• Korean Chemical Engineering Research
• /
• v.40 no.6
• /
• pp.741-745
• /
• 2002

Yttria-stabilized zirconia(YSZ) nanopowders were prepared by sol-gel method using zirconium-n-butoxide(ZNB) and yttrium nitrate as precursors. In addition, the effect of water content added during the hydrolysis reaction of ZNB was investigated on the phase composition and pore structure of the product powders. The phase composition of YSZ nanopowders with calcination temperatures showed the same trend, irrespective of $H_2O$ amounts added during the hydrolysis reaction of ZNB. All powders dried at $100^{\circ}C$ were amorphous and transformed to cubic phase at $400^{\circ}C$, which converted to tetragonal phase at $1,000^{\circ}C$. Monoclinic phase also appeared at $1,000^{\circ}C$. The powders showed the mixture of tetragonal and monoclinic phases from $1,000^{\circ}C$ to $1,400^{\circ}C$. The pore size distributions of the dried powders prepared with small amounts of water(less than or equal to $H_2O/ZNB=20$) showed mesopores, while those prepared with large amounts of water(greater than or equal to $H_2O/ZNB=50$) exhibited micropores.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.755-760
• /
• 1996

Sol-gel processing was used to prepare PZT fibers. Titanium isopropoxide Zirconium n-butoxide and lead acetate trihydrate were used as starting materials and TEA(triethanolamine) was added to form stabilized Pb-Ti-Zr complex alkoxide, Effects of catalysts and various solvents on the state of precursor sol gelation reaction fiber spinnability pyrolysis and crystallization were also investiated.

• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.617-625
• /
• 1995

In order to reduce reflectance of soda-lime glass having average reflectance of 7.35% and refractive index of 1.53, single (SiO2), double (SiO2/20SiO2-80ZrO2), and triple (SiO2/ZrO2/75SiO2-25ZrO2) layers were designed and fabricated on the glass substrate by Sol-Gel method. Stble sols of SiO2-ZrO2 binary system for antireflective (AR) coatings were synthesized with tetraethyl orthosilicate (TEOS) and zirconium n-butoxide as precursors and ethylacetoacetate (EAcAc) as a chelating agent in an atmosphere environment. Films were deposited on soda-lime glass at the withdrawal rates of 3~11 cm/min using the prepared polymeric sols by dip-coating and they were heat-treated at 45$0^{\circ}C$ for 10 min to obtain homogeneous, amorphous and crack-free films. In case of SiO2-ZrO2 binary system, refractive index of film increased with an increase of ZrO2 mol%. Designed optical constant of films could be obtained through varying the withdrawal rate. In the visible region (380~780nm), reflectance was measured with UV/VIS/NIR Spectrophotometer. Average reflectances of the prepared single-layer [SiO2 (n=1.46, t=103nm)], double-layer [SiO2 (n=1.46, t=1-4nm)/20SiO2-80ZrO2 (n=1.81, t=82nm)], and triple-layer [SiO2 (n=1.46, t=104nm)/ZrO2 (n=1.90, t=80nm)/75SiO2-25ZrO2 (n=1.61, t=94 nm)] were 4.74%, 0.75% and 0.38%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.95-105
• /
• 1995

Ceria(CeO2) stabilized zirconia(CeSZ) sol was synthesized with zirconium n-butoxide Zr(OC4H9)4 and cerium nitrate hexahydrate Ce(NO3)3.6H2O as precursors and ethylacetoacetate(EAcAc) as a chelating agent under atmosphere. CeSZ films were deposited on AISI 304 stainless steel using the prepared polymeric sol by dipcoating and the coating characteristics were investigated by XRD, ellipsometry, scratch test and SEM. The CeSZ film began to crystallize from amorphous to tetragonal phase at 40$0^{\circ}C$ and it was not converted into monoclinic phase up to 100$0^{\circ}C$ by the addition of 16mol% CeO2 as a stabilizer which could suppress phase transformation of zirconia. The CeSZ films were prepared by varying the EAcAc contents and the cncentration of CeSZ sol and measured the thickness and refractive index. From these results, it was found that the EAcAc contents and concentration of CeSZ coating sol evidently affect the densification of CeSZ film. The CeSZ film coated with 0.4M CeSZ sol and heat-treated at $600^{\circ}C$ for 10min had thickness of 50nm and 17% porosity. The CeSZ film on 304 stainless steel effectively acted as a protective layer against oxidation up to 80$0^{\circ}C$ and had superior corrosion resistance in 25% H2SO4 solution for 4.5 hrs.