.1
• /
• pp.40-46
• /
• 1999

Zn-Ni alloy electrodeposition on steel has been examined by means of X-ray diffraction and scanning electron microscopy. The effect of current density, $Ni^{2+}$ ion concentration, and $Cl^-$ ion concentration on the structure as well as morphology of the electrodeposit have been studied. The Ni content of the electrodeposit increased with decreasing current density in the range studied in this work. The Ni content of the electrodeposit also increased with increasing $Ni^{2+}$ ion and $Cl^-$ ion concentrations. The structure change of the electrodeposit was closely related to the Ni content. In fact, the mixture phase of ${\eta}$ and ${\gamma}$ was found below 10 wt.% of Ni while the ${\gamma}$ phase only was observed above 10 wt.% of Ni. In addition, the lattice parameter, a, of then phase structure increased and the lattice parameter, c, of it decreased as the Ni content of the electrodeposit increased. The morphology of the electrodeposit varied from the plate-like shape to the fine granular shape depending upon the change in composition and structure of the electrodeposit.