• 한국건축시공학회지
• /
• 제21권6호
• /
• pp.539-550
• /
• 2021

일반 전기 아크에 의한 금속용사공법에 비해 시공속도와 효율성능이 우수한 플라즈마 아크 용사장비를 개발하여 이 플라즈마 용사장비에 의한 코팅의 부식특성 평가가 요구되었다. 본 연구에서는 일반 탄소강에 Zn 및 Zn-15Al을 플라즈마 아크 금속 용사법으로 코팅한 후 해수 환경과 유사한 3.5wt.% NaCl 용액에 침지하여 내식성을 평가하였다. SEM 및 XRD에 의한 표면 형상 분석 시험 결과, Zn 코팅이 다공성이고 침상 형태로 되어 있어 용액의 침투가 용이하여 부식 속도가 빠른 것을 알 수 있었다. 반면, Zn-15Al 코팅은 균일하고 조밀한 형태를 보여 부식을 억제하는 것으로 나타났다.

• 한국표면공학회지
• /
• 제46권3호
• /
• pp.116-119
• /
• 2013

To improve the corrosion resistance of an electrogalvanized steel sheet, we deposited magnesium film on it using a vacuum evaporation method and annealed the films at $250-330^{\circ}C$. The zinc-magnesium alloy is consequently formed by diffusion of magnesium into the zinc coating. From the anodic polarization test in 3% NaCl solution, the films annealed at $270-310^{\circ}C$ showed better corrosion resistance than others. In X-ray diffraction analysis, $ZnMg_2$ was detected through out the temperature range, whereas $Mg_2Zn_{11}$ and $FeZn_{13}$ were detected only in the film annealed at $310^{\circ}C$. The depth composition profile showed that the compositions of Mg at $270-290^{\circ}C$ are evenly and deeply distributed in the film surface layer. These results demonstrate that $270-290^{\circ}C$ is a proper temperature range to produce a layer of $MgZn_2$ intermetallic compound to act as a homogeneous passive layer.

• 한국표면공학회지
• /
• 제26권1호
• /
• pp.11-21
• /
• 1993

The relationship between the amount of deposited-Zn and the adhesion of Zn film has beend investigated. This study changed the mild steel substrate temperature range of $100^{\circ}C$~$250^{\circ}C$, with the aim of studying the adhesion of Zn film coated by PVD on substrates in 10-2~10-3torr and deoxidant gas atmospheres 50%H2~50%N2 and 75%H2+25%N2. The result revealed that the adhesion of Zn film was remarkably good in a 75% H2+25%N2 gas atmosphere as well as deoxidant time was short, and with increasing the substrate tempera-ture up to $250^{\circ}C$. Whiled the amount of deposition tended to increase linearly with time at constant evaporation temperature. It was almost constant when the substrate temperature was lower than $200^{\circ}C$, slightly decreased between $200^{\circ}C$ and $250^{\circ}C$ and significantly decreased at $300^{\circ}C$.

• 소성∙가공
• /
• 제32권6호
• /
• pp.344-351
• /
• 2023

The use of Zn-Al-Mg alloy coatings for enhancing the corrosion resistance of steel sheets is gaining prominence over traditional Zn coatings. There is a growing demand for the development of thermal spray wires made from Zn-Al-Mg alloys, as a replacement for the existing wires produced using Al and Zn. This is particularly crucial to secure corrosion resistance and durability in the damaged areas of coated steel sheets caused by deformation and welding. This study focuses on the casting and extrusion processes of Zn-2Al-1Mg alloy for the fabrication of such spray wires and analyzes the changes in microstructure during the extrusion process. The Zn-2Al-1Mg alloy, cast in molds, was subjected to a heat treatment at 250 ℃ for 3 hours prior to extrusion. The extrusion process was carried out by heating both the material and the mold up to 300 ℃. Microstructural analysis was conducted using FE-SEM and EDS to differentiate each phase. The mechanical properties of the cast specimen were evaluated through compression tests at temperatures ranging from 200 to 300 ℃, with strain rates of 0.1 to 5 sec^-1. Vickers hardness testing was utilized to assess the inhomogeneity of mechanical properties in the radial direction of the extruded material. Finite Element Analysis (FEA) was employed to understand the inhomogeneity in stress and strain distribution during extrusion, which aids in understanding the impact of heterogeneous deformation on the microstructure during the process.

