• The Journal of the Convergence on Culture Technology
• /
• v.10 no.1
• /
• pp.363-368
• /
• 2024

Steel structures used in marine environments, such as ships, offshore structures or sub-structures in wind power generation facilities are prone to corrosion. In this study, the corrosion fatigue crack propagation characteristics due to the environmental load are examined by experiment at -1050 mV vs. SCE, which is equivalent to the anti-corrosion potential of zinc anodes that are widely used as sacrificial anodes. In this study, for this purpose, an experimental study is conducted on the effect of cathodic protection on the propagation of fatigue cracks in the seawater environment under the condition of -1050 mV vs. SCE, considering the wave period in synthetic seawater. Cathodic protection prevents corrosion; however, excessive protection generates hydrogen through chemical reactions as well as calcareous deposits. The fatigue crack propagation rate appeared to be faster than the rate in a seawater corrosion environment at the early stages of the experiment. As the crack length and stress intensity factor K increased, the crack propagation rate became slower than the fatigue crack propagation rate in seawater. However, the crack growth rate was faster than that in the atmosphere.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.2
• /
• pp.56-66
• /
• 1995

Recently, with theraped advancement in th oceanology such an ocean-going vessel and oceanic structures, there is a need to study the cavitation erosion-corrosion control of pump impeller, the partial element of ocean machinery, for more effective operation. Especially, the cathodic protection (impressed current method & Al-sacrificial anode method) was applied to sea water, and Cu-alloy material mixed Zn & Al was used as a control method of cavitation erosion-corrosion. In this study, used the piezoelectric vibrator with 20KHz, 24.mu.m to cavity generation apparatus, and investigated the weight loss, weight loss rate, electrode potential & current density etc. under this condition. According to test result, thos describes how to indentify an influence of the cathodic protection and Al & Zn addition in material development for the control of cavitation erosion-corrosion, and those will serve as fundamental data on the cavitation erosion-corrosion control of oceanic centrifugal pump.

• Journal of the Korean Chemical Society
• /
• v.46 no.5
• /
• pp.444-456
• /
• 2002

To protect the occurrence of the oxidation of car body, we developed antioxidizing device made with sacrificial anode. Because car body is made of iron and iron-alloy and oxidation potential of Mg, Al and Zn is higher than that of iron, sacrificial anodes were made with Mg, Al and Zn. Accordingly, Mg, Al and Zn are better oxidizing than car body, iron and iron-alloy can be protected from oxidizing. We have made an antioxidizing device and evaluated their anti-corrosive effect for iron piece in the solution of hydrochloric, nitric and sulfuric acid using balance, SEM and XPS. When iron pieces were connected with antioxidizing device of car body, weight loss by oxidation was remarkably reduced and surface corrosion of iron piece was protected. It was shown that the surface of iron pieces which is not con-nected to the device was changed to iron(Ⅲ) oxide, Fe$_2$O$_3$. Therefore, if this device is attached to car body, corrosion and oxidation of car body will be reduced, considerably.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.232-233
• /
• 2005

Stainless steel has been stably used closed by passivity oxidation films($Cr_2O_3$) is made by neutral atmospheric environment. However, passivity oxidation films of the surface of stainless steel occasionally comes to be destroyed in seawater which is influenced by an environment having halogen ion like $Cl^-$, then, localization corrosion comes to occur. Stainless steel 304 for shaft system material of the small-size FRP fishing boat on seawater environments made an experiment on simulation of sacrifical anode(Al, Zn). Through these experiment and study, following results have been obtained ; According to the field inspection and corrosion simulation, the corrosion on the 2nd class stainless steel shaft(STS 304) in FRP fishing boat has been verified to occur by crevice corrosion and galvanic corrosion etc.. According to the comparison and analysis of Stainless steel 304 shaft materials after simulation leaving unprotected and applying cathodic protection, unprotected shaft specimen of stainless steel 304 was severely corroded, but, protected shaft specimen was not totally corroded. This result is assumed to be made by the facts that anodic reaction, $Fe{\rightarrow}Fe^{2+}$ + $2e^-$, has been restricted by the cathodic protection current of sacrificial anode material.

• Journal of the Korea Convergence Society
• /
• v.9 no.10
• /
• pp.271-276
• /
• 2018

In the industry, Zn galvanizing on the steel using the principle of sacrificial anode is used. The steel have some problem, specially corrosion problem. To solve corrosion problem, Zn-Mn alloy plating has been studied as one of the measures to increase the corrosion resistance rather than pure zinc plating. It is possible to be applied to automotive parts requiring high corrosion resistance even though the plating cost is high. In this study, Zn-Mn alloys were electrodeposited from an acidic chloride bath. The influence of the electrolytic conditions on the composition of the alloy plating in the chloride bath was investigated. As the current density of the cathode increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. As the temperature of the electrolyte increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. The results are explained by the cathode overvoltage curve of Mn and Zn.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.271-272
• /
• 2006

