• 한국표면공학회지
• /
• 제32권3호
• /
• pp.452-455
• /
• 1999

ORV which vaporizes LNG to NG is consisted of tube and header whose substrate is aluminum alloy. The corrosion of the tube is very severe because of sea water being used as the heating source. In this research to protect ORV substrate material, the corrosion behavior of aluminum alloys was investigated for the sacrificial role of Al-Zn alloy for ORV tubes. The electrochemical behavior of aluminum alloys in sea water was investigated. The corrosion behavior of thermally-sprayed and cladded samples were compared through salt spray tests. Al-Zn alloy can act as a sacrificial anode and cladded Al-Zn alloy has a better corrosion resistance than that of thermally sprayed one. The galvanic effect of Al-Zn to substrate material was conformed from scratched sample tests.

• Corrosion Science and Technology
• /
• 제6권6호
• /
• pp.269-274
• /
• 2007

The corrosion of steel in concrete is significant in marine environment. Salt damage is one of the most detrimental causes to concrete bridges and port structures. Especially, the splash and tidal zones around water line are comparatively important in terms of safety and life-time point of view. During the last several decades, cathodic protection (cp) has been commonly accepted as an effective technique for corrosion control in concrete structures. Zn-mesh sacrificial anode has been recently developed and started to apply to the bridge column cp in marine condition. The detailed parameters regarding Zn-mesh cp technique, however, have not well understood so far. This study is to investigate how much Zn-mesh cp influences along the concrete column at elevated temperature. About 100 cm column specimens with eight of 10 cm segment rebars have been used to measure the variation of cp potential with the distance from Zn-mesh anode at both $10^{\circ}C$ and $40^{\circ}C$ in natural seawater. The cp potential change and current diminishment along the column specimens have been discussed for the optimum design of cp by Zn-mesh sacrificial anode.

• Journal of Electrochemical Science and Technology
• /
• 제14권4호
• /
• pp.349-360
• /
• 2023

This study investigated the tri-metallic galvanic coupling of different metals in the tubes, fillers, and fins of a heat exchanger. The goal was to prevent corrosion of the tubes using the fin as a sacrificial anode while ensuring that the filler metal has a more noble potential than the fin, to avoid detachment. The metals were arranged in descending order of corrosion potential, with the noblest potential assigned to the tube, followed by the filler metal and the fin. To address a reduction in protection current of the fin, the filler metal was modified by adding Zn to decrease its corrosion potential. However, increasing the Zn content of filler metal also increases its corrosion current. The study examined three different filler metals, considering their corrosion potential, and kinetics. The results suggest that a filler metal with 1.5 wt.% Zn addition is optimal for providing cathodic protection to the tube while reducing the reaction rate of the sacrificial anode.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.773-776
• /
• 2008

해양환경에서 철근 콘크리트의 부식은 매우 심하며, 염해는 콘크리트 교량과 항만 구조물의 부식을 일으키는 주요 요인 중 하나이다. 특히 비말대 및 간만대의 수면 부분은 구조물의 안전과 수명의 관점에서 볼 때 매우 중요하다. 지난 수십 년간 토목, 건축분야에서 콘크리트구조물 부식을 억제하기 위한 방식법 중 음극방식(cathodic protection, CP)은 많은 발전을 이룩하였으며 이제 보편화되는 추세에 있다. 최근 해양환경에서 콘크리트구조물의 음극방식을 위해 아연 메쉬 희생양극법이 개발 소개되었으나 아직까지도 이에 대한 구체적 내용이 잘 알려지지 않은 상태이다. 따라서 본 연구에서는 아연 메쉬 음극방식이 환경인자에 따라 콘크리트교각에 어떤 영향을 미치는지에 대하여 조사하였다. 아연 메쉬와 철근의 거리에 따라 음극방식 효과를 측정하기 위하여 약 100cm의 파일 시험편에 10cm 세그먼트 철근 8개를 설치하였으며, 아연 메쉬 희생양극에 의한 음극방식의 설계에 관련된 정보를 얻고자 파일 시험편의 높이에 따른 음극방식 전위의 변화와 전류의 감소치를 측정하였다.