• Korean Chemical Engineering Research
• /
• 제49권6호
• /
• pp.745-751
• /
• 2011

내부식성이 강화된 새로운 방청안료를 개발하기 위한 연구의 일환으로, 본 연구에서는 높은 내부식성을 제공하는 아연 및 세륨 이온 교환된 제올라이트를 도입하였다. 그리고 이온교환 제올라이트를 이용하여 프라이머 도료 제조 및 도장을 수행한 후, 그것의 방식성능을 측정하였다. 도장을 위한 금속 기재는 아연도금(galvanized, GI) 강판이었고, 도장된 강판의 방식성능은 electrochemical impedance spectroscopy(EIS)와 scanning vibrating electrode technique(SVET)으로 측정되었다. EIS 및 절단면의 내부식성을 확인하기 위한 SVET 측정으로부터 세륨이온 교환된 제올라이트가 가장 높은 효율을 제시하였고, 아연 및 세륨 이온 교환된 제올라이트의 경우 GI 강판에 대하여 cathodic 부식 방지제로 기여함을 확인할 수 있었다.

• Journal of Welding and Joining
• /
• 제18권3호
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.49-56
• /
• 1997

Effect of process parameters on the quality of condenser discharge weld for coated sheet steels was discussed. The welding specimens were coated with pure Zn of 20/20 g/m2 in the production line. Direct measurements of welding parameters such as the discharge current, the pressures and the voltage drop across the electrodes were carried out with welding process monitoring system. High speed camera was also utilized to analyze the weld formation process. Test results indicated that the relation between weld strength and applied energy was stabilized at the acceptable welding heat input range. It was thought that the acceptable welding heat input should be redefined based on the monitored data because the calculated value of the welding heat input could hardly be utilized if the discharge condition was changed. Mechanical test results and high speed photographs showed that expulsion deteriorated the weld quality and the strength at the same time especially when the size of the spatter was large enough to carry the molten metal, which should form the nugget, out of the welding spot. Results also demonstrated that the discharge current should be applied at the appropriate time during the process because sufficient nugget was not produced if the time was deviated from the optimum range.

• 한국레이저가공학회지
• /
• 제2권3호
• /
• pp.42-51
• /
• 1999

This research was conducted as a fundamental study to apply tailored blank welding technique into automotive production process. The materials used in this study were 2.0mm thickness low carbon steel sheets and 1.2mm Zn-coated low carbon steel sheets. To ensure the reproducibility and to consider various factors, experiments were. conducted by applying Taguchi experimental method with 6 factors. Every welding process was repeated 3 times to offset the effect of uncontrolled factors. Elongation and LDH(Limited Dome Height)were measured to evaluate formability of specimens and Optical microscopy, XRD, SEM, and EDS analysis were performed to observe the microstructures and to determine the solidification mode in the weld. The elongation of specimen welded with optimum condition was 83% of base metal, and LDH was 84% of base metal. In case of laser treated specimen where Zn coating was removed, elongation was 85% of base metal, and LDH was 85% of base metal. In fusion zone, phases were consisted of quasi-polygonal ferrite, banitic ferrite, and martensite.

• Corrosion Science and Technology
• /
• 제5권2호
• /
• pp.39-44
• /
• 2006

The dissolution amount of Zn plate was $0.058mg/cm^2$ in the non-magnetically treated solution, and was $0.059mg/cm^2$ in the magnetically treated solution after 24 hours of immersion. The magnetic treatment had no effect to corrosion of Zn plate as pH on surface was not recognized the difference. The addition of Zn(II) ion in the solution was prepared to the effects of corrosion and dissolution of Fe. The regularity was not obtained the effect of the magnetic treatment on the dissolution of Fe plate.

• 한국표면공학회지
• /
• 제34권6호
• /
• pp.537-544
• /
• 2001

In the present study, tin-zinc alloys were coated on a cold-rolled steel sheet with variations of electrolyte concentration, additives quantity and current density employing the Hull cell and circulation cell simulator. With an addition of additives of 2m1/L, tin-zinc deposits containing 10 to 40 percent Zn revealed a good surface appearance with weak acidic electrolytes. The organic additives suppressed the Sn deposition rate and thus increased the zinc contents in tin-zinc coating layers. The zinc contents in the tin-zinc coating layers depended almost linearly on the concentrations of metal ions of tin and zinc. Temperature of the electrolyte affected the composition tin-zinc coating layer. However, the concentration of complexants revealed little effectiveness. The surface morphology of tin-zinc coating showed dense tin and zinc phases with fine equiaxed grains with the high current density.