Zinc confers high corrosion resistance by acting as a sacrificial anode, and a zinc coating improves the appearance of steel. Chromate conversion coating (CCC) films are still one of the most efficient surface treatments for steel. Although such films can self-repair via the dissolution of Cr(VI), dissolved Cr(VI) have adverse effects on humans, and the environment. Therefore, we examined the corrosion protection property and morphology of colloidal silica conversion films as an alternative to CCC films. The corrosion behavior was investigated in 3% NaCl solution using electrochemical techniques, including electrochemical impedance spectroscopy, open circuit potential, and the salt spray test(SST). Corrosion was implied by the appearance of red rust on the specimen surface. In corrosion resistance at 3% NaCl solution, red rust appeared at 15-20, 55-70, and 83-98 days on Zn-electroplated steel, colloidal silica conversion-coated specimens, and CCC-coated specimens, respectively. In the salt spray test, the colloidal silica film provided better corrosion protection than CCC films, i.e., red rust appeared at 96 hours on the Zn-electroplated steel sheet, at 432 hours with the CCC films, and at 888 hours with silica conversion coating.

• Journal of the Korea Convergence Society
• /
• v.8 no.11
• /
• pp.307-312
• /
• 2017

In the industry, galvanizing using the principle of sacrificial anode is used Zn-Ni alloy plating was developed as one of the measures to increase the corrosion resistance rather than pure zinc plating. The alloy plating layer has a corrosion resistance of 4-5 times that of the pure zinc plating layer, so that it is applied to automotive parts requiring high corrosion resistance even though the plating cost is high. The amount of Zn-Ni alloy plating solution is a sulfuric acid bath, a chlorinated bath, an alkali bath, and an ammonia bath. Here, the influence of the electrolytic conditions on the composition of the alloy plating in the chloride bath was investigated. The results are explained by the cathode overvoltage and the diffusion coefficient. In general, as the overvoltage of the cathode increases, the concentration polarization becomes more important than the activation polarization. The concentration polarization is determined by element diffusion in the diffusion layer. That is, as the overvoltage of the cathode increases, the Zn content having a large diffusion coefficient increases.

• Journal of Korea Ship Safrty Technology Authority
• /
• s.21
• /
• pp.66-77
• /
• 2006

Stainless steel has been stably used closed by passivity oxidation films(Cr₂O₃) is made by neutral atmospheric environment. However, passivity oxidaton films of the surface of stainless steel occasionally comes to be destroyed in seawater which is influenced by an environment having galogen ion like Cl‾, then, localization corrosion comes to occur Stainless steel 304 for shaft system material of the small-size FRP fishing boat on seawater environments made an experiment on simulation of sacrifical anode(Al, Zn). Through these experiment and study, following results have been obtained ; According to the field inspection and corrosion simulation, the corrosion on the 2nd class stainless steel shaft(STS304) in FRP fishing boat has been verified to occur by crevice corrosion and galvanic corrosion etc., According to the comparison and analysis of Stainless steel 304 was severely corroded, but, protected shaft specimen was not totallay corroded. This result is assumed to be made by the facts that anodic reaction, Fe → fe²+＋ 2e¯, has been restricted by the cathodic protection current of sacrificial anode material.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1065-1068
• /
• 2008

Marine bridges are readily deteriorated due to the exposure to marine environment. The concrete deterioration occurred by corrosion of steel in concrete is mainly relevant to chloride in seawater. Chloride ions penetrate through porous concrete, and then reach to the reinforcing steel, and finally corroded them. The corrosion by-products(rusts) increase the volume as much as 6 to 10 times of origin steel. this creates expanding pressure and tensile stress, which cause the structures cracking and spalling. Sometimes the rebar corrosion is accelerated, and then collapsed catastrophically. In order to prevent corrosion damage, it is important to understand well regarding the reason of concrete corrosion, the quantification of its damage, and protection method/system to stop or to mitigate the corrosion. In this study, slab specimens were fabricated to evaluate the effect of cathodic protection which was simulated to marine bridges, and/or port structures. Zn-mesh sacrificial anode has been applied as a chathodic protection system and accelerated test conditions, i.e. temperature and salt concentration have been used in this study.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.166-171
• /
• 2016

Cathodic protection is widely recognized as the most cost effective and technically appropriate corrosion prevention methodology for the port, offshore structures, ships. When applying the cathodic protection method to metal facilities in seawater, on the surface of the metal facilities a compound of calcium carbonate($CaCO_3$) or magnesium hydroxide($Mg(OH)_2$) films are formed by $Ca^{2+}$ and $Mg^{2+}$ ions among the many ionic components dissolving in the seawater. And calcareous deposit films such as $CaCO_3$ and $Mg(OH)_2$ etc. are formed by the surface of the steel product. These calcareous deposit film functions as a barrier against the corrosive environment, leading to a decrease in current demand. On the other hand, the general calcareous deposit film is a compound like ceramics. Therefore, there may be some problems such as weaker adhesive power and the longer time of film formation uniting with the base metal. In this study, we tried to determine and control the optimal condition through applying the principle of cathodic current process to form calcareous deposit film of uniform and compact on steel plate. The quantity of precipitates was analyzed, and both the morphology, component and crystal structure were analyzed as well through SEM, EDS and XRD. And based on the previous analysis, it was elucidated mechanism of calcareous deposit film formed in the sacrificial anode type (Al, Zn) and current density (1, 3, $5A/m^2$) conditions. In addition, the taping test was performed to evaluate the adhesion.