• 한국항해항만학회지
• /
• 제39권4호
• /
• pp.277-283
• /
• 2015

함정에 사용되는 선체재료로는 연강, 고장력강, 고강도강, 알루미늄 합금 및 복합재료 등이 있다. 그 중 함정의 선체는 수밀과 강도의 유지 및 탑재장비의 지지 등 기본적인 기능을 위하여 철강 재료를 주로 사용하고 있다. 함정의 주 임무는 해양에서 작전을 수행하는 것이므로 해수에 의한 선체 부식이 필연적으로 발생하게 된다. 선체의 부식을 방지하기 위하여 도장 방법, 희생양극법 및 강제 전류 방식이 사용되고 있다. 특히 Al 및 Zn을 활용한 희생양극법의 경우 부식특성 개선을 위하여 인듐(In), 카드뮴(Cd) 및 납(Pb) 등의 중금속이 첨가되어 있다. 하지만 이러한 중금속은 인체 및 환경에 매우 유해하므로 전 세계적으로 사용이 점차 규제되고 있다. 이에 본 논문에서는 인체 및 환경에 무해한 미세원소(Ma, Ca, Ce 및 Sn)를 첨가하여 Al 및 Zn 합금을 제조하였다. 제조된 함정용 Al 및 Zn 희생양극의 효율 특성 측정을 위하여 SEM, XRD, 동전위 분극실험 및 전류효율 평가를 실시하였으며, 실험결과 Al-3Zn-0.6Sn 및 Zn-3Sn 합금의 양극 성능이 다른 합금 보다 효율성이 우수하였다.

• 한국산학기술학회논문지
• /
• 제18권3호
• /
• pp.681-686
• /
• 2017

태양광 모듈에서 태양전지를 연결해주는 인터커넥터로 리본 솔더로 SnPbAg가 사용되고, 옥외 태양광 발전에 장기간 노출시 리본의 부식으로 인한 열화가 흔히 관찰된다. 이러한 부식현상으로 인하여 리본과 태양전지의 접합이 약해져 접촉저항이 증가하고, 또한 리본 자체의 직렬 저항이 증가하게 되어 태양전지의 전압 전류 곡선에서 충진률 손실로 출력이 저하된다. 본 논문에서는 리본의 부식을 완화시킬 수 있는 방법으로 희생양극법을 이용하여 순수 알루미늄 및 아연, 알루미늄, 아연 그리고 마그네슘의 합금을 이용한 5가지 희생양극 소재의 부식에 의한 열화 저감을 연구하였다. 전기화학적 방법으로 희생양극 소재의 개방회로 전위와 폐쇄회로 전위를 측정하였고, 포텐시오다이나믹 분극 곡선을 측정하고, 영저항전류계를 이용하여 리본과 소재간의 갈바닉 전류를 측정하였다. 또한, 아세트산과, NaCl에 리본과 희생양극 소재의 부착 전후의 침지시험과 4셀 미니모듈로 제작한 후 1500시간 고온고습 시험 전후 출력을 평가하였다. 그 결과 Al-3Mg와 Al-3Zn-1Mg의 희생양극 소재가 부식속도가 느리고, 출력저하를 저감시킬 뿐만 아니라 장기 안정성에도 효과적인 것으로 평가된다.

