• Journal of Welding and Joining
• /
• v.31 no.4
• /
• pp.7-12
• /
• 2013

The dissimilar welding between magnesium alloy and steel sheet was required in automobile industry to increase the strength of the dissimilar joints. Laser brazing is one of the good joining processes for Mgsteel dissimilar joint. In this study, the effect of coating materials was evaluated on the laser brazing for the dissimilar joint between AZ31 and coated steels such as Zn, Sn and Ni. Diode direct laser was used to braze the lap-edge joint with Mg600 filler wire and Superior #21 flux. The wettability was best on Zn coated steel. The interlayer was formed at the interface between brazement and steel for all coating materials. The strengths of brazed specimen were 146.5N/mm, 204.6N/mm and 101.6N/mm for Zn, Sn and Ni coated steel respectively.

• Korean Journal of Metals and Materials
• /
• v.50 no.3
• /
• pp.224-232
• /
• 2012

In this study, the effect of hot-stamping heat treatment on the microstructure and hardness of TWB(Tailor Welded Blank) laser joints in Al-Si-coated boron steel and Zn-coated DP(Dual Phase)590 steel was investigated. In the TWB joints without heat treatment, hardness profiles showed local hardness deviation near the fusion zone. However, there was no hardness deviation in the heat treated specimen and its hardness was higher than that of the one without the heat treatment, due to a fully martensite microstructure. In the TWB joints of both the boron and DP steels, the maximum hardnesses were observed at the HAZ(Heat Affected Zone) near the base metal, and the hardness decreased gradually to the base metal. In the heat treated joints, the hardnesses of the HAZ and the base metal of the boron steel side were similar to the maximum hardness of the weld, while those of the HAZ and the base metal of the DP steel side were higher than the maximum hardness.

• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.6
• /
• pp.283-291
• /
• 2012

In order to increase the anti-oxidation property during the tailor welding blanked hot press forming process for a high strength boron steel sheet, we performed a different coating method on the boron-steel sheet such as 87% Al - 13% Si and Fe - 8.87 Zn dipping plating procedure. However, during laser welding process, the Al-Si coated steel sheet has showed a low tensile strength and about half value of elongation than the original boron-steel sheet. Aluminum and silicon, elements of coating layer were diffused into the boron-steel matrix and have shown a low strength result than non-coated specimen. On the other hand, Zinc-coated boron-steel has expectedly showed a excellent tensile strength and micro-harness value in the welded area like original boron-steel.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.533-542
• /
• 2010

The specific motivation for joining an Al alloy and Zn-coated steel arises from the need to save fuel consumption by weight reduction and to enhance the durability of vehicle structures in the automobile industry. In this study, the lap joining A6K31 Al alloy (top) and SGARC340 Zn-coated steel (bottom) sheets with a thickness of 1.0 mm and 0.8 mm, respectively, was carried out using the friction stir weld (FSW) technique. The probe of a tool did not contact the surface of the lower Zn-coated steel sheet. The friction stir welding was carried out at rotation speeds of 1500 rpm and travel speeds of 80~200 mm/min. The effects of tool geometry and welding speed on the mechanical properties and the structure of a joint were investigated. The tensile properties for the joints welded with a larger tool were better than those for the joints done with a smaller tool. A good correlation between the tensile load and area of the welded region were observed. The bond strength using a larger tool (M4 and M3) decreased with an increase in welding speed. Most fractures occurred along the interface between the Zn-coated steel and the Al alloy. However, in certain conditions with a lower welding speed, fractures occurred at the A6K31 Al alloy.

• 연구논문집
• /
• s.23
• /
• pp.109-120
• /
• 1993

A study on corrosion and adhesion properties of evaporated Zn-Cr films were conducted on steel strip by two-source evaporater. Corrosion resistance of Zn-Cr coated steel was evaluated by salt spray test in 5% NaCl. Adhesion property of Zn-Cr films on steel substrate was evaluated by tape test after $180^\circC$ bending. Adhesion was improved with increasing the Cr content and reached the maximum at the Cr content of 6 to 8wt%. Corrosion resistance was enhanced with increasing the Cr content and improved by rolling Zn-Cr coated specimen, as a post-treatment.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.1
• /
• pp.69-76
• /
• 2023

The effects of hairline treatment on surface blackening and thermal diffusion behaviors of Zn-Al-Mg alloy coated steel sheet were evaluated by the three-dimensional surface profiler and laser-flash technique. The metallographic observation of coating damages by hairline treatments showed that several cracks were initiated and propagated along the interface between primary Zn/eutectic phases. As the hairline processing became more severe, the crack occurrence frequency in eutectic phase of coating layer and the surface roughness increased, which had a proportional relationship with the level of blackening on the coating surface. In addition, the higher interfacial areas of the blackened coating surface, caused by the hairline process, led to an increase in thermal diffusivity and conductivity of the coated steel sheet. On the other hand, when the coating damage by hairline treatment was excessive and the steel substrate was exposed, there was little difference between the thermal diffusivity/conductivity of the untreated sample though the blackening degree was higher than that of untreated sample. This work suggests that the increase in the surface areas of the coating layer without exposure to steel substrate through hairline treatment can be one of the effective technical strategies for the development of Zn-Al-Mg alloy coated steel sheets with higher blackening level and thermal diffusivity.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1992.03a
• /
• pp.71-82
• /
• 1992

The frictional characteristics of Zn-Ni coated steel sheets were investigated by draw bead test and strip draw test. In strip draw test, the frictional characteristics were evaluated by the drawing force ratio (Tc/Ts) for half coating-stripped specimens. It is clarified that the drawing force ratio obtained by strip draw test is a convenient parameter compared to coefficient of friction obtained by draw bead test to evaluate the frictional characteristics of Zn-Ni coated steel sheets.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.191-191
• /
• 2000

The mechanism of the blowhole and the pit formation in lap-jointed fillet CO₂ arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage.2) Most of the pits was back-filled at the last stage of their formation. (Received September 27, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.64-68
• /
• 2000

The mechanism of the blowhole and the pit formation in lap-jointed fillet Co₂arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows: 1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage. 2) Most of the pits was back-filled at the last stage of their formation.

• Corrosion Science and Technology
• /
• v.20 no.1
• /
• pp.7-14
• /
• 2021

PosMAC^® is a brand of Zn-Mg-Al hot-dip coated steel sheet developed by POSCO. PosMAC^® can form dense surface oxides in corrosive environments, providing advanced corrosion resistance compared to traditional Zn coatings such as GI and GA. PosMAC^® 3.0 is available for construction and solar energy systems in severe outdoor environments. PosMAC^®1.5 has better surface quality. It is suitable for automotive and home appliances. Compared to GI and GA, PosMAC^® shows significantly less weight reduction due to corrosion, even with a lower coating thickness. Thin coating of PosMAC^® provides advanced quality and productivity in arc welding applications due to its less generation of Zn fume and spatters. In repeated friction tests, PosMAC^® showed lower surface friction coefficient than conventional coatings such as GA, GI, and lubricant film coated GA. Industrial demand for PosMAC^® steel is expected to increase in the near future due to benefits of anti-corrosion and robust application performance of PosMAC^® steel.