• 한국표면공학회지
• /
• 제48권2호
• /
• pp.68-72
• /
• 2015

The corrosion behavior of metals and alloys for the safety of offshore structures in seawater was investigated for the application of sacrificial anodes. The experiments were focused on the polarization behaviors and the surface morphology of each metal after experiments. Pure Zn, pure Al (Al1050), Al alloys (Al5052, Al6061), Mg alloys (AZ31, AZ91D) and steel (SCM440) were assessed in 3.5% sodium chloride solution by means of potentiodynamic polarization to verify the galvanic corrosion potential ($E_{couple}$). Potentiostat plots were plotted to compare the surface and corrosion current density ($i_{couple}$) of metals as sacrificial anodes in seawater to protect steel alloy as a cathode. Al alloys showed the best performance as a sacrificial anode, on the other hand, Mg alloys showed overprotection behavior. The surface morphologies of sacrificial anodes were observed by FESEM and compared.

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.105-116
• /
• 2011

Ships and offshore structures are exposed to harsh marine environments, and maintenance and repair are becoming increasingly important to the industry and the economy. The major corrosion phenomenons of metals and alloys in marine environment are pitting corrosion, stress corrosion cracking, crevice corrosion, fatigue corrosion, cavitation-erosion and etc. due to the effect of chloride ions and is quite serious. Methods of protection against corrosion can generally be divided into two groups: anodic protection and cathodic protection. Anodic protection is limited to the passivity characteristics of a material in its environment, while cathodic protection can apply methods such as sacrificial anode cathodic protection and impressed current cathodic protection. Sacrificial anode methods using Al and Zn alloys are widely used for marine structures and vessels intended for use in seawater. Impressed current cathodic protection methods are also widely used in marine environments, but tend to generate problems related to hydrogen embrittlement caused by hydrogen gas generation. Therefore, it is important to the proper maintenance and operation of the various corrosion protection systems for ship in the harsh marine environment.

• 한국표면공학회지
• /
• 제39권1호
• /
• pp.25-34
• /
• 2006

Al-Mg alloy, an open rack vaporizer(ORV) material was reported to be corroded in seawater environments though the ORV material was coupled to thermally sprayed Al-Zn alloy functioning a sacrificial anode. In addition, the corrosion behavior based on the calculated corrosion potential did not match the observed corrosion behavior. Hence, the goal of this study is to get better understanding on Al or Al-Mg alloy coupled to Al-Zn alloy and to provide the calculated corrosion potential representing the corrosion behavior of the ORV material by immersion test, electrochemical tests, and calculation of corrosion and galvanic potential. The corrosion potentials of Al and Al alloys also depended on alloying element as well as surface defects. The corrosion potentials of Al and Al-Mg alloy were changed with time. In the meantime, the corrosion potentials of Al-Zn alloys were not. The corrosion rates of Al-Zn alloys were exponentially increased with zinc contents. The phenomena were explained with the stability of passive film proved by passive current density depending on pH and confirmed by the model proposed by McCafferty. Dissimilar material crevice corrosion (DMCC) test shows that higher content of zinc caused Al-Mg alloy corroded more rapidly, which was due to the fact that higher corrosion rate of Al-Zn makes [$H^+$] and [$Cl^-$] more concentrated within pit solution to corrode Al-Mg alloy. Considering electrochemical reactions within pit as well as bulk in the calculation gives better prediction on the corrosion behavior of Al and Al-Mg alloy as well as the capability of Al-Zn alloy for corrosion protection.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.343-348
• /
• 2015

In this paper, arc Zn thermal spray coating was carried out on the SS400 steel, and then various electrochemical characteristics and surface damage behavior of Zn thermal spray coating layer were analyzed. As the results, the potential of Zn thermal spray coating layer presented driving voltage above 300 mV compare to that of SS400 steel. The passivity characteristic in anodic polarization curve was not presented. It was adequate to as sacrificial anode material. In the surface damage after galvanostatic experiments, uniform corrosion tendency of Zn thermal spray coating layer was clearly observed with acceleration of the dissolution reaction. In conclusion, Zn thermal spray coating could be determined to represent the corrosion protection effect by stable sacrificial anodic cathodic protection method in seawater because it had sufficient driving voltage and uniform corrosion damage tendency for the SS400 